CN1729249A - Polyethylene composition for producing L-ring drums - Google Patents
Polyethylene composition for producing L-ring drums Download PDFInfo
- Publication number
- CN1729249A CN1729249A CNA2003801072971A CN200380107297A CN1729249A CN 1729249 A CN1729249 A CN 1729249A CN A2003801072971 A CNA2003801072971 A CN A2003801072971A CN 200380107297 A CN200380107297 A CN 200380107297A CN 1729249 A CN1729249 A CN 1729249A
- Authority
- CN
- China
- Prior art keywords
- weight
- scope
- polyethylene composition
- polyethylene
- molecular weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a polyethylene composition with multimodal molecular mass distribution, which is particularly suitable for the blow molding of L-ring drums having a volume in the range of from 50 to 250 dm<SUP>3 </SUP>(I). The composition has a density in the range of from 0.950 to 0.956 g/cm<SUP>3 </SUP>at 23 DEG C. and a MFR<SUB>1gp/21.6 </SUB>in the range from 1.5 to 3.5 dg/min. It comprises from 35 to 45% by weight of a low-molecular-mass ethylene homopolymer A, from 34 to 44% by weight of a high-molecular-mass copolymer B made from ethylene and from another 1-olefin having from 4 to 8 carbon atoms, and from 18 to 26 % by weight of an ultrahigh-molecular-mass ethylene copolymer C.
Description
The present invention relates to have the polyethylene composition of multimodal shape molecular weight distribution, it is particularly suitable for blowing capacity (volume) at 50-250dm
3(1) the L-ring drums of scope, with relate to this method for compositions of preparation, be in the presence of the catalyst system of forming by Z-type catalyst and promotor such as triethyl aluminum, triisobutyl aluminium, alkyl aluminum chloride and alkyl-al hydride, to be undertaken by the multistep method of forming by the successive slurry polymerization.The invention still further relates to the L-annular container of producing by blowing by said composition.
Polyethylene is widely used for the production requirement material and has extra high physical strength, high erosion resistance and various types of moulded works of cocksure permanent stability.Poly another special benefits is that it also has good chemical-resistant and is light material inherently.
EP-A-603 has described before 935 a kind ofly based on polyethylene with have the blow molding composition of bimodal shape molecular weight distribution, and is suitable for producing the moulded work with good mechanical properties.
US-A5,338,589 have described and have a kind ofly had even the material of wideer molecular weight distribution, and by using from WO91/1 8934 known high durability (mileage) Preparation of Catalyst, wherein the magnesium alkoxide uses with gelatinous suspensoid form.Unexpectedly, have been found that and in moulded work, use this material to allow to improve simultaneously the character of in the hypocrystalline thermoplastics, oppositely being correlated with usually that these particularly are stiffness on the one hand and are stress cracking resistance and toughness on the other hand.
Yet this known bimodal shape product has low relatively melt strength especially in the course of processing.This means that the parison of extruding will rupture through the molten state of being everlasting, it is responsive to make that extrusion can not receive ground to processing.In addition, especially when producing the heavy-walled container, find wall thickness since curing prepolymer melt from the upper area of mould to the bottom zone flows but uneven.
Therefore, the objective of the invention is to develop a kind of polyethylene composition that is used for blowing, it demonstrates the further improvement above all known materials in by the processing of blowing with production L-ring drums.Especially, the high fondant-strength of composition should allow to operate expressing technique for a long time and not have parison to destroy, and the composition swelling ratio of accurately adjusting should allow the optimization of wall thickness control.In addition, moulding compound must have enough toughness for the V shape lifting of fully loaded L-ring drums and truck haul(ing).
We have been surprised to find that this purpose realizes by starting described composition, the characteristic features of said composition is the low-molecular-weight ethylenic homopolymer A that it comprises 35-45% weight, the high molecular weight copolymer B that is made by ethene and another kind of 1-alkene with 4-8 carbon atom of 34-44% weight and the ultra-high-molecular-weight polyethylene multipolymer C of 18-26% weight, wherein all percent value are based on the gross weight of moulding compound.
The invention still further relates to slurry polymerization with cascade prepares this method for compositions and relates to thus composition and make capacity or volume at 50-250dm
3(1) method of scope and L-ring drums with quite excellent mechanical intensive property.
It is 0.950-0.956g/cm that polyethylene polymer of the present invention has at 23 ℃
3Density in the scope and three wide peak shape molecular weight distribution.High molecular weight copolymer B only contains other olefin monomer unit with 4-8 carbon atom of low ratio, promptly less than 0.1% weight.The example of these comonomers has 1-butylene, 1-amylene, 1-hexene, 1-octene or 4-methyl-1-pentene.The Alathon of ultra-high molecular weight or multipolymer C also contain one or more the above-mentioned comonomers in the 0.1-0.6% weight range.
The melt-flow index ISO1133 that polymer composition of the present invention has is in the scope of 1.5-3.5dg/min, with MFR
190/21.6Expression and viscosity number VN
TotAt 500-600cm
3In the scope of/g, according to ISO/R 1191 in naphthalane 135 ℃ of measurements.
Three peak shapes be three independently molecular weight distribution position of centre of gravity measuring and can describing by means of the polymkeric substance that in the successive polymerization stage, forms according to the viscosity number VN of lSO/R 1191.Therefore, the relevant band width of the polymkeric substance that forms in each stage of reaction is as follows:
After first polymerization stage to the viscosity number VN of polymer measurement
1Viscosity number VN with low molecular weight polyethylene A
ABe consistent, and be at 160-220cm according to the present invention
3In the scope of/g.
After second polymerization stage to the viscosity number VN of polymer measurement
2The viscosity number VN that is not equal to the High molecular weight polyethylene B that in second polymerization stage, forms
B, but the viscosity number of the mixture of representation polymer A and polymer B, VN
BOnly can determine by calculating.According to the present invention, VN
2Be at 230-320cm
3In the scope of/g.
After the trimerization step of reaction to the viscosity number VN of polymer measurement
3The viscosity number VN that is not equal to the ultrahigh molecular weight copolymer C that in the trimerization step of reaction, forms
c, but representation polymer A, the viscosity number of the mixture of polymer B and polymkeric substance C, VN
cOnly can determine by calculating.According to the present invention, VN
3Be at 500-600cm
3In the scope of/g.
Polyethylene by in slurry in 60-90 ℃ temperature range, obtain at polymerization single polymerization monomer under the pressure of 0.15-1MPa and in the presence of the high-mileage ziegler catalyst that constitutes as organo-aluminium compound by transistion metal compound and triethyl aluminum.Polyreaction is carried out in three stages, i.e. in the stage of three serial arrangement, each molecular weight is regulated by means of the hydrogen charging.
Polyethylene composition of the present invention can comprise other additive and polyethylene side by side.The example of these additives has thermo-stabilizer, antioxidant, UV absorption agent, photostabilizer, metal passivator destroys the compound of superoxide and consumption in 0-10% weight, preferably at the alkaline auxiliary stablizer of 0-5% weight, and filler, toughener, softening agent, lubricant, emulsifying agent, pigment, optical brightener, fire retardant, static inhibitor, whipping agent, or their combination, total amount is a 0-50% weight, based on the gross weight of mixture.
Composition of the present invention is particularly suitable for blow molding process producing the L-ring drums, by at first plastifying polyethylene composition and then be expressed in the mould by die head in forcing machine in 200-250 ℃ temperature range, blows at this and to be cooled then and to solidify.
Composition of the present invention is in the special good processing properties of blow molding process generation that is used for producing the L-ring drums, because it has the swelling ratio in the 180-220% scope, the L-ring drums of Sheng Chaning has extra high physical strength thus, because moulding compound of the present invention has at 60-90KJ/m
2Notched Izod impact strength (ISO) in the scope.Its stress cracking resistance (FNCT) is in the scope of 15-25h.
Notched Izod impact strength (ISO) according to ISO 179-1/leA/DIN 53453 23 ℃ of mensuration.Specimen size is that 10 * 4 * 80mm and V breach use 45 to insert, and the degree of depth is that 2mm and breach base radius are 0.25mm.
The stress cracking resistance of moulding compound of the present invention is determined by internal test method and is provided with hour (h).This laboratory method by M.Fleissner at Kunststoffe 77 (1987), the 45th and subsequently page or leaf describe and corresponding to ISO/CD 16770, the latter enters into force.The disclosure text display in creep test, measure determining of crack growth slowly to the sample that has circumferential notch and carry out according to ISO1167 long-term in and the fragility cross section of hydrostatic pressure test between exist and concern.As the medium that promotes stress cracking and when using the tensile stress of 3.5MPa down for 80 ℃, rupture time shortens because the stress time of causing is shortened by breach (1.6mm/ blade) at ethylene glycol.Sample is by producing from following three samples that are of a size of 10 * 10mm * 110mm of the thick compacting bladed saw of 10mm.These samples are being made a center breach (seeing Fig. 5 in the open text) for this purpose and on the special blanking units with blade.Notch depth is 1.6mm.
Work embodiment
Be arranged in series three reactors in ethene continuous processing polymerization.As WO 91/18934, the Ziegler of the 5.5mmol/h of embodiment 2 described preparations amount is urged agent, but operand is 2.2 in WO, is added in first reactor with thinner (hexane), ethene and the hydrogen of 150mmol/h triethyl aluminum and capacity.Adjust ethene amount (=49.4kg/h) and the amount (18g/h) of hydrogen so that the percentage of ethene of measuring in the gas phase of first reactor and hydrogen is respectively 49% volume and 43% volume, remaining is the mixture of the thinner of nitrogen and evaporation.
Polyreaction in first reactor is carried out at 73 ℃.
Then the slurry in first reactor is transferred in second reactor, wherein the per-cent of hydrogen has been reduced to 20% volume in the gas phase, and the 1-butylene of 15g/h joins in this reactor with the ethene of 46.9kg/h.The amount of hydrogen is by intermediary H
2Depressurization and reducing.In the gas phase of second reactor, be measured to 72% volume of ethylene, 20% volume of hydrogen and<0.1% volume 1-butylene, remaining is the mixture of the thinner of nitrogen and evaporation.
Polyreaction in second reactor is carried out at 85 ℃.
Slurry in second reactor is transferred in the 3rd reactor, with further middle H
2Depressurization is adjusted the amount of hydrogen in the gas phase of the 3rd reactor less than 0.1% volume.
The 1-butylene of 90g/h and the ethene of 27.2kg/h are added in the 3rd reactor together.In the gas phase of the 3rd reactor, be measured to 91% volume of ethylene, less than the per-cent of 0.1% volume of hydrogen and 0.22% volume 1-butylene, remaining is the mixture of the thinner of nitrogen and evaporation.
Polyreaction in the 3rd reactor is carried out at 76 ℃.
The desired long-term polymerisation catalysts activity of above-mentioned Cascading Methods provides by the Z-type catalyst of the described specific development of beginning among the WO.Measuring of this catalyzer availability is its extra high hydrogen-sensitivity and 1-8 hour for a long time even high reactivity.
From the polymer slurries that leaves the 3rd reactor, remove thinner, with the granulation then of polymkeric substance drying.
Below shown in table 1 provided viscosity number and the quantitative ratio w of polymer A, B and C in the polyethylene composition of embodiment 1 preparation
A, w
B, and w
c
Table 1
Embodiment | |
Density [g/cm 3] | 0.953 |
?MFR 190/21,6[dg/min] | 2.6 |
?W A[% weight] | 40 |
?W B[% weight] | 38 |
?W c[% weight] | 22 |
?VN 1[cm 3/g] | 210 |
?VN 2[cm 3/g] | 260 |
?VN tot[cm 3/g] | 540 |
?SR[%] | 200 |
?FNCT[h] | 17.5 |
?NIS ISO[kJ/m 2] | 80 |
The physical properties abbreviation has following meaning in the table 1:
-SR (=swelling ratio) is with [%] expression, at 190 ℃ and shearing rate 1440S
-1Measure in the high pressure capillary rheometer in the 2/2 rounded section die head that has conical entrance (angle=15 °) down.
-FNCT=represents with [h] with the stress cracking resistance (full notch creep test) of the close beta method test of M.Fleissner.
-NIS
ISO=notched Izod impact strength, according to described in the ISO 179-1/leA/DIN 53453 23 ℃ of mensuration, with [kJ/m
2] expression.
Claims (10)
1. polyethylene composition with multimodal shape molecular weight distribution has at 23 ℃ and is 0.950-0.956g/cm
3Density and the MFR in the 1.5-3.5dg/min scope in the scope
190/21.6The low-molecular-weight ethylenic homopolymer A that comprises 35-45% weight, the high molecular weight copolymer B that is made by ethene and another kind of 1-alkene with 4-8 carbon atom of 34-44% weight and the ultra-high-molecular-weight polyethylene multipolymer C of 18-26% weight, wherein all percent value are based on the gross weight of moulding compound.
2. polyethylene molding composition as claimed in claim 1, wherein high molecular weight copolymer B contain based on the weight meter of multipolymer B less than the comonomer with 4-8 carbon atom of the low ratio of 0.1% weight and wherein the ethylene copolymer C of ultra-high molecular weight contain based on the comonomer in the weight meter 0.1-0.6% weight range of multipolymer C.
3. as the polyethylene composition of claim 1 or 2, it contains 1-butylene as comonomer, 1-amylene, 1-hexene, 1-octene, 4-methyl-1-pentene, or the mixture of these comonomers.
4. as one or multinomial polyethylene composition among the claim 1-3, the viscosity number VN that has
TotBe 500-600cm
3/ g, according to ISO/R1191 in naphthalane 135 ℃ of measurements.
5. as one or multinomial polyethylene composition among the claim 1-4, it has the swelling ratio in the 180-220% scope, at 60-90KJ/m
2Notched Izod impact strength (ISO) and the stress cracking resistance in the 15-25h scope (FNCT) in the scope.
6. produce method as one or multinomial polyethylene composition among the claim 1-5, wherein monomer in slurry in 60-90 ℃ temperature range, under the pressure of 0.15-1.0MPa scope, with polymerization in the presence of the high-mileage ziegler catalyst that constitutes by transistion metal compound and organo-aluminium compound, this method comprises carries out polyreaction in three stages, and wherein the poly molecular weight for preparing in each stage is regulated by means of hydrogen.
7. method as claimed in claim 6, the concentration of wherein regulating hydrogen in first polymerization stage is so that the viscosity number VN of low molecular weight polyethylene A
1At 160-220cm
3In/g the scope.
8. as the method for claim 6 or 7, the concentration of wherein regulating hydrogen in second polymerization stage is so that the viscosity number VN of the mixture of polymer A and polymer B
2At 230-320cm
3In/g the scope.
9. as each method of claim 6-8, the concentration of wherein regulating trimerization hydrogen in the stage is so that the viscosity number VN of the mixture of polymer A, polymer B and polymkeric substance C
3At 500-600cm
3In/g the scope.
10. be used for the production capacity at 50-250dm as one or multinomial polyethylene composition among the claim 1-5
3(1) purposes of the L-ring drums in the scope wherein at first plastifies polyethylene composition and then is expressed in the mould by die head in 200-250 ℃ temperature range in forcing machine, blow at this to be cooled then and to solidify.