CN1806975A - Method for preparing copper zinc alloy powder - Google Patents
Method for preparing copper zinc alloy powder Download PDFInfo
- Publication number
- CN1806975A CN1806975A CN 200610003856 CN200610003856A CN1806975A CN 1806975 A CN1806975 A CN 1806975A CN 200610003856 CN200610003856 CN 200610003856 CN 200610003856 A CN200610003856 A CN 200610003856A CN 1806975 A CN1806975 A CN 1806975A
- Authority
- CN
- China
- Prior art keywords
- alloy powder
- copper
- zinc alloy
- zinc
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates the method for preparation of copper-zinc alloy powder, comprising the following steps: adding the 80-90wt% zinc powder and 10- 20% copper citrate powder into autoclave with agitator, entering agitator, heating to 100-450Deg.C, carrying out carbonation for 1-3 hours, cooling , and getting the copper-zinc alloy powder. The cost is low. Using the method, the product possesses the high activity.
Description
Technical Field
The invention relates to a preparation method of an alloy, in particular to a preparation method of novel copper-zinc alloy powder.
Background
Diethyl zinc is one of the most important catalyst monomers used in the process of researching and producing carbon dioxide-based fully-degradable plastic resin, and meanwhile, diethyl zinc is also an MO source of an important growth method MOCVD of a compound semiconductor film material, is an important doping agent of materials such as gallium arsenide and the like, and can also be used for preparing materials such as ZnSe, ZnS and the like. The purity requirement of diethyl zinc in the MOCVD process is very high, and if the diethyl zinc contains many impurities, the photoelectric properties of the prepared material are directly influenced.
However, the preparation cost of producing diethyl zinc at home and abroad is very high at present, and the main factors influencing the cost of diethyl zinc comprise the cost of copper-zinc alloy powder. At present, the copper-zinc alloy powder is produced in China mainly by hot melting and spraying or vacuum coating and then strongly mechanically stirring or ultrasonically crushing to form nanoscale flaky copper-zinc alloy powder. For example, the patent of invention patent of nano-scale sheet copper-zinc alloy powder and the manufacturing method thereof, which is disclosed by the intellectual property office of China at 2005, 5 month and 18 days, has the patent application number of 200310110526.7. Theinvention relates to a nano-scale flaky copper-zinc alloy powder and a manufacturing method thereof. The weight percentage of the flaky copper-zinc alloy powder is 68-93 percent of copper, 6-30 percent of zinc and 0.2-1.6 percent of aluminum. The present invention adopts film coating process to continuously deposit Cu, Zn and other elements onto ultrathin organic film substrate, and after the organic ultrathin film is removed by solvent, the ultrathin film is crushed into nanometer level flaky alloy powder, which is then dried, surface coated, modified and polished to obtain nanometer level flaky Cu-Zn alloy powder. The invention adopts a slowly moving composite substrate which is constructed by a soluble ultrathin organic film and a flexible substrate and has an extremely smooth and clean surface, and deposited atoms move along the surface of the ultrathin organic film and are condensed on a stable state or a metastable state position on the surface of the ultrathin organic film to form a nano film with a compact structure and a smooth and flat surface. The nano-scale flaky copper-zinc alloy powder obtained by the invention has uniform particle thickness, flat and smooth particle surface, 30-100nm of particle thickness, 0.1-3pm of particle diameter and 30-900 of diameter-thickness ratio. The preparation process of the method is complex, the consumption ratio of raw materials is large, and the selling price is about 5 ten thousand yuan/ton generally.
Disclosure of Invention
Compared with the prior art, the invention aims to provide the preparation method of the novel copper-zinc alloy powder, which has low production cost, easy initiation and stable reaction process.
In order to realize the purpose, the preparation method adopted by the invention comprises the following steps: a preparation method of novel copper-zinc alloy powder comprises the following production processes:
a. adding zinc powder accounting for 80-90% of the total weight and copper citrate powder accounting for 10-20% of the total weight into a reaction kettle;
b. introducing inert gas into the reaction kettle, and replacing air in the reaction kettle;
c. heating the reaction kettle to 100-450 ℃ under the stirring state for reaction, and cooling to room temperature after the reaction is carried out for 1-3 hours to obtain the copper-zinc alloy powder.
The preparation reaction of the invention is as follows:
the granularity of the zinc powder is 40-100 meshes. The inert gas is nitrogen.
The preparation process of the invention has the characteristics that: 1. the production cost is low. The production cost of the preparation process is about 1.3 ten thousand yuan/ton, which is greatly lower than the production cost of about 5 ten thousand yuan/ton of the prior production process; 2. the preparation process of the invention has simple and stable reaction process and easy initiation in the production process, and the produced copper-zinc alloy powder has the characteristic of high activity.
Detailed Description
Example 1:
580 g of 40-mesh zinc powder and 130 g of copper citrate powder are added into a reaction kettle with a stirring device, nitrogen is used for fully replacing air in the reaction kettle, the reaction kettle is heated to 450 ℃ for carbonization while stirring, the reaction is finished for 1 hour, and the reaction is cooled to room temperature to obtain the novel copper-zinc alloy powder. The heating mode is electric heating. The alloy powder is used for preparing diethyl zinc, and has the characteristics of high initiation speed, high yield, high purity and stable reaction process.
Example 2:
1040 g of 80-mesh zinc powder and 200 g of copper citrate powder are added into a reaction kettle with a stirring device, argon is introduced into the reactor, air in the reaction kettle is fully replaced, the reaction kettle is electrically heated to 100 ℃ for carbonization while stirring, the reaction is finished for 3 hours, and the reaction is cooled to room temperature to obtain the novel copper-zinc alloy powder. The alloy powder is used for preparing diethyl zinc, and has the characteristics of high initiation speed, high yield, high purity and stable reaction process.
Claims (3)
1. A preparation method of novel copper-zinc alloy powder comprises the following production processes:
a. adding zinc powder accounting for 80-90% of the total weight and copper citrate powder accounting for 10-20% of the total weight into a reaction kettle;
b. introducing inert gas into the reaction kettle, and replacing air in the reaction kettle;
c. heating the reaction kettle to 100-450 ℃ under the stirring state for reaction, and cooling to room temperature after the reaction is carried out for 1-3 hours to obtain the copper-zinc alloy powder.
2. The method for producing a novel copper-zinc alloy powder according to claim 1, wherein the particle size of the zinc powder is 40 to 100 mesh.
3. The method according to claim 1, wherein the inertgas is nitrogen or argon.