CN202000036U - Anti-microbial hollow PET (Polyethylene Terephthalate) fiber - Google Patents
Anti-microbial hollow PET (Polyethylene Terephthalate) fiber Download PDFInfo
- Publication number
- CN202000036U CN202000036U CN2010206823086U CN201020682308U CN202000036U CN 202000036 U CN202000036 U CN 202000036U CN 2010206823086 U CN2010206823086 U CN 2010206823086U CN 201020682308 U CN201020682308 U CN 201020682308U CN 202000036 U CN202000036 U CN 202000036U
- Authority
- CN
- China
- Prior art keywords
- fiber
- pet
- polyethylene terephthalate
- utility
- hollow shape
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model relates to an anti-microbial hollow PET (Polyethylene Terephthalate) fiber, which is characterized in that the cross section of the fiber is hollow, the ratio of inter diameter and outer diameter is 1:3, and the fiber denier number is 1-5 deniers. The fiber has the advantages that the technique process is simple, the existing devices can be used to carry out production, the effectiveness is enhanced, and the application range of the fiber is wide.
Description
[technical field]
The utility model relates to the functional fibre field, specifically, is a kind of antibiotic hollow shape PET fiber.
[background technology]
At present, PET industry from 21 century production capacity sharply increase, present domestic polyester production capacity is above 2,000 ten thousand tons/year, but the utilization of capacity is very low, cost of material height, added value of product are hanged down and are caused many reasons such as the finished product price is low to cause numerous polyester losses of enterprise serious, the stop device of much having to close, in this case, Development and Production high added value functional polyester product, energy saving and cost lowering become the theme of numerous enterprises Future Development.On the other hand, along with the raising of social life level, people are more and more higher to the requirement of clothing comfortableness, and progress of science and technology also provides possibility for the improvement of comfort of fabric energy.
Polyester fiber is the first kind of synthetic fiber, and its output accounts for more than 80% of chemical fibre total output, because of its good cost performance is widely used in garment material and other non-field of taking.Yet the functional polyalkylene ester fiber becomes people's research focus, thereby improves the added value of traditional fibre.And the exploitation of antibiotic doughnut has been complied with above-mentioned trend just and has been launched.
[utility model content]
The purpose of this utility model is the shortcoming of customer service prior art, and a kind of antibiotic hollow shape PET fiber is provided.
For realizing above purpose, the technical solution adopted in the utility model is:
A kind of antibiotic hollow shape PET fiber, this fiber is by antibacterial matrices and PET section, and blend is after the hollow spinneret melt spinning makes, and the mass percent of material component is: antibacterial matrices is 1～10%, and the mass fraction of PET is 90～99%;
Described fiber cross section is a hollow shape;
The ratio of the interior external diameter of described fiber is 1: 3;
Described fiber Denier was 1～5 dawn;
Described antibacterial matrices is a nano silver antibacterial material, the white plates particle; Antiseptic content: 85%; Fusing point: 140 ℃; Decomposition temperature: 310 ℃; Products characteristics: possess good dispersiveness;
The good effect of a kind of antibiotic hollow shape PET fiber of the utility model is:
(1) technological process of the present utility model is simple, can produce at existing equipment, increases the benefit;
(2) product purpose of the present utility model is extensive.
[description of drawings]
Fig. 1 cross-sectional structure schematic diagram of the present utility model.
[specific embodiment]
Below in conjunction with accompanying drawing the utility model is described further.
Embodiment 1:
See also accompanying drawing 1, a kind of antibiotic hollow shape PET fiber, the mass percent of material component is: antibacterial matrices is 3%, the mass fraction of PET is 97%, antibacterial matrices and PET section are mixed earlier, carry out spinning by the technology of melt spinning, spinnerets is the hollow spray filament plate; Long filament is carried out the fiber that required specification was processed and be cut into to boundling, drawing-off, two dimension or three dimensional coil crimp;
The ratio of the interior external diameter of described fiber is 1: 3.
The dawn number of the fiber that finally makes was 1 dawn.
Embodiment 2:
See also accompanying drawing 1, a kind of antibiotic hollow shape PET fiber, the mass percent of material component is: antibacterial matrices is 6%, the mass fraction of PET is 94%; Antibacterial matrices and PET section are mixed earlier, carry out spinning by the technology of melt spinning, spinnerets is the hollow spray filament plate; Long filament is carried out the fiber that required specification was processed and be cut into to boundling, drawing-off, two dimension or three dimensional coil crimp;
The ratio of the interior external diameter of described fiber is 1: 3.
The dawn number of the fiber that finally makes was 3 dawn.
Embodiment 3:
See also accompanying drawing 1, a kind of antibiotic hollow shape PET fiber, the mass percent of material component is: antibacterial matrices is 9%, the mass fraction of PET is 91%, antibacterial matrices and PET section are mixed earlier, carry out spinning by the technology of melt spinning, spinnerets is the hollow spray filament plate; Long filament is carried out the fiber that required specification was processed and be cut into to boundling, drawing-off, two dimension or three dimensional coil crimp;
The ratio of the interior external diameter of described fiber is 1: 3.
The dawn number of the fiber that finally makes was 5 dawn.
The above only is a preferred implementation of the present utility model; should be pointed out that for those skilled in the art, under the prerequisite that does not break away from the utility model design; can also make some improvements and modifications, these improvements and modifications also should be considered as in the protection domain of the present utility model.
Claims (3)
1. an antibiotic hollow shape PET fiber is characterized in that, described fiber cross section is a hollow shape.
2. a kind of antibiotic hollow shape PET fiber as claimed in claim 1 is characterized in that the ratio of the interior external diameter of described fiber is 1: 3.
3. a kind of antibiotic hollow shape PET fiber as claimed in claim 1 is characterized in that described fiber Denier was 1～5 dawn.