CN1888350A - Wet coating self-adhering waterproof coiled material and producing method and construction method thereof - Google Patents
Wet coating self-adhering waterproof coiled material and producing method and construction method thereof Download PDFInfo
- Publication number
- CN1888350A CN1888350A CN 200610200760 CN200610200760A CN1888350A CN 1888350 A CN1888350 A CN 1888350A CN 200610200760 CN200610200760 CN 200610200760 CN 200610200760 A CN200610200760 A CN 200610200760A CN 1888350 A CN1888350 A CN 1888350A
- Authority
- CN
- China
- Prior art keywords
- coiled material
- self
- wet coating
- waterproof coiled
- coating self
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a wet-stickable self-adhesive water-proof sheet material, its production method and construction method. It is characterized by that said invention uses butyl rubber and high-grade oxidated asphalt, makes them undergo the process of high-temperature mixing treatment, adds acryl water-absorbing resin, operation oil, filler and flow-resisting agent, makes them undergo the process of high-speed dispersion treatment so as to obtain self-adhesive seal water-proof material, dip-coating said self-adhesive seal water-proof material onto one surface of high-molecular water-proof sheet material carrier, then makes the above-mentioned material undergo the processes of calendaring, extruding and layering isolating layer as anti-adhesion layer, then makes a flexible protective layer be stuck on another surface of the above-mentioned high-molecular water-roof sheet material, so that the invented wet-stickable self-adhesive water-proof sheet material can be obtained.
Description
(1), technical field
The present invention relates to a kind of waterproof roll and production method thereof and job practices.
(2), background technology
Existing waterproofing materials mainly is high polymer SBS modified bitumen and synthetic polymeric waterproofing material etc., waterproof rolls such as high polymer SBS modified bitumen and synthetic high polymer are the waterproof materials faster of demand growth in recent years, it has solved asphalt felt high temperature trickling in the past, the defective of low-temperature embrittleness, boundary of works area is wider, is the waterproof product of Ministry of Construction's emphasis popularization and develop actively.But basic unit's primary coat is adopted in existing waterproofing materials construction, is coated with the blowtorch heating is roasting, or with the binding agent bonding, easily produces oil smoke and toxic gas, and it is healthy to diminish the constructor, also can produce pollution to environment.And existing waterproofing materials is higher to Base Smoothness and water content requirement, basic unit's water content is required below 9%, and often do not reach in operating process, not only influences the duration, also has influence on waterproof effect.As do not reach standard, and construction back waterproofing course easily produces bubble, and problems such as water are scurried in delamination, also can occur can not realizing waterproof under water because of the not firm seepage phenomenon that causes of overlap joint.Existing waterproof roll does not have the suspender belt that passes the flexible anti sheath, is difficult for being connected and fixed in the construction of facades such as tunnel, and construction is inconvenient.
(3), summary of the invention
The purpose of this invention is to provide a kind of wet coating self-adhering waterproof coiled material and production method thereof and job practices, the waterproofing course that solves cold-adhered easily produces bubble, and the problem of water is easily scurried in easily delamination; And solve the problem of carrying out waterproof construction in wet environment and the water; Also solve high score subclass coiled material because of the not firm leakage problems that causes of overlap joint; Solve waterproof roll simultaneously and in the construction of facades such as tunnel, be difficult for being connected and fixed the problem that construction is inconvenient.
Technical scheme of the present invention: this wet coating self-adhering waterproof coiled material, it is characterized in that this coiled material has sticking folded following each layer of order: separation layer, self-adhesive sealant, macromolecule water-proof sheet material, adhesive linkage, flexible anti sheath, above-mentioned flexible anti sheath is installed with suspender belt, expose at suspender belt two, is used for colligation.
Above-mentioned macromolecule water-proof sheet material can be high density polyethylene (HDPE), low density polyethylene (LDPE), polyvinyl chloride, polyvinyl acetate synthetic resin, ethene, vinyl acetate pitch mixture macromolecule water-proof sheet material or modified bituminous pitch coiled material.
Above-mentioned flexible anti sheath can be nonwoven, cloth, polyethylene felt, felt, malthoid, glass felt or macromolecule plastic film.
Above-mentioned separation layer can be silicone oil paper or polyester insulating film.
The material of above-mentioned self-adhesive sealant is the butyl rubber modified bitumen, and its mixing ratio by weight is as follows:
Butyl rubber 268; 8～28%;
Oxidized asphalt: 30～50%;
Acrylic acid water-absorbing resin: 1～8%;
Process oil: 5～35%;
Filler: 5～25%;
Stop-off gent: 1～5%.
Aforesaid operations oil comprises naphthene base crude oil or three-way base oil.
Above-mentioned filler comprises fossil meal or carbon black.
Above-mentioned stop-off gent comprises fume colloidal silica and glue.
The production method of above-mentioned wet coating self-adhering waterproof coiled material, it is characterized in that: by butyl rubber, High Quality Oxidized Asphalt through high-temperature mixing, add the acrylic acid water-absorbing resin, process oil, filler, stop-off gent are made from bonding waterproof sealing material through high speed dispersion, dip-coating is on macromolecule water-proof sheet material carrier one side, through rolling, extruding, spread separation layer as adherent layer, and the flexible anti sheath is pasted macromolecule water-proof sheet material carrier another side, put on suspender belt again, make wet coating self-adhering waterproof coiled material.
The job practices of above-mentioned wet coating self-adhering waterproof coiled material, it is characterized in that: the fixture of pre-buried band hook in concrete basic unit, with the flexible protective aspect of wet coating self-adhering waterproof coiled material to concrete basic unit, and fix by the hook of suspender belt and fixture, throw off the separation layer of wet coating self-adhering waterproof coiled material, make the concrete deck on self-adhesive sealant surface, waterproof roll and concrete deck fully are sealing adhesive.
Beneficial effect: cold-adhered water-tight performance of the present invention is good, and it is to add acroleic acid macromolecular absorbent resin and macromolecule water-proof sheet material is a carrier with butyl rubber and high-quality asphalt, by dipping process, is the waterproof roll that adherent layer is made with the separation layer.The flexible protective layer has self-adhesion, waterproof, three kinds of functions of protection, can also make wet coating self-adhering waterproof coiled material have protective effect as the carrier of hanging suspender belt, and be easy in the facade construction fixing.Owing to penetrate the suspender belt that fixedly colligation is used in the flexible anti sheath, make the facade of waterproof roll fixing very convenient.In construction, can adopt to overlay anti-subsides method or routine and just pasting legal system and make waterproof construction, utilize the moisture of cement mortar, the migration by water-absorbing resin reaches fully waterproof roll and is sealing adhesive, but reaches wet environment construction and subaqueous work.Waterproofing materials construction of the present invention does not need to be coated with the blowtorch heating is roasting without basic unit's primary coat, bonds without binding agent yet.Intensity height of the present invention, elongation per unit length are big, acid and alkali-resistance, ageing-resistant, corrosion-resistant, anti-puncture, self-healing property, cold construction, solvent-free volatilization are arranged, safety and environmental protection, no hidden fire-fighting danger, construction are convenient, but bond in wet environment or the water, duration can be saved, accelerate speed of application, guarantee waterproof effect and construction quality, energy-conserving and environment-protective.The invention solves existing waterproofing materials and easily produce bubble, the problem of carrying out waterproof construction in water problems and wet environment and the water is easily scurried in easily delamination, has especially solved high score subclass coiled material because of the not firm leakage problems that causes of overlap joint.Be mainly used in the construction works higher such as underground, tunnel, bridge, subway, planted roof to waterproof requirement.
(4), description of drawings
Fig. 1 is the structural representation of the embodiment of the invention one.
Fig. 2 is the structural representation of the embodiment of the invention two.
Fig. 3 is a construction application schematic diagram of the present invention;
Fig. 4 is the schematic diagram of the fixture of band hook.
Fig. 5 is the thin portion of the fixed point of a job practices of the present invention structural representation.
1-wet coating self-adhering waterproof coiled material, 11-separation layer, 12-self-adhesive sealant, 13-macromolecule water-proof sheet material, 14-adhesive linkage, 15-flexible anti sheath, 16-suspender belt.
2-concrete deck, 3-concrete basic unit, 4-fixture, the pre-buried grid sheet of 41-, 42-hook.
(5), the specific embodiment
Embodiment one is referring to Fig. 1: sticking folded following each layer of this wet coating self-adhering waterproof coiled material 1 order: separation layer 11, self-adhesive sealant 12, macromolecule water-proof sheet material 13, adhesive linkage 14, flexible anti sheath 15, above-mentioned flexible anti sheath is installed with suspender belt 16, expose at suspender belt two, is used for colligation.
Self-adhesive sealant 12 has self-healing property, cold construction, solvent-free volatilization, safety and environmental protection, no hidden fire-fighting danger, construction are convenient, but bond in wet environment or the water, the material of above-mentioned macromolecule water-proof sheet material 13 can be selected high density polyethylene, low density polyethylene, polyvinylchloride, polyvinyl acetate EVA, ethene, vinyl acetate pitch mixture ECB or modified bituminous pitch coiled material.The thickness of above-mentioned macromolecule water-proof sheet material or modified bituminous pitch coiled material is 0.5～2.0mm, has that intensity height, elongation per unit length are big, a function of acid and alkali-resistance, the puncture of ageing-resistant, corrosion-resistant and anti-root system of plant.Above-mentioned flexible anti sheath 15 can be selected the macromolecule plastic film of nonwoven, resin fibre cloth, polyethylene felt, felt, malthoid, glass felt or 0.1-0.5 millimeters thick.Above-mentioned separation layer can be selected silicone oil paper or polyester insulating film.
Embodiment two is referring to Fig. 2: just pasting under the condition of construction, nonwoven layer 15, adhesive linkage 14 and suspender belt 16 also can omit.
The material of above-mentioned self-adhesive sealant is the butyl rubber modified bitumen, and mixing ratio by weight is as follows:
Butyl rubber 268; 8～28% any number.
High Quality Oxidized Asphalt: 30～50% any number.
Acrylic acid water-absorbing resin: 1～8% any number.
Process oil: 5～35% any number, process oil can be selected naphthene base crude oil or three-way base oil.
Filler: 5～25% any number, filler can be selected fossil meal or carbon black.
Stop-off gent: 1～5% any number, stop-off gent can be selected fume colloidal silica.
The production method of above-mentioned wet coating self-adhering waterproof coiled material, by butyl rubber, High Quality Oxidized Asphalt through high-temperature mixing, add the acrylic acid water-absorbing resin, process oil, filler, stop-off gent are made from bonding waterproof sealing material through high speed dispersion, dip-coating is on macromolecule water-proof sheet material carrier one side, through rolling, extruding, spread separation layer as adherent layer, and nonwoven layer is pasted macromolecule water-proof sheet material carrier another side, put on suspender belt 16 again, make wet coating self-adhering waterproof coiled material.
Referring to Fig. 3, Fig. 5, wet coating self-adhering waterproof coiled material overlay anti-subsides job practices 1: the fixture 4 that pre-buried band is linked up with concrete basic unit 3 in earlier, with the flexible anti sheath 15 of wet coating self-adhering waterproof coiled material towards concrete basic unit 3, and fix by the suspender belt 16 and the hook of fixture 4, also can directly the hook of fixture 4 be passed the flexible anti sheath 15 of wet coating self-adhering waterproof coiled material, then, throw off the separation layer of wet coating self-adhering waterproof coiled material, make concrete deck 2 on the surface of self-adhesive sealant 12, the water translocation of concrete deck cement mortar fully is sealing adhesive waterproof roll and concrete deck to the wet coating self-adhering waterproof coiled material that contains the acrylic acid water-absorbing resin.
The embodiment of fixture 4 is referring to Fig. 4, and it comprises pre-buried grid sheet 41 and is fixed on the hook 42 of one with pre-buried grid sheet.
Just pasting job practices 2: remove suspender belt and barrier paper, the self-adhesion sealant of self-adhesive coiled material of the present invention towards building structure, along bullet is good in advance construction line paving, paste coiled material and press national regulation and overlap the 10cmm paving with first when paving second is pasted, seal with special-purpose sealing compound then.During the facade construction, at first scrub cleaning agent, direct then paving coiled material of the present invention, laying method and the same program of plane construction.After finishing, paving hand over the owner to check and accept, directly the backfill 37 lime earth.
Claims (10)
1. wet coating self-adhering waterproof coiled material is characterized in that this coiled material has sticking folded following each layer of order: separation layer, self-adhesive sealant, macromolecule water-proof sheet material, adhesive linkage, flexible anti sheath, and above-mentioned flexible anti sheath is installed with suspender belt, and expose at suspender belt two.
2. wet coating self-adhering waterproof coiled material according to claim 1 is characterized in that: above-mentioned macromolecule water-proof sheet material is high density polyethylene (HDPE), low density polyethylene (LDPE), polyvinyl chloride, polyvinyl acetate synthetic resin, ethene, vinyl acetate pitch mixture macromolecule water-proof sheet material or modified bituminous pitch coiled material.
3. wet coating self-adhering waterproof coiled material according to claim 2 is characterized in that: above-mentioned flexible anti sheath is nonwoven, cloth, polyethylene felt, felt, malthoid, glass felt or macromolecule plastic film.
4. wet coating self-adhering waterproof coiled material according to claim 3 is characterized in that: above-mentioned separation layer is silicone oil paper or polyester insulating film.
5. wet coating self-adhering waterproof coiled material according to claim 4 is characterized in that: the material of above-mentioned self-adhesive sealant is the butyl rubber modified bitumen, and its mixing ratio by weight is as follows:
Butyl rubber 268; 8～28%;
Oxidized asphalt: 30～50%;
Acrylic acid water-absorbing resin: 1～8%;
Process oil: 5～35%;
Filler: 5～25%;
Stop-off gent: 1～5%.
6. wet coating self-adhering waterproof coiled material according to claim 5 is characterized in that: aforesaid operations oil comprises naphthene base crude oil or three-way base oil.
7. wet coating self-adhering waterproof coiled material according to claim 5 is characterized in that: above-mentioned filler comprises fossil meal or carbon black.
8. wet coating self-adhering waterproof coiled material according to claim 5 is characterized in that: above-mentioned stop-off gent comprises fume colloidal silica and glue.
9. according to the production method of any described wet coating self-adhering waterproof coiled material of claim 5 to 8, it is characterized in that: by butyl rubber, High Quality Oxidized Asphalt through high-temperature mixing, add the acrylic acid water-absorbing resin, process oil, filler, stop-off gent, make from bonding waterproof sealing material through high speed dispersion, dip-coating is on macromolecule water-proof sheet material carrier one side, through rolling, extruding, the shop separation layer is as adherent layer, and the flexible anti sheath pasted macromolecule water-proof sheet material carrier another side, put on suspender belt again, make wet coating self-adhering waterproof coiled material.
10. according to the job practices of any described wet coating self-adhering waterproof coiled material of claim 1 to 8, it is characterized in that: the fixture of pre-buried band hook in concrete basic unit, with the flexible protective aspect of wet coating self-adhering waterproof coiled material to concrete basic unit, and fix by the hook of suspender belt and fixture, throw off the separation layer of wet coating self-adhering waterproof coiled material, make the concrete deck on self-adhesive sealant surface, waterproof roll and concrete deck fully are sealing adhesive.