CN1657493A - 一种抗静电、抗电磁辐射、抗菌陶瓷 - Google Patents

一种抗静电、抗电磁辐射、抗菌陶瓷 Download PDF

Info

Publication number
CN1657493A
CN1657493A CN 200410016447 CN200410016447A CN1657493A CN 1657493 A CN1657493 A CN 1657493A CN 200410016447 CN200410016447 CN 200410016447 CN 200410016447 A CN200410016447 A CN 200410016447A CN 1657493 A CN1657493 A CN 1657493A
Authority
CN
China
Prior art keywords
radiation
electromagnetic
ceramic
antistatic
sintering
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 200410016447
Other languages
English (en)
Inventor
詹树雄
詹明光
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANGHAI YAXIYA CERAMIC CO Ltd
Original Assignee
SHANGHAI YAXIYA CERAMIC CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI YAXIYA CERAMIC CO Ltd filed Critical SHANGHAI YAXIYA CERAMIC CO Ltd
Priority to CN 200410016447 priority Critical patent/CN1657493A/zh
Publication of CN1657493A publication Critical patent/CN1657493A/zh
Pending legal-status Critical Current

Abstract

一种具有抗静电、抗电磁辐射、抗菌陶瓷，采用稀土复合磷酸钠、Zr2P2O3、SiO2或TiO2细化晶粒微粉，经受控高温烧结而成。本发明的陶瓷体在内部形成了[NZP]结构，分子式可以表达为Na3Zr2Si2PO12或NaZr2Ti2P3O12。

Description

一种抗静电、抗电磁辐射、抗菌陶瓷
技术领域：
本发明涉及一种陶瓷，尤其是一种具有抗菌、抗静电、抗电磁辐射的多功能陶瓷。
背景技术：
目前，特种生产环境要求，如抗静电、抗菌、抗辐射等，都需经过专门的处理。抗静电是采用在地面和墙体埋设导电金属物质，抗辐射需要在墙面和地面铺设防电磁辅射的材料，或用防电磁辅射的涂料进行粉刷，抗菌则需要增加专门的抗菌设备，或在装饰材料内添加抗菌剂。
随着经济的发展，大量电子和生物医药企业的生产环境需要进行抗菌、抗静电、防电磁辐射的处理，否则受静电和电磁辐射的干扰，会严重影响精密仪器设备的运转和产品的校准。另外，人们对生活环境的意识越来越高，对于能够屏蔽电站等高频电磁发射场的电磁辐射的要求越来越大。因此，对具有抗菌、防辐射等特种功能的内、外装饰材料的需求正越来越大。
瓷砖是常用的建筑装潢材料，如果能赋予瓷砖特殊的功能，就能方便、廉价地满足上述这些特殊的装饰要求。目前抗菌瓷砖较为普遍，一般是在瓷砖内添加抗菌剂，但市场上还没有抗静电和抗电磁辐射的瓷砖，更没有将上述三种功能融为一体的多功能瓷砖。
发明内容：
本发明提供一种新型的，集抗菌、抗静电、抗电磁辐射的多功能瓷砖，其主要机理是在Zr-Si-P或Zr-Ti-P结构的陶瓷基料中加入含Na离子的稀土复合磷酸盐材料，经受控的烧结过程，可在陶瓷体内部形成[NZP]结构，[NZP]结构的很大特点就是金属离子在单位晶胞内产生不稳定游离，可以起到干扰、吸收电磁辐射和γ射线的作用。而且，在电场作用下，金属离子的游离即可成为一种定向移动，从而使陶瓷材料具有一定的导电性能，可以将静电导向地面。此外，金属离子的游离特性，可以对生物活性物质产生氧化作用，从而起到灭菌的效果。
下面结合实施例，具体说明本发明瓷砖的制备方法：
将各1mol的Zr2P2O3和SiO2或TiO2细化晶粒微粉，加3％的稀土复合磷酸钠充分搅拌混合，置于填有石墨垫片的钢模具内，迅速加高温至1200℃烧结1小时，然后快速退火，用0.01mol的NaHCO3溶液喷洒降温，待低于50℃后浸入0.01mol的NaHCO3溶液，使Na+得到充分置换，然后取出。再加入0.01％的烧结助剂ZrN，重新加温至400℃反应烧结2小时，再以30℃/h的速度升温至1200℃，继续高温烧结48小时，然后退火降温冷却，即可得到本发明物质。其分子式可以表达为Na3Zr2Si2PO12或NaZr2Ti2P3O12。
对最终得到的成品进行测试，其对黄色葡萄球菌的杀灭率达到90％；导电率达到10-7Ω-1.cm-1；电磁辐射和γ射线透过率为20％。[NZP]结构陶瓷最早应用于做催化剂的骨架，而民用方面开发应用很少，近来由于[NZP]独特的结构产生许多功能，其应用开发成果逐渐增多。本发明利用稀土材料制备[NZP]结构陶瓷瓷砖，既是在这一领域进行了有益的赏试。

Claims (4)

1、一种抗静电、抗电磁辐射、抗菌陶瓷，其特征是：采用稀土复合磷酸钠和Zr2P2O3、SiO2或TiO2细化晶粒微粉混合高温烧制。
2、一种抗静电、抗电磁辐射、抗菌陶瓷，其特征是：烧制过程符合如下程序：迅速加高温至1200℃烧结，然后快速退火，用0.01mol的NaHCO3溶液喷洒降温，待低于50℃后浸入0.01mol的NaHCO3溶液，然后取出。再加入0.01％的烧结助剂ZrN，重新加温至400℃反应烧结，再以30℃/h的速度升温至1200℃，继续高温烧结，然后退火降温冷却。
3、一种抗静电、抗电磁辐射、抗菌陶瓷，其特征是：分子式可以表达为Na3Zr2Si2PO12或NaZr2Ti2P3O12。
4、根据权利要求1、2、3所描述之陶瓷体，其特征是：抗菌效果达到90％；导电率达到10-7Ω-1.cm-1；电磁辐射和γ射线透过率为20％。
CN 200410016447 2004-02-19 2004-02-19 一种抗静电、抗电磁辐射、抗菌陶瓷 Pending CN1657493A (zh)