The preparation method of cation guar gum graft copolymer retention and drainage agent and application
Technical field
The present invention relates to a kind of paper pulp and help the preparation method who filters reinforcing agent with multi-functional retention, be suitable for wood pulp, secondary stock and straw pulp system reach to produce the system that high-grade functional paper is a purpose.
Background technology
At present paper industry widespread usage molecular weight cation acrylamide (CPAM) up to a million is as retention and drainage aid agent, but CPAM is easily biological-degradable not, residual monomer toxicity is very big, limited the application in paper for daily use and high-grade paper, and excessive CPAM can cause paper pulp system charge reversal, reduce the retention aid and filtering aid performance greatly, and influence into the evenness of paper and the stable operation of paper machine.Starch derivatives, especially cationic starch gains universal acceptance as dry strength agent.But owing to differ in the starch material source, of a great variety, therefore the ratio difference of side chain/straight chain has a strong impact on its modified product quality of stability, has limited it and has applied.And starch need pass through the long-time gelatinization of high temperature in use, with the promotion dissolving, and the amidin easily biological-degradable of low concentration, the polysaccharide strand ruptures, and has a strong impact on the action effect of product.Therefore domestic starch conversion product can only be used to produce low grade products such as corrugated paper, boxboard, domestic medium-and-large-sized paper mill and speciality paper, and high-grade paper enterprise but is ready the starch series of products of selecting for use external major company to produce, thereby causes a large amount of flow-away of foreign exchange.
ZL99113919.4 has announced a kind of straw pulp for making paper high effective retention filter aid, the multi-element synergistic type starch derivatives that the process three-step reaction obtains, this invention production complex process, at last also will add the composite synergist of polyacrylamide and active silicic acid, the use amount in straw pulp is 0.8-1.2%.
Guar gum is a kind of natural galactomannan gum, extracts to obtain from the endosperm of the guar seed that originates in ground such as India, Pakistan.The guar gum main chain is that the unit is formed by connecting by (1,4) β-D mannose, and side chain is made up of single α-D galactolipin and is joined with (1,6) key and main chain.Molecular structure is similar with cellulose, determined and cellulosic natural sympathy, can when improve paper fiber fines and filler retention and drainage effect, not influence the evenness of paper and improve its strength character, therefore in paper industry, have application promise in clinical practice.
In recent years, since the plantation of guar gum, harvesting, purifying is pulverized and is realized industrialization, and the price advantage of its raw material makes first appearance.As a kind of abundant plant resources, the outstanding biodegradability of guar gum has been alleviated the problem of environmental pollution of paper industry.Mainly comprise two aspects about recent Progress in Modification of Guar Gum, first guar gum etherification modified, disclose the aqueous solution that contains non-ionic cation replacement guar gum as USP5733854 and had excellent light transmission, USP3326890, USP3350186, USP3483121 disclose the preparation technology of hydroxyalkyl guar gum and the preparation of carboxymethyl guar glue.It two is graft modifications of guar gum and vinyl, and the vinyl monomer of giving the guar gum new capability comprises: acrylamide, acrylic acid and acrylate and propylene cyanogen, vinylpyridine etc.Wherein, studying maximum is acrylamide monomer, because easily polymerization of acrylamide, the product of various application purpose different molecular weights is satisfied in the preparation of cutting the garment according to the figure by the technology adjustment, in sewage flocculation treatment, oil field chemical, aspects such as drag reducer and papermaking chemical product are approved widely.Wherein, guar gum, the aqueous solution graft copolymer of HPG and carboxymethyl guar glue and acrylamide is integrated the advantage of natural polymer and synthetic high polymer, in sewage flocculation treatment, the research of heavy metal absorbent aspect is many, but also be not used in the paper making wet part chemical process, especially about the aqueous solution graft polymerization technique of cation guar gum and acrylamide and in paper-making process, be used as retention and drainage aid agent and reinforcing agent still belongs to blank.
Summary of the invention
The objective of the invention is to overcome the shortcoming of prior art, provide that a kind of stable performance, raw material sources are abundant, cost is lower, the preparation method of the cation guar gum graft copolymer paper retention and filter aid of environmental protection.
Another object of the present invention is to provide the application of the guar gum paper retention and filter aid of method for preparing.
Purpose of the present invention is achieved through the following technical solutions:
The preparation method of cation guar gum graft copolymer retention and drainage agent comprises the steps:
A. cation etherification reaction: earlier the former powder of guar gum is dispersed in the mixed solution of low-carbon alcohols and water, logical nitrogen, stirring at room is even, adds the 3-chloro-2-hydroxypropyl-trimethyl ammonium chloride cationic etherifying agent aqueous solution, drip alkali catalyst, mix, under 40-75 ℃ temperature, reacted 2-6 hour cool to room temperature then, the pH value is adjusted to 6-7, through suction filtration, drying obtains the cation guar gum product;
B. graft polymerization reaction: with the product of step a, be mixed with the cation guar gum colourless transparent solution of 1-5%, logical nitrogen stirs, the dilute acid soln that adds initator cerium salt, and acrylamide and cationic vinyl monomer mixed aqueous solution, add the auxiliary agent A of potassium chlorate or potassium peroxydisulfate subsequently, in 10-65 ℃ of reaction after 2-24 hour, with diluted sodium hydroxide solution pH is transferred to 6-7, obtain cation guar gum graft copolymer retention and drainage agent; The addition of described acrylamide is 2~10 times of cation guar gum product quality.
Low-carbon alcohols in the low-carbon alcohols of described step a and the mixed solution of water is selected absolute ethyl alcohol, industrial alcohol and isopropyl alcohol, and the mass ratio of low-carbon alcohols and water is 2: 1-7: 1.
Described cationic etherifying agent 3-chloro-2-hydroxypropyl-trimethyl ammonium chloride consumption is the 5-40% of guar gum, the viscosity of its consumption decision cation substitution value and final products.
The alkali catalyst of described step a is a NaOH, and concentration is 10%-60%, and sodium hydroxide concentration is the 5%-40% of guar gum quality, and optimum consumption is 5%-25%, the complexity that its consumption decision reaction is carried out and the viscosity of final products.
The suction filtration of described step a, drying are to place 50-75 ℃ vacuum drying oven to dry by the fire 10h-24h the filter cake behind the suction filtration.
In the 40-75 ℃ of cationization range of reaction temperature of described step a, temperature is high more, and etherificate efficient is also high more, and is the highest above 70%; When minimum, etherificate efficient can be low to moderate 20%, will cause wastage of material.Above-mentioned preferred temperature is 45-75 ℃.
The cationic vinyl monomer of described step b is selected from methylacryoyloxyethyl trimethyl ammonium chloride, acrylyl oxy-ethyl-trimethyl salmiac, dimethyl diallyl ammonium chloride, and the mass ratio of cationic monomer and acrylamide is 0.1: 1-1: 1.In general, the cationic monomer price is expensive in acrylamide, so satisfying under the situation of application requirements, the consumption of cationic monomer should reduce.The acrylamide consumption depends on the molecular weight requirement to final products, and generally speaking, molecular weight is recommended as the papermaking drying strengthening agent at 20-80 ten thousand, and molecular weight can be considered as retention and drainage aid agent 1,000,000-7,000,000.
The initator cerium salt of described step b is ammonium ceric nitrate or Cericammoniumsulfate, and its consumption is the 1-15% of cation guar gum product quality, preferred 2-8%;
Auxiliary agent A potassium chlorate or the potassium peroxydisulfate of described step b constitute oxidation/reduction initiator system as synergist and cerium salt, reduce chain and cause activation energy, promote the quick generation of macromolecular radical.Therefore can significantly improve polymerization speed; With not with helping A to compare, make the consumption of cerium salt reduce 10-20%, its use amount is the 1-100% of cerium salt initiators.Optimum amount is 5-30%.
Preferred 10-65 ℃ of described step b graft polymerization reaction temperature, high temperature can reach reaction end in the very fast time, descend but the meeting of products molecule quality is obvious, also can increase the content of methacrylamide homopolymer.
The graft polymerization reaction time of wanting required for the present invention is 2-24h, and preferred 2-12h is closely related with reaction temperature and initiator amount.
Final products form of the present invention can be the solid or the aqueous solution.For the occasion that needs solid product, finish the back in reaction and inject industrial alcohol, needn't add the adjusting PH with base value, to impel the generation of white depositions, this white precipitate is replaced with absolute alcohol, obtains grain products through 50-75 ℃ vacuum drying oven baking 10-24h, is crushed into pressed powder.Normal temperature becomes the aqueous solution of 0.1-0.5% to get final product with cold-water solution.
The cation guar gum graft copolymer paper retention and filter aid of the present invention's preparation can be used as the paper pulp retention and drainage aid agent, and its using method is with paper retention and filter aid commonly used.The cation guar gum graft copolymer paper retention and filter aid of the present invention's preparation is used for the dosage 0.02-0.1% (with respect to oven dry stock) of leaf wood oar, according to the height of beating degree, the content of fiber fines and the height of amount of filler are selected the addition of the product of the present invention's preparation.When selecting correct consumption for use, can obviously improve the retention of tiny component, retention is first brought up to more than 80% from blank 40%, freeness drops to about 28 ° of SR from 45 ° of blank SR, when the pearl filler dosage is 20% (with respect to oven dry stock), total retention is brought up to more than 76.8% from 38.3% of blank, the winnofil retention is brought up to about 78.8% from 25.6% of blank, quantitatively obviously increasing of hand papermaking, tensile index improves 10-20%, tear index improves 15-30%, and fracture length improves 10-20%.Therefore use product of the present invention obviously to improve the retention of fiber fines and filler, improve the drainage rate of press section, improve the mechanical property of paper, be beneficial to environmental protection and reduce the production cost of papermaking enterprise, have the characteristics of low dosage high-efficiency multi-function.
Reaction principle of the present invention is as follows:
R1---alkyl, carbon number are 0-1.
R2---alkyl, carbon number are 2.
The number of repeat unit of n1---acrylamide, the integer between the 1-5000.
N2---sun is from the number of repeat unit of monomer, the integer between the 1-500.
Cation guar gum graft copolymer retention and drainage agent of the present invention is meant the graft copolymer that guar gum obtains through cation etherificate and graft polymerization reaction, and this copolymer can be used as the retention and drainage aid agent of paper-making industry.
With respect to prior art, of the present invention have following advantage and an effect:
Utilize the multi-functional paper making additive of cation guar gum of the inventive method preparation, have the quaternary ammonium cation group in the molecule, pass through charge neutralization with fiber fines electronegative in the paper pulp, the electric double layer of compressing grains reduces when repulsive force is reduced to less than Van der Waals'attractive force its current potential, collision causes cohesion between particle, promotes keeping of fiber fines; In the invention products molecule also grafting the polyacrylamide amine side chain of moderate length, the macromolecular chain segment that formation soluble in water is unfolded, suspended material in the one end absorption paper pulp, the other end is caught other particle by crane span structure, thereby promote the flocculating setting of particulate matter, tiny component is further kept.This auxiliary agent molecule and fiber form a large amount of hydrogen bonds, can also increase the mechanical property of paper product.
The mannose backbone of invention product has similar plants fibrocyte structure, thereby fiber is had good affinity; It can be adsorbed in fiber surface rapidly, reduce and in and the elecrtonegativity of fiber surface, make the slurry current potential close, reduce between the particle and the mutual repulsive force between the fiber, and neat solid netted bridge crosslinking structure is arranged well-balancedly and be combined into to mixed and disorderly unordered fiber to equipotential.Its characteristic shows as:
1) can promote keeping of tiny component and filler, improve the white-water system degree of purification, reduce the plain boiled water turbidity;
2) improve drainability, reduce beating degree, be easy to increase and copy the chart speed degree,
3) retention of increase sizing agent reduces consumption, improves the influence of sizing agent to paper strength.
The multi-functional paper making additive of cation guar gum of the present invention preparation is met water in room temperature and can be dissolved into settled solution fast, compares with the modified starch chemicals, does not need the high temperature gelatinization, and is simple to operate, is beneficial to cut down the consumption of energy and reduce equipment investment.Product of the present invention is because of synthetic high polymer on the side chain graft, it is very big to make its antibiont degradation capability and cation guar gum compare raising with guar gum, 1% aqueous solution is constant substantially in the above viscosity of room temperature placement two weeks, retention and drainage effect is unaffected, and the starch based retention and drainage aid agent must be prepared use on the same day same day, otherwise serviceability can not get guaranteeing.
When using product of the present invention, can be according to the pulp kind, the addition of beating degree and other auxiliary agents is adjusted its consumption, thus the performance synergistic function enlarges the suitable paper kind scope of product of the present invention, as: speciality paper, high-grade cigarette paper and drawing paper.
The specific embodiment
The present invention will be further described below in conjunction with embodiment.Except as otherwise noted, among the embodiment consumption of material and percentage all with dry weight basis.
Embodiment 1
The not purified former powder of guar gum of 100 grams, be distributed in the mixed liquor of 40 gram alcohol and 10 gram water, join in the common there-necked flask, logical nitrogen, stirring at room is even, the solution that adds 10 gram 3-chloro-2-hydroxypropyl-trimethyl ammonium chlorides and 10 gram water, drip 10 gram sodium hydrate aqueous solutions (naoh concentration 50%), mix, then material is placed 65 ℃ of constant temperature oven reactions after 3.5 hours, cool to room temperature, with arriving 6-7 with pH in the little acetic acid,, place 65 ℃ vacuum drying oven to dry by the fire 12h filter cake through suction filtration, obtain the cation guar gum product, recording the cation substitution value is 0.015.
Get the said goods 10 grams, be dissolved in the 833 gram distilled water, obtain colourless transparent solution, feeding nitrogen stirs, the salpeter solution that adds ammonium ceric nitrate, promptly 0.2 gram ammonium ceric nitrate is dissolved in 5ml, concentration is the dilute nitric acid solution of 2mol/l, add the mixed solution of 40 gram acrylamides and 4 gram methylacryoyloxyethyl trimethyl ammonium chloride solution and 60 gram water then, add auxiliary agent A potassium chlorate at last, consumption is 0.02 gram, in 50 ℃ of reaction 2h, transferring pH with diluted sodium hydroxide solution is 6-7, obtains solid content and be 5.5% product solution, the conversion ratio 94% of monomer.
Embodiment 2
The not purified former powder of guar gum of 100 grams, be distributed in the mixed liquor of 70 gram alcohol and 10 gram water, join in the common there-necked flask, logical nitrogen, stirring at room is even, the solution that adds 25 gram 3-chloro-2-hydroxypropyl-trimethyl ammonium chlorides and 10 gram water, Dropwise 50 gram sodium hydrate aqueous solution (naoh concentration 10%) mixes, and then material is placed 75 ℃ of constant temperature oven reactions after 6 hours, cool to room temperature, with arriving 6-7 with pH in the little acetic acid, suction filtration places 50 ℃ vacuum drying oven to dry by the fire 24h filter cake, obtain the cation guar gum product, recording the cation substitution value is 0.036.
Get the said goods 10 grams, be dissolved in the 190 gram distilled water, obtain colourless transparent solution, feeding nitrogen stirs, the salpeter solution that adds ammonium ceric nitrate, promptly 0.5 gram Cericammoniumsulfate is dissolved in 5ml, concentration is in the dilute nitric acid solution of 2mol/l, adds the mixed solution of 20 gram acrylamides and 20 gram methylacryoyloxyethyl trimethyl ammonium chloride solution and 20 gram water then, adds the auxiliary agent A potassium peroxydisulfate at last, consumption is 0.025 gram, in 10 ℃ of reaction 24h, with industrial alcohol precipitation reaction mass, the white precipitate of formation was replaced with absolute alcohol after reaction finished, vacuum drying oven baking 12h through 65 ℃ obtains grain products, is crushed into pressed powder.The conversion ratio 96% of monomer.
Embodiment 3
The not purified former powder of guar gum of 100 grams, be distributed in the mixed liquor of 20 gram alcohol and 10 gram water, join in the common there-necked flask, logical nitrogen, stirring at room is even, the solution that adds 5 gram 3-chloro-2-hydroxypropyl-trimethyl ammonium chlorides and 10 gram water, dripping 10 gram sodium hydrate aqueous solution (naoh concentration 50%) high-speed stirred mixes, then material is placed 40 ℃ of constant temperature oven reactions after 6 hours, cool to room temperature is with arriving 6-7 with pH in the little acetic acid, through suction filtration, place 75 ℃ vacuum drying oven to dry by the fire 10h filter cake, obtain the cation guar gum product, recording the cation substitution value is 0.008.
Get the said goods 10 grams, be dissolved in the 323 gram distilled water, obtain colourless transparent solution, feeding nitrogen stirs, the salpeter solution that adds ammonium ceric nitrate, promptly 0.8 gram Cericammoniumsulfate is dissolved in 5ml, concentration is in the dilute nitric acid solution of 2mol/l, adds the mixed solution of 100 gram acrylamides and 20 gram methylacryoyloxyethyl trimethyl ammonium chloride solution and 60 gram water then, adds auxiliary agent A potassium chlorate at last, helping the A consumption is 0.08 gram, in 65 ℃ of reaction 2h, with industrial alcohol precipitation reaction mass, the white precipitate of formation was replaced with absolute alcohol after reaction finished, baking 10h obtains grain products in 75 ℃ vacuum drying oven, is crushed into pressed powder.The conversion ratio 97% of monomer.
Embodiment 4
The not purified former powder of guar gum of 100 grams, be distributed in the mixed liquor of 70 gram alcohol and 10 gram water, join in the common there-necked flask, logical nitrogen, stirring at room is even, the solution that adds 40 gram 3-chloro-2-hydroxypropyl-trimethyl ammonium chlorides and 20 gram water, drip 66.6 gram sodium hydrate aqueous solutions (naoh concentration 60%), mix, then material is placed 45 ℃ of constant temperature oven reactions after 6 hours, cool to room temperature, with arriving 6-7 with pH in the little acetic acid,, place 65 ℃ vacuum drying oven to dry by the fire 12h filter cake through suction filtration, obtain the cation guar gum product, recording the cation substitution value is 0.045.
Get the said goods 10 grams, be dissolved in the 656 gram distilled water, obtain colourless transparent solution, feeding nitrogen stirs, the salpeter solution that adds ammonium ceric nitrate, promptly 0.5 gram Cericammoniumsulfate is dissolved in 5ml, concentration is in the dilute nitric acid solution of 2mol/l, adds the mixed solution of 50 gram acrylamides and 25 gram dimethyl diallyl ammonium chlorides and 40 gram water then, adds the auxiliary agent A potassium peroxydisulfate at last, helping the A consumption is 0.5 gram, in 55 ℃ of reaction 4h, with industrial alcohol precipitation reaction mass, the white precipitate of formation was replaced with absolute alcohol after reaction finished, vacuum drying oven baking 24h through 50 ℃ obtains grain products, is crushed into pressed powder.The conversion ratio 93% of monomer.
Embodiment 5
The not purified former powder of guar gum of 100 grams, be distributed in the mixed liquor of 60 gram alcohol and 10 gram water, join in the common there-necked flask, logical nitrogen, stirring at room is even, the solution that adds 25 gram 3-chloro-2-hydroxypropyl-trimethyl ammonium chlorides and 10 gram water, Dropwise 50 gram sodium hydrate aqueous solution (naoh concentration 50%) high-speed stirred mixes, then material is placed 75 ℃ of constant temperature oven reactions after 2 hours, cool to room temperature is with arriving 6-7 with pH in the little acetic acid, through suction filtration, place 55 ℃ vacuum drying oven to dry by the fire 15h filter cake, obtain the cation guar gum product, recording the cation substitution value is 0.030.
Get the said goods 10 grams, be dissolved in the 990 gram distilled water, obtain colourless transparent solution, feeding nitrogen stirs, the salpeter solution that adds ammonium ceric nitrate, promptly 1.5 gram Cericammoniumsulfates are dissolved in 5ml, concentration is in the dilute nitric acid solution of 2mol/l, adds the mixed solution of 30 gram acrylamides and 6 gram methylacryoyloxyethyl trimethyl ammonium chloride solution and 20 gram water then, adds auxiliary agent A potassium chlorate at last, helping the A consumption is 0.15 gram, in 50 ℃ of reaction 4h, with industrial alcohol precipitation reaction mass, the white precipitate of formation was with replacing in the absolute alcohol after reaction finished, vacuum drying oven baking 12h through 65 ℃ obtains grain products, is crushed into pressed powder.The conversion ratio 94% of monomer.
Embodiment 6
The not purified former powder of guar gum of 100 grams, be distributed in the mixed liquor of 40 gram alcohol and 10 gram water, join in the common there-necked flask, logical nitrogen, stirring at room is even, the solution that adds 15 gram 3-chloro-2-hydroxypropyl-trimethyl ammonium chlorides and 10 gram water, drip 12 gram sodium hydrate aqueous solutions (naoh concentration 50%), mix, then material is placed 45 ℃ of constant temperature oven reactions after 6 hours, cool to room temperature, with arriving 6-7 with pH in the little acetic acid,, place 65 ℃ vacuum drying oven to dry by the fire 12h filter cake through suction filtration, obtain the cation guar gum product, recording the cation substitution value is 0.025.
Get the said goods 10 grams, be dissolved in the 490 gram distilled water, obtain colourless transparent solution, feeding nitrogen stirs, the salpeter solution that adds ammonium ceric nitrate, promptly 0.6 gram Cericammoniumsulfate is dissolved in 5ml, concentration is in the dilute nitric acid solution of 2mol/l, add the mixed solution of 30 gram acrylamides and 10 gram acrylyl oxy-ethyl-trimethyl salmiacs and 20 gram water then, add the auxiliary agent A potassium peroxydisulfate at last, helping the A consumption is 0.18 gram, in 50 ℃ of reaction 4h, reaction finishes the back, and to transfer pH with diluted sodium hydroxide solution be 6-7, obtains solid content and be 8.2% product solution, the conversion ratio 94% of monomer.
Application Example 1
The product of embodiment 2 preparation is added the running water dilution, be mixed with 1% aqueous solution, be added in the leaf wood pulp suspension of concentration 0.5% according to the consumption of table 1 (calculating with dry pulp), other technology is with common paper technology.Utilize DDJ dynamic drainage analyzer to survey its retention performance, and measure freeness simultaneously.
Used laboratory apparatus: conductivity gauge; The PH meter; Schooper-Riegler beating degree tester; Dynamic drainage analyzer (DDJ); 2100P type nephelometer.DDJ dynamic drainage analyzer and nephelometer are used.
Experimental procedure: it is 0.5% suspension 400ml that two gram oven dry stocks are mixed with concentration, stir fast, the l% aqueous solution that adds embodiment 2 preparations of amount of calculation after 1 minute, mix after 1 minute, all pour into suspension among the DDJ, rotating speed with 750r/m stirs simultaneously, use manual time-keeping, open the liquid valve immediately after stirring for 10 seconds, stop to stir after accessing 100ml filtrate, measure the turbidity of this 100ml filtrate with nephelometer, be scaled filter liquor concentration (being machine water concentration), calculate the initial journey retention according to filter liquor concentration and paper stock concentration then.The initial journey retention is meant that slurry stays the percentage of total solid in solid content on the page and the slurry by wire-cloth.Computing formula is: initial journey retention (FPR)=(1-filter liquor concentration/sample solution concentration) * 100%.Experimental data sees Table 1.
Process conditions: PH7.0, electrical conductivity 2000 μ s/cm, rotating speed 750r/m, not filled.
Table 1 cation melon glueds joint the retention aid and filtering aid performance of graft copolymer
Dosage (%) | Initial journey retention (%) | Freeness (° SR) |
0 | 43 | 42 |
0.02 | 78.2 | 27 |
0.04 | 80.5 | 27 |
0.06 | 82.3 | 26 |
0.08 | 86.1 | 26 |
0.1 | 86.1 | 26 |
As can be seen from Table 1: patented product of the present invention is added to hardwood pulp suspension system in 0.02%-0.1% (with oven dry stock) consumption, because this water-soluble additive molecule is positively charged, by the electronegative fiber fines of charging neutrality, promote unstability, the cohesion of fiber, thereby tiny component is kept on forming net.And the polyacrylamide amine side chain that is connected with mannose backbone, has different length, one end adsorption particle, the other end adsorbs other particles, promotes the flocculating setting of suspended material by building bridge, machine water concentration is reduced, freeness obviously descends, and drops to 26 ° of SR from 42 ° of SR, has improved the water filtering performance of paper web, alleviate the oven dry load of press section, saved the valuable energy.The initial journey retention brings up to 78.2% from 43%, the highlyest brings up to 86.1%, and this shows the interpolation a little auxiliary, improves keeping of tiny component greatly, reduces tiny component concentrations in the plain boiled water, reduces and copies the paper cost; Help paper industry plain boiled water and recycle, alleviate the pollution of paper industry environment.
Application Example 2
The product of embodiment 3 preparation is added the running water dilution be mixed with 1% aqueous solution, be added in the leaf wood pulp suspension of concentration 0.5% according to the consumption of table 2 (calculating with dry pulp), other technology is with common paper technology.By hand papermaking, the mechanical property of test paper product.
Table 2 cation melon glueds joint strengthening the property of graft copolymer retention and drainage aid agent
Dosage (%) | Quantitatively, g/m
2 | Tensile index, Nm/g | Fracture length, KM | Tear index, mN.m
2/g
|
0 | 59.10 | 43.27 | 4.41 | 7.04 |
0.02 | 60.0 | 45.12 | 4.53 | 7.84 |
0.04 | 60.5 | 47.10 | 4.75 | 8.02 |
0.08 | 61.0 | 48.36 | 4.93 | 8.74 |
0.1 | 61.1 | 48.53 | 4.99 | 8.79 |
As seen from Table 2, add product of the present invention, the mechanical property of write by hand paper product is improved, as when consumption is 0.08%, the quantitatively obviously increase of hand papermaking, tensile index improves 11.8%, and tear index improves 24.1%, and fracture length improves 11.8%.
Application Example 3
Estimate the retention performance of product with DDJ dynamic drainage instrument and Schooper-Riegler beating degree tester to pearl filler.Other is with Application Example 1.
Process conditions: PH7.0, electrical conductivity 2000us/cm, rotating speed 750r/m, amount of filler 20% (with respect to oven dry stock).
The cation melon gluedd joint the retention aid and filtering aid performance of graft copolymer when table 3 was filled
Dosage (%) | Total retention (%) | The winnofil retention, % |
0 | 43.3 | 38.3 |
0.02 | 75.2 | 74.8 |
0.04 | 79.8 | 78.2 |
0.06 | 79.4 | 80.2 |
0.08 | 76.9 | 79.6 |
0.1 | 77.1 | 79.1 |
As can be seen from Table 3: the embodiment of the invention 2 products are added to the hardwood pulp suspension system that adds pearl filler in 0.02%-0.1% (with dry pulp) consumption, will improve the retention of fiber fines and filler greatly.For example, when consumption is 0.06%, make total retention improve 83.4%, the winnofil retention improves 109%, thereby can promote keeping of a large amount of inexpensive pearl fillers, is beneficial to the reduction white water consistency, reduces paper cost.