CN1821438A - Sputtering apparatus and sputter film deposition method - Google Patents
Sputtering apparatus and sputter film deposition method Download PDFInfo
- Publication number
- CN1821438A CN1821438A CN 200610059588 CN200610059588A CN1821438A CN 1821438 A CN1821438 A CN 1821438A CN 200610059588 CN200610059588 CN 200610059588 CN 200610059588 A CN200610059588 A CN 200610059588A CN 1821438 A CN1821438 A CN 1821438A
- Authority
- CN
- China
- Prior art keywords
- magnetron
- film
- film forming
- target
- light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention is sputtering apparatus and sputtering filming process. The turntable type sputtering apparatus possessing cavity with base plate holder has common magnetron and AC magnetron set simultaneously for application in forming low refraction index film and high refraction index film. During the filming process, AC magnetron is first used until reaching 90 % designed film thickness, and only common magnetron is then used for further filming, and this can reach high film thickness control accuracy and high production efficiency.
Description
The application be that February 6, application number in 2002 are 02804597.1 the applying date, denomination of invention divides an application for the patent application of " sputter equipment and spatter film forming method ".
Technical field
The present invention relates to be applicable to the sputter equipment and the spatter film forming method of film formation process such as optical filter, be particularly related to and be applicable to sputter equipment and the spatter film forming method of the used WDM of manufacturing WDM (Wavelength Division Multiplexing, wavelength-division multiplex) technology with spectral filter.
Background technology
In Japanese patent laid-open 3-253568 communique, disclosed and on substrates such as sheet glass, carried out the carousel-type sputter equipment that film forming is used.The carousel-type sputter equipment is the sputter equipment of rotary batch-type, has following structures, and promptly the substrate retainer (going barrel) of the polygon cylindricality of configuration in chamber is put the magnetron that maintains rectangular target inboard the sending out of chamber wall simultaneously.One side makes the substrate retainer rotation that substrate has been installed, and one in the face of the magnetron supply power, makes the top generation plasma of target, introduces the reactant gases of regulation simultaneously in chamber, by carrying out film forming like this.
In addition, according to Japanese patent laid-open 11-241162 communique, the method for utilizing the thickness in the optical measuring device watch-keeping film forming to carry out sputter has been proposed.
Recently, the WDM spectral filter that the WDM technology that receives publicity in the field of opticfiber communication is used is with the film of low-index material (SiO for example
2Film) with the film of high-index material (Ta for example
2O
5Film) alternate combinations, stacked very many layers (for example about 100 layers) and forming.When making such optical multilayer, importantly to correctly form the thickness of each layer according to design load, hope a kind of high speed of exploitation and high precision are carried out the technology that film forming is used.
Figure 27 is the synoptic diagram of optical multilayer film forming usefulness sputter equipment in the past.In approximate circle tubular chamber 200, dispose polygon tubular substrate retainer 202, at each side installation base plate 204 of substrate retainer 202.In the chamber wall inboard, low refractive index film is set forms the magnetron sputter source 206 of usefulness and the magnetron sputter source 208 that high refractive index film forms usefulness, the former is equipped with low refractive index film and forms with target (for example Si target) 210, and the latter is equipped with high refractive index film and is formed with target (for example Ti target) 212.
But the problem that above-mentioned film deposition system in the past exists is to be difficult to carry out high-precision thickness management, for the thickness precision is provided, must corresponding reduction film forming speed, and productivity significantly reduces.
Though the Japanese Patent spy opens the description that clear 49-115085 communique does not have relevant carousel-type sputter equipment, but a kind of method is proposed, it is in film formation process, sputter equipment is supplied with the energy intermittently, measure thickness at energy off period (during stopping to supply with), then this result is fed back to energy supplyystem.But the shortcoming of this method is that film formation process hockets with the measurement operation, because film forming is interrupted in measurement, therefore produces rate variance.
In addition, as described in Japanese patent laid-open 3-253568 communique, in the sputter equipment (method) of two power supplys that adopt two negative electrodes and this negative electrode supply power is used, realize under the situation of uniform film thickness trying hard to, because two negative electrodes are film forming in couples, therefore for the principal element that influences film forming speed (state on magnetic field, added voltage, target surface and air pressure etc.), must reduce two difference between the negative electrode.But, being difficult to make two term harmonizations that negative electrode is relevant, the result is not easy to control the even of thickness.
The present invention carries out in view of such situation just, and purpose is to provide and can controls thickness and high sputter equipment and the spatter film forming method of productivity with high precision.In addition, purpose is to provide than can simplyr reaching uniform film thickness originally and can the implement device miniaturization reaching sputter equipment and spatter film forming method cheaply.
Summary of the invention
In order to reach aforementioned purpose, the described carousel-type sputter equipment in the application the 1st aspect, described carousel-type sputter equipment has following structure, it is Polygons or circular drum that the cross section that rotates freely promptly is set in chamber, the substrate retainer is set on the outer surface of this drum, at the inboard of chamber wall configuration magnetron sputter source, described magnetron sputter source is by target and keep the magnetron of this target partly to constitute, described target utilizes described magnetron partly to keep, make the shaft parallel of itself and described drum, this sputter equipment has the film thickness measurement device of measuring the thickness that is contained in the film that forms on the substrate of described substrate retainer in film forming, described target is supplied with the power subsystem of sputter desired power, and the measuring result of utilizing described film thickness measurement device to obtain is controlled and is influenced the parameter control of film forming amount device.
According to the present invention, in the carousel-type sputter equipment, can in film forming, monitor thickness, this message feedback to Controlling System, is controlled then.As the parameter control that influences the film forming amount, except the power control of shielding power supply, the control of the rotating speed of substrate retainer (drum), baffle opening, sputtering pressure etc. in addition.For example, when stopping film forming, stop to supply with the power of shielding power supply or close baffle plate etc.
As the described sputter equipment in the application the 2nd aspect, comprise that the AC type magnetron sputter source and the single magnetron of anode/cathode relation that alternately switches two targets of disposed adjacent with assigned frequency partly go up the magnetron sputter source that target is installed.
As " single magnetron is partly gone up the magnetron sputter source that target is installed ", except DC (direct current) type magnetron sputter source, also have RF (high frequency) type magnetron sputter source and pulse mode (adding volts DS at interval) type magnetron sputter source etc. with certain hour.
AC type magnetron sputter source is partly gone up the magnetron sputter source that target is installed with single magnetron and is compared, can the high speed film forming.The present invention adopts this two kinds of sputtering sources just simultaneously, realizes at a high speed and the high precision film forming.
In this case, as described in the application the 3rd aspect, has following control form, promptly begin to utilize described AC type magnetron sputter source to carry out the high speed film forming from film forming, before film forming reaches target film thickness a certain amount of after, then stop to utilize described AC type magnetron sputter source to carry out film forming, switch to and only utilize described single magnetron partly to go up the low speed film forming of the magnetron sputter source that target is installed, carry out film forming till described target film thickness.By such control, can carry out high-precision film thickness monitoring.
Have again, as described in the application the 4th aspect, preferably carry out the form of following control, promptly in described low speed film forming, utilize described film thickness measurement device to monitor thickness, arrive moment of described target film thickness detecting thickness, stop to utilize described single magnetron partly to go up the magnetron sputter source that target is installed and carry out film forming.And, normally in film forming, monitor thickness all the time.
Only using the magnetron sputter source that target is installed on the single magnetron part to carry out between the low speed film stage thickness being monitored, give Controlling System with its message feedback, by like this can be with high precision control thickness more.
The described carousel-type sputter equipment in the application the 5th aspect, described carousel-type sputter equipment has following structure, it is Polygons or circular drum that the cross section that rotates freely promptly is set in chamber, the substrate retainer is set on the outer surface of this drum, in the configuration of the inboard of chamber wall by target and the magnetron sputter source that keeps the magnetron of this target partly to constitute, described target utilizes described magnetron partly to keep, make the shaft parallel of itself and described drum, this sputter equipment only have switch disposed adjacent mutually with assigned frequency the AC type magnetron sputter source of anode/cathode relation of two targets as described magnetron sputter source, have film thickness measurement device one side in film forming simultaneously and make described drum rotation one planar survey be contained in the thickness of the film that forms on the substrate of described substrate retainer, described target is supplied with the power subsystem of sputter desired power, and the measuring result of utilizing described film thickness measurement device to obtain is controlled and is influenced the parameter control of film forming amount device.
When formation requires film thickness error to be the stacked film of 1% order of magnitude, only use high speed AC type magnetron, just can form the film that meets the demands.
When the present invention being used to make WDM and alternately forming the device that low refractive index film and high refractive index film use like that with the used optical multilayer film deposition system of spectral filter etc., as described in the application the 6th aspect, adopt to have to be provided with simultaneously and the low refractive index film film forming is housed forms the magnetron sputter source of usefulness and the sputter equipment of high refractive index film film forming with the structure of the magnetron sputter source of the high refractive index film formation usefulness of target is housed with the low refractive index film of target.
Form the magnetron sputter source of usefulness and each sputtering source that high refractive index film forms the magnetron sputter source of usefulness about low refractive index film, by utilizing the magnetron sputter source combination that target is housed on AC type magnetron sputter source and the single magnetron part to constitute respectively, thereby in the film formation process of the film formation process of low refractive index film and high refractive index film, can realize high speed film forming and high precision control film forming.
Certainly, thickness precision as requested also can be only to use AC type magnetron to carry out film forming form.
According to the described form in the application the 7th aspect, described film thickness measurement device has the infrared rays receiver of output behind the transmitted light of the described measuring light of the light projector device of described substrate irradiation measuring light and the described substrate of acceptance irradiation or the reflected light with the corresponding electrical signal of this light income, in described drum rotation, by shining measuring light to described substrate, carry out the measurement of described thickness from described light projector device.
The relevant film thickness measurement device of this form is not directly to measure thickness, but measures indirect information.Be that film thickness measurement device is made of light projector device and infrared rays receiver, infrared rays receiver output and the corresponding electrical signal of accepting of light quantity.Measuring light adopts the monochromatic measurement light of 550nm for example or the monochromatic measurement light of the 549nm shorter than its wavelength.But be not limited to from the form of light projector device irradiation monochromatic measurement light, the form that also has is light projector device irradiation white (non-selected wavelength) measuring light, forms monochromatic ray at sensitive side.
Shown in the application the 8th aspect, deliver to machine unit from the electrical signal (being subjected to optical signal) of infrared rays receiver output, utilize machine unit to calculate transmissivity information or reflectivity information.Machine unit can be included in the film thickness measurement device as required, also can be included in the control device.
According to the described form in the application the 9th aspect, described machine unit is 0 ° according to the input angle of described measuring light and is subjected to optical signal from what described infrared rays receiver obtained when comprising near 0 ° predetermined angular scope, try to achieve and corresponding transmissivity of input angle or reflectivity, obtain the data of the relation of expression input angle and transmissivity or reflectivity.
In the carousel-type sputter equipment, because substrate retainer rotation, therefore under the situation that light projector device that film thickness measuring is used and infrared rays receiver are fixedly installed on prescribed position, the input angle of measuring light is changing all the time.When calculating vertical incidence in (input angle is 0 °) predetermined angular scope before and after it 1 or multiple spot are subjected to optical signal, try to achieve transmissivity or the reflectivity relation with respect to input angle.
The profile of the input angle that the utilization expression obtains like this and the relation of transmissivity or reflectivity (expression is with respect to the curve of the transmissivity or the reflectance varies of input angle) can accurately determine film forming terminal point etc.For example by the profile relatively calculated with have the existing profile of product of objective optics characteristic, or utilize the methods such as change of shape of the profile that real-time follow-up calculates, can determine film forming terminal point.
In addition, send out other form as the present invention, just like the described form in the application the 10th aspect, described film thickness measurement device have to the light projector device of the described substrate multiple measuring light that illumination wavelength is different selectively and accept the transmitted light of described measuring light of the described substrate of irradiation or reflected light after be transformed to infrared rays receiver with the corresponding electrical signal of this light income, in the rotation of described drum, by shining measuring light to described substrate, carry out the measurement of described thickness from described light projector device.For example, switch the measuring light of using 550nm and 549nm selectively.
As described in the application the 11st aspect, deliver to machine unit from the electrical signal (being subjected to optical signal) of infrared rays receiver output, utilize machine unit to calculate the transmissivity information or the reflectivity information of the multiple measuring light different with respect to described wavelength.
According to the described form in the application the 12nd aspect, described machine unit is according to the multiple measuring light different with respect to described wavelength, input angle is respectively 0 ° and be subjected to optical signal from what described infrared rays receiver obtained when comprising near 0 ° predetermined angular scope, try to achieve and corresponding transmissivity of input angle or reflectivity, obtain the data of the relation of expression input angle and transmissivity or reflectivity.
Have, just like the described form in the application the 13rd aspect, described machine unit is similar to conversion according to the data of the relation of the described expression input angle that obtains and transmissivity or reflectivity, calculates spectral-transmission favtor or spectral reflectivity again.
According to the data of transmissivity that obtains in the predetermined angular scope or reflectivity, utilize angular transformation is tried to achieve the operational method of approximation for wavelength, can try to achieve the spectral-transmission favtor or the spectral reflectivity of the side that this measurement wavelength of wavelength ratio will grow.By utilizing the different multiple measuring light of wavelength to measure transmissivity or reflectivity, can carry out the higher measurement of precision.
In addition, in the sputter equipment of the invention described above, also has a kind of ideal form, its constitute have according to the monochromatic measurement light of provision wavelengths in its input angle at 0 ° and be subjected to optical signal from what described infrared rays receiver obtained when comprising near 0 ° predetermined angular scope, try to achieve with corresponding transmissivity of input angle or reflectivity, obtain the data of expression input angle and the relation of transmissivity or reflectivity and first measurement function of its formation curve; Calculate second measurement function of mean value of data of the relation of the aforementioned expression input angle that obtains and transmissivity or reflectivity; Carry out conversion, calculate the 3rd measurement function of spectral-transmission favtor or spectral reflectivity according to the data of the relation of the described expression input angle that obtains and transmissivity or reflectivity; And the measuring light of the side that will lack with the described provision wavelengths of wavelength ratio is tried to achieve and corresponding transmissivity of input angle or reflectivity at 0 ° and the optical signal that is subjected to that obtains from described infrared rays receiver when comprising near 0 ° predetermined angular scope in its input angle, obtain the data of expression with respect to the relation of the transmissivity of input angle or impingement rate, and be similar to conversion with respect to the data of the relation of the transmissivity of input angle or reflectivity according to this expression that obtains, calculate the 4th measurement function of spectral-transmission favtor or spectral reflectivity, in described first to fourth measurement function, according to the stage of film formation process, the measurement function that corresponding switching utilized or its combination.
When making optical multilayer, owing to the stage corresponding to film process, the optical property of film changes, and therefore is suitable for the measuring method in each stage by employing, can try hard to improve measuring accuracy and film thickness monitoring precision.
According to the form shown in the application the 14th aspect, it is characterized in that described film thickness measurement device is arranged on the position of leaving described magnetron sputter source.So-called " position of leaving ", be meant " with near the magnetron medullary ray of infrared rays receiver (by the magnetron center and with the vertical line of target seating surface) with the intersection point of chamber outer wall as benchmark, along the girth on the outer wall surface leave more than the 150mm in the horizontal direction, the position more than the 900mm particularly ".By making measure portion leave film formation space, can reduce the interference that produces because of plasma light, can carry out high-precision measurement.
Have, shown in the application the 15th aspect, the cone (cylindrical body that opacifying property is arranged) around the transmitted light of the described measuring light of additional encirclement or the light path that reflected light passes through is by covering the plasma scattered light from film formation space so again.In this case, preferably shown in the application the 16th aspect, make described chamber and described cone electric insulation, form floating potential.In addition, the form shown in the application the 17th aspect preferably also, promptly the leading section of described cone install can reduce because of and described substrate between the anti-reflection member of influence of the scattered light that causes of multipath reflection.
Utilize such form, can reduce the interference that causes because of plasma light significantly, can carry out high-precision measurement from film formation space.
The sputter equipment that the application the 18th aspect is relevant, has the AC type magnetron sputter source of anode/cathode relation that alternately switches two targets of disposed adjacent with assigned frequency, single magnetron is partly gone up the magnetron sputter source that target is installed, and control device, described control device is controlled, making begins to utilize described AC type magnetron sputter source to carry out the high speed film forming from film forming, before reaching target film thickness, film forming stop to utilize described AC type magnetron sputter source to carry out film forming after a certain amount of, switch to and only utilize described low speed film forming of on single magnetron part, the magnetron sputter source of target being installed, carry out film forming till described target film thickness.
The present invention uses AC type magnetron sputter source to reach the magnetron sputter source that target is installed on single magnetron part to realize that high speed is film forming simultaneously, can realize high-precision film thickness monitoring simultaneously, it is desirable to be applicable to the carousel-type sputter equipment especially.
As other form of the present invention, be according to the described sputter equipment in the application the 19th aspect, when described target was in position with described substrate subtend now and concerns, described target surface had the angle of inclination of regulation, makes that the target surface of described substrate opposite is not parallel with respect to real estate.
So-called " the position relation of subtend ", mean the substrate retainer the substrate seating surface central point with from the distance of the central point of the magnetron part of this substrate seating surface for hour.In addition, under the situation of AC type magnetron sputter source, the central point of two targets of disposed adjacent (two targets are made as a whole central point when seeing a magnetron part as) is interpreted as " central point of magnetron part ".
The angle of inclination is the angle that is designed to the best according to the structure condition of the sputter equipment that target is installed.That is, target surface is tilted.By adopting such apsacline target, can adjust the direction of splashing of sputtered atom, can adjust the substrate of rotation and the various conditions such as relation of distance between the target and angle simultaneously, realize reaching uniform film thickness along the direction of motion of substrate.Certainly, also can there be a kind of form to be, in a carousel-type sputter equipment, mixes the plate target (target commonly used) and the apsacline target of the present invention that exist in the past.
The described invention in the application the 20th aspect provides the device relevant with the application the 1st aspect and invents corresponding method invention.That is, the method that the application the 20th aspect is relevant is to adopt the carousel-type sputter equipment to carry out film forming spatter film forming method, and described carousel-type device has following structure.It is Polygons or circular drum that the cross section that rotates freely promptly is set in chamber, the substrate retainer is set on the outer surface of this drum, at the inboard of chamber wall configuration magnetron sputter source, described magnetron sputter source is by target and keep the magnetron of this target partly to constitute, described target utilizes described magnetron partly to keep, make the shaft parallel of itself and described drum, described spatter film forming method is characterised in that this method is included in the film thickness measuring operation of measuring the thickness that is contained in the film that forms on the substrate of described substrate retainer in the film forming, and the information of utilizing the measuring result that described film thickness measuring operation obtains is controlled and is influenced the parameter control of film forming amount operation.
The described invention in the application the 21st aspect provides the device relevant with the application the 18th aspect and invents corresponding method invention.Promptly, the method of the application the 21st aspect, be to adopt sputter equipment to carry out film forming spatter film forming method, described sputter equipment has the AC type magnetron sputter source of anode/cathode relation that alternately switches 2 targets of disposed adjacent with assigned frequency, and single magnetron is partly gone up the magnetron sputter source that target is installed, described spatter film forming method is characterised in that, this method begins to utilize described AC type magnetron sputter source to carry out the high speed film forming from film forming, before reaching target film thickness, film forming stop to utilize described AC type magnetron sputter source to carry out film forming after a certain amount of, switch to and only utilize described low speed film forming of on single magnetron part, the magnetron sputter source of target being installed, carry out film forming till described target film.
In this case, preferably the form shown in the application the 22nd aspect is promptly measured thickness in film forming, and utilizes the parameter that the information that obtains in the described measurement is controlled influences the film forming amount.
The application's described invention in the 23rd to 32 aspect provides relevant with the application the 5th and 7 and even 15 aspects respectively device and invents corresponding method invention, and the described invention in the application the 33rd aspect provides the device relevant with the application the 19th aspect and invents corresponding method invention.
Description of drawings
Figure 1 shows that the floor map that the relevant optical multilayer film forming of the invention process form constitutes with sputter equipment.
Fig. 2 is the stereographic map of the substrate retainer that uses in the device shown in Figure 1.
Figure 3 shows that the example of the thickness monitor signal graphic representation of present embodiment.
Figure 4 shows that the spectral pattern figure of the bandpass optical filter of making according to present embodiment.
Fig. 5 uses the synoptic diagram of sputter equipment for the relevant optical multilayer film forming of other example of the present invention.
The synoptic diagram of the example of the additional anti-haftplatte of the sputter equipment shown in Fig. 6 presentation graphs 5.
Figure 7 shows that the synoptic diagram of various cathode arrangement examples.
Figure 8 shows that the target of main use among the present invention and the chart of mould material example.
Figure 9 shows that the chart of the substrate example that uses among the present invention.
Figure 10 uses the pie graph of sputter equipment for the relevant optical multilayer film forming of other example of the present invention.
Figure 11 shows that the detailed formation skeleton diagram of the thickness system of supervision of utilizing halogen lamp.
Figure 12 shows that the detailed formation skeleton diagram of the thickness system of supervision of utilizing variable wavelength laser.
Figure 13 is the synoptic diagram of film thickness distribution ununiformity in the explanation carousel-type sputter equipment in the past.
Figure 14 (a) is the sectional view of the relevant target of the invention process form, (b) is its orthographic plan.
Figure 15 is the synoptic diagram of the effect of explanation inclination shape target.
Figure 16 carries out the graphic representation of film forming film thickness distribution for relatively utilizing inclination shape target shown in Figure 14 to carry out film forming film thickness distribution with utilizing in the past plate shaped target (target commonly used).
Figure 17 is applicable to the pie graph of high speed film forming with the inclination shape target of sputtering source.
Figure 18 carries out the graphic representation of film forming film thickness distribution for relatively utilizing inclination shape target shown in Figure 17 to carry out film forming film thickness distribution with utilizing in the past plate shaped target (target commonly used).
Figure 19 is applicable to high speed film forming other formation example synoptic diagram with the inclination shape target of sputtering source.
Figure 20 shows that and on glass substrate, form TiO
2The optical transmittance change curve of wavelength 550nm during film.
Shown in Figure 21 for forming by glass/(TiO
292.9nm/SiO
257.3nm)
7/ TiO
2185.8nm/ (SiO
257.3nm/TiO
292.9nm)
7Membrane structure constitute 29 layers of single chamber bandpass optical filter (centre wavelength is 550nm) time the transmission change graphic representation that produces of wavelength 550nm measuring light.
The graphic representation of the relation of transmisivity data that in film forming, obtains for the interval A among Figure 21 shown in Figure 22 and angle.
The graphic representation of the relation for the transmissivity in film forming, measured after the 28th layer among Figure 21 and angle shown in Figure 23.
Figure 24 is for the graphic representation of measuring transmittance graph data that wavelength 550nm, input angle the obtain spectral-transmission favtor through being similar to conversion and obtaining in 0 ° ± 10 ° scope.
Graphic representation for the transmittance graph data that in 0 ° ± 10 ° scope, obtain with measurement wavelength 549nm, input angle shown in Figure 25.
Figure 26 is the graphic representation of the spectral-transmission favtor that data shown in Figure 25 is similar to conversion and obtains.
Shown in Figure 27 is the formation synoptic diagram of optical multilayer film forming usefulness sputter equipment in the past.
Figure 28 is the orthographic plan of substrate retainer.
Shown in Figure 29 is the orthographic plan of other form of substrate retainer.
Shown in Figure 30 is the floor map that the relevant optical multilayer film forming of the invention process form constitutes with sputter equipment.
Figure 31 is the sectional view along the 31-31 line of Figure 30.
Figure 32 is the orthographic plan of cone.
Figure 33 is the side elevational view of cone.
Shown in Figure 34 is the overview of membrane structure and the chart of thin film-forming method.
Figure 35 is for only adopting the film deposition system sketch drawing of the magnetron of AC mode.
Shown in Figure 36 is the chart of membrane property evaluation result.
The table look-up of the membrane property target value that requires for optical multilayer shown in Figure 37.
Label declaration
10 sputter equipments, 12 chambers, 14 substrate retainers, 14 substrate retainers, 14A measures and uses the hole, 16 central shafts (rotating shaft), 17 drums, 18 substrates, 18A, 18B monitored object substrate, 20 magnetron sputter sources (low refractive index film forms and uses magnetron sputter source), 21 magnetron parts, 22 power supplys, 23 magnetrons commonly used, the 23A medullary ray, 24,25 magnetron parts, 26 AC power, the 27AC magnetron, the 27A medullary ray, 30 magnetron sputter sources (high refractive index film forms and uses magnetron sputter source), 31 magnetron parts, 32 power supplys, 33 magnetrons commonly used, the 33A medullary ray, 34,35 magnetron parts, 36 AC power, the 37AC magnetron, the 37A medullary ray, 40 halogen lamps, 41 monochromators, 42 optical fiber, 44 light projector heads (film thickness measurement device), 46 are subjected to shaven head (film thickness measurement device), 48 light receiving areas reason unit, 49 control amplifiers, 50 Personal Computer (control device, machine unit), 51CPU (control device, machine unit), 52,53, the 54Ti target, 62,63, the 64Si target, 70 sputter equipments, 72,74,76,78 baffle plates, 80 anti-haftplattes, the head of 82 reflection-type watch-dogs, 84 episcotisters, 85 photomultiplier cells, 86 lamp power supplys, 87 light-dividing devices, 88 photorectifiers, 90 variable wavelength lasers, 92 targets, 92A, 92B target scarp, the 92C crest line, 94,95,96,97 targets, 96A, 96B, 97A, the 97B scarp, 100 sputter equipments, 120 cones, 122 supports, 124 stay pipes, 126 insulcretes, 128 insulation coverings, 130 shading covers, 131 holes, 140 film deposition systems, 142 magnetron controlling boards, 151, the 152Ta target, 161, the 162Si target, 200 chambers, 202 substrate retainers, 204 substrates, 206 low refractive index films form uses magnetron sputter source, 208 high refractive index moulds form uses magnetron sputter source, 210,212 targets, 214 central shafts, 216,218 shielding power supplies.
Embodiment
The desirable example of sputter equipment of the present invention and spatter film forming method is described below with reference to the accompanying drawings.
Figure 1 shows that the floor map that the relevant optical multilayer film forming of the invention process form constitutes with sputter equipment.Fig. 2 is the stereographic map of the substrate retainer of use in this device.Sputter equipment 10 shown in Figure 1 is to have following structure to constitute the carousel-type sputter equipment, promptly in the cylindrical cavity 12 of high 1.5m, diameter 1.5m, it is (not shown among Fig. 1 to have drum, be label 17 among Fig. 2) reach the substrate retainer 14 that on the outer surface of this drum 17, is provided with, each the substrate retainer 14 that constitutes the dodecagon of diameter 1m can be that rotation center is rotated and supports with the central shaft 16 of drum 17.
The chamber 12 that becomes reaction chamber is connected with not shown off-gas pump, can access the needed low pressure of sputter.In addition, also be provided with in chamber 12 and introduce air feeder and the loading door that the needed gas of sputter is used, this is not shown in the drawings.In addition, the inwall of chamber 12 has with drum 17 and separates approximate predetermined distance and the shape (interior toroidal) of subtend.
As shown in Figure 2, substrate retainer 14 is installed in the outer surface of the drum 17 of drum, with the drum that can rotate freely 17 rotations that are provided with.In addition, the shape of drum 17 is not limited to round shape, also can be polygon tubular (cross section is a Polygons) etc.
As shown in Figure 1, film forming is installed with substrate (for example being glass substrate) 18 on substrate retainer 14, substrate retainer 14 is along with the rotation of the drum that utilizes not shown rotating driving device to drive, and (for example 6rpm rotates with certain rotating speed.Low refractive index film is set respectively in the inboard of chamber 12 to be formed with magnetron sputter source 20 and high refractive index film formation magnetron sputter source 30.The length that these magnetron sputter sources 20 and 30 are short transverses is the rectangular magnetron sputtering source of 1.2m, makes the front of substrate 18 by magnetron sputter source 20 or 30, film forming.
Equally, magnetron sputter source 30 is to utilize single magnetron part 31 is connected the combination of the magnetron commonly used 33 of power supplys 32 and the AC magnetron 37 that two magnetron parts 34 and 35 is connected an AC power 36 and constitutes.
In addition, sputter equipment 10 has halogen lamp 40, monochromator 41, optical fiber 42, light projector head 44, is subjected to shaven head 46 and light receiving area reason unit 48 as the device (thickness system of supervision) of measuring thickness in the film forming.Utilize monochromator 41 to carry out by optical fiber 42, guiding light projector head 44 into after wavelength selects from the light of halogen lamp 40.Light projector head 44 is arranged on the inboard (inboard of drum 17) of substrate retainer 14, from substrate 18 irradiates lights of light projector head 44 to rotation.As shown in figure 28, the vertical middle portion at substrate retainer 14 forms along sense of rotation than opening (measure the use hole) 14A of long light by usefulness.Measure the size (being 30mm in this example) that forms the roughly the same degree of spot diameter of projection light with the longitudinal length of hole 14A, light is measured by this and is used hole 14A, irradiation monitored object substrate 18A.The width of measuring the length direction of using hole 14A is big more, and the ranges of incidence angles of measuring light is wide more.In addition, also can be form as shown in figure 29, promptly, measure thickness measuring the monitored object substrate 18B that the film thickness measuring special use is installed with the part of hole 14A.
In the outside of chamber shown in Figure 1 12, be provided with and be subjected to shaven head 46.Be provided with at the outer wall of chamber 12 and guide light into be subjected to shaven head 46 window (not shown).The light that sees through substrate 18 is with being accepted by shaven head 46, be transformed to the corresponding electrical signal of light income after, deliver to light receiving area and manage unit 48.The signal processing that the signal of the light receiving area reason 48 pairs of acceptance in unit is stipulated is transformed to the take off data that computer is imported usefulness.Deliver to Personal Computer in the take off data 50 that light receiving area reason unit 48 is handled.
In Fig. 1, the Lights section of the optical measuring device of using as film thickness measuring is to adopt halogen lamp 40 and monochromator 41, but the Lights section of the employed optical measuring device of film thickness monitoring system is not limited to the formation example of Fig. 1, can select suitable light source according to measuring object.For example when manufacturing WDM uses spectral filter, adopt the tunable laser (variable wavelength laser) of wavelength 1460~1580nm.In addition, being not limited to adopt the form of monochromatic measurement light, also can be to form unicolor form with white measuring light in light receiving unit one side.Compare with the form of utilizing monochromatic measurement light, form unicolor form, have and disturb few advantage in light receiving unit one side.
The following describes the action of the sputter equipment 10 that constitutes as mentioned above.What following embodiment illustrated is to utilize reactive sputtering to form SiO respectively
2Film is as low refractive index film and form TiO
2Film is as the example of high refractive index film.
At the beginning, form each magnetron part 31,34 and 35 of using magnetron sputter source 30 at high refractive index film Ti targets 52,53 and 54 are installed, form with magnetron sputter source 20 each magnetron part 21,24 and 25 at low refractive index film Si target 62,63 and 64 is installed.The size of target commonly used adopts the target of high 1.1m, wide 15cm, and the size of each target that AC uses adopts the target of high 1.1m, wide 10cm.
In addition, on each substrate retainer 14, vertically arrange each 9 glass substrate that thick 1.1mm, 10cm are square is installed.Then, utilize rotor pump that chamber 12 is evacuated to 5pa earlier after, bleeding with cryopump reaches 1 * 10
-5Pa.
Then, argon gas is introduced in the chamber 12 by mass flow controller with the flow of 30sccm with flow and the oxygen of 100sccm.At this moment air pressure is 0.4pa.In addition, sccm is the flow (cm under the standard state (0 ℃, a normal atmosphere)
3/ minute).
In order to form SiO
2Film, the magnetron commonly used 23 that Si target 62 is installed is supplied with the square wave pulse power (frequency is 50KHZ) of direct current 10KW the AC magnetron 27 that Si target 63 and 64 are installed is supplied with the power that exchanges 20KW, close the baffle plate (not shown among Fig. 1) that disposes between target and substrate, carry out 5 minutes pre-arcing, open baffle plate between the two then, carry out film forming.
In film forming, utilize above-mentioned thickness system of supervision that the substrate on the substrate retainer 14 18 is measured transmissivity.Because therefore the corresponding variation with film forming thickness of transmissivity of substrate 18 by monitoring transmissivity, can grasp thickness.For the purpose of reference, Figure 3 shows that the thickness monitor signal example of present embodiment.
One side utilizes the thickness system of supervision to monitor thickness, and one side is carried out film forming, reaches at 90% o'clock that designs thickness in film forming, stops 27 power supplies of AC magnetron are only carried out film forming with magnetron 23 commonly used.In film forming, with the measuring result of Personal Computer 50 calculating transmissivities, give each power supply 26 and 22 with the message feedback of this measuring result, by controlling like this, make and improve the homogeneity of film forming, make thickness reach the design thickness simultaneously along the sense of rotation of substrate 18.In addition, the rotating speed that also can control basal plate retainer 14 or the aperture (switching amount) of baffle plate are adjusted film forming.
Then, in order to form TiO
2Film is supplied with the power of direct current 15KW to the magnetron commonly used 33 that Ti target 52 is installed, and the AC magnetron 37 that Ti target 53 and 54 are installed is supplied with the power that exchanges 30KW, with SiO
2The film formation process of film is identical, and after carrying out 5 minutes pre-arcing, the baffle plate of opening between the two carries out film forming.At TiO
2Too, reach at 90% o'clock that designs thickness under the situation of film, stop 37 power supplies of AC magnetron are only carried out film forming with magnetron 33 commonly used in film forming.In film forming, give each power supply 36 and 32 with the measurement feedback of transmissivity, to improve the homogeneity of film, carry out correct thickness management, this point and SiO
2The film formation process of film is identical, repeats above-mentioned SiO
2The film formation process of film and TiO
2The film formation process of film is made glass (substrate)/SiO
2(94.2nm)/TiO
2(57.3nm)/SiO
2(94.2nm)/TiO
2(57.3nm)/SiO
2(94.2nm)/TiO
2(57.3nm)/SiO
2(188.2nm)/TiO
2(57.3nm)/SiO
2(94.2nm)/TiO
2(57.3nm)/SiO
2(94.2nm)/TiO
2(57.3nm)/SiO
213 layers of bandpass optical filter (94.2nm).In addition, such membrane structure is expressed as glass/(SiO
294.2nm/TiO
257.3nm)
3/ SiO
2188.2nm/ (TiO
257.3nm/SiO
294.2nm)
3
Figure 4 shows that the spectral response curve of the bandpass optical filter that this is made.Black circle (●) among this figure is a design load, and solid line is depicted as the spectral response curve measuring result of utilizing the bandpass optical filter that present embodiment makes.Be for relatively shown in the dotted line, the spectral response curve measuring result of the bandpass optical filter that to be expression make with the sputter equipment that does not have the AC magnetron of previous embodiment, Figure 27 of the feedback system of power supply is not constituted like that.According to shown in Figure 4, the bandpass optical filter that adopts the present invention to make has approximate spectral response curve according to design load, but with not to the feedback of power supply and the bandpass optical filter of making has peak value in the wavelength place transmissivity different with the design wavelength (550nm) of bandpass optical filter.
By utilizing the relevant sputter equipment of this example 10, can on substrate 18, form multilayer film at a high speed, and can carry out film thickness monitoring with high precision, can make WDM with spectral filter and dichroic mirror etc. with high productivity.
In the case of the above embodiments, reach 90% thickness of design thickness before, be to make AC magnetron and magnetron work commonly used simultaneously, only stop the discharge of AC magnetron then, only make magnetron commonly used continue discharge, but control mode does not limit this example.For example also can be only with AC magnetron film forming reach 90%, then only with the such control method of magnetron film forming commonly used.Certainly, the moment that stops the AC magnetron is not limited to the 90% film forming moment of design thickness, can suitably set.
In addition, in the above-described embodiments, be in the AC magnetron power supply (arrive the design thickness 90% before during) also be that one side monitors that thickness simultaneously carries out film thickness monitoring, though monitor but also can in to the power supply of AC magnetron, carry out thickness, but portion carries out film thickness monitoring, supply power and the resulting thickness predictor of sputtering time according to investigation are in advance carried out time management, stop the AC magnetron is powered through after the specified time.Then, also can adopt the form that when only beginning film forming, begins film thickness monitoring (for example power supply being carried out feedback control) with magnetron commonly used.
The place (measurement point) of measuring thickness on substrate 18 can be a place of substrate 18 middle portions, also can be carry out the many places measurement along horizontal (being called " working direction ") of sense of rotation, to measure horizontal film thickness distribution.Also can be along a plurality of film thickness measurement devices of vertical configuration of the rotating shaft of substrate retainer 14 (light projector head 44 and be subjected to shaven head 46), adopt in many places longitudinally and carry out the form of film thickness measuring.
During film forming, substrate retainer 14 is in rotating state all the time, and the measurement of transmissivity is that the circle to substrate retainer 14 carries out one or once above sampling (preferably once sampled in each limit of dodecagonal, amount to 12 times).For example, the rotating mechanism of substrate retainer 14 has substrate mounting face that revolution 1 circle produces the rotational position sensor of a signal and substrate retainer 14 produces signal when the prescribed position by the circumferential direction decision substrate position transmitter, the signal that these position transducers are produced is measured each time sampling as triggering signal.
In addition, even omit these position transducers,, therefore also can measure owing to can obtain by carrying out the periodic measurement signal that continuously measured obtains.But, by utilizing position transducer,, therefore can carry out correct measurement as mentioned above owing to can clearly grasp the relation of measurement signal and measuring position.
Like this, the transmisivity data that obtains under the substrate rotating state conspires to create the data into the relation of expression transmissivity of film and angle.It is that 0 ° transmissivity is that the line at center becomes the such numerical value of symmetry that this serial data is got input angle with measuring light in theory.Utilize this symmetry, can access input angle and be 0 ° transmissivity, can also be with the approximate spectral response curve that is transformed to of angular relation.Method about approximate conversion will be described in detail with Figure 21 to Figure 26.
The following describes the variation of above-mentioned example.
Fig. 5 is the synoptic diagram of the relevant optical multilayer film forming of other example with sputter equipment 70.In Fig. 5, the part additional phase identical label together with Fig. 1, it illustrates omission.In addition, in Fig. 5, for graphic simplicity, the halogen lamp 40 that do not draw among the figure, monochromator 41, optical fiber 42, light receiving area reason unit 48 and Personal Computer 50 etc. constitute (also identical in Fig. 6 and Fig. 7).
In the sputter equipment 70 shown in Figure 5, form two portions of usefulness and high refractive index film formation usefulness for low refractive index film, its magnetron 23 commonly used and 33 and the place that is provided with of AC magnetron 27 and 37 be spaced, baffle plate 72,74,76,78 to be opened/closed is set respectively between each magnetron (23,33,27,37) and substrate 18.In the figure, expression forms the state of low refractive index film, be configured in the magnetron commonly used 23 of low refractive index film formation usefulness and the baffle plate 72 and 76 of AC magnetron 27 fronts and be in open mode, high refractive index film forms the magnetron commonly used 33 of usefulness and the baffle plate 74 and 78 of AC magnetron 37 fronts is in closing condition and be configured in.
Among this figure, utilizing reactive sputtering process to obtain desirable thickness constantly, by closing baffle plate 72 and 76, can determine film formation reaction is stopped, the baffle plate 74 and 78 by closing the no sputtering source of film forming simultaneously can prevent the deterioration of target.If the film forming of low refractive index film finishes, then open baffle plate 74 and 78, carry out the film forming of high refractive index film.
In addition, as shown in Figure 6, also preferably adopt form at the anti-haftplatte 80 of the left and right sides of each magnetron (23,33,27,37) configuration.Anti-haftplatte 80 has the effect that prevents that plasma from moving into, and only to being positioned at the positive substrate 18 of magnetron part filming function is arranged, and prevents substrate (adjacent substrate) film forming in addition.Utilize anti-haftplatte 80 surround respectively each magnetron sputter source about, by isoionic influence that not produced by other magnetron sputter source, prevent from target is adhered to impurity.
Figure 7 shows that the variation diagram of cathode arrangement.When enforcement is of the present invention, shown in Fig. 7 (a) to (d), various forms can be arranged for cathode arrangement." H " label among this figure represents that high refractive index forms the negative electrode (magnetron part) of usefulness, and " L " expression low refractive index film forms negative electrode (the magnetron part of usefulness.Fig. 7 (a) forms the example that negative electrode that the negative electrode of usefulness and low refractive index film form usefulness separates configuration with high refractive index film, as Fig. 5 explanation.Fig. 7 (b) is for fear of isoionic interference, makes high refractive index film form the negative electrode of usefulness and the adjacent example of negative electrode that low refractive index film forms usefulness.Fig. 7 (c) is the interference that monitors for fear of to thickness, monitored position is set in the example of the position of leaving negative electrode.Fig. 7 (d) is depicted as the example that adopts transmission-type supervision and reflection-type to monitor the device of conduct measurement thickness simultaneously.
Transmission-type monitor as Fig. 1 explanation like that, be with light projector head 44 and be subjected to the device of the transmissivity of bare headed 46 measurement substrates 18.Reflection-type monitors it is from the beginning 82 to substrate 18 irradiates lights, accepts its reflected light with 82 again, is subjected to optical signal to come the device of measurement of reflectivity by analysis.Though do not draw among the figure, it also is to use the halogen lamp identical with Fig. 1 40, monochromator 41 and optical fiber 42, with measuring light guide that reflection-type monitors into 82, by being subjected to light signal processing device, deliver to Personal Computer 50 with 82 light (reflected light) that receive.
Shown in Fig. 7 (d), adopt transmission-type to monitor at the same time and situation that reflection-type monitors under, preferably adopt the low zone of transmissivity to control and form that the measuring result of the high zone employing transmissivity of transmissivity is controlled with the measuring result of reflectivity.Promptly, preestablishing becomes judgement transmission-type/reflective control switching transmissivity (judgment standard value) of benchmark, when transmissivity is lower than this judgement substrate value, utilize the measuring result of reflectivity to control, when transmissivity is higher than the judgment standard value, utilize the measuring result of transmissivity to control.
Target that mainly uses when Figure 8 shows that the invention process and mould material.As low-index material, have and adopt aforesaid Si target to form SiO
2The form of film, also useful in addition SiC target forms SiO
2The form of film adopts the alloys target of Si and Al to form by SiO in addition
2And AL
2O
3The form of the oxide film that constitutes etc.
About high-index material too, except the form of useful aforesaid Ti target formation TiO2 film, in addition as shown in Figure 8, can form various mould materials by selecting target.In addition, target can also be with the oxide compound that can carry out the DC sputter, nitride, oxynitride, carbide etc. except metal (conductive material), and this does not draw in Fig. 8.
The example of the substrate that utilizes when Figure 9 shows that the invention process.As shown in the drawing, WDM uses the WMS (devitrified glass) of OHARA company production with in the spectral filter.In addition, the substrate as other spectral filter is used can use various glass shown in Figure 9 such as colourless transparent plate glass, hard glass and artificial crystal according to purposes.
The following describes other example of the present invention.
Figure 10 is the pie graph of the relevant optical multilayer film forming of other example with sputter equipment 100.In the figure, for Fig. 1 and the identical or similar part additional phase of device shown in Figure 5 with label, it illustrates omission.In Figure 10, the AC magnetron 27 that indicates the magnetron commonly used 23 of " low speed film forming 1 " and indicate " high speed film forming 1 " is sputtering sources that the low refractive index film film forming is used.In addition, the AC magnetron 37 that indicates the magnetron commonly used 33 of " low speed film forming 2 " and indicate " high speed film forming 2 " is sputtering sources that the high refractive index film film forming is used.
These magnetrons 23,27,33,37 are towards the configuration of the direction of rotation center, make its their medullary ray 23A, 27A, 33A and 37A (be by each magnetron center and with the vertical line of target seating surface) intersect with the rotation center (central shaft 16) of substrate retainer 14.As shown in figure 10, if utilize the inscribed circle of the dodecagon of substrate retainer 14 formations to be 15A, circumcircle is 15B, and then substrate retainer 14 is to the distance of each magnetron 23,27,33 and 37, along with the rotation of substrate retainer 14, in scope, change from inscribed circle 15A to circumscribed circle 15B.State in the figure is that the distance of central point and the central point of each magnetron 23,27,33 of seeing from this substrate seating surface and 37 of the substrate seating surface of substrate retainer 14 is hour state (state that the position of substrate and target subtend concerns)
When adopting halogen lamp 40 as the light source of thickness system of supervision, as shown in figure 10, at the output configuration dimmer 84 of monochromator 41.Utilize dimmer 84 periodically to cover output light (monochromatic ray), the computing of removing the light source interference components by the comparers that utilize like this in the light receiving area reason unit 48 from monochromator 41.Light receiving area reason unit 48 has output makes the modulation signal of dimmer 84 actions, the magnitude of voltage that is subjected to optical signal that will import simultaneously be transformed to the control amplifier (indicating label 49 among Figure 11) that offers CPU51 after the numerary signal.
Figure 11 shows that the detailed formation skeleton diagram of the thickness system of supervision of utilizing halogen lamp.Halogen lamp 40 is accepted the power supplied with from lamp power supply 86 and luminous.After utilizing monochromator 41 to form monochromatic ray by the light (white light) of halogen lamp 40 irradiation, be incident to dimmer 84.Dimmer 84 is according to the modulation signal action that is provided by control amplifier 49, by the modulated monochromatic ray of dimmer 84 outputs.This modulated monochromatic ray utilizes light-dividing device (half-mirror etc.) 87 to be divided into two.Wherein a part is introduced becomes in the chamber 12 of film formation space, the substrate 18 of irradiation measuring object (be equivalent to measure and use sample).The light of transparency carrier 18 is incident to photomultiplier cell 85, is transformed to the light quantity correspondent voltage signal with transmitted light.By the voltage signal of photomultiplier cell 85 output, utilize control amplifier 49 to be transformed to numerary signal after, deliver to CPU51.
In addition, utilize another part light of light-dividing device 87 beam split, be incident to photorectifier 88 as obtaining the light that light source information uses.49 pairs of photorectifiers 88 of control amplifier provide the modulation signal synchronous with dimmer 84, from the light quantity correspondent voltage signal of photorectifier 88 outputs with the light source direct sunshine of monochromator 41 outgoing.From the voltage signal of photorectifier 88 output is transformed to numerary signal control amplifier 49 after, deliver to CPU51.
CPU51 carries out the calculating of transmissivity, the calculating of blooming and the calculating of rate of film build etc. according to the data of the transmitted light of importing from control amplifier 49 and the data of light source direct sunshine.
Also can be not limited to adopt white light with halogen lamp 40 to utilize monochromator 41 to form the form of irradiated substrate 18 behind the monochromatic ray, but, form monochromatic ray at sensitive side with white measuring light irradiated substrate 18.In this case, be subjected to the leading portion configuration monochromator of shaven head 46.Form monochromatic form and compare at sensitive side, can reduce interference with the form of monochromatic measurement light.
Also can adopt system shown in Figure 12 to constitute, constitute to replace system shown in Figure 11.In Figure 12, to or similar portions additional phase together label identical with Figure 11, it illustrates omission.In example shown in Figure 12, the Lights section adopts variable wavelength laser 90, utilizes the grating in the variable wavelength laser cell to select output wavelength.In addition, because the output of variable wavelength laser 90 is stable, therefore do not need the supervision of light source direct sunshine illustrated in fig. 11.In Figure 12, use synthetic monochromatic ray, but also can be with not synthetic.In addition, light-dividing device 87 shown in Figure 12 also can omit.
But, the carousel-type sputter equipment since its structure is an one side make constitute regular polygon each substrate retainer rotation, one side is carried out film forming, therefore as Japanese patent laid-open 3-253568 communique is also pointed out, be positioned at the part on the limit of regular polygon and be positioned at part on the rib, it closely reaches different with respect to the relation of the real estate angle of target with the short circuit of target.Therefore, sputtered atom adheres to the probability difference with respect to substrate, has the uneven tendency of sense of rotation (one side rotation one side, then is called " working direction " according to this meaning along substrate transverse width direction progressive direction) of film thickness distribution with respect to substrate.
Figure 13 shows that its synoptic diagram.Figure 13 (a) is depicted as part around the limit that is positioned at the regular polygon that is made of substrate retainer 202 near the state of target 210, and the rib that Figure 13 (b) is depicted as regular polygon is near the state of target 210.In addition, label 220 is liner plates that the magnetron part of target 210 is installed.Sputtered atom adhere to probability depend on from target 210 to substrate each position on 204 apart from r and direction thereof (be called " vector<r〉") and vector<r with the included angle of real estate.
As Figure 13 (a) and (b), because rotation along with substrate retainer 202, be positioned at the part around the limit of regular polygon and be positioned at the vector<r of the part around the rib〉and angle φ change, therefore in film in the past, shown in Figure 13 (c), exist the peripheral part of substrate 204 to adhere to the tendency of the thickness of more atom, peripheral part greater than centre portions.
In the present invention, even in order to reach film thickness distribution, the relevant sputter equipment 100 of this example adopts target shown in Figure 14.Figure 14 (a) is a sectional view, and Figure 14 (b) is an orthographic plan.This target 92 is to be applicable to the label 23 of Figure 10 and the target of the sputtering source that the low speed film forming shown in the label 33 is used, as shown in figure 14, the upper surface of target is that central position (along the crest line 92C of the rotor shaft direction of drum 17) formed spike, two directions tilt to the left and right then, promptly have the shape of so-called roof shape (inverted v-shaped).Tilt angle theta with respect to the horizontal plane depends on the distance (mean diameter in the design etc.) between limit number, diameter, size of substrate, substrate and the target of the regular polygon of substrate retainer 14 formations, in order to realize that film thickness distribution is even, be designed to best angle.
Target in the past is certain plate shaped of thickness of slab, and when concerning in the position that is in substrate and target subtend, real estate and target surface are in parastate (with reference to Figure 13 (a)).On the contrary, when target 92 shown in Figure 14 concerns in the position that is in substrate and target subtend, become target surface keeps some angles (tilt angle theta) a little with respect to real estate state.
If adopt the target 92 that constitutes as mentioned above, then as Figure 15 (a) and (b), because sputtered atom penetrates from target scarp 92A and 92B, so its distribution of splashing (density of sputtered atom) is to launch (promptly becoming the emission of V font) along the normal direction of target scarp 92A and 92B.In addition, fine taking into account becomes the target of atom outgoing plane scarp 92A and 92B to the distance of each position of substrate 18 and direction thereof (vector<r 〉) and vector<r〉with the various conditions such as relation of the included angle of real estate, overall consideration in addition, like this shown in Figure 15 (c), can realize that uniform film thickness distributes along the working direction of substrate 18 (among the figure laterally).
Figure 16 carries out the graphic representation of film forming film thickness distribution for relatively adopting inclination shape target 92 of the present invention and carry out film forming film thickness distribution and adopt in the past plate shaped target (target commonly used).Curve shown in this figure is the experimental result that obtains under following implementation condition.Promptly, in sputter equipment shown in Figure 10 100, adopt each substrate retainer of the dodecagon that constitutes diameter 1m, the distance of getting between substrate and the target is 60mm, substrate size is that 35cm is square, carries out film forming result and inclination shape target 92 (tilt angle theta=5 °) is installed is carried out film forming result in that " target commonly used " is installed on sputtering source with the described low speed film forming of label 23 (or 33).In addition, each the face installation base plate retainer expansion fixture on substrate retainer surface is installed the square substrate of 35cm.
As can be seen from Figure 16, if with target commonly used, then the thickness of peripheral part is greater than the thickness of substrate center, but under the situation of inclination shape target 92 of the present invention, thickness becomes even along the distribution of working direction.
The sputtering source of using with above-mentioned low speed film forming is identical, for the sputtering source of using with the high speed film forming shown in label 27 and 37 among Figure 10, can adopt inclination shape target 94 and 95 shown in Figure 17.Target 94 shown in the orthographic plan of the sectional view of Figure 17 (a) and Figure 17 (b) can be used as the target shown in the label 63 and 54 of Figure 10.In addition, Figure 17 (c) and (d) shown in target 95 can with shown in the label 64 and 53 of Figure 10 as target.Use in the sputtering source (AC magnetron) in the high speed film forming, owing to make the target surface of two targets of disposed adjacent tilt can not reach uniform film thickness to same direction, so these two targets will be to be the relation configuration of line symmetry (perhaps proximal line symmetry) mutually.
Each target 94 shown in Figure 17 and 95 tilt angle theta are that the actual conditions that depends on sputter equipment is designed to best angle.As also illustrating among Fig. 1, because the AC magnetron used of high speed film forming is alternately to switch in the anode/cathode relation of the target that two adjacent magnetrons partly install and can work as a sputtering source on the whole, therefore as shown in figure 17, about target 94 and 95 have (the only one-sided inclination of single scarp respectively, be so-called wedge shape), like this when these two targets 94 and 95 are used in combination, constitute the roof shape target surface identical with target illustrated in fig. 14 92.About the effect of target shown in Figure 17 94 and 95, then identical with Figure 15.
Figure 18 is the graphic representation that relatively adopts the film thickness distribution that AC the magnetron film thickness distribution that produces and the AC magnetron that adopts plate shaped target (target commonly used) in the past of inclination shape target 94 shown in Figure 17 and 95 produce.Curve shown in Figure 180 is the experimental result that obtains under following implementation condition.Promptly, in sputter equipment shown in Figure 10 100, adopt each substrate retainer of the dodecagon that constitutes diameter 1m, get between substrate and the target apart from being 60mm, substrate size is that 35cm is square, carries out film forming result and inclination shape target 94 is installed and 95 (both tilt angle theta all are 5 °) carries out film forming result in that " target commonly used " is installed on sputtering source with the described high speed film forming of label 27 (or 37).In addition, each the face installation base plate retainer expansion fixture on substrate retainer surface is installed the square substrate of 35cm.
As can be seen from Figure 18, if with target commonly used, then the thickness of peripheral part is greater than the thickness of substrate center, but under the situation of inclination shape target of the present invention, thickness becomes even along the distribution of working direction.
Also can be to adopt target 96 shown in Figure 19 and 97 form, to replace target shown in Figure 17 94 and 95.That is, with the target 94 of the 96 displacement Figure 17 of the target shown in Figure 19 (a) and (b), with the target 95 of the 97 displacement Figure 17 of the target shown in Figure 19 (c), (d).Target shown in Figure 19 is applicable to that target 96 about the AC magnetron and 97 upper surface form the form of roof shape (" A " shape) respectively.In this case, the pitch angle (θ 2) of the scarp 96B in the pitch angle of Nei Ce scarp 96A and 97A (θ 1) and the outside and 97B is the desired value that structure condition of depending on sputter equipment 100 etc. is designed to.By like this, can realize thickness being evenly distributed in working direction.
The following describes other example of relevant thickness method for monitoring.
For blooming nd (here, n is the specific refractory power of film, and d is the physics thickness) as target, if the light that adopts the wavelength X satisfy following formula (1) is as measuring light,
(formula 1)
nd=mλ/4 ……(1)
In the formula, m is a positive integer, and λ is a light wavelength
Make this measuring light vertically inject substrate in the film forming (input angle=0 °), measure its transmissivity (or reflectivity), then when the blooming of formed film becomes 1/4 integral multiple of measuring wavelength X (when satisfying above-mentioned formula (1)), transmissivity (or reflectivity) reaches extreme value.
Figure 20 shows that and on glass substrate, form TiO
2(n=2.4) during film transmissivity with respect to the change curve of measuring wavelength 550nm.In the figure, transverse axis is represented film forming thickness (geometrical film thickness d), and the longitudinal axis is represented transmissivity.As shown in the drawing, when blooming nd was the integral multiple of λ/4, transmissivity showed as extreme value.
Utilize such phenomenon,, adopt the light of the measurement wavelength X that satisfies above-mentioned formula (1), just can carry out thickness supervision and film forming control thickness as target.
But under the situation of the carousel-type sputter equipment shown in Fig. 1 or Figure 10, therefore input angle and measuring position (monitored position) of measuring light are changing always because substrate retainer 14 is in rotation.When the input angle of measuring light changes,, then be difficult to carry out the control of high-precision measurement and film forming if great changes will take place for the value of transmissivity.In fact, under the situation of film more than 10 layers that constitutes, cause that the extreme value place of transmissivity and transmissivity change, therefore be difficult to carry out film thickness measuring and film forming is controlled with in the past method because the input angle of measuring light changes.
About addressing the above problem the method for usefulness, describe with concrete example below.
Shown in Figure 21 is to form by glass/(TiO
292.9nm/SiO
257.3nm)
7/ TiO
2185.8nm/ (SiO
257.3nm/TiO
292.9nm)
7Membrane structure constitute 29 layers of single chamber bandpass optical filter (centre wavelength 550nm) time wavelength 550nm the change curve of the transmissivity that causes of measuring light.
If be conceived to the optical property of the film in each stage in the film process, then as shown in figure 21, can be divided into four intervals of interval A~D.
Interval A (the first layer~12nd layer) is that transmissivity and thickness have very big relation and the interval that has nothing to do basically with the input angle of measuring light.In fact, 0 ° of incident transmissivity is consistent basically with the value of 10 ° of incident transmissivities.Interval B (the 13rd layer~the 18th layer) is that transmissivity and thickness have nothing to do substantially, have nothing to do substantially with input angle again and the variation interval seldom of transmissivity.Interval C (the 19th layer~the 29th layer) is promptly relevant with thickness, the relevant interval with input angle again.0 ° of incident transmissivity and 10 ° of incident transmissivities have a great difference, 10 ° of incident transmissivity numerical value little (less than 10%).In addition, interval D (the 29th layer) adjusts the interval that optical characteristics is used.
In each interval, carry out the control of suitable supervision and film forming respectively, just can improve the controllability of the optical property that monitors precision and film.The following describes the control method in each interval.
Film thickness monitoring among the<interval A 〉
Obtain the graphic representation of the relation of transmisivity data and angle in the film for the first layer, the second layer, the 3rd layer and the 9th layer formation shown in Figure 22.From the interval (interval A) of the first layer to the Floor 12, as shown in figure 22, even input angle changes, transmissivity is also constant basically.Thereby, the transmisivity data that obtains continuously in the substrate rotation in being scope about ± 5 °~± 15 °, input angle is averaged, by so substantially the same numerical value of transmissivity can access with vertical incidence the time.Transmissivity during then according to the vertical incidence that obtains calculates the time that transmissivity reaches extreme value, and the value of transmissivity reaches the moment of the value that becomes extreme value actually, stops film forming, adopts such method can control thickness.In addition, because the substrate 18 that becomes measuring object in rotation, when 0 ° of incident, be that the center of substrate 18 is measured, and input angle is big more therefore.What then monitor is the position of departing from substrate center more.But, owing to utilize the inclination shape target of Figure 14 to Figure 19 explanation.Therefore even along the film thickness distribution of substrate working direction, if consider in conjunction with this point, even then monitored position change, also can the correct measurement thickness.
Film in the<interval B 〉
In the 13rd layer to the 18th layer interval, because the value of transmissivity is little, the variation of the transmissivity that causes with respect to the thickness increase is little, therefore is difficult to carry out high-precision film thickness monitoring.Thereby, in this interval B, transmissivity is data and image data for reference only, main according to the transmission change amount in the film formation process of the first layer to the Floor 12 and the relation of film formation time, calculate current rate of film build, one to the time that can access desired thickness, then stops film forming, adopts such method to control thickness with film formation time.
Film among the<interval C 〉
Shown in Figure 23 is the graphic representation of the relation of the 28th layer of later transmissivity and angle.From the 19th layer to the 29th interval (interval C), as shown in figure 23,, therefore be difficult to the control method that adopts interval A such owing to the value of transmissivity depends on that angle changes.But, as shown in figure 23, because the point of the transmissivity when the expression input angle is 0 ° becomes transmittance graph and the crossing point of the symmetric symmetry axis of line that utilizes measurement to obtain, therefore even without the expression input angle strictness triggering function in 0 ° the moment, also can be by the transmisivity data of utilizing measurement to obtain being carried out calculation process, the transmissivity of (input angle is 0 °) when trying to achieve vertical incidence.In addition, the transmittance graph peak that can measure according to utilization, with respect to the velocity of variation or the area (being curve shape) of angle, judgement obtains the thickness of extreme value.Have again, be similar to conversion, as shown in figure 24, can access the spectral-transmission favtor of long wavelength's one side of measuring wavelength X by angle is changed the transmittance graph that obtains.
Shown in Figure 24 for to input angle being the graphic representation that the data of the transmittance graph obtained in 0 ° ± 10 ° the scope are similar to the spectral-transmission favtor that conversion obtains.By utilizing the data of ± 10 ° of scopes, can predict and measure wavelength (=550nm) long wavelength's one side is the spectral-transmission favtor of 550nm≤λ≤552.35nm.This predictor as shown in figure 24, and is consistent with high precision with the spectral-transmission favtor (spectral-transmission favtor of Que Rening by experiment) of reality.
Film among the<interval D 〉
Continuous successively film forming process, because actual thickness can produce error with respect to target film thickness, therefore can not obtain desirable optical characteristics sometimes from the first layer.Under these circumstances, the layer that carries out the optical characteristics correction is set in film process.In this example, revise the layer (final layer) of usefulness as this with the 29th layer, with it as interval D.
In the D of this interval, utilize from satisfy the such measurement wavelength of formula (1) (λ=550nm) a little to short wavelength's one lateral deviation from the measuring light of wavelength, carry out the measurement of transmissivity.In this example, utilize the measuring light of wavelength X=549nm to measure, obtain signal shown in Figure 25.Utilize the take off data that obtains like this, identical with C between aforementioned zones, by being similar to conversion, as shown in figure 26, long wavelength's one side that can try to achieve measurement wavelength X=549nm is the spectral-transmission favtor of 549nm≤λ≤551.35nm.
The spectral-transmission favtor of trying to achieve like this is consistent with actual spectral-transmission favtor, and consistent degree reaches high precision.In film formation process, obtain the change curve of spectral-transmission favtor shown in Figure 26, all can see by reaching " bandwidth " etc. for " centre wavelength ", " transmissivity of specific wavelength " of the optical property of bandpass optical filter like this.Thereby, can simultaneously confirm to make its satisfied performance as target, one side compensates thickness (being optical characteristics), can improve the qualification rate (percentage of A-class goods) of product like this.In above-mentioned example, be the light that adopts λ=549nm as from measure wavelength X=550nm a little to short wavelength's one lateral deviation from measuring light, can change according to the kind and the number of plies of the film of wanting to measure but measure the light wavelength of using.
In above-mentioned example, described is the example that calculates transmissivity, but when the invention process, also can calculate reflectivity, to replace transmissivity, perhaps calculates with transmissivity.
(improving the technology that thickness monitors precision)
The following describes the method that improves the film thickness measuring precision.
When in film forming, measuring the optical characteristics of transmissivity or reflectivity, the problem that exists is, light receiving unit can detect from the light beyond the light projector unit (mainly being the plasma light in the film formation space generation of magnetron part periphery), is difficult to carry out high-precision spectral measurement.For this problem, adopt and the synchronous synchronizing amplifier of chopper frequency, just can reduce interference.
But,, therefore be difficult to remove fully this interference because the plasma luminescence intensity in the spatter film forming is unsettled in time.Particularly when the measurement light intensity was measured under more weak condition, existence caused the interferential problem because of the plasma scattering.
In order to solve such problem, in example of the present invention, measure portion (light receiving unit and light projector unit) is departed from configuration with respect to film formation space along the circumferential direction that the substrate retainer rotates, to reduce the influence of plasma light.In example shown in Figure 30, from the position of magnetron (23,27,33,37) configuration along the circumferential direction away from the position, the allocating and measuring part.In addition, in Figure 30, for the part additional phase identical with Fig. 1 label together, it illustrates omission.As shown in figure 30, make the detection position leave film formation space,, carry out high-precision supervision by improving the S/N ratio like this.
The amount of leaving of film formation space and monitored position (distance) can be carried out various designs according to the apparatus structure of reality, but with medullary ray and the chamber outer wall intersection point near the magnetron of light receiving unit is reference point, be preferably to get and leave position more than the 150mm in the horizontal direction, preferably get and leave the above position of 900mm along the girth on the outside wall surface.
Have, be preferably in and be subjected between shaven head 46 and the light projector head 44, promptly configured length is approximately equal to the cone 120 at chamber 12 and substrate retainer 14 intervals between measurement that chamber wall forms is with window and substrate retainer, with the light path of covering measuring light.In addition, make this cone 120 and chamber 12 electric insulations, be in floating dummy status, by interdicting plasma scattered light so widely from film formation space.
Figure 31 is the sectional view along the 31-31 line of Figure 30.As shown in figure 31, be subjected to shaven head 46 to be installed in the outer wall of chamber 12 by support 122.Cone 120 is installed in the inwall of chamber 12, makes it hide the light path of measuring light.In addition, label 124 is stay pipes of supporting optical fiber 42.
Figure 32 is the orthographic plan of cone 120, and Figure 33 is the side elevational view of cone 120.Metallic substance such as this body and function SUS304 of cone 120 form, and this cone 120 is installed on the chamber 12 by insulcrete 126 intermediaries.Use insulation covering 128 during installation, utilize not shown screw to fix.In addition, as the material of insulcrete 126 and insulation covering 128, the special teflon of fluorine resin (trade name of tetrafluoroethylene) for example preferably.Certainly, also can be the form that forms the body of cone 120 with special teflon and other insulating material.
Leading section at cone 120 is provided with shading cover 130.Shading cover 130 utilizes blackish special teflon to form, and is formed centrally the hole 131 that is similar to identical size with the spot diameter of projection light in shading cover 130.In addition, be in when floating state at cone 120 bodies, though the material as shading cover 130 also can use the such conductor of SUS304, but in this example, influence for the scattered light that suppresses to produce because of the multipath reflection between substrate 18 and the shading cover 130, from preventing the viewpoint of multipath reflection, use black special teflon.
Utilize aforesaid method, can reduce the interference that causes because of plasma light significantly, even under chopper frequency is lower situation about 270HZ, also can carry out high-precision measurement.According to experiment as can be known, by the cone 120 that floating-potential is set, the S/N ratio has improved 200 times.Illustration method among Figure 30 to Figure 33 can be applicable to each example that illustrates among Fig. 1 to Figure 26.
(only using the example of AC magnetron)
At the example described in the above-mentioned example be, be provided with at the same time in the carousel-type sputter equipment of magnetron of the magnetron of AC mode and current version and carry out film forming, the measurement of the optical characteristics (transmissivity or reflectivity) by carrying out film continuously in addition, when the difference of the thickness in target film thickness and film forming is big, make high-speed side magnetron (AC magnetron) and low speed survey magnetron (magnetron commonly used) discharge simultaneously, carry out film forming, if reduce with the difference of target film thickness, then only carry out film forming with the low speed side magnetron, by carrying out accurate film thickness monitoring like this, can access stacked film with desirable optical characteristics.Morphotic device like this is to be that the high film of thickness precision below 0.01% is required in order to form communication with the such film thickness error of bandpass optical filter.
With last different be, as shown in figure 34, low-reflection film, streamline spectral filter (edge filter) (infrared reflection spectral filter, ultraviolet reflection spectral filter, infrared and ultraviolet line reflection spectral filter, visible light reflecting filter etc.) and polarizing filter etc. that the purposes of using for indicating meter, projector, lighting fixtures, various camera gun such as component are used, these film thickness error are only required under the situation of the membrane structure about 1~5%, just can meet the demands with the device formation that does not have the low speed film forming with magnetron.
Only requiring the device of stacked film of such specification of 1% left and right sides order of magnitude as forming film thickness error, is not use low speed film forming magnetron, and usefulness high speed film forming magnetron film forming only the following describes the such method and the form of device.
The synoptic diagram of the film deposition system for the magnetron of only using the AC mode shown in Figure 35.In the figure, for the label same with the identical or similar part additional phase of the example of Fig. 1, it illustrates omission.This film deposition system 140 is carousel-type sputter equipments, has following formation, it is in the cylindrical cavity 12 of high 1.5m, diameter 1.5m, each the substrate retainer 14 that constitutes the dodecagon of diameter 1m can be with central shaft 16 as the rotation center rotation and support, in the configuration of the inboard of chamber wall with the rectangular target of two long 1m AC magnetron 27 and 37 as one group.The substrate retainer 14 that is loaded with substrate 18 is rotated with the speed of 30rpm, and substrate 18 is by the front of AC magnetron 27 and 37, and film forming.This routine film deposition system 140 is provided with the AC magnetron 27 and 37 that low refractive index film forms usefulness and high refractive index film formation usefulness respectively.
This film deposition system 140 will pass through monochromator 41, dimmer 84 and optical fiber 42 from the light of halogen lamp 40, guide light projector head 44 into, and the substrate in the rotation is shone measuring light from light projector head 44.The light that substrate 18 is crossed in transmission passes through substrate retainer 14 and measures the cone of using between the window 120, accepts light on integrating sphere that is subjected to shaven head 46 and photorectifier.Like this, one side is carried out film forming, the transmissivity of the film of a planar survey substrate 18 and formation.
Calculate this measuring result with Personal Computer 50, feed back to magnetron controlling board 142 again, make to reach desirable thickness.In addition, magnetron controlling board 142 is control control sections to AC magnetron 27 and 37 power supplys of powering etc.As mentioned above, the AC magnetron is with two magnetron cathodes and row arrangement, when a magnetron is negative electrode, another magnetron becomes anode, be high frequency exchange negative electrode and anodic magnetron with tens KHZ, by control film forming parameter, make that the moving area at reactive sputtering keeps filming condition, can stablize and form at a high speed the film of oxide compound or nitride etc. like this.
Certainly, as the form of target, also can adopt the inclination shape target of Figure 17 or Figure 19 explanation.
The following describes the film forming order of using film deposition system shown in Figure 35.
At first, on the AC magnetron 37 of high refractive index film formation usefulness, Ta target 151 and 152 is installed, on the AC magnetron 27 of low refractive index film formation usefulness Si target 161 and 162 is installed simultaneously, the glass substrate 18 that thick 1.1mm, 10cm is square is installed on the substrate retainer 14.Then, with not shown rotor pump vacuum chamber 12 is evacuated to 5pa earlier after, be pumped to 2 * 10 with turbomolecular pump again
-4Pa.
After bleeding, the gas introduction port that forms side from high refractive index film is introduced the argon gas of 370sccm and the oxygen of 180sccm, begins discharge.Form the AC magnetron 37 of usefulness for high refractive index film, control power or gas flow etc. make to be held in membrane stage near moving area or its, carry out film forming with the film forming speed of the about 0.4nm of substrate retainer 14 each circle.At this moment, one side is carried out film forming, and each circle of one side changes the measurement of transmissivity
According to the transmisivity data that obtains like this, calculate present film forming thickness with respect to desired thickness, this result is fed back magnetron controlling board 142.If arrive target film thickness, then stop power supply to AC magnetron 37, perhaps in stage near target film thickness, close baffle plate (till the flapper closure substrate holder also rotate several circles~tens circles close) with low speed with such speed, by controlling like this, make that uniform film thickness reaches design load simultaneously on the sense of rotation.
In addition, in above-mentioned feedback control, also can consider the poor of target film thickness and present thickness,,, improve the thickness precision, shorten film formation time to control film forming speed by stages by changing the film forming parameter.
Then, be SiO in order to carry out low refractive index film
2Film forming, introduce the argon gas of 250sccm and the oxygen of 140sccm, begin discharge.For AC magnetron 27, control voltage makes to be held in membrane stage near moving area or its, carries out film forming with the film forming speed of the about 0.4nm of substrate retainer 14 each circle.At this moment, use method identical when forming with high refractive index film, each circle is measured transmissivity, and control AC magnetron 27 is to obtain desirable thickness.
Alternate repetition forms high refractive index film and low refractive index film like this, makes the visible light reflecting filter.
In addition, according to method same as described above, on the silicon wafer of diameter 10cm, form substrate/Ta
2O
5(200nm)/SiO
2(200nm)/Ta
2O
5(200nm)/SiO
2(200nm)/Ta
2O
5(200nm)/SiO
2(200nm)/Ta
2O
5(200nm)/SiO
2(200nm)/Ta
2O
5(200nm)/SiO
210 layers of stacked film (200nm).
Before and after this film forming, the surface of silicon wafer is used the FLX THINFILMS STRESS MEASUREMENT SYSTEM (FLX thin-film stress measuring system) of Tencor Instruments company) FleXus F2320, measure radius-of-curvature, poor according to this observed value, the stress of obtaining stacked film is stress under compression, is 17Mpa.
Shown in Figure 36 is the evaluation result of membrane property.In addition, in this chart, for the purpose of comparison, charge to the evaluation result of 34 layer of 4 μ m stacked film of the evaluation result of only using the film forming 26 layer of 3.0 μ m stacked film of DC mode magnetron and evaporation product simultaneously.The measuring method of projects is as described below.
Membrane stress uses the FleXus F2320 of the FLX THIN FILMS STRESSMEASUREMENT SYSTEM of Tencor Instruments company, measures before the film forming and the diameter 10cm silicon substrate warpage (radius-of-curvature) after the film forming, by trying to achieve like this.
Specific refractory power and reduction coefficient use J.A, and the spectrum polarizing light ellipsograph WVASE32 of Woollam Co.Inc. tries to achieve.
Turbidity value uses the muddy instrument TC-HIII of limited commercial firm Tokyo electricity look to try to achieve.
Slipperiness uses the multifunctional apparatus SPA-400 of Seiko instrument Co., Ltd. to try to achieve.
The method of trying to achieve of wavelength shift is as described below.1, the automated optical element measuring apparatus ART-25GT of the Japanese beam split of use Co., Ltd., the spectral-transmission favtor of measure sample.2, sample is put into the minienvironment trier SH-220 of Tabyspec Co., Ltd., under 60 ℃, the imposing a condition of 90%RH, placed 120 hours.3, sample is taken out from minienvironment trier SH-220, use automated optical element measuring apparatus ART-25GT, the measure spectrum transmissivity.4, with the difference of above-mentioned 1~3 measuring result as wavelength shift.
Shown in Figure 37 is as a reference the desired membrane property target value of optical multilayer table look-up.
Extremely shown in Figure 36 as Figure 35, if only use the AC magnetron to carry out film forming, then at membrane stress, specific refractory power, reduction coefficient.Turbidity value, slipperiness, weather resistance aspects such as (wavelength shifts) can obtain excellent result.In addition, the result who obtains in the thickness below about 4 μ m is with DC sputter and vapour deposition method, and along with thickness increases, its surfaceness (Ra) increases, but uses the AC sputtering method, and then irrelevant with thickness, surfaceness demonstrates the less numerical value in about 0.5nm left and right sides.
Industrial practicality
As mentioned above, according to the present invention, in the carousel-type sputter equipment, owing in film forming, monitor thickness, And utilize the parameter of this information control effect film forming amount, and therefore can correctly control thickness, can be with height production Rate forms the film of desired thickness.
According to other form of the present invention, owing to use simultaneously AC type magnetron sputter source to reach at single magnetic control The magnetron sputter source of target is installed on the tube portion, is being reached before a certain amount of of design thickness (target film thickness), Use AC type magnetron sputter source to carry out the high speed film forming, after obtaining a certain amount of film forming, stop to utilize AC Magnetron sputter source carries out film forming, only uses the magnetron sputter source that target is installed in single magnetron part, Therefore can control accurately thickness, can be with the high production rate film forming.
Having, as the film thickness measuring gimmick, is to utilize expression to measure incidence angle and transmissivity or the reflectivity of light again The change curve of relation, terminal point by can accurately determining like this film forming etc.
According to other other form of the present invention, be to carry out according to the relation of transmissivity or reflectivity and incidence angle Be similar to conversion, can grasp in real time the appearance curve of spectral-transmission favtor or spectral reflectivity, they are fed back to Film thickness monitoring is by being finish-machined to the profile of final products desirable (desirable optics like this The product of performance). By like this, can increase substantially the percentage of A-class goods of product.
In addition, according to other other form of the present invention, in the carousel-type sputter equipment, adopt inclination shape target Replace plate shaped target in the past, perhaps use simultaneously with it, by like this can on the direction of advance of substrate Realize easily uniform film thickness. As Unexamined Patent 3-253568 number disclose, adopt two negative electrodes and This negative electrode is provided in the sputtering method (device) of two power supplys that power uses, try hard to realize uniform film thickness The time, the film forming speed of two negative electrodes is equated, but in fact between negative electrode, be difficult to reduce to affect film forming The difference of principal element. The method according to this invention and device are owing to try hard to make the cathodic electricity of uniform film thickness Origin system can only have a power supply and consist of, so its advantage is, to the shadow of aforementioned principal element Sound is little, can realize more simply uniform film thickness, and simultaneously compared with the past, the formation of device is compactness and valency also Lattice are low.
According to desired thickness precision, also can not use DC type magnetron, only use AC type magnetron Carry out film forming. By using AC type magnetron to carry out film forming, can access the multilayer film of excellent.
In addition, in the present invention, as the device that improves the film thickness measuring precision, be the position that makes measure portion Away from film formation space, by reducing like this impact of measuring ionic medium light. The recycling cone surrounds Around the light path that measurement light passes through, with this cone and chamber insulation, at the electric state of floating that is in, Can interdict significantly like this plasma scattered light from film formation space.
Claims (9)
1. carousel-type sputter equipment, described carousel-type sputter equipment has following structure, that is:
It is Polygons or circular drum that the cross section that rotates freely is set in chamber, and a plurality of substrate retainers are set on the outer surface of this drum,
Dispose a plurality of magnetron sputter sources in the inboard of chamber wall,
Each magnetron sputter source is by target and keep the magnetron of this target partly to constitute,
Described target utilizes described magnetron partly to keep, and makes the shaft parallel of itself and described drum,
Described sputter equipment comprises:
In film forming, measure the film thickness measurement device of the thickness of the film that forms on the substrate that is contained on one of described a plurality of substrate retainers;
Each target is supplied with the power subsystem of sputter desired power; And
The measuring result of utilizing described film thickness measurement device to obtain is controlled influences the parameter control of film forming amount device.
2. sputter equipment as claimed in claim 1 is characterized in that,
Described a plurality of magnetron sputter source is the low refractive index film film forming to be housed with the magnetron sputter source of target and the combination of high refractive index film film forming with the magnetron sputter source of target is housed.
3. sputter equipment as claimed in claim 1 is characterized in that,
Described film thickness measurement device has the light projector device to substrate irradiation measuring light, and the infrared rays receiver of accepting behind the transmitted light of described measuring light of the described substrate of irradiation or the reflected light to produce electrical signal in response to described transmitted light or catoptrical light income, when described drum rotates, by shining measuring light to described substrate, carry out described film thickness measuring from described light projector device.
4. sputter equipment as claimed in claim 3 is characterized in that, also comprises:
According to signal, calculate the machine unit of transmissivity information or reflectivity information from described infrared rays receiver output.
5. sputter equipment as claimed in claim 3 is characterized in that,
Described film thickness measurement device is arranged on the position of leaving described a plurality of magnetron sputter sources.
6. a spatter film forming method is to adopt the carousel-type sputter equipment to carry out film forming spatter film forming method, and described carousel-type sputter equipment has following structure, that is:
It is Polygons or circular drum that the cross section that rotates freely is set in chamber,
A plurality of substrate retainers are set on the outer surface of this drum,
At a plurality of magnetron sputter sources of the inboard of chamber wall configuration, each magnetron sputter source is by target and keep the magnetron of this target partly to constitute,
Described target utilizes described magnetron partly to keep, and makes the shaft parallel of itself and described drum,
Described method comprises following operation:
In film forming, measure the film thickness measuring operation of the thickness of the film that forms on the substrate that is contained on one of described a plurality of substrate retainers;
Utilizing the measuring result that obtains in the described film thickness measuring operation to control influences the parameter control of film forming amount operation.
7. spatter film forming method as claimed in claim 6 is characterized in that, also comprises:
One side makes described drum rotation, a light projector operation in the face of substrate irradiation measuring light;
Acceptance shine behind the transmitted light of the described measuring light on the described substrate or the reflected light in response to this transmitted light or catoptrical light income and produce electrical signal be subjected to the light operation.
8. spatter film forming method as claimed in claim 7 is characterized in that, also comprises:
According to the described operational process that is subjected to the light operation to obtain calculated signals transmissivity information or reflectivity information.
9. spatter film forming method as claimed in claim 6 is characterized in that,
Described thickness is to measure in the position of leaving described a plurality of magnetron part, thereby makes the disadvantageous effect of the plasma light that produces in described a plurality of magnetron part minimize.