CN1923478A - Bamboo wood and preparation method thereof - Google Patents
Bamboo wood and preparation method thereof Download PDFInfo
- Publication number
- CN1923478A CN1923478A CN 200610048697 CN200610048697A CN1923478A CN 1923478 A CN1923478 A CN 1923478A CN 200610048697 CN200610048697 CN 200610048697 CN 200610048697 A CN200610048697 A CN 200610048697A CN 1923478 A CN1923478 A CN 1923478A
- Authority
- CN
- China
- Prior art keywords
- temperature
- bamboo
- minutes
- agent
- carry out
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a bamboo section and relative production. Wherein, it comprises cutting, high-temperature boiling, drying at constant-temperature, high-pressure carbonizing, accurately milling, colored sheeting, coating fireproof agent, thermally compressing, dressing, secondary thermally compressing, dressing, coating paint, treating it with preserve agent, hydraulic glue and insect protected agent. the invention has uniform strength, better mechanical property, high flexible modulus and high impact resistance.
Description
Technical field
The present invention relates to building materials technology field, specifically a kind of bamboo wood and preparation method thereof.
Background technology
Modern society's world population increases suddenly; consuming the resource of the earth in a large number; because human standard to the free living demand improves constantly; tropical rain forest is annual to disappear about 1,200 ten thousand hectares; natural calamities such as whole world temperature rising atmosphere pollution are more and more serious to the pressure that modern society brings; how to solve the contradiction of human society and organic growth; following society must reflect on oneself influencing after 21 century the principal element in the human social development; safeguard earth environment jointly, make it better to be protected.The natural resources of preserving our planet, making full use of resource has become significant problem in the economic construction.And effective utilization of bamboo resource can replenish the deficiency of timber resources in a large number.
The mankind are used in daily necessities with bamboo since ancient times, in the apparatus, along with the progress in epoch, the purposes of bamboo has also expanded in the construction timber, because the timber of common use need be grown and can be utilized in about 50 years, and bamboo is short growth period, and general 3-5 is become a useful person and just can be used.Bamboo resource is abundant on the earth, and according to statistics, about 1,400 ten thousand-2,000 ten thousand hectares of the whole world if the rational and effective felling utilizes, and substitutes valuable timber resources, and this will be the contribution greatly to human society.
Summary of the invention
The purpose of this invention is to provide a kind of integrated timber for building that utilizes the bamboo resource preparation, and the preparation method of this integrated timber.
The bamboo beauty, tough and tensile, intensity is high, corrosion resistant, be suitable for various weather growths, bamboo species number kind more than 500 in the world at present, and Yunnan has kind more than 200 approximately, the bamboo wood for building that the present invention uses is selected mao bamboon (phyllostachysheteroclavar has another name called bamboo, cat head bamboo, Meng Zongzhu) for use, it is that China's distribution is the widest, area maximum, the bamboo kind of economic benefit the best.Mao bamboon is the scattered bamboo of single-shaft variant, is the tallest and the biggest bamboo kind in the scattered bamboo class, general high 10～8m, and the diameter of a cross-section of a tree trunk 1.3 meters above the ground 6～15cm is up to more than the 20m, the thickest 20cm that reaches, the long 10～25cm of internode is that length can reach 45cm.Mao bamboon is the strongest bamboo of resistance, and average temperature of the whole year is 14～20 ℃, and extreme lowest temperature is 14～16 ℃, annual precipitation 800～1900mm, and height above sea level 300～800m is good to all growing below the height above sea level 2100rrlm, and the big white heavy snow of ability.
The present invention has developed the bamboo wood that is used for building under the situation of bamboo characteristic of having analyzed and researched.This integrated timber is prepared from by the following method:
1, select 3～5 years growth bamboo woods for use, carry out the bamboo chip machining, the bamboo chip slice thickness is 5～6mm, the about 20mm of width, length 50～100cm;
2, high temperature smokes and boil (add entry smoke boil): temperature is 83～93 ℃, adds anticorrisive agent five boron chlorides of water consumption 0.5%, and smoking the time of boiling is 20～30 minutes;
3, constant temperature drying: use the common wood drying process, 7～8 days time, 63～70 ℃ of baking temperatures, moisture content＜12%;
4, high pressure carbonization: dried timber is placed the vacuum carburization stove, 125～175 ℃ of temperature, 40～60 minutes time;
5, accurate dried milling: standard machinery processing, reach the splicing requirement, remove burr, overlap etc.;
6, sheet is made in color separation: because of the bamboo chip aberration that occurs after the carbonization treatment, close color of the same race is spliced;
7, coating fireproof agent: carry out surface applied with fireproof agent, and be coated with upper glue layer;
8, organize bad hot pressing: behind the gluing, be spliced into the canonical form piece, with 500～1000 tons of hydraulic flat press concora crush 45～60 minutes, 45～65 ℃ of temperature, pressure 10～15kg/cm
2
9, S4S: remove unnecessary burr, Fei Jiao;
10, broach finger: carry out finger with special-purpose finger joint machine;
11, secondary hot pressing: 500～1000 tons of hydraulic flat press ends were pressed normal temperature state, pressure 10～15kg/cm 45～60 minutes
2
12, S4S: be processed into the finished product materials on request;
13, applying coating: with above-mentioned product material of G8 type outer wall applying coating;
14, finished product warehouse-in after anticorrosion, damp proof, insect-prevention treatment.
Integrated timber of the present invention has following outstanding advantage:
1, color and luster is two kinds of Natural color and charing looks, and ring is obviously clear, and Natural color keeps the natural colored of this life of former bamboo, the further degreasing desugar of middle temperature charring process, and vermins-proof effect is better, makes product have cigarette and smokes and dark brown sensation.
2, the bamboo wood average moisture content is below 9%, strength of materials equilibrium, and machining property is good.
3, use NS2000 fireproof agent and G8 type outer wall coating to carry out surface treatment, better to product in various aspects of performance such as operation, soil resistance, drying property, patience, waterproof, fire prevention.
4, the present invention is directed to selected bamboo wood clean timber (Japan cypress wood) has been carried out the physical mechanics contrast experiment, its intensity is 1.5-2 times of timber, it has high-strength elastic modelling quantity and impact resistance, to its rotproofness, compare to firing resistance and outdoor resisting temperature parameter experiment, reach a conclusion, the spy of the excellence of bamboo wood manages rerum natura and the particularity in construction timber, and manufacturing expense is quite exceptional cheaply.
Intensity comparison sheet such as table 1: table one
| Title | The project aridity | Proportion | Tensile strength. kg/cm | Compression strength kg/cm | Bending strength kg/cm | Surrender purity 10kg/cm | Fracture strength kg/cm |
| Bamboo | 12℃ | 0.63 | 1760 | 780 | 1440 | 125 | 170 |
| Japan cypress wood | 12℃ | 0.44 | 1200 | 400 | 750 | 90 | 75 |
The specific embodiment
Embodiment 1:
1, select 3～5 years greenwoods for use, carry out the bamboo chip machining, the bamboo chip slice thickness is 5～6mm, the about 20mm of width, length 50～100cm;
2, high temperature smokes and boils (add entry smoke boil), and temperature is 83～93 ℃, adds water consumption anticorrisive agent five boron chlorides 0.5%, and smoking the time of boiling is 20～30 minutes;
3, constant temperature drying: use the common wood drying process, 7～8 days time, 63～70 ℃ of baking temperatures, moisture content＜12%;
4, high pressure carbonization: dried timber is placed the vacuum carburization stove, 125～175 ℃ of temperature, 40～60 minutes time;
5, accurate dried milling: standard machinery processing, processing dimension reaches the splicing requirement, removes burr, overlap etc.;
6, sheet is made in color separation: because of the bamboo chip aberration that occurs after the carbonization treatment, close color of the same race is spliced;
7, coating fireproof agent: carry out surface applied with NS2000 fireproof agent (commercially available prod), and be coated with gluing (RY1988 glue, commercially available prod) layer;
8, organize bad hot pressing: behind the gluing, be spliced into canonical form piece (dislocation intersect splicing), with 500～1000 tons of hydraulic flat press concora crush 45～60 minutes, 45～65 ℃ of temperature, pressure 10～15kg/cm
2
9, S4S: remove unnecessary burr, Fei Jiao;
10, broach finger: carry out finger with special-purpose finger joint machine;
11, secondary hot pressing: 500～1000 tons of hydraulic flat press ends were pressed normal temperature state, pressure 10～15kg/cm 45～60 minutes
2
12, S4S: be processed into the finished product materials on request;
13, applying coating: with above-mentioned product material of G8 type outer wall applying coating;
14, finished product warehouse-in after anticorrosion, damp proof, insect-prevention treatment.
Embodiment 2:(Application Example)
Bamboo wood of the present invention is used for the wall constructing process residential structure construction technology of construction timber, is used for structural beams, wall material, roofing material, Liang Jishuan; Indoor furniture floor: decoration panel etc.Material property experiment entrusts Japanese NEOWOOD company to finish, and experiment material 15 * 91 * 610mm sees Table 2, table 3.
Table two physical property table
| Pilot project | Unit | The result | Test method | Remarks |
| Moisture content | ％ | Average 9 | JAS | |
| Dipping is peeled off | ％ | 85-100 | JAS | Shell high length/total length ratio |
| Flexibility | mm | Average 0.12 | JAS | |
| Wear-resisting | Outward appearance | No significant change | Japan JISK 1454 | 100 change |
| Hardness | Compare with pencil 2H | 2H | Japan JISK 5400 | Coating ordinary test method |
| Chemical residue (drying) | B.P.H | Average 74 | ASTME303 | |
| Chemical residue (not dry) | B.P.H | Average 15 | ASTME303 |
Table trioxin burst size
| The benchmark project | Content of formaldehyde mg/L | Assay method |
| Brightness dragon sample | 0.1 below | JISA 5908 |
| JAS F1 product | 0.5 more than | The normal plywood specification is measured |
Claims (1)
1, a kind of bamboo wood is characterized in that preparing by the following method and gets:
1) select 3～5 years growth bamboo woods for use, carry out the bamboo chip machining, the bamboo chip slice thickness is 5～6mm, the about 20mm of width, length 50～100cm;
2) high temperature smokes and boils: temperature is 83～93 ℃, adds water consumption anticorrisive agent five boron chlorides 0.5%, and smoking the time of boiling is 20～30 minutes;
3) constant temperature drying: use the common wood drying process, 7～8 days time, 63～70 ℃ of baking temperatures, moisture content＜12%;
4) high pressure carbonization: dried timber is placed the vacuum carburization stove, 125～175 ℃ of temperature, 40～60 minutes time;
5) accurate dried milling: standard machinery processing, reach the splicing requirement, remove burr, overlap etc.;
6) sheet is made in color separation: because of the bamboo chip aberration that occurs after the carbonization treatment, close color of the same race is spliced;
7) coating fireproof agent: carry out surface applied with fireproof agent, and be coated with upper glue layer;
8) organize bad hot pressing: behind the gluing, be spliced into the canonical form piece, with 500～1000 tons of hydraulic flat press concora crush 45～60 minutes, 45～65 ℃ of temperature, pressure 10～15kg/cm
2
9) S4S: remove unnecessary burr, Fei Jiao;
10) broach finger: carry out finger with special-purpose finger joint machine;
11) secondary hot pressing: 500～1000 tons of hydraulic flat press ends were pressed normal temperature state, pressure 10～15kg/cm 45～60 minutes
2
12) S4S: be processed into the finished product materials on request;
13) applying coating: with above-mentioned product material of outer wall applying coating;
14) finished product warehouse-in after anticorrosion, damp proof, insect-prevention treatment.