CN1978560A - Ecological nano enamel paint - Google Patents
Ecological nano enamel paint Download PDFInfo
- Publication number
- CN1978560A CN1978560A CN 200510125930 CN200510125930A CN1978560A CN 1978560 A CN1978560 A CN 1978560A CN 200510125930 CN200510125930 CN 200510125930 CN 200510125930 A CN200510125930 A CN 200510125930A CN 1978560 A CN1978560 A CN 1978560A
- Authority
- CN
- China
- Prior art keywords
- enamel paint
- ecological nano
- ecological
- nano enamel
- nano
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
This invention discloses a kind of ecological nano enamel lacquer containing crude materials white the following mixture ratios: 10~60% of white cement 425#, 10~60% of calcium hydroxide, 10~50% of talcum powder, 10~50% of heavy calcium carbonate, 15~50% titanium white powder, 15~40% methyl cellulose, 0.2-10%. of neutral nano hydrophobing agent, 3-15%. of carboxymethyl hydroxyetheyl cellulose 0.2-10%. of MCP801, 0.2-10%. of rubber powder. The said ecological nano enamel lacquer in this invention is characteristic of high strength, crack resistance, corrosion resistance, scrub resistance and simple construction.
Description
Technical field
The present invention relates to a kind of dope for inner wall of architecture, particularly a kind of ecological nano enamel paint.
Background technology
At present, a lot of interior wall coatings are arranged on the market, as: putty powder, mainly have following defective in application: 1, intensity is relatively poor, and is not wear-resisting, easily comes off, not water-fastly easily go mouldy, what have is then not corrosion-resistant, and such coating bring very big inconvenience more or less all can for construction and life staying idle at home.
Summary of the invention
The invention solves the technical problem that prior art exists, provide that a kind of intensity is big, the ecological nano of cracking resistance, corrosion-resistant, scrubbing resistance and easy construction is enamel paint.
In order to achieve the above object, the technical scheme taked of the present invention is:
A kind of ecological nano enamel paint comprises following proportion raw material:
White cement 425
#: 10-60%, calcium hydroxide: 10-60%,
Talcum powder: 10-50%, water-ground limestone: 10-50%,
Titanium dioxide: 15-40%, methylcellulose gum: 0.2-10 ‰,
Neutral nano-sized hydrophobic agent: 3-15 ‰, methyl hydroxyethylcellulose: 0.2-10 ‰,
MCP801 rubber powder: 0.2-10 ‰
Preferred version of the present invention is: described talcous fineness is: the 300-800 order, and whiteness is: the 90-95 degree;
Preferred version of the present invention is: described water-ground limestone fineness is: the 300-800 order, and whiteness is: the 90-95 degree;
Preferred version of the present invention is: the viscosity of described methylcellulose gum is: 20,000-100,000 centipoises;
Preferred version of the present invention is: the viscosity of described methyl hydroxyethylcellulose is: 20,000-100,000 centipoises;
The present invention is owing to adopting above technical scheme, so have following characteristics:
1, select materials is convenient, and raw material of the present invention all is common commercially available material;
2, simple for production, manufacture craft of the present invention is simple;
3, result of use is good: ecological nano enamel paint of the present invention, and blade coating is accessible during construction, and grinability reaches 40%-70%; Have good water tolerance, water-fast 96 hours no abnormal; Have good alkali resistance, alkaline-resisting 48 hours no abnormal; Have very strong sticking power, after tested, standard state intensity reaches 0.65Mpa, and immersion back cohesive strength is 0.51Mpa.The present invention also has low temperature resistant characteristic, after tested, and-5 ℃ of freezing 4 hours no changes.
Embodiment
With reference to accompanying drawing embodiment, will be described in detail embodiment of the present utility model.
Embodiment 1
Ecological nano enamel paint comprises following proportion raw material:
White cement 425
#: 21%, calcium hydroxide: 28%,
Talcum powder: 12%, water-ground limestone: 18%,
Titanium dioxide: 19.5%, methylcellulose gum: 2 ‰,
Neutral nano-sized hydrophobic agent: 4 ‰, methyl hydroxyethylcellulose: 5 ‰,
MCP801 rubber powder: 4 ‰
Wherein, talcous fineness is: 800 orders, and whiteness is: 95 degree; The water-ground limestone fineness is: 800 orders, and whiteness is: 93 degree; The viscosity of described methylcellulose gum is 80,000 centipoises; The viscosity of described methyl hydroxyethylcellulose is: 50,000 centipoises;
Embodiment 2
Ecological nano enamel paint comprises following proportion raw material:
White cement 425
#: 40%, calcium hydroxide: 15%,
Talcum powder: 13%, water-ground limestone: 15%,
Titanium dioxide: 15.5%, methylcellulose gum: 1.5 ‰,
Neutral nano-sized hydrophobic agent: 5 ‰, methyl hydroxyethylcellulose: 3 ‰,
MCP801 rubber powder: 5.5 ‰
Wherein, talcous fineness is: 600 orders, and whiteness is: 90 degree; The water-ground limestone fineness is: 550 orders, and whiteness is: 92 degree; The viscosity of described methylcellulose gum is 3.5 ten thousand centipoises; The viscosity of described methyl hydroxyethylcellulose is: 5.5 ten thousand centipoises.
Ecological nano enamel paint of the present invention can add corresponding proportion raw material in the container, and stirring with stirrer gets final product.
Claims (5)
1, a kind of ecological nano enamel paint comprises following proportion raw material:
White cement 425
#: 10-60%, calcium hydroxide: 10-60%,
Talcum powder: 10-50%, water-ground limestone: 10-50%,
Titanium dioxide: 15-40%, methylcellulose gum: 0.2-10 ‰,
Neutral nano-sized hydrophobic agent: 3-15 ‰, methyl hydroxyethylcellulose: 0.2-10 ‰,
MCP801 rubber powder: 0.2-10 ‰.
2, ecological nano enamel paint according to claim 1 is characterized in that, described talcous fineness is: the 300-800 order, whiteness is: the 90-95 degree.
3, ecological nano enamel paint according to claim 1 is characterized in that, described water-ground limestone fineness is: the 300-800 order, whiteness is: the 90-95 degree.
4, ecological nano enamel paint according to claim 1 is characterized in that, the viscosity of described methylcellulose gum is: 20,000-100,000 centipoises.
5, ecological nano enamel paint according to claim 1 is characterized in that, the viscosity of described methyl hydroxyethylcellulose is: 20,000-100,000 centipoises.