The radium-shine paper of a kind of transfer frosted
Technical field
The utility model relates to the wrapping paper field, the radium-shine cigarette wrapping paper of specifically a kind of transfer frosted.
Background technology
With regard to cigarette package, mostly high-grade cigarette is that the packing of requirement product has the visual effect of comparison grace, common white card, gold and silver card, radium-shine paperboard are widely used, the form of expression is more single, be difficult to realize some special product effect, as semi-transparent half of similar porcelain and jadeware mute visual effect; Offset printing dumb paint China ink also is difficult to embody the visual effect of product in the typography, though and means such as silk-screen snowflake, fission can embody the visual effect of product, but means are more single, and ink for screen printing is difficult to satisfy cigarette wrapping paper to the residual requirement of VOCs (volatile organic compounds).
The utility model content
Technical problem to be solved in the utility model is to overcome the defective that above-mentioned prior art exists, provide a kind of surface to have the wrapping paper of frosted structure at common radium-shine paper, make the utility model visually have texture and third dimension, make the level of product abundanter.
For this reason, the utility model adopts following technical scheme: the radium-shine paper of a kind of transfer frosted, comprise ply of paper, ply of paper is composite transferring glue layer, aluminium lamination and release layer successively from inside to outside, mold pressing one laser information layer on the described release layer, the outer surface that it is characterized in that described laser information layer is a frosting, and frosting makes radium-shine paper have more third dimension and texture.The used ply of paper of the utility model is a common paper, as art post paperboard etc.
The utility model is made the physical arrangement of frosted by mechanical mode on the PET basement membrane, be coated with release layer, molding laser Information Level then on PET frosted film, aluminize, series of process step such as compound, transfer obtains.
As the further of technique scheme improved and replenish, the utility model is taked following technical measures:
The above-mentioned radium-shine paper of transfer frosted, the outer surface of laser information layer is coated with a layer of varnish, changes the color of paper as required by the mode of coating varnish, as gold.
The above-mentioned radium-shine paper of transfer frosted, the thickness of release layer is the 2-3 micron, also can adjust thickness according to the actual needs.
The utility model has increased the frosted structure on the basis of common radium-shine paper, visually have texture and third dimension, makes the final products level abundanter, has realized the semi-transparent half texture effect of making mute of porcelain and jadeware; Solved the residual defective problem of VOCs that ink for screen printing, offset ink exist simultaneously.
Below in conjunction with specification drawings and specific embodiments the utility model is further described.
Description of drawings
Fig. 1 is the structural representation of the utility model embodiment 1.
Fig. 2 is the vertical view of Fig. 1.
Fig. 3 is the structural representation of the utility model embodiment 2.
The specific embodiment
Embodiment 1
The radium-shine paper of transfer frosted as shown in Figure 1, ply of paper 1 is composite transferring glue layer 2, aluminium lamination 3 and release layer 4 (being dope layer) successively from inside to outside, the thickness of aluminium lamination is the 0.036-0.04 micron, the thickness of release layer is the 2-3 micron, mold pressing one laser information layer 5 on the release layer 4, the outer surface of laser information layer 5 is frosting 6 (see figure 2)s.
Preparation method of the present utility model is: earlier making the frosted structure at the PET basement membrane becomes PET frosted film, on PET frosted film, be coated with then release layer, laser molding, vacuum aluminum-coated, coating transfer glue, compound with paper, shift and peel off the series of process step and obtain.
Embodiment 2
As shown in Figure 3, embodiment 2 is that with the difference of embodiment 1 embodiment 2 is coated with the layer of varnish 7 that a thickness is the 1.5-2.5 micron at the outer surface of laser information layer 5 again.
The above only is preferred embodiment of the present utility model, is not structure of the present utility model is done any pro forma restriction.Every foundation technical spirit of the present utility model all falls in the protection domain of the present utility model any simple modification, equivalent variations and modification that above embodiment did.