CN1693044A - Art for preparing high density bamboo timber - Google Patents
Art for preparing high density bamboo timber Download PDFInfo
- Publication number
- CN1693044A CN1693044A CN 200510018534 CN200510018534A CN1693044A CN 1693044 A CN1693044 A CN 1693044A CN 200510018534 CN200510018534 CN 200510018534 CN 200510018534 A CN200510018534 A CN 200510018534A CN 1693044 A CN1693044 A CN 1693044A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- silk
- disjunctor
- wire drawing
- chip
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A high-density square bamboo material is made up of bamboo through cutting short, making bamboo strips, making bamboo wires, carbonizing, skimming bleaching, baking glueing, combining, die pressing and high-temp and -pressure solidifying.
Description
Technical field
The present invention relates to a kind of preparation technology of high-density bamboo material square stock.
Background technology
Not only mao bamboon is required high with the integrated square stock of bamboo chip, and consumable quantity is big, the cost height, also seam is obvious between its product surface bamboo chip and the bamboo chip, very stiff at first glance, assembly has slightly unreasonablely will produce distortion, and the integrated square stock of existing bamboo chip can't satisfy modern life people to natural, attractive in appearance, generous, simple and unsophisticated, elegant pursuit.Therefore, people are making great efforts the various novel bamboo product ornament materials of research and development, realize replacing with bamboo the purpose of high-grade timber.
Summary of the invention
Purpose of the present invention just provides a kind of preparation technology of high-density bamboo material square stock.
The present invention is achieved like this, and its process for producing comprises the steps:
(1) cuts out material: use fresh mao bamboon,, be sawn into plurality of sections by the requirement of product processing length;
(2) burst: the bamboo chip that with wafer separator mao bamboon is divided into thick 1.2-5mm, wide 12-26mm according to the thickness of mao bamboon;
(3) draw roundish bamboo thread and crushed bamboo thread: bamboo plate is pulled into circular bamboo circle wire drawing or bamboo plate is come along its fiber decomposition with wire disintegrating machine with machine drawing, make it to become the broken silk of disjunctor traditional instrument sheet and bamboo (bamboo chip disjunctor silk refers to the bamboo chip silk that some bamboo silks connect together and constitute, and the broken silk of bamboo refers to that wire disintegrating machine is broken into bamboo chip the bamboo silk that does not connect together);
(4) carbonization and degreasing bleaching: the broken silk of bamboo chip disjunctor silk, bamboo, the wire drawing of bamboo circle were put in the carbide furnace under 2.5 ∽, 4.5 atmospheric pressure carbonization 1-4 hour, perhaps the wire drawing of bamboo circle, bamboo chip disjunctor silk and the broken silk of bamboo are put into hydrogen peroxide, under 100 ℃ of temperature of 60 ℃ of ∽, soak, carry out the degreasing bleaching and handle;
(5) dry: the wire drawing of bamboo circle, bamboo chip disjunctor silk and the broken silk of bamboo after carbonization, degreasing bleaching are handled are sent in the dry kiln and are dried, and slough moisture content;
(6) applying glue: the bamboo circle wire drawing after will drying, bamboo chip disjunctor silk and the broken silk of bamboo are executed adhesive (main glue is urea-formaldehyde resin adhesive and phenolic resin glue), and the bamboo silk moisture content of having executed glue needs the bamboo silk to be dried as surpassing 20% between 12%-20% again;
(7) assembly: the wire drawing of bamboo circle, bamboo chip disjunctor silk and the broken silk of bamboo that will execute glue are put into internal mold by vertical (same direction), form the square stock semifinished product;
(8) patrix high pressure: the square stock semifinished product that assembly is good is at 60kg/m
2∽ 170kg/m
2Pressure under carry out high-pressure molding;
(9) hot setting: with the solidifying and setting under 90-120 ℃ temperature of the finished product behind the high-pressure molding, the demoulding is after planing promptly obtains smooth smooth, the highdensity clearly bamboo wood square stock of bamboo line.
The present invention by cut material, a burst, draw roundish bamboo thread and crushed bamboo thread, carbonization and degreasing bleaching, series of process steps such as oven dry, applying glue, assembly, patrix high pressure, hot setting, produce highdensity bamboo wood square stock, utilize bamboo wood fully, utilization rate of bamboo is more than 90%, reduced production cost, the attached value of the square stock of being produced is high, class is high, has satisfied the needs of industries such as hotel, dwelling house, furniture, decoration, automobile, boats and ships, container, aviation.
The specific embodiment
Embodiment (one)
The present invention adopts following processing step to produce the high-density bamboo material square stock:
(1) cuts out material: get some in fresh mao bamboon,, be sawn into plurality of sections by 2 meters length requirements;
(2) burst: the bamboo chip that with wafer separator mao bamboon is divided into thick 3mm, wide 20mm according to the thickness of mao bamboon;
(3) draw roundish bamboo thread and crushed bamboo thread: bamboo plate is pulled into circular bamboo circle wire drawing or bamboo plate is decomposed along its fiber with machine drawing and come, make it to become broken of disjunctor traditional instrument sheet and bamboo with wire disintegrating machine;
(4) carbonization: the broken silk of bamboo chip disjunctor silk, bamboo, the wire drawing of bamboo circle were put in the carbide furnace under 3 atmospheric pressure carbonization 3 hours;
(5) dry: the wire drawing of the circle of the bamboo after the carbonization, bamboo chip disjunctor silk and the broken silk of bamboo are sent in the dry kiln dried, slough moisture content;
(6) applying glue: the bamboo circle wire drawing after will drying, bamboo chip disjunctor silk and the broken silk of bamboo are executed urea-formaldehyde resin adhesive;
(7) assembly: the wire drawing of bamboo circle, bamboo chip disjunctor silk and the broken silk of bamboo that will execute glue are put into internal mold by vertical (same direction), form the square stock semifinished product;
(8) patrix high pressure: the square stock semifinished product that assembly is good is at 100kg/m
2Pressure under carry out high-pressure molding;
(9) hot setting: with the solidifying and setting under 100 ℃ temperature of the finished product behind the high-pressure molding, the demoulding is after planing promptly obtains smooth smooth, the highdensity clearly bamboo wood square stock of bamboo line.
Embodiment (two)
The present invention adopts following processing step to produce the high-density bamboo material square stock:
(1) cuts out material: get some in fresh mao bamboon,, be sawn into plurality of sections by 2 meters length requirements;
(2) burst: the bamboo chip that with wafer separator mao bamboon is divided into thick 1.2mm, wide 12mm according to the thickness of mao bamboon;
(3) draw roundish bamboo thread and crushed bamboo thread: bamboo plate is pulled into circular bamboo circle wire drawing or bamboo plate is decomposed along its fiber with machine drawing and come, make it to become broken of disjunctor traditional instrument sheet and bamboo with wire disintegrating machine;
(4) degreasing bleaching: the wire drawing of bamboo circle, bamboo chip disjunctor silk and the broken silk of bamboo are put into hydrogen peroxide, under 80 ℃ of temperature, soak, carry out the degreasing bleaching and handle;
(5) dry: the bamboo circle wire drawing after the degreasing bleaching is handled, bamboo chip disjunctor silk and the broken silk of bamboo are sent in the dry kiln and are dried, and slough moisture content;
(6) applying glue: the bamboo circle wire drawing after will drying, bamboo chip disjunctor silk and the broken silk of bamboo are executed urea-formaldehyde resin adhesive;
(7) assembly: the wire drawing of bamboo circle, bamboo chip disjunctor silk and the broken silk of bamboo that will execute glue are put into internal mold by vertical (same direction), form the square stock semifinished product;
(8) patrix high pressure: the square stock semifinished product that assembly is good is at 60kg/m
2Pressure under carry out high-pressure molding;
(9) hot setting: with the solidifying and setting under 90 ℃ temperature of the finished product behind the high-pressure molding, the demoulding is after planing promptly obtains smooth smooth, the highdensity clearly bamboo wood square stock of bamboo line.
Embodiment (three)
The present invention adopts following processing step to produce the high-density bamboo material square stock:
(1) cuts out material: get some in fresh mao bamboon,, be sawn into plurality of sections by 1.5 meters length requirements;
(2) burst: the bamboo chip that with wafer separator mao bamboon is divided into thick 5mm, wide 26mm according to the thickness of mao bamboon;
(3) draw roundish bamboo thread and crushed bamboo thread: bamboo plate is pulled into circular bamboo circle wire drawing or bamboo plate is decomposed along its fiber with machine drawing and come, make it to become broken of disjunctor traditional instrument sheet and bamboo with wire disintegrating machine;
(4) degreasing bleaching: the wire drawing of bamboo circle, bamboo chip disjunctor silk and the broken silk of bamboo are put into hydrogen peroxide, under 100 ℃ of temperature, soak, carry out the degreasing bleaching and handle;
(5) dry: the bamboo circle wire drawing after the degreasing bleaching is handled, bamboo chip disjunctor silk and the broken silk of bamboo are sent in the dry kiln and are dried, and slough moisture content;
(6) applying glue: the bamboo circle wire drawing after will drying, bamboo chip disjunctor silk and the broken silk of bamboo are executed phenolic resin glue;
(7) base: the wire drawing of bamboo circle, bamboo chip disjunctor silk and the broken silk of bamboo that will execute glue are put into internal mold by vertical (same direction), form the square stock semifinished product;
(8) patrix high pressure: the square stock semifinished product that assembly is good is at 170kg/m
2Pressure under carry out high-pressure molding;
(9) hot setting: with the solidifying and setting under 120 ℃ temperature of the finished product behind the high-pressure molding, the demoulding is after planing promptly obtains smooth smooth, the highdensity clearly bamboo wood square stock of bamboo line.
Claims (1)
1, a kind of preparation technology of high-density bamboo material square stock is characterized in that adopting following method step:
(1) cuts out material: use fresh mao bamboon,, be sawn into plurality of sections by the requirement of product processing length;
(2) burst: the bamboo chip that with wafer separator mao bamboon is divided into thick 1.2-5mm, wide 12-26mm according to the thickness of mao bamboon;
(3) draw roundish bamboo thread and crushed bamboo thread: bamboo plate is pulled into circular bamboo circle wire drawing or bamboo plate is decomposed along its fiber with machine drawing and come, make it to become broken of bamboo chip disjunctor silk and bamboo with wire disintegrating machine;
(4) carbonization and degreasing bleaching: the broken silk of bamboo chip disjunctor silk, bamboo, the wire drawing of bamboo circle were put in the carbide furnace under 2.5 ∽, 4.5 atmospheric pressure carbonization 1-4 hour, perhaps the wire drawing of bamboo circle, bamboo chip disjunctor silk and the broken silk of bamboo are put into hydrogen peroxide, under 100 ℃ of temperature of 60 ℃ of ∽, soak, carry out the degreasing bleaching and handle;
(5) dry: bamboo chip disjunctor silk after carbonization, degreasing bleaching are handled and the broken silk of bamboo are sent in the dry kiln and are dried, and slough moisture content;
(6) applying glue: the bamboo circle wire drawing after will drying, bamboo chip disjunctor silk and the broken silk of bamboo are executed adhesive, and the bamboo silk moisture content of having executed glue is between 12%-20%;
(7) assembly: the wire drawing of bamboo circle, bamboo chip disjunctor silk and the broken silk of bamboo that will execute glue are put into internal mold by vertical (same direction), form the square stock semifinished product;
(8) patrix high pressure: the square stock semifinished product that assembly is good is at 60kg/m
2∽ 170kg/m
2Pressure under carry out high-pressure molding;
(9) hot setting: with the solidifying and setting under 90-120 ℃ temperature of the finished product behind the high-pressure molding, the demoulding is after planing promptly obtains smooth smooth, the highdensity clearly bamboo wood square stock of bamboo line.