CN1721360A - Modifier for water reducing agent of calcium lignosulfonate, sodium lignosulfonate and magnesium lignosulfonate, etc. - Google Patents
Modifier for water reducing agent of calcium lignosulfonate, sodium lignosulfonate and magnesium lignosulfonate, etc. Download PDFInfo
- Publication number
- CN1721360A CN1721360A CN 200510025717 CN200510025717A CN1721360A CN 1721360 A CN1721360 A CN 1721360A CN 200510025717 CN200510025717 CN 200510025717 CN 200510025717 A CN200510025717 A CN 200510025717A CN 1721360 A CN1721360 A CN 1721360A
- Authority
- CN
- China
- Prior art keywords
- lignosulfonate
- sodium
- reducing agent
- water reducing
- wooden
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The modifier for lignosulfonate water reducing agent of calcium lignosulfonate, sodium lignosulfonate, magnesium lignosulfonate, etc consists of sodium phosphate 39.5-95 wt%, sodium sulfate 4-60 wt%, and sodium dodecyl sulfate 0.5-8 wt%. The present invention may be used in papermaking industry, admixture industry and concrete industry. The modifier can raise the water reducing rate of lignosulfonate water reducing agent and modify common lignosulfonate water reducing agent into high efficiency water reducing agent for concrete pumping.
Description
Technical field
The present invention relates to a kind of concrete admixture, be specifically related to dedicated modified dose of sulfonated lignin water reducers such as wooden calcium, wooden sodium or wooden magnesium.
Background technology:
The mortar water-reducing rate of cement water reducing agent is an important techniques index, the requirement of standard GB 8706-1997: coventional type water reducer first grade is not less than 8%, and salable product are not less than 5%; The high efficiency water reducing agent first grade is not less than 12%, and salable product are not less than 10%.The wooden calcium that China's paper industry effluent discharge is made, wooden sodium or wooden magnesium etc. (comprising Russian import wood sodium) sulfonated lignin water reducer, their sand-cement slurry water-reducing rate is all between 8%～9%, meet China's coventional type water reducer first grade standard, and do not reach the high efficiency water reducing agent standard.
Summary of the invention
At the deficiency that prior art exists, the object of the present invention is to provide the properties-correcting agent of sulfonated lignin water reducers such as a kind of wooden calcium, wooden sodium or wooden magnesium, it can improve the water-reducing rate of coventional type water reducer.
Realize that goal of the invention technical scheme of the present invention is as follows:
The properties-correcting agent of sulfonated lignin water reducers such as a kind of wooden calcium, wooden sodium or wooden magnesium, its composition and proportioning (weight percentage) are as follows: sodium phosphate 39.5%～95%, sodium sulfate 4%～60%, sodium lauryl sulphate 0.5%～8%, above-mentioned three kinds of raw materials are mixed with mixer by proportioning, promptly get dedicated modified dose of sulfonated lignin water reducer.
Properties-correcting agent of the present invention is mainly used in:
1, paper industry: all is pulpwood with materials such as timber, straw, bagasse, awns bar or bamboos, spent pulping liquor with subtraction or acid polishing formation, all can be by recommending volume directly to mix properties-correcting agent of the present invention in the waste liquid, the modified lignin mahogany sulfonate power-product of making through the evaporation concentration spraying drying, can the expensive naphthalene of equivalent replacement be or anthracene series high-efficiency water-reducing agent product, turn waste into wealth, promote the well-being of mankind, produce good economic benefit and social benefit.
2, admixture industry: the lignosulfonic acid product salt is carried out modification use, equivalent replacement expensive naphthalene system or anthracene series high-efficiency water-reducing agent product guaranteeing to greatly reduce production cost under the additive product capability and performance situation, produce excellent economic.
3, commerical ready-mixed concrete industry: lignosulfonic acid salt water reducer through modification again with the composite use of other high efficiency water reducing agents, not only reduced production cost, and to the cohesiveness of commerical ready-mixed concrete, reduce performances such as loss of slump and the pumping effect that improves significantly.
The properties-correcting agent of sulfonated lignin water reducer provided by the invention, it can not only improve the water-reducing rate of coventional type water reducer, the modification of lignosulfonic acid salt coventional type water reducer can also be become high efficiency water reducing agent to use, be re-dubbed concrete pump-feed agent with other high efficiency water reducing agent, energy equivalent substitution high efficiency water reducing agent has very high economic benefit and social benefit.
Embodiment
How further specify the present invention below by specific embodiment realizes:
Embodiment 1
Get 39.5 kilograms of sodium phosphates, 60 kilograms in sodium sulfate, sodium lauryl sulphate is put into the mixer mixing for 0.5 kilogram and is promptly got properties-correcting agent of the present invention.
Embodiment 2
Get 50 kilograms of sodium phosphates, 43 kilograms in sodium sulfate, sodium lauryl sulphate is put into the mixer mixing for 7 kilograms and is promptly got properties-correcting agent of the present invention.
Embodiment 3
Get 95 kilograms of sodium phosphates, 4 kilograms in sodium sulfate, sodium lauryl sulphate is put into the mixer mixing for 1 kilogram and is promptly got properties-correcting agent of the present invention.
Embodiment 4
Get 45 kilograms of sodium phosphates, 47 kilograms in sodium sulfate, sodium lauryl sulphate is put into the mixer mixing for 8 kilograms and is promptly got properties-correcting agent of the present invention.
Embodiment 5
Get 60 kilograms of sodium phosphates, 37 kilograms in sodium sulfate, sodium lauryl sulphate is put into the mixer mixing for 3 kilograms and is promptly got properties-correcting agent of the present invention.
Embodiment 6
Get 70 kilograms of sodium phosphates, 25 kilograms in sodium sulfate, sodium lauryl sulphate is put into the mixer mixing for 5 kilograms and is promptly got properties-correcting agent of the present invention.
Embodiment 7
Get 80 kilograms of sodium phosphates, 16 kilograms in sodium sulfate, sodium lauryl sulphate is put into the mixer mixing for 4 kilograms and is promptly got properties-correcting agent of the present invention.
Experiment detects and shows, after in the pulvis of wooden calcium, wooden sodium or wooden magnesium etc. (comprise Russian import wood sodium) sulfonated lignin water reducer, mixing the properties-correcting agent 0.5%～2.5% that the present invention makes, its water-reducing rate reaches the high efficiency water reducing agent national standard by 8%～9% original raising 12%～14%.Also the present invention directly can be mixed in the spent pulping liquor of discharge by the recommendation volume for lignin sulfonate modified dose, make (wooden calcium, wooden sodium or wooden magnesium) sulfonated lignin power-product of modification again through the evaporation concentration spraying drying, make its product performance reach the high efficiency water reducing agent national standard.
Data are further detailed the performance of properties-correcting agent of the present invention by experiment:
Table one is performance contrasts such as mortar water-reducing rate before and after wooden calcium, wooden sodium and the modification of three kinds of sulfonated lignin water reducers of wooden magnesium and strength of cement.
Table one
| Numbering | Cement | The water reducer kind | Volume 0.25% pulvis (g) | Cement consumption (g) | Water consumption (g) | Standard sand (g) | Sand-cement slurry degree of mobilization (mm) | Water-reducing rate % | Ultimate compression strength (Mpa) | |
| 3 days | 28 days | |||||||||
| 1 | Dragon's pool PO 42.5 | Blank | 0 | 450 | 225 | 1350 | 180 | 19.5 | 44.0 | |
| 2 | Innovation wood calcium not | 1.125 | 204 | 183 | 9 | 23.0 | 50.7 | |||
| 3 | Innovation wood sodium not | 204 | 180 | 9 | 22.1 | 49.5 | ||||
| 4 | Common import wood sodium | 204 | 184 | 9 | 22.3 | 51.9 | ||||
| 5 | Innovation wood magnesium not | 207 | 181 | 8 | 24.1 | 53.0 | ||||
| 6 | Innovation wood calcium | 194 | 175 | 14 | 23.9 | 52.4 | ||||
| 7 | Innovation wood sodium | 198 | 182 | 12 | 23.2 | 50.6 | ||||
| 8 | Modification import wood sodium | 196 | 181 | 13 | 23.6 | 52.1 | ||||
| 9 | Innovation wood magnesium | 198 | 179 | 12 | 24.8 | 52.8 | ||||
Table one experiment shows: the mortar water-reducing rate of the sulfonated lignin water reducer after the modification brings up to 12%～14% from original 8%～9%.Ultimate compression strength improved and improved 15%～20% in 19%～27%, 28 days in three days.
Table two contrasts for the sulfonated lignin water reducer after the modification and naphthalene system or anthracene series high-efficiency water-reducing agent are re-dubbed slump and the ultimate compression strength that concrete pump-feed agent mixes behind the concrete.
</entry></row></tbody></tgroup></table></tables>
Table two experiment shows: the sulfonated lignin water reducer after the modification can the expensive naphthalene of equivalent substitution be or the anthracene series high-efficiency water-reducing agent, the slump increased value is greater than 100mm, three days and 28 days compressive strength rates reach 98% (national standard: be not less than 85%), after mixing properties-correcting agent the reinforcing bar non-corroding is endangered, also greatly reduce the composite cost of concrete pump-feed agent, economic benefit is very remarkable.
Table three is for mixing spent pulping liquor (concentration 50%) the water-based water reducer of properties-correcting agent of the present invention and the innovation wood calcium of making through the evaporation concentration spraying drying, wooden magnesium power-product experiment contrast by the recommendation volume.
Table three
| Numbering | Dragon's pool PO 42.5 cement consumptions (g) | The waste liquid of doping vario-property agent paper pulp (concentration 50%) (%) | Modified lignin mahogany sulfonate dry powder (%) | Standard sand (g) | Water consumption (g) | Mortar degree of mobilization (mm) | Water-reducing rate (%) | Ultimate compression strength (Mpa) | |
| R3 | R28 | ||||||||
| 1 | 450 | 0 | 0 | 1350 | 225 | 180 | 0 | 18.2 | 44.0 |
| 2 | 450 | Wood calcium aqua 0.5 | 0 | 196 | 182 | 13 | 23.5 | 50.9 | |
| 3 | 450 | 0 | Wood calcium 0.25 | 196 | 185 | 13 | 23.4 | 51.8 | |
| 4 | 450 | Wood magnesium aqua 0.5 | 0 | 198 | 179 | 12 | 24.0 | 52.9 | |
| 5 | 450 | 0 | Wood magnesium 0.25 | 198 | 178 | 12 | 24.3 | 53.1 | |
Table three experiment shows: do not changing production technique, do not increasing under the situation of machinery equipment, properties-correcting agent of the present invention by the water reducer of spent pulping liquor concentration 50% aqua of recommending volume to mix and the modified lignin mahogany sulfonate dry powder water reducer product of making through the evaporation concentration spraying drying, identical with ultimate compression strength through contrast mortar water-reducing rate, modified effect is good equally.
Claims (1)
1, the properties-correcting agent of sulfonated lignin water reducers such as a kind of wooden calcium, wooden sodium or wooden magnesium, its composition and proportioning are as follows:
Sodium phosphate 39.5%～95%
Sodium sulfate 4%～60%
Sodium lauryl sulphate 0.5%～8%
Above percentage ratio is weight percentage.