CN1887811A - Glaze material for surface of ceramic tile - Google Patents
Glaze material for surface of ceramic tile Download PDFInfo
- Publication number
- CN1887811A CN1887811A CN 200610036552 CN200610036552A CN1887811A CN 1887811 A CN1887811 A CN 1887811A CN 200610036552 CN200610036552 CN 200610036552 CN 200610036552 A CN200610036552 A CN 200610036552A CN 1887811 A CN1887811 A CN 1887811A
- Authority
- CN
- China
- Prior art keywords
- weight part
- glaze
- weigh portions
- powder
- weigh
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The glaze material for surface of ceramic tile consists of clay, zirconium silicate, ceramic stone powder, quartz powder, limestone and other mineral materials as well as low temperature flux clinker and coloring compound. Its material components include Li2O/Na2O/K2O 1.0-25 weigh portions, certain amount of 0-20 weigh portions, MgO 0-10 weigh portions, SiO2 50-85 weigh portions, Al2O3 2.0-20 weigh portions, B2O3 0.5-30 weigh portions, ZrO2 0-25 weigh portions, TiO2 0-30 weigh portions, ZnO 0.5-50 weigh portions, BaO 2-15 weigh portions, P2O5 0-20 weigh portions, PbO 0-50 weigh portions, and coloring compound or inorganic pigment 0.5-30 weigh portions. The glaze material for surface of ceramic tile has the decoration effect similar to that of artistic ceramic glaze and glambe glaze.
Description
Technical field
The present invention relates to the raw material of ceramic, more particularly relate to a kind of glaze that ceramic tile surface obtains to have traditional art glaze transmutation glaze effect that is used for.
Background technology
The ceramic product of traditional ceramics artistic glaze transmutation glaze effect, because it is its outward appearance has allusion, natural, aesthetic such as color and luster is changeful, very popular.But the traditional ceramics artistic glaze can only be at firing temperature more than 1300 ℃, could obtain required transmutation artistic effect under the condition such as firing time more than 8 hours, has the production cost height, the shortcoming of narrow application range; And existing ceramic tile working condition is about 1200 ℃, burnt till fast in 50～120 minutes etc., is to make ceramic tile surface obtain the transmutation glaze effect of similar traditional ceramics artistic glaze with conventional formulation; Thereby the tradition burn till the transmutation glaze the firing temperature height, the speed of burning till is slow, manufacturing cost is high, firing condition be difficult to control.
Summary of the invention
Purpose of the present invention is exactly in order to solve above-mentioned deficiency, and provide a kind of under existing ceramic tile working condition, promptly 1200 ± 20 ℃ of firing temperatures, firing period can make ceramic tile surface that the glaze of traditional ceramics artistic glaze transmutation glaze effect is arranged in the time of 50～120 minutes.
The technical solution that the present invention adopts in order to reach above-mentioned effect is as follows:
A kind ofly be used for the serial glaze product that ceramic tile surface has transmutation glaze effect, it is characterized in that, it is made of flux frit and coloring oxide or coloring compound or mineral dye of raw mineral materials such as clay or ball clay or calcined clay, zirconium silicate, porcelain stone powder or pottery stone powder, silica powder, Wingdale, rhombspar, zinc oxide, calcium phosphate, wollastonite, barium carbonate, aluminum oxide powder, titanium dioxide, triphane, Feldspar Powder and burning talcum powder etc. and low temperature, concrete following feed composition and proportioning, 1.0～25 weight part Li of adopting
2O/Na
2O/K
2O, 0～20 weight part CaO, 0～10 weight part MgO, 50～85 weight part SiO
2, 2.0～20 weight part Al
2O
3, 0.5～30 weight part B
2O
3, 0～25 weight part ZrO
2, 0～30 weight part TiO
2, 0.5～50 weight part ZnO, 2～15 weight part BaO, 0～20 weight part P
2O
5, 0～50 weight part PbO, 0.5～30 weight part coloring oxide or coloring compound or mineral dye, get the batching of said components during preparation ready, in mixing machine, mix and get final product.
The effect that the present invention adopts above-mentioned technical solution to reach is:
The present invention series glaze can be used in 1200 ℃ ± 20 ℃ of firing temperatures, firing period and the ceramic tile that working condition is produced such as burn till in 50～120 minutes fast, makes ceramic tile surface that the transmutation glaze effect of similar traditional ceramics artistic glaze be arranged.
Embodiment
The present invention is used for the serial glaze product that ceramic tile surface has transmutation glaze effect, constitute by flux frit and coloring oxide, coloring compound, mineral dye of raw mineral materials such as clay or ball clay or calcined clay, zirconium silicate, porcelain stone powder or pottery stone powder, silica powder, Wingdale, rhombspar, zinc oxide, calcium phosphate, wollastonite, barium carbonate, aluminum oxide powder, titanium dioxide, triphane, Feldspar Powder and burning talcum powder etc. and low temperature, concrete following feed composition and proportioning, the 1.0 weight part Li of adopting
2O/Na
2O/K
2O, 10 weight part CaO, 2 weight part MgO, 52 weight part SiO
2, 10 weight part Al
2O
3, 5 weight part B
2O
3, 5 weight part ZrO
2, 5 weight part TiO
2, 10 weight part ZnO, 2 weight part BaO, 5 weight part P
2O
5, 15 weight part PbO, 3 weight part coloring oxides or coloring compound or mineral dye.
Its preparation process is, gets the batching of said components ready, mixes to get final product in mixing machine.
The present invention also has another embodiment, promptly concrete following feed composition and proportioning, the 1.5 weight part Li of adopting
2O/Na
2O/K
2O, 5 weight part CaO, 3.5 weight part MgO, 60 weight part SiO
2, 5 weight part Al
2O
3, 6 weight part B
2O
3, 4 weight part ZrO
2, 5 weight part TiO
2, 15 weight part ZnO, 5 weight part BaO, 3 weight part P
2O
5, 5 weight part PbO, 2 weight part coloring oxides or coloring compound or mineral dye.
Its preparation process is, gets the batching of said components ready, mixes to get final product in mixing machine.
During use, with glaze of the present invention to suitable quantity of water, place the ball mill endosphere to wear into the glaze slip that requires fineness, then this glaze slip is coated the ceramic tile base surface of executing the cosmetic glaze or not executing the cosmetic glaze, add coloured silk, drying, burnt till fast through general ceramic tile production process again through about 1200 ℃, 50～120 minutes, be the ceramic tile finished product, ceramic tile surface has the transmutation glaze effect of similar traditional ceramics artistic glaze.
Claims (1)
1, a kind ofly is used for the glaze that ceramic tile surface has transmutation glaze effect, it is characterized in that, it is made of through uniform mixing flux frit and coloring oxide or coloring compound or mineral dye of raw mineral materials such as clay or ball clay or calcined clay, zirconium silicate, porcelain stone powder or pottery stone powder, silica powder, Wingdale, rhombspar, zinc oxide, calcium phosphate, wollastonite, barium carbonate, aluminum oxide powder, titanium dioxide, triphane, Feldspar Powder and burning talcum powder etc. and low temperature, specifically adopts following feed composition and proportioning: 1.0～25 weight part Li
2O/Na
2O/K
2O, 0～20 weight part CaO, 0～10 weight part MgO, 50～85 weight part SiO
2, 2.0～20 weight part Al
2O
3, 0.5～30 weight part B
2O
3, 0～25 weight part ZrO
2, 0～30 weight part TiO
2, 0.5～50 weight part ZnO, 2～15 weight part BaO, 0～20 weight part P
2O
5, 0～50 weight part PbO, 0.5～30 weight part coloring oxide or coloring compound or mineral dye.