CN1821105A - Suspending type magnetic particle for adsorbing oil dirt on water and its preparing method - Google Patents
Suspending type magnetic particle for adsorbing oil dirt on water and its preparing method Download PDFInfo
- Publication number
- CN1821105A CN1821105A CN 200610024637 CN200610024637A CN1821105A CN 1821105 A CN1821105 A CN 1821105A CN 200610024637 CN200610024637 CN 200610024637 CN 200610024637 A CN200610024637 A CN 200610024637A CN 1821105 A CN1821105 A CN 1821105A
- Authority
- CN
- China
- Prior art keywords
- magnetic particle
- ferrite
- type magnetic
- cenosphere
- suspending type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The suspended magnetic particle for adsorbing oil in water and its preparation process is disclosed. The suspended magnetic particle is prepared with hollow bead of industrial slag and flyash as carrier, and through depositing ferrite on to the surface to form magnetic particle and surface treatment. It is spread to pollut water to constitute suspended magnetic particle-oil mixing system, and under the action of the magnetic field, the suspended magnetic particle-oil mixing system is controlled to move so as to reach the oil pollution treating aim. The hollow bead has the chemical composition of SiO2 and Al2O3 mainly and has no environmental pollution. The used suspended magnetic particle may be adsorbed, collected and treated properly for reuse.
Description
Technical field
The present invention relates to a kind of control of adsorbing oil dirt on water, suspending type magnetic particle of improvement and preparation method thereof of being used for.
Background technology
In modern society, oil occupies extremely important status as the energy.Yet, in exploitation, processing, transportation and the use of oil, a considerable amount of Oil spills being arranged, discard in rivers and ocean basin, considerable in addition Chemicals belong to oil phase, in case enter the waters, will cause great threat to environment.Administer the waters petroleum pollution and become the task of top priority.Removing oil pollution of waters dyes and is unusual difficulty.The improvement of petroleum pollution has chemical process and physical method in the world at present.
Chemical process:, adopt emulsification dispersion, oil-collecting or coagulate oily method improvement by pollution condition.To the oil film of thickness less than 1 millimeter, it is effective adopting the oil pollution of chemical oil spill dispersant cleaning water body.Yet the medicine that chemical debridement methods consumption is a large amount of also may produce secondary pollution.
Physical method: comprise the oil fence, contamination removing ship and attached retrieving arrangement and oil absorption material.These methods are with the variation of sea situation and meteorological conditions, and it is bigger to reclaim capacity variation, when working conditions is abominable, because the upheaval of the motion of ocean current, wave rises and falls, make the greasy dirt of water surface be easy to drift with the tide, and enlarge contaminated area.
Utilizing magnetic liquid to remove the sea greasy dirt is a kind of novel surface and oil contaminant recycling and control method: spray magnetic liquid at water pollution oil meter face, under the action of a magnetic field, greasy dirt produces orientation and moves, reclaims.
Summary of the invention
The invention provides a kind of adsorbing oil dirt on water control of Sustainable development requirement, suspending type magnetic particle of administering and preparation method thereof of meeting, the magnetic particle spreading that makes is in the greasy dirt surface, can form suspending type magnetic particle one greasy dirt mixed system with greasy dirt, under the action of a magnetic field, thereby magnetic particle one fluid mixed system reaches oil pollution of waters control, administers purpose to the field direction motion.
The present invention is achieved through the following technical solutions: adopt industrial residue coal fly ash hollow micro bead (to call cenosphere in the following text) as carrier, the parcel ferrite layer makes suspending type magnetic particle on the cenosphere surface.The chemical constitution of cenosphere is mainly SiO
2, Al
2O
3, cenosphere and ferrite mass ratio are 1: 1~1: 5.
Described ferrite is meant spinel type ferrite and hexaplanar magneto-plumbite type ferrite (ferrite that nickel, cobalt, manganese, barium, strontium, zinc and above each elements compounding are mixed and obtained).
Adopt chemical process or physical method to make suspending type magnetic particle at cenosphere surface parcel ferrite layer.Chemical process is meant: any method in coprecipitation method, hydrothermal synthesis method, microemulsion method, metal alkoxide sol-gel method, polymer-network gel method, citrate sol-gel method, organic coordination compound precursor process, self propagating high temperature synthesis method, the sintering process.Physical method is meant: adhesion process, mix any method of technology.
Suspending type magnetic particle and tensio-active agent stir the back spreading in the greasy dirt surface, can form suspending type magnetic particle-greasy dirt mixed system with greasy dirt.Under the action of a magnetic field, the magnetic particle of formation-fluid mixed system produces controlled motion.
The suspending type magnetic particle that makes as shown in Figure 1.1 is the ferrite integument in the diagram; 2 is cenosphere.
Effect of the present invention: the magnetic particle that makes is suspended in the fluid surface, even after water body inside is sunk in stirring, still can float the maintenance suspended state.With suspending type magnetic particle spreading oil pollution of waters surface, magnetic particle adsorbs greasy dirt and forms the magnetic mixed system with greasy dirt.Under the action of a magnetic field, thereby the magnetic particle of formation-fluid mixed system reaches oil pollution of waters control, administers purpose to the field direction motion.
The chemical constitution of cenosphere is mainly SiO
2, Al
2O
3,, can not cause secondary pollution to environment for one of earth's crust mineral composition material.After suspending type magnetic particle was adsorbed, collects simultaneously, through oil removal treatment, the basic no change of its magnetic properties still can be reused.The oil pollution of adopting the suspension type magnetic adsorptive material to administer water surrounding meets Sustainable development requirements such as the ecological economy, recycling economy.
Description of drawings
Fig. 1 is a suspending type magnetic particle structural representation of the present invention.
Embodiment
How further specify the present invention below in conjunction with specific embodiment realizes:
Embodiment 1: adopt the citrate gel sol gel process to prepare suspending type magnetic particle:
1. make presoma with citric acid complex iron nitrate, nitrate of baryta: by stoichiometric ratio Ba (NO
3)
2: Fe (NO
3)
3: citric acid=take by weighing raw material at 1: 12: 19, add dissolved in distilled water, splashing into ammoniacal liquor regulator solution pH value is 7;
2. add cenosphere in the presoma, cenosphere and ferrite mass ratio are 1: 1~1: 5;
3. solution places 90 ℃ of stirred in water bath 4~5h, to liquid be the heavy-gravity colloidal;
4. prepared colloidal sol places 120 ℃ of 4h of baking oven, obtains desiccant gel;
5. gel places in the retort furnace and is heated to 850 ℃ with 60 ℃/h temperature rise rate, naturally cooling behind the insulation 2h.
Embodiment 2: adopt coprecipitation method to prepare suspending type magnetic particle:
1. prepare FeCl respectively
36H
2O, FeCl
24H
2O, NaOH solution;
2. with the FeCl for preparing
36H
2O, FeCl
24H
2O solution is poured in the NaOH solution, adds cenosphere, and cenosphere and ferrite mass ratio are 1: 1~1: 5, evenly is stirred to reaction and finishes under the temperature about 80 ℃;
3. neutralize Fe with HCl
3O
4Precipitation is wrapped in the cenosphere surface;
4. with the cleaning of resultant water, whizzer separation, the vacuum-drying that obtain.
Embodiment 3: adopt the adhesion process method to prepare suspending type magnetic particle:
1. take by weighing (measuring) cenosphere, ferrite powder and styrene-propene yogurt liquid respectively in 1: 1: 0.1 ratio;
2. ferrite powder and even stirring of styrene-propene yogurt liquid are obtained mixture;
3. after mixture coagulates, the sclerosis, obtain powder through the ball mill pulverizing.
Claims (5)
1, a kind of suspending type magnetic particle that is used for adsorbing oil dirt on water is characterized in that:
Cenosphere surface parcel ferrite layer, cenosphere and ferrite mass ratio are 1: 1~1: 5.
2, a kind of suspending type magnetic particle that is used for adsorbing oil dirt on water according to claim 1 is characterized in that:
Ferrite is meant spinel type ferrite and hexaplanar magneto-plumbite type ferrite (ferrite that nickel, cobalt, manganese, barium, strontium, zinc and above each elements compounding are mixed and obtained).
3, a kind of preparation method who is used for the suspending type magnetic particle of adsorbing oil dirt on water according to claim 1 is characterized in that:
Adopt chemical process to prepare suspending type magnetic particle at cenosphere surface parcel ferrite, chemical process is meant: any method in coprecipitation method, hydrothermal synthesis method, microemulsion method, metal alkoxide sol-gel method, polymer-network gel method, citrate sol-gel method, organic coordination compound precursor process, self propagating high temperature synthesis method, the sintering process.
4, a kind of preparation method who is used for the suspending type magnetic particle of adsorbing oil dirt on water according to claim 1 is characterized in that:
Adopt physical method to prepare the preparation method of suspending type magnetic particle at cenosphere surface parcel ferrite, physical method is meant: adhesion process, mix any method in the technology.
5, a kind of preparation method who is used for the suspending type magnetic particle of adsorbing oil dirt on water according to claim 1 is characterized in that:
Method 1. usefulness citric acid Prepared by Sol Gel Method suspending type magnetic particles
(1) makes presoma with citric acid complex iron nitrate, nitrate of baryta: by stoichiometric ratio Ba (NO
3)
2: Fe (NO
3)
3: citric acid=take by weighing raw material at 1: 12: 19, add dissolved in distilled water, splashing into ammoniacal liquor regulator solution pH value is 7;
(2) add cenosphere in the presoma, cenosphere and ferrite mass ratio are 1: 1~1: 5;
(3) solution places 90 ℃ of stirred in water bath 4~5h, to liquid be the heavy-gravity colloidal;
(4) prepared colloidal sol places 120 ℃ of 4h of baking oven, obtains desiccant gel;
(5) gel places in the retort furnace and is heated to 850 ℃ with 60 ℃/h temperature rise rate, naturally cooling behind the insulation 2h;
Method 2. adopts coprecipitation method to prepare suspending type magnetic particle:
(1) prepares FeCl respectively
36H
2O, FeCl
24H
2O, NaOH solution;
(2) with the FeCl for preparing
36H
2O, FeCl
24H
2O solution is poured in the NaOH solution, adds cenosphere, and cenosphere and ferrite mass ratio are 1: 1~1: 5, evenly is stirred to reaction and finishes under the temperature about 80 ℃;
(3) neutralize Fe with HCl
3O
4Precipitation is wrapped in the cenosphere surface;
(4) with the cleaning of resultant water, whizzer separation, the vacuum-drying that obtain; Method 3. adopts the adhesion process method to prepare suspending type magnetic particle:
(1) takes by weighing (measuring) cenosphere, ferrite powder and styrene-propene yogurt liquid respectively in 1: 1: 0.1 ratio;
(2) ferrite powder and even stirring of styrene-propene yogurt liquid are obtained mixture;
(3) after mixture coagulates, the sclerosis, obtain powder through the ball mill pulverizing.