CN201863438U - Multiplayer large-area titanium and multi-metal explosive clad plate - Google Patents
Multiplayer large-area titanium and multi-metal explosive clad plate Download PDFInfo
- Publication number
- CN201863438U CN201863438U CN2010205901143U CN201020590114U CN201863438U CN 201863438 U CN201863438 U CN 201863438U CN 2010205901143 U CN2010205901143 U CN 2010205901143U CN 201020590114 U CN201020590114 U CN 201020590114U CN 201863438 U CN201863438 U CN 201863438U
- Authority
- CN
- China
- Prior art keywords
- plate
- titanium
- compound
- carbon steel
- cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a multiplayer large-area titanium and multi-metal explosive clad plate, which consists of an explosive clad baseplate and a compound plate, wherein the baseplate is a carbon steel plate with the thickness of 10mm-120mm, the compound plate is a plate with four layers, and comprises a titanium plate which is arranged at the lower surface of the carbon steel plate and an aluminium plate, a leadplate and a titanium plate which are sequentially arranged on the upper surface of the carbon steel plate, the thicknesses of the titanium plate, the aluminium plate and the leadplate are between 2mm-14mm, and the cross section of the compound surface of every two plates is combined in a metallurgical way into a toothed shape. The explosive clad plate disclosed by the utility model has large plate width, more layers, good performance, high combination strength, light weight, wear resistance, no welding and convenience in installation, a series of performance requirements of users on temperature and pressure resistance, corrosion resistance and the like are met, the rare metals are also saved in China, so the sustainable development is benefited. The cross section of the compound surface of the base plate and the compound plate is combined in a metallurgical way into a toothed shape, and the combination strength is high.
Description
Technical field
The utility model belongs to the composite plate technical field, relates to big width of cloth titanium of a kind of multilayer and multiple metallic explosive composite plate.
Background technology
Titanium belongs to rare metal, has characteristics such as elevated temperature strength is good, good corrosion resistance, and titanium also has plasticity, and the percentage elongation of high purity titanium can reach 50%-60%, and the contraction percentage of area can reach 70%-80%, but intensity is low, should not make structural material.Because titanium is non-renewable, promptly is subjected to the restriction of material and price, so guaranteeing not reduce under the situation of service life and performance the industrial composite plates that adopt titanium and multiple metal more.And the titanium composite plate has also solved the problem of intensity, and titanium and other metal composite are in the same place, and forms the structure of multilayer, can improve the intensity of titanium greatly, significantly reduces its plasticity.Existing titanium composite plate, can only obtain the small size titanium composite plate of layer 2-3 by the method for direct rolling composite plate (also claiming Pressure Welding or Solid-State Welding), yet, adopt rolling method can not make the big face width of cloth, number of plies composite plate how, it has the shortcoming that little, the compound number of plies of the plate width of cloth is few and performance is not high, can not satisfy the production needs.
Summary of the invention
The purpose of this utility model provides big width of cloth titanium of a kind of multilayer and multiple metallic explosive composite plate, and the plate width of cloth is big, the number of plies is many, performance is good.
The technical scheme that the utility model adopted is, big width of cloth titanium of multilayer and multiple metallic explosive composite plate, form by compound substrate and the compound plate of blast, wherein, substrate is the carbon steel sheet of thickness 10mm-120mm, and compound plate is 4 laminates, and compound plate is included in the titanium plate of carbon steel sheet lower surface setting and the aluminium sheet that sets gradually at the carbon steel sheet upper surface, stereotype, titanium plate, the thickness of titanium plate, aluminium sheet, stereotype is 2 mm-14mm, and the cross section of the composite surface between each laminate is the dentation metallurgical binding.
Feature of the present utility model also is,
Substrate and compound plate unflatness≤2mm/m, oxygen content≤0.5%, the plate width of cloth are 30 m
2-45m
2
Big width of cloth titanium of the utility model multilayer and multiple metallic explosive composite plate, the plate width of cloth is big, the number of plies is many, performance is good, bond strength is high, in light weight, wear-resistant, does not need welding, simple installation.The cross section of composite surface is the dentation metallurgical binding between substrate and the compound plate, the bond strength height.Can not only satisfy people it is possessed a series of performance requirements such as high temperature resistant, high pressure, anticorrosive, radiation proof, and save national rare metal, help sustainable development.This product is widely used in China's electric power, chemical industry and nuclear industry field.
Description of drawings
Fig. 1 is the structural representation of the utility model explosive clad plate.
Among the figure, 1. carbon steel sheet, 2. titanium plate, 3. aluminium sheet, 4. stereotype.
The specific embodiment
Below in conjunction with the drawings and specific embodiments the utility model is elaborated.
The structure of big width of cloth titanium of the utility model multilayer and multiple metallic explosive composite plate, as shown in Figure 1, form by compound substrate and the compound plate of blast, wherein, substrate is the carbon steel sheet 1 of thickness 10mm-120mm, and compound plate is 4 laminates, compound plate is included in the titanium plate 2 that carbon steel sheet 1 lower surface is provided with, and the aluminium sheet 3, stereotype 4, the titanium plate 2 that set gradually at carbon steel sheet 1 upper surface, the thickness of aluminium sheet 3, stereotype 4, titanium plate 2 is 2mm-14mm, and the cross section of the composite surface between each laminate is the dentation metallurgical binding.
Big width of cloth titanium of the utility model multilayer and multiple metallic explosive composite plate, substrate and compound plate adopt the sheet material of unflatness≤2mm/m, and substrate, compound plate oxygen content≤0.5%, the thickness of substrate are 10 mm-120mm, and the thickness that compound plate is every layer is 2mm-14mm; The plate width of cloth of substrate and compound plate is 30 m
2-45m
2
Big width of cloth titanium of the utility model multilayer and multiple metallic explosive composite plate, be to combine by the compound mode of exploding, earlier on the ground with the substrate horizontal positioned, on substrate, set up compound plate, promptly the outstanding substrate top 10mm-12mm that is placed on of compound plate-titanium plate is highly located by the fulcrums such as tiny copper of laying some, on compound plate, be paved with explosive, plugging the primer core explodes compound, then with compound good and to carry out the second time through the composite of aligning polishing as base material compound, the base material steel faces up, all the other each piece compound plates of overlapping placement on this base material, support between each plate, laying the capacity explosive on the superiors' compound plate carries out compound, can directly make five layers of explosive clad plate like this, the compound low explosion velocity rock bulking ammonium nitrate explosive of choosing that explodes, explosive thickness is 35 mm-40mm, adopt limit portion to detonate then, each laminate is combined with each other by the formed TRANSIENT HIGH TEMPERATURE high pressure of the Mohaupt effect of explosive.
By check, titanium that makes and multiple metallic explosive composite plate are in conjunction with rate 99.9%-100%; Shear strength Jb180-230Mpa is greater than setting>200 Mpa of the corresponding Nippon Standard JISG160 in the world; Unflatness :≤2mm/m, individual face width of cloth reaches 30m
2-45m
2Can not only satisfy people through the metal material after compound and it be possessed a series of performance requirements such as high temperature resistant, high pressure, anticorrosive, radiation proof, and save national rare metal, help sustainable development.
Claims (2)
1. big width of cloth titanium of a multilayer and multiple metallic explosive composite plate, it is characterized in that, form by compound substrate and the compound plate of blast, wherein, described substrate is the carbon steel sheet (1) of thickness 10mm-120mm, described compound plate is 4 laminates, compound plate is included in the titanium plate (2) that carbon steel sheet (1) lower surface is provided with and the aluminium sheet (3) that sets gradually at carbon steel sheet (1) upper surface, stereotype (4), titanium plate (2), the thickness of described titanium plate (2), aluminium sheet (3), stereotype (4) is 2 mm-14mm, and the cross section of the composite surface between each laminate is the dentation metallurgical binding.
2. big width of cloth titanium of multilayer according to claim 1 and multiple metallic explosive composite plate is characterized in that described substrate and compound plate unflatness≤2mm/m, oxygen content≤0.5%, the plate width of cloth are 30 m
2-45m
2