CN1948005A - Method for partial metallization on paper - Google Patents
Method for partial metallization on paper Download PDFInfo
- Publication number
- CN1948005A CN1948005A CN 200510100280 CN200510100280A CN1948005A CN 1948005 A CN1948005 A CN 1948005A CN 200510100280 CN200510100280 CN 200510100280 CN 200510100280 A CN200510100280 A CN 200510100280A CN 1948005 A CN1948005 A CN 1948005A
- Authority
- CN
- China
- Prior art keywords
- film
- paper
- metallization
- utilize
- pattern
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A method for locally plating metal material onto paper as packing material includes such steps as preparing the designed characters and pattern on a chloroparaffin film, plating metal material, coating adhesive on a paper, attaching said film onto the adhesive layer on paper, and removing the film to make the metal plated characters and pattern to stay on paper.
Description
Technical field
The present invention relates to a kind of method of metallization, especially relate to a kind of method of partial metallization on paper, be mainly used in packaging material, but be not limited to this.
Background technology
In modern society, along with improving constantly that development of technology and people require, the packing instructions of commodity are also more and more higher, and the technology content of packing is also improving constantly.Simultaneously again because market economy perfect inadequately, also have some fake and forged phenomenons, particularly be worth on the product high, that profit is big at those, therefore being packaged in many times also needs to possess antiforge function, so that the consumer distinguishes easily, avoid buying counterfeit product.
Such as tobacco business, just often need the packing of comparison fineness, for the serious relatively counterfeit phenomenon in cigarette market, also there are the needs of the content that further develops skill in the packing of cigarette, to possess certain anti-fake effect.
The plating bronze printing belongs to material and as packaging material, prevails at present on the paper of special use, and such packing is sensuously more luxurious.But prior art has generally adopted the mode of spraying, and can only spray full size, make paper color pattern dullness can not form literal, pattern or the combination of the two of wishing appearance, can not satisfy the needs of attractive packages so fully, also be unfavorable for product false proof simultaneously.
The objective of the invention is to provide a kind of can be in the method for partial metallization on paper, thereby can utilize various proper metal materials, predetermined literal, pattern or the combination of the two plating are printed on the paper, the packaging material that such paper is done can be more attractive in appearance, and can better play anti-fake effect.
Summary of the invention
The object of the present invention is achieved like this: a kind of method of partial metallization on paper, may further comprise the steps,
A) even coating composition on a film, and make default literal or pattern or the combination of the two thereon;
B) even coating composition on paper;
C) film described in the step a) being carried out metallization handles;
D) carry out film behind the metallization and the described paper of step b) compound;
E) peel off film on the metallization paper.
Simultaneously,
Above-mentioned film is the enpara film.
Above-mentioned film is the PET film.
The above-mentioned default literal or pattern or the combination of the two of making on film is further comprising the steps of,
Aa) utilize laser engraving machine on the version rod, to carve out default literal or pattern or the combination of the two;
Ab) utilize moulding press that the literal on the above-mentioned version rod or pattern or the combination mold pressing of the two are reacted on the above-mentioned film.
Preferably, utilize coating machine that coating evenly is applied on the above-mentioned film.
Above-mentioned film behind the metallization and above-mentioned paper are carried out compound further comprising the steps of,
Da) utilize glue that above-mentioned film and above-mentioned paper is bonding;
Db) utilize the force value of compounding machine by presetting, above-mentioned film and paper after bonding is compound, so that literal on the above-mentioned film or pattern or the combination of the two are transferred on the above-mentioned paper.
Preferably, utilize stripping machine to peel off film on the above-mentioned metallization paper.
A kind of method of partial metallization on paper also comprises step,
F) the above-mentioned paper of having peeled off film is printed colouring.
Above-mentioned metal material is set to aluminium.
Preferably, utilize aluminum-spraying machine to the processing of aluminizing of above-mentioned film.
Realize above-mentioned technical scheme, just can realize purpose of the present invention.Can on paper, belong to material by local plating bronze printing, thereby predetermined literal, pattern or the combination of the two can be printed on the paper with the metal material plating, not only attractive in appearance, also can better play anti-fake effect.
Description of drawings
Fig. 1 is the block diagram of method of the present invention;
Fig. 2 is the applying step figure that aluminizes of method of the present invention.
Specific embodiment
Describe preferred embodiment of the present invention in detail below in conjunction with accompanying drawing,, can clearerly find out and understand advantage of the present invention place by description to preferred embodiment of the present invention.
As Fig. 1, method of the present invention at first is step s1, to the even coating composition of film surface; Be step s2, on the film that has been coated with coating, make the combination of default literal, pattern or character pattern thereafter; Be step s3 again, the plating bronze printing belongs to material on above-mentioned film.In step s1, s2, s3, carry out step s4, i.e. even coating composition on body paper.Carry out step s5 after above-mentioned steps is finished again, it is compound that the film that literal, pattern will be arranged and the paper that has been coated with coating carry out, and forms compound material, and make literal on the film, design transfer to paper.Carry out step s6 at last, film on the paper of compound good metallization is peeled off, the metallization layer of other parts can come off along with peeling off of film like this, can stay literal, the pattern of metallization on the paper, thereby finally realize method of the present invention, the part plates metal material on paper.
Usually need plate bronze printing and belong to material and all can select aluminium on paper, material is suitable, and is simultaneously also economical and beautiful.If use other metal materials to plate seal, with the method basically identical that uses aluminium.Below only just on paper the step of the embodiment of local aluminizing be elaborated again, use the step of the embodiment of other metal materials just not give unnecessary details one by one.
As Fig. 2, at first carry out step s11, utilize laser engraving machine on the version rod, to carve out default literal, pattern or the combination of the two; Carry out step s12 simultaneously, utilize coating machine on film, evenly to be coated with special coating.Be step s13 then, utilize moulding press will be coated with film behind the special coating and above-mentioned version rod mold pressing, make literal, pattern or the combination mold pressing of the two of carving on the version rod be reacted on the film.Carry out step s14 again, utilize aluminum-spraying machine that the film surface that default literal, pattern or the two combination have been arranged is aluminized, form surperficial aluminium lamination.When finishing above these steps s11, s12, s13, s14, carry out step s15, on body paper, evenly be coated with special coating.After this carry out step s16, will be coated with the body paper of coating and have the film of literal, pattern or the two combination bonding with glue; Be step s17 below, utilize compounding machine to make above-mentioned film and body paper compound, thereby literal, pattern or the combination of the two on the film are transferred on the body paper by certain pressure.Carry out step s18 again, utilize stripping machine, the film on the above-mentioned compound good paper of aluminizing is peeled off, the material layer of aluminizing of other parts can come off along with peeling off of film like this, can stay literal, the pattern of the material of aluminizing on the paper.Can also carry out step s19 at last, the body paper of aluminizing of above-mentioned formation is printed colouring, reach the color effects that needs.
After above-mentioned step is all finished, local aluminizing on the paper has been formed the paper of literal, pattern or the combination of the two, can cut again or crosscut, become suitable specification, so that as the packaging material of wishing in advance, such as the packaging material of cigarette.
Especially, the film that uses in the above step can be enpara film or plastic sheeting, preferably adopts PET film or OPP film, can obtain effect preferably.
The product made from method of the present invention is as packaging material, and is not only elegant in appearance, has the effect of improving the grade, and also possesses tangible antifalse effect.
Here it is to be noted: those of ordinary skill in the art can make various suitable distortion or replacement on basis of the present invention, but all these distortion or replacement all should belong to protection scope of the present invention.
Claims (10)
1, a kind of method of partial metallization on paper is characterized in that: may further comprise the steps,
A) even coating composition on a film, and make default literal or pattern or the combination of the two thereon;
B) even coating composition on paper;
C) film described in the step a) being carried out metallization handles;
D) carry out film behind the metallization and the described paper of step b) compound;
E) peel off film on the metallization paper.
2, the method for a kind of partial metallization on paper according to claim 1 is characterized in that: described film is enpara film or plastic sheeting.
3, the method for a kind of partial metallization on paper according to claim 1 and 2 is characterized in that: described film is PET film or OPP film.
4, the method for a kind of partial metallization on paper according to claim 1 is characterized in that: the described default literal or pattern or the combination of the two of making on film is further comprising the steps of,
Aa) utilize laser engraving machine on the version rod, to carve out default literal or pattern or the combination of the two;
Ab) utilize moulding press that the literal on the described version rod or pattern or the combination mold pressing of the two are reacted on the described film.
5, the method for a kind of partial metallization on paper according to claim 1 is characterized in that: utilize coating machine that coating evenly is applied on the described film.
6, the method for a kind of partial metallization on paper according to claim 1 is characterized in that: the film behind the metallization and described paper are carried out compound further comprising the steps of,
Da) utilize glue that described film and described paper is bonding;
Db) utilize the force value of compounding machine by presetting, described film and paper after bonding is compound, so that literal on the described film or pattern or the combination of the two are transferred on the described paper.
7, the method for a kind of partial metallization on paper according to claim 1 is characterized in that: utilize stripping machine to peel off film on the described metallization paper.
8, the method for a kind of partial metallization on paper according to claim 1 is characterized in that: also comprise step,
F) the described paper of having peeled off film is printed colouring.
9, the method for a kind of partial metallization on paper according to claim 1 is characterized in that: described metal material is set to aluminium.
10, according to the method for claim 1 or 9 described a kind of partial metallization on paper, it is characterized in that: utilize aluminum-spraying machine the processing of aluminizing of described film.