CN1789200A - Materials prescription for producing graphite electrode nipple bolt - Google Patents
Materials prescription for producing graphite electrode nipple bolt Download PDFInfo
- Publication number
- CN1789200A CN1789200A CN 200410093915 CN200410093915A CN1789200A CN 1789200 A CN1789200 A CN 1789200A CN 200410093915 CN200410093915 CN 200410093915 CN 200410093915 A CN200410093915 A CN 200410093915A CN 1789200 A CN1789200 A CN 1789200A
- Authority
- CN
- China
- Prior art keywords
- graphite electrode
- raw materials
- joint bolt
- composition
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides the formula of raw material for making carbon graphite electrode contact plug, which comprises the following constituents (by weight proportions): coal tar 50-70 parts, using incineration pulverized coke 10-30 parts, graphite powder 10-20 parts, and foaming agent 1.5-2.5 parts.
Description
Affiliated field:
The present invention relates to a kind of raw material that is used for being produced on the graphite electrode nipple bolt that Electric furnace steel making uses.
Background technology:
When Graphite Electrodes uses in Electric furnace steel making and since vibration such as the electric arc impact that produces in when steel-making, thermal shocking, mechanical shock and misoperation tend to produce electrode loosening, thread off, even the phenomenon of fracture has a strong impact on Electric furnace steel making.Though advantages such as conical joint has contact area big, and is easy to operate, and stressing conditions is good are compared with the linear pattern joint, if loosening and dropout in use takes place, it causes whole possibility that comes off bigger.At present, prevent that the loosening method of electrode contact from mainly containing: joint bolt, joint cream, joint powder, nipple pin etc.Its center tap bolt is a kind of method preferably.The ordinary couplings bolt is made raw material usually based on after-smithing petroleum coke and potassium permanganate, and the joint bolt that this kind raw material is made influences the joint conductive and heat-conductive easily.
Summary of the invention:
Purpose of the present invention just is to overcome above-mentioned the deficiencies in the prior art, and a kind of proportioning raw materials that is used for being produced on the graphite electrode nipple bolt that Electric furnace steel making uses is provided.It is loosening that the joint bolt that utilizes this prescription to produce can prevent that the Graphite Electrodes junction from taking place, and the phenomenon of threading off or rupturing is guaranteed the graphite electrode nipple close-coupled, reduces consumption of electrode and power consumption.
Technical scheme of the present invention is: a kind of being used to made new carbon graphite electrode joint bolt composition of raw materials, and it is characterized in that: it is made by following materials of weight proportions: coal-tar pitch 50-70 part, forge back coke powder 10-30 part, Graphite Powder 99 10-20 part whipping agent 1.5-2.5 part.
65 parts of described coal-tar pitch, forge 20 parts of the coke powders in back, 2 parts of 13 parts of whipping agents of Graphite Powder 99.
Described granularity requirements of forging the back coke powder below 200 mesh sieves, purity is 100%, its technical indicator is as follows: ash≤0.4%, sulfur≤0.4%, moisture content≤0.05%, true specific gravity 〉=2.10g/cm
3, carbon content 〉=98.5%.
The granularity requirements of described Graphite Powder 99 below 200 mesh sieves, purity is 100%, its technical indicator is as follows: ash≤0.3%, sulfur≤0.04%, moisture content≤0.05%, true specific gravity 〉=2.18g/cm
3, carbon content 〉=99%.
Described coal-tar pitch technical indicator is as follows: softening temperature 100-115 ℃, the stupid insolubles 28-35% of first, quinoline insolubles 8-14%, ash<0.3%, moisture content<5%, β resin>18%, coking value>53%.
Described whipping agent is selected vulkacit H for use.
Advantage of the present invention is: the carbon graphite electrode joint bolt of making of the present invention can prevent that the Graphite Electrodes junction from taking place to become flexible, and the phenomenon of threading off or rupturing is guaranteed the graphite electrode nipple close-coupled, reduces consumption of electrode and power consumption.
Embodiment:
To forge back coke powder and Graphite Powder 99 and carry out 200 mesh sieve sortings respectively, get following standby of 200 orders.Calculate with every weight part 1 gram, get granularity and be that 200 orders are following, purity be 100% forge back coke powder 20 grams, its technical indicator is as follows: ash≤0.4%, sulfur≤0.4%, moisture content≤0.05%, true specific gravity 〉=2.10g/cm
3, carbon content 〉=98.5%; Get granularity and be that 200 orders are following, purity is 100% Graphite Powder 99 13 grams, its technical indicator is as follows: ash≤0.3%, sulfur≤0.04%, moisture content≤0.05%, true specific gravity 〉=2.18g/cm
3, carbon content 〉=99%; Get coal-tar pitch 65 gram, its technical indicator is as follows: softening temperature 100-115 ℃, the stupid insolubles 28-35% of first, quinoline insolubles 8-14%, ash<0.3%, moisture content<5%, β resin>18% coking value>53%; Get whipping agent (vulkacit H) 2 grams.With coal-tar pitch, forge back coke powder, Graphite Powder 99 and whipping agent thorough mixing after, can obtain being used to make the raw material of new carbon graphite electrode joint bolt.
As follows with the carbon graphite electrode joint bolt (B) that the present invention makes with the effect comparison of the joint bolt (A) of traditional raw material making:
1, the physical and chemical index contrast is as follows:
Project | V(%) | A(%) | W(%) | C(%) | dk(g/cm 3) | |
Target value | ≤35 | ≤3.5 | ≤5 | ≥60 | >1.5 | |
Actual value | A | 34.6 | 2.4 | 0.15 | 64.5 | 1.52 |
B | 32.2 | 0.4 | 0.09 | 69.5 | 1.54 |
Can find out that from These parameters B side's superior performance can reduce the influence of butt junction conductive and heat-conductive.
2, the expansion character contrast is as follows:
In loft drier, do two experiments of expansion temperature and ratio of expansion:
Can find out that from These parameters B can improve expansion character, and the back volume stability that expands.
Claims (6)
1, a kind of composition of raw materials that is used to make new carbon graphite electrode joint bolt, it is characterized in that: it is made by following materials of weight proportions: coal-tar pitch 50-70 part, forge back coke powder 10-30 part, Graphite Powder 99 10-20 part whipping agent 1.5-2.5 part.
2, the composition of raw materials that is used to make new carbon graphite electrode joint bolt according to claim 1 is characterized in that: 65 parts of described coal-tar pitch, forge 20 parts of the coke powders in back, 2 parts of 13 parts of whipping agents of Graphite Powder 99.
3, the composition of raw materials that is used to make new carbon graphite electrode joint bolt according to claim 1, it is characterized in that: described granularity requirements of forging the back coke powder below 200 mesh sieves, purity is 100%, its technical indicator is as follows: ash≤0.4%, sulfur≤0.4%, moisture content≤0.05%, true specific gravity 〉=2.10g/cm
3, carbon content 〉=98.5%.
4, the composition of raw materials that is used to make new carbon graphite electrode joint bolt according to claim 1, it is characterized in that: the granularity requirements of described Graphite Powder 99 below 200 mesh sieves, purity is 100%, its technical indicator is as follows: ash≤0.3%, sulfur≤0.04%, moisture content≤0.05%, true specific gravity 〉=2.18g/cm
3, carbon content 〉=99%.
5, the composition of raw materials that is used to make new carbon graphite electrode joint bolt according to claim 1, it is characterized in that: described coal-tar pitch technical indicator is as follows: softening temperature 100-115 ℃, the stupid insolubles 28-35% of first, quinoline insolubles 8-14%, ash<0.3%, moisture content<5%, β resin>18%, coking value>53%.
6, the composition of raw materials that is used to make new carbon graphite electrode joint bolt according to claim 1, it is characterized in that: described whipping agent is selected vulkacit H for use.