CN1994726A - Production method of floor covering with illuminant colorful spots - Google Patents
Production method of floor covering with illuminant colorful spots Download PDFInfo
- Publication number
- CN1994726A CN1994726A CN 200610161645 CN200610161645A CN1994726A CN 1994726 A CN1994726 A CN 1994726A CN 200610161645 CN200610161645 CN 200610161645 CN 200610161645 A CN200610161645 A CN 200610161645A CN 1994726 A CN1994726 A CN 1994726A
- Authority
- CN
- China
- Prior art keywords
- point
- spontaneous
- deals
- illuminant
- floor covering
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a method for preparing colorful lighting floor leather, wherein it comprises that: first preparing lighting colorful points; distributing the points via distributor to the surface of leather base fused and protruded by protrude machine; hot wind machine fuses and compresses it; then cooling, drawing, cutting and coiling into the leather. Said point is formed by 100 deals polychloroethylene resin, 20-30 deals of powder accumulation lighting material, 35-40 deals of dioctyl phthalate, 1. 5-2. 5 deals of liquid barium cadmium zinc, 0.35-0.4 deals silane coupler and some paints. And its production comprises that: mixing said materials into high-speed mixer; adding mixture into protrude machine via sheet mould to be drawn; breaking the sheet in breaker; screening into point. The inventive leather can receive ultraviolet light to light at night.
Description
Technical field
The present invention relates to a kind of flooring laminate, be specifically related to a kind of preparation method of floor covering with illuminant colorful spots.Be mainly used in the laying on automobile, train and steamer floor, also can be used for other building and make indoor floor.
Background technology
Before the present invention made, what be used in the past that the auxilliary material of establishing automobile, train and steamer floor adopts all was common flooring laminate.In being travelled in the way in traffic such as automobile, when its peripheral environment changes, as night running or when daytime, automobile passed through tunnel etc., because common flooring laminate can be not luminous, cause indoor very dark, can influence passenger's vision like this, again can influence other passenger and have a rest if turn on the room light lamp this moment.
The objective of the invention is to overcome above-mentioned deficiency, provide can receive ultraviolet ray irradiation a kind of daytime and hold light, can self send the preparation method of the floor covering with illuminant colorful spots of colored radiance night.
The object of the present invention is achieved like this: a kind of preparation method of floor covering with illuminant colorful spots; it is characterized in that it is to prepare spontaneous honorable point earlier; then spontaneous honorable point is dialled the flooring laminate substrate surface that spreads the molten condition of extruding through the extruder die head with grain scattering machine; the fusion of reusable heat blower fan blowing hot-air, embossing are after floor covering with illuminant colorful spots is made in cooling, traction, cutting, rolling
Described spontaneous honorable point mainly is made up of the raw material of following weight portion:
100 parts of Corvics
The spontaneous material 20-30 of Powdered light accumulation type part
Dioctyl phthalate 35-40 part
Liquid barium cadmium zinc 1.5-2.5 part
Silane coupling agent 0.35-0.4 part
Dyestuff is an amount of
The preparation method of described spontaneous honorable point is:
Step 1, get Corvic, Powdered light storage type self luminous material, dioctyl phthalate, liquid barium cadmium zinc, silane coupling agent and dyestuff by proportioning, drop into the high speed kneader and stir, feeding sequence is thrown powder, back throw liq material earlier.
Step 2, the temperature of kneader is risen to 50-60 ℃, first stirring at low speed 2-3 minute, after uprise again speed be stirred to warm 90-110 ℃ in material can discharging to the cooling and stirring machine carry out cooling and stirring to material warm can pack below 45 ℃ standby.
Step 3, the material that will stir join extruder through the sheet die pulling-on piece.
Step 4, the sheet material that will draw are pulverized through pulverizer, and sieving, it is standby to generate color point.
The preparation method of floor covering with illuminant colorful spots of the present invention, described silane coupling agent is silane coupling agent SG-SI900.
The used Powdered light storage type self luminous material of the present invention is realized self light emission function by absorbing various visible lights, especially the shortwave light below 450 nanometers is had very strong absorbability.This material presents appearance colour own at Liang Chu, and the light of different colours is then sent in the dark place, presents the function of good low emergency lighting, sign and decoration.
Consider that spontaneous honorable point will have certain transparency ability luminous, therefore select for use dyestuff as colouring agent, consider the dyestuff non-refractory again, so will select that transparency is good for use, the Corvic of the degree of polymerization 700 of low-molecular-weight, low temperature moulding good (forming temperature 135-140 ℃) is as the base-material of coloured silk point; Because the use of pulverous heat stabilizer such as hard ester acid etc. can reduce the transparency of color point, thereby reduce the illumination effect of color point, therefore heat stabilizer adopts liquid barium cadmium zinc, consider the affinity that will strengthen luminescent material and resin to increase illumination effect, in coloured silk point material, added coupling agent.
The specific embodiment
Embodiment:
One, prepares color point
The dyestuff of step 1, the polyvinyl chloride resin powder 100kg that gets the degree of polymerization 700, the spontaneous material 25kg of Powdered light accumulation type, phthalic acid two sad 40kg, liquid barium cadmium zinc 2kg, silane coupling agent SG-SI900 0.375kg and color fastness 7-8 level is an amount of, dropping into high low speed kneader stirs, feeding sequence is thrown powder earlier, back throw liq material
Step 2, the temperature of kneader is risen to 60 ℃, first stirring at low speed 2 minutes, after uprise again speed be stirred to warm 90-110 ℃ in material can discharging to the cooling and stirring machine carry out cooling and stirring to material warm 45 ℃ can pack standby,
Step 3, the material that will stir join extruder through the sheet die pulling-on piece, and the thickness of pulling-on piece is 0.3mm,
Step 4, the sheet material (film) that will draw are pulverized through pulverizer, and it is standby to be screened into color point.
Two, the color point of preparation flooring laminate
With the flooring laminate raw material through high-speed mixer mixing, banbury banburying, extrude, pulverizing, single screw extrusion machine die head be extruded into the molten state sheet material, lining is non-woven fabric compounded at the back side of this molten state sheet material, color point is spread with spreader in the front, the fusion of air-heater blowing hot-air, embossing is again through cooling off, draw, cut, be wound into floor covering with illuminant colorful spots finished product warehouse-in.
Claims (2)
1, a kind of preparation method of floor covering with illuminant colorful spots; it is characterized in that it is to prepare spontaneous honorable point earlier; then spontaneous honorable point is dialled the flooring laminate substrate surface that spreads the molten condition of extruding through the extruder die head with grain scattering machine; the fusion of reusable heat blower fan blowing hot-air, embossing; after floor covering with illuminant colorful spots is made in cooling, traction, cutting, rolling
Described spontaneous honorable point mainly is made up of the raw material of following weight portion:
100 parts of Corvics
The spontaneous material 20-30 of Powdered light accumulation type part
Dioctyl phthalate 35-40 part
Liquid barium cadmium zinc 1.5-2.5 part
Silane coupling agent 0.35-0.4 part
Dyestuff is an amount of
The preparation method of described spontaneous honorable point is:
Step 1, get polyvinyl chloride resin powder, the spontaneous material of Powdered photic light accumulation type, dioctyl phthalate, liquid barium cadmium zinc, silane coupling agent and dyestuff by proportioning, drop into the high speed kneader and stir, feeding sequence is thrown powder earlier, back throw liq material,
Step 2, the temperature of kneader is risen to 50-60 ℃, first stirring at low speed 2-3 minute, after uprise again speed be stirred to warm 90-110 ℃ in material can discharging to the cooling and stirring machine carry out cooling and stirring to material warm can pack below 45 ℃ standby,
Step 3, the material that will stir join extruder through the sheet die pulling-on piece,
Step 4, the sheet material that will draw are pulverized through pulverizer, and sieving, it is standby to generate color point.
2, the preparation method of a kind of floor covering with illuminant colorful spots according to claim 1 is characterized in that described silane coupling agent is coupling agent SG-SI900.