CN202213255U - Glass fiber substrate PVC (Poly Vinyl Chloride) printing wall plastic - Google Patents
Glass fiber substrate PVC (Poly Vinyl Chloride) printing wall plastic Download PDFInfo
- Publication number
- CN202213255U CN202213255U CN2011202299452U CN201120229945U CN202213255U CN 202213255 U CN202213255 U CN 202213255U CN 2011202299452 U CN2011202299452 U CN 2011202299452U CN 201120229945 U CN201120229945 U CN 201120229945U CN 202213255 U CN202213255 U CN 202213255U
- Authority
- CN
- China
- Prior art keywords
- pvc
- layer
- glass fiber
- fiber substrate
- printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
The utility model relates to glass fiber substrate PVC (Poly Vinyl Chloride) printing wall plastic which consists of a surface UV (ultraviolet) processing layer, a PVC printing layer, a substrate coating layer and a bottom back composite layer from top to bottom, wherein the surface UV processing layer is laid on the PVC printing layer; and the PVC printing layer, the substrate coating layer and the bottom back composite layer are connected through hot pressing. Compared with the prior art, the glass fiber substrate PVC printing wall plastic has higher size stability, stronger pollution tolerance, and is environmental-friendly, flame-retardant, corrosion-resistant and mouldproof, and has clearer and more natural pattern and wider applicability; and the defects that the existing wallpaper has low breadth, is easy to go mouldy, is easy to age and discolor, is difficult to clean and has poor fire resistance, and that the existing textile wall paper is easy to go mouldy, is difficult to clean, has poor fire resistance and the like, can be all overcome, so that the glass fiber substrate PVC printing wall plastic can be widely applied to the public places such as a hospital, a school, an exhibition hall, a hotel and the like.
Description
Technical field
The utility model relates to a kind of wallpaper, especially relates to a kind of fiberglass substrate PVC printing wall and moulds.
Background technology
Mostly wall covering material product in the market is wallpaper, wall paper, decorative panel, and it is functional, all there is defective in various degree in usability.Show mainly that moisture-proof is poor, resistance to soiling is poor, poor dimensional stability, poor fire, service life are short etc.The utility model relates to an improvement fiberglass substrate PVC wall and moulds; PVC is coated with the method for scraping, PVC print process, three kinds of technologies of PVC composite algorithm organically combines, this method is higher than other process products made thereby dimensional stabilitys, resistance to soiling is stronger, more clear and natural, applicability are wider for environmental protection flame retardant, anticorrosion mildew-resistant, pattern.
The utility model content
The purpose of the utility model be exactly provide in order to overcome the defective that above-mentioned prior art exists that a kind of stability is higher, resistance to soiling is stronger, more clear and natural, fiberglass substrate PVC printing wall that applicability is wider are moulded for environmental protection flame retardant, anticorrosion mildew-resistant, pattern.
The purpose of the utility model can realize through following technical scheme:
A kind of fiberglass substrate PVC printing wall is moulded; It is characterized in that; This wall is moulded to be coated with by surperficial UV processing layer, PVC printed layers, base material and is scraped layer and back of the body composite bed in the end constitutes from top to bottom; Described surperficial UV processing layer is laid on the PVC printed layers, and PVC printed layers, base material are coated with scrapes layer and end back of the body composite bed connects through hot pressing.
Described surperficial UV processing layer is a layer of polyurethane.
Described PVC printed layers thickness is 0.1~0.2mm.
Described base material is coated with scrapes layer for being coated with the glass layer of PVC thickener.
The thickness of back of the body composite bed of the described end is 1~4mm.
The polyvinyl chloride resin of the back of the body composite bed of the described end and the hot pressing composite bed of calcium carbonate.
Compared with prior art, the utility model dimensional stability is higher, resistance to soiling is stronger, more clear and natural, applicability are wider for environmental protection flame retardant, anticorrosion mildew-resistant, pattern, and it is narrow to overcome existing wallpaper fabric width; Easy mouldy, be prone to weather stain, be difficult for cleaning; Poor fire and existing wall paper are prone to mouldy; Be difficult for to clean, shortcomings such as poor fire, thus can extensive use hospital, the public place of school, exhibition center, hotel etc.
Description of drawings
Fig. 1 is the structural representation of the utility model.
1 scrapes layer, 4 and is that the end carries on the back composite bed for base material is coated with for PVC printed layers, 3 for surperficial UV processing layer, 2 among the figure.
The specific embodiment
Below in conjunction with accompanying drawing and specific embodiment the utility model is elaborated.
A kind of fiberglass substrate PVC printing wall is moulded; Its structure is as shown in Figure 1, and this wall is moulded to be coated with by surperficial UV processing layer 1, PVC printed layers 2, base material and scraped layer 3 and end back of the body composite bed 4 constitutes from top to bottom, and surperficial UV processing layer 1 is laid on the PVC printed layers 2; PVC printed layers 2, base material are coated with scrapes layer 3 and back of the body composite bed 4 in the end connects through hot pressing; Surface UV processing layer 1 is a layer of polyurethane, and PVC printed layers 2 thickness are 0.1mm, and the end thickness of back of the body composite bed 4 is 1mm.
The manufacturing approach that fiberglass substrate PVC printing wall is moulded may further comprise the steps:
(1) base material is coated with the manufacturing of scraping layer
A, get the raw materials ready according to following component and content:
PVC paste resin (PVC) 100kg, diisononyl phthalate (DINP) 65kg, calcium carbonate 100kg, stabilizing agent 3kg, thinner 15kg, titanium white powder 3kg, fire retardant 7kg; Wherein stabilizing agent adopts zinc stearate; Thinner is that PVC sticks with paste thinner TXIB, and fire retardant is TCEP;
B, above-mentioned raw materials is dropped into the high speed dispersor high speed by prescription stir 10min; Change stirring at low speed 8min then over to; Vacuumizing and exhausting while stirring; The mixed PVC thickener that obtains is squeezed in the high-order storage vat through air pump, and glass fibre is advanced being coated with on the kerf, and the PVC thickener leans on ball valve control flow to be evenly coated on the glass fibre being coated with cutter position; The glass fibre that coats the PVC thickener gets into and to cool off after the gel roller is heated as gel state, gets into the 12M baking oven then and plastifies the back cooling and promptly obtain base material and be coated with and scrape layer;
(2) manufacturing of end back of the body composite bed
A, get the raw materials ready according to following component and content:
Corvic (PVC) 100kg, calcium carbonate 150kg, stabilizing agent zinc stearate 3kg, diisononyl phthalate (DINP) 35kg, titanium white powder 10kg, fire retardant MCA 7kg;
B, feed intake according to prescription and to mix in high-speed mixer, utilize then and roll the turbine plasticizing, plasticization temperature is controlled to be 155 ℃; Adopt filter to filter the impurity of removing wherein again, filtration temperature is controlled to be 165 ℃, through four-roll calender calendering formation and embossing; The temperature of No. 1 roller of four-roll calender is 178 ℃, and the temperature of No. two rollers is 178 ℃, and the temperature of No. three rollers is 175 ℃; The temperature of No. four rollers is 173 ℃, gets after the cooling cutting edge and carries on the back composite bed on earth;
(3) the film intaglio printing of PVC printed layers
Be the white PVC film of 0.1mm is printed out different colours, decorative pattern through version roller, printing ink on 5 look intaglio plate printing machines pattern with the ready-made thickness of calender, promptly obtain the PVC printed layers after the drying;
(4) hot pressing is compound
PVC printed layers, base material be coated with scrape layer and back of the body composite bed in the end places on the MULTILAYER COMPOSITE machine,, obtain fiberglass substrate PVC printing wall and mould semi-finished product through preheating, flattening, applying, refrigerating work procedure;
(5) surperficial UV handles
Mould half-finished upper surface at fiberglass substrate PVC printing wall and be coated with and tie up one deck polyurethane coating, and solidify through ultraviolet equipment, the thermal stress cancellation element, the cooling rolling obtains fiberglass substrate PVC wall and moulds.
A kind of fiberglass substrate PVC printing wall is moulded; Be coated with by surperficial UV processing layer, PVC printed layers, base material and scrape layer and back of the body composite bed in the end constitutes from top to bottom; Described surperficial UV processing layer is laid on the PVC printed layers, and PVC printed layers, base material are coated with scrapes layer and end back of the body composite bed connects through hot pressing, and wherein surperficial UV processing layer is a layer of polyurethane; PVC printed layers thickness is 0.2mm, and end back of the body composite bed thickness is 4mm.
Claims (5)
1. a fiberglass substrate PVC printing wall is moulded; It is characterized in that; This wall is moulded to be coated with by surperficial UV processing layer, PVC printed layers, base material and is scraped layer and back of the body composite bed in the end constitutes from top to bottom; Described surperficial UV processing layer is laid on the PVC printed layers, and PVC printed layers, base material are coated with scrapes layer and end back of the body composite bed connects through hot pressing.
2. a kind of fiberglass substrate PVC printing wall according to claim 1 is moulded, and it is characterized in that described surperficial UV processing layer is a layer of polyurethane.
3. a kind of fiberglass substrate PVC printing wall according to claim 1 is moulded, and it is characterized in that described PVC printed layers thickness is 0.1~0.2mm.
4. a kind of fiberglass substrate PVC printing wall according to claim 1 is moulded, and it is characterized in that, described base material is coated with scrapes layer for being coated with the glass layer of PVC thickener.
5. a kind of fiberglass substrate PVC printing wall according to claim 1 is moulded, and it is characterized in that, the thickness of back of the body composite bed of the described end is 1~4mm.