CN1646741A - Elastic fiber and use thereof - Google Patents
Elastic fiber and use thereof Download PDFInfo
- Publication number
- CN1646741A CN1646741A CNA038090775A CN03809077A CN1646741A CN 1646741 A CN1646741 A CN 1646741A CN A038090775 A CNA038090775 A CN A038090775A CN 03809077 A CN03809077 A CN 03809077A CN 1646741 A CN1646741 A CN 1646741A
- Authority
- CN
- China
- Prior art keywords
- fabric
- elastomer
- fiber
- silk
- stocking
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
An elastic fiber comprising organic and/or inorganic high moisture absorption and release fine particles, characterized in that the elastic fiber exhibits a maximum temperature rise at moisture absorption and/or water absorption of 2 C or higher; and a woven or knit fabric, or clothing such as an inner wear or stockings, characterized in that the elastic fiber is used in at least part thereof. The employment of this construction has enabled providing an elastic fiber that can be formed into a stretch fabric being thin and of light weight, exhibiting high moisture retention and further ensuring comfort and sensuousness. Moreover, the elastic fiber ensures desirable after-texturing passage, has excellent heat resistance, and can quickly remove steam occurring by sweating at exercise from the skin to thereby enable providing stretch clothing free from becoming stuffy.
Description
Technical field
The present invention relates to the purposes of a kind of elastomer with moisture absorption exothermicity and braided fabric thereof etc. and the manufacture method of knitted fabric.
Background technology
At present, the cloth of emphasis heat insulating ability trends towards thickening gradually or becomes heavy.When putting on these cloth, there are problems, for example Heavy Weight, be difficult for movable, fashion is impaired, feel sense of discomfort such as sultry when perhaps causing on electric car on and off duty etc., perspiring owing to the hydrofuge after perspiring is insufficient, also have after the temperature of sweat descends to produce the sensation etc. of feeling cold, so wish on the market that a kind of quality occurring approaches and the good cloth of heat insulating ability.
Particularly use the retractility cloth of elastomer etc. can be close to skin, above-mentioned sense of discomfort can show significantly especially when making thick cloth in order to ensure heat insulating ability.In addition, in the purposes of utilizing its fit to pursue aesthetic feeling for example in stocking, the pantyhose etc., if thickening then aesthetic feeling when wearing can reduce mostly greatly.
In order to ensure the heat insulating ability of these thin cloth, to have carried out various researchs at present, but just changed knitting technology weave mostly or select general silk, its effect is abundant not enough, and can not get guaranteeing simultaneously the cloth of heat insulating ability, light weight, comfortableness, aesthetic feeling.
In addition, synthetic fiber such as polyester fiber or nylon fiber and polyurethane elastomeric fiber are different from so-called cotton or natural fabrics such as wool, silk, and wherein hydrophilic functional group's content is few, the therefore general hygroscopicity that lacks.Therefore researcher's hydrophiling technology of synthetic fiber that studied for a long period of time is is for example recorded and narrated in 491 pages of the 47th 10 phases of volume of dyeing industry, has proposed various hydrophilic processing.
Be used to improve the absorptive technology of polyurethanes elastomer, be disclosed in the Japanese Patent Application Publication spy and open in the flat 11-81046 communique.The manufacture method that possesses high-hydroscopicity, high bioaffinity and good physical strength and processability good water-insoluble, nonionic water imbibition polyurethane silk simultaneously and utilize melt spinning is wherein disclosed.But, since the water absorptivity 200% or more and the formation fiber macromolecule self have high water absorbing capacity, thereby swelling can take place and present warmth sensation in this fiber fiber surface when when washing and absorbing sweat, therefore has problems sometimes when using as the dress material purposes.
Open in the 2001-98423 communique the Japanese Patent Application Publication spy, disclosing and having used the hydrophily polyalcohol by the polyol component as matrix polymer is that water-soluble poly alkylene ether polyalcohol improves the hygroscopic technology of polyurethanes elastomer.Also disclose and to solve the spy thus and open problem in the flat 11-81046 communique,, but also had following problem even when being used for the dress material purposes, also the influence of swelling can be reduced to the degree that can not influence feel.
In the technology that improves polyurethanes elastomer poisture-penetrability, in the method for mixing high water absorbency polymer, polymer as high-hydroscopicity for example has polyacrylic polymer, vinylic polymers, polyamide polymers, high-hydroscopicity polyether polyols with reduced unsaturation etc., but exist because these high water absorbency polymers are local, rerum natura therefore can occur and reduce and the impaired problem of stability of spinning process.Also have, because this high water absorbency polymer does not generally have crosslinked, can produce swelling by suction, make polyurethanes elastomer swelling in the same manner when importing above-mentioned hydrophily polyalcohol, in bag core or knitting process sometimes along with scum silica frost attached to bringing out so-called fracture of wire and the problem that waits aspect the processing afterwards off quality on the guide etc.
On the other hand, the stable on heating requirement to the polyurethanes elastomer in recent years improves gradually, particularly is desirable to provide the polyurethanes elastomer that can interweave with the polyester fiber that needs high-temperature pressure dyeing always.At such requirement, as open flat 5-186557 communique the Japanese Patent Application Publication spy, the spy opens in the flat 7-102035 communique disclosed, as improving the stable on heating technology of polyurethanes elastomer, be known that after being shaped to polyether polyols with reduced unsaturation and carry out the technology that macromolecule quantizes by heat treatment by polyurethane solutions.But, though the polyurethanes elastomer that obtains by these technology increases at the heat treated heat resistance in the processing of back, be difficult to control grey cloth performance and amount corresponding to purpose, qualification rate is relatively poor, and is having problems aspect the back processing trafficability characteristic.
Also have, if import above-mentioned hydrophily in polyol component, the heat treated heat resistance that then is directed in the processing of back reduces, thereby has the problem that interweaves with the polyester fiber that needs high-temperature pressure dyeing of being difficult to.
Narrate at the prior art of braided fabric below.The braided fabric of forming by non-elastic fibres such as polyester fiber, polyamide-based fiber, cellulosic fibre and elastic polyurethane class; because the elongation function admirable, therefore can be used to pantyhose and socks sole, brassiere, tie up other elastic cotton overcoat bands such as coat, resilient doublet, the base fabric of elastic webbing, the medical application of motion body harness class and many-sided purposes such as base fabric of resilient protection cover such as tight underwears such as tripe, Lingerie (foundation) and sweat shirts such as underskirt, swimsuit or type body clothes, ski trousers, elasticity garrha clothing.
Particularly in the undies purposes, owing to have the retractility and the thinness of appropriateness, the composite fabric of elastic yarn such as carbamate and nylon is just becoming main flow.But, because the distinctive poisture-penetrability of synthetic fiber is bad, feeling of oppression and heat becomes problem, as the means that solve feeling of oppression and heat, except utilizing above-mentioned hygroscopicity polyurethane, open flat 9-228155 communique and the special hygroscopicity nylon-type that discloses utilization improvement nylon fiber moisture-absorption characteristics in the flat 9-256278 communique of opening for example Japanese Patent Application Publication spy.
As the desired comfortableness of undershirt, adopt humidity control effect and heat-insulating property to estimate, oneself generate heat at first in dress, inhibition effective substances as the sense of feeling cold to heating effect with after perspiring, open in flat 9-158040 communique and the Te Kai 2000-303353 communique for example Japanese Patent Application Publication spy, disclose the moisture absorption heat release fiber of acrylic compounds.But the fiber that obtains mainly is a staple fibre, because mechanical performance is poor slightly, is difficult to obtain spun yarn and thin knitted fabric, and by also becoming elastic yarn with the elastic yarn of carbamates is compound, still aesthetic feeling becomes and can not meet the demands sometimes in addition.
Open in the 2002-38375 communique for example Japanese Patent Application Publication spy in addition, proposed in the processing of back, to adopt resin bonding method and glycerol polymerization method acrylic compounds moisture absorption exothermicity resin particle to be anchored at the method on nylon or mylar surface, but the moisture absorption particle also is present in surface layer yarn, the problem of problem that is clamminess in the time of also can having moisture absorption sometimes or washing resistance shortcoming and feel sclerosis.
Prior art at stocking is described below.Since nylon yarn occurred, as the dress ornament that improves women's payment to a porter U.S., stocking had obtained popularizing, along with the appearance of pantyhose has more increased its consumption.Advanced along with preference, the consumer is the commodity of demand different stage gradually also,, article more transparent and that retractility is higher occurred that is.As 1 example wherein, can enumerate the support type stocking that requires fastening sense stronger, the stocking of the cladded yarn of use Spandex (spandex) fiber and nylon yarn has also appearred, nowadays become main flow.Synthetic thread intensity height can obtain thin and the good stocking of wear, sees significant from this respect, but owing to approaches the shortcoming of heat insulating ability shortcoming when therefore having severe cold again.Because hygroscopicity is low, the feeling of oppression and heat when also wishing to perspire is improved in addition.In addition this feeling of oppression and heat can cause the foreign odor in the footwear, thereby becomes women's a worry.
In synthetic fiber, also there are a lot of hygroscopicity fiber with excellent, but the intensity of most of synthetic fiber is lower, therefore be not suitable in the stocking of thin and pursuit durability, the long filament that can be used in the stocking mainly is nylon or polyester, the standard aqueous rate height of nylon in synthetic fiber particularly, intensity is also high, therefore can use Tynex.But problem is also many between freeze-up and during heat.As what severe cold was used thick panty girdle arranged also, but for the young woman who pays attention to looks this is had a lot of discontented.When heat,, also pay attention to outward appearance and fastening sense on the contrary, even it is more therefore to be discontented with the situation of also wearing it though the situation of not wearing is barefoot also arranged.
In recent years, improving gradually, and the compound silk of elastic yarn such as carbamate and nylon is just becoming main flow for the requirement of the strong stocking of the fastening sense that is called as support type.As the means that solve feeling of oppression and heat, try to utilize the hygroscopicity nylon yarn of having improved above-mentioned nylon fiber moisture-absorption characteristics, also utilized above-mentioned hygroscopicity polyurethane, and it is moist and be imbued with the stocking of comfortableness to have proposed to improve suction thus, but also fail to improve the effect of moisture absorption heat release and antibacterial and deodouring.
The moisture absorption exothermal effect is known in existing cotton and wool fibre, but identical with above-mentioned panty girdle, is not suitable for equally in women's stocking of thin and pursuit aesthetic feeling.
In view of these present situations, for example opening the Japanese Patent Application Publication spy has proposed to use in back processing adhering resin moisture absorption heat release resin particle to be fixed on method on the stocking that the compound silk by nylon and elastic polyurethane silk constitutes in the 2001-131802 communique, but the moisture absorption particle also is present in the nylon yarn of top layer, therefore problem that is clamminess when having moisture absorption and washing resistance become easily insufficient, also can cause the feel sclerosis sometimes.
Below mainly the prior art of long fiber fabric is described.
In all sports, usually for warm muscle and joint before setting in motion to prevent injured and to improve locomitivity, all warm up.Particularly warm-up even more important in the outdoor game when severe cold.
At this moment the player wears warm-up suit, although existing clothes has heat insulation effect, owing to do not have heating effect, therefore warm-up also the needs than the long time.For fear of this situation and warm up effectively at short notice and when wearing the thick clothes that hinders motility, its muscle power can be consumed a part.Can certainly carry thermals source such as hand warmer in clothes, but so only heat can local warming, its effect is limited, also can hinder motion in addition.
In addition, in the golf and skiing of outdoor prolonged exercise in winter, wish to have the clothes of heating effect.Except sportswear, also wish to possess the effect of heating in addition for general clothes of using winter and underwear class.
Here, as the fiber with hygroscopicity and adjustment effect, for example can enumerating, the Japanese Patent Application Publication spy opens the cross-linked acrylic acid fibrid of putting down in writing in the flat 9-59872 communique.But the cross-linked acrylic acid fibrid does not have suitable retractility in sportswear etc., does not consider movability especially yet.
In addition, mainly as spun fabric, in the work clothes of under all professional occasions, wearing, the heat insulation effect of in common clothes, being pursued and decorative effect, also pursue the effect of protection health.For example for the Work Clothes that outdoor work is used, require it can prevent wound and cover ultraviolet ray with protection skin etc.In addition, therapeutic medical uniform and some experiments with uniform in, require to have and can prevent the effect polluted because of health that bacterium etc. causes etc.
On the other hand, in Work Clothes, also require appropriateness to keep temperature and humidity and operation easily in the clothes, particularly in working the clothes of usefulness outdoor winter, require to possess heat insulation effect and sweat can be released into the outer effect of clothes.
Under the situation that must have moisture absorption or absorbent function, mainly use cotton, but, therefore can feel to be clamminess or when the work rest, feel to feel cold because cotton fiber does not have rapid-drying properties.From this aspect, the heat insulation effect of wool cloth is good with the effect that makes the saturating extremely outside of moisture in the clothes, but poor as the mechanical endurance of Work Clothes.
Here as fiber, be known that above-mentioned cross-linked acrylic acid fibrid with hygroscopicity and adjustment effect.But the cross-linked acrylic acid fibrid does not have the retractility that is suitable for Work Clothes etc., does not consider movability especially yet.
Summary of the invention
Problem of the present invention is divided into following the 1st~4 problem.
The 1st problem of the present invention is to provide and is suitable for the heat insulating ability height, also has elastomer in the retractility cloth of comfortableness and aesthetic feeling, provide in addition be suitable for that back processing trafficability characteristic is good, the elastomer in the steam of the generation of perspiring when having excellent heat resistance and can from skin, remove motion fast and the not sultry elastic garment.
The 2nd problem of the present invention is to provide moisture absorption exothermicity height, owing to this heat release has good heat insulating ability and the also good knitted fabric of retractility, particularly provide because good, the good knitted fabric of warm-up effect when sports of heating effect that moisture absorption causes.Be provided in addition and have both snugness of fit, fashion, wholesomeness, durability in the underwear purposes etc. and, provide the underwear that uses this knitted fabric in addition the knitted fabric of the characteristics of skin gentleness.
The 3rd problem of the present invention is to give the stocking hygroscopicity, has heating effect and not sultry and can keep the stocking of comfort conditions when moisture absorption is provided, and further provides to have antibiosis and deodorization effects and the also good stocking of washing resistance concurrently.
The 4th problem of the present invention is to provide clothes with movability when heating effect and the knitted fabric that is applicable to it.
The inventor etc. have carried out wholwe-hearted research in order to solve above-mentioned problem, and the result has finished the present invention finally.Be that the present invention is by constituting with the lower part.
1. an elastomer is characterized in that, the maximum temperature ascending amount when moisture absorption and/or suction is more than 2 ℃.
2. the elastomer of record is characterized in that the hydroscopicity under 20 ℃ * 65%RH is more than 0.5% in the above-mentioned the 1st, and the hydroscopicity under the 20 ℃ * 95%RH is more than 1.5%.
3. the elastomer of record is characterized in that in the above-mentioned the 1st, satisfies following formula (1) and (2).
PSD(%)≥60%............................................(1)
PSW (%)≤75%............................................ (2) (wherein, PSD is illustrated under elongation 100% and the xeothermic condition 190 ℃ of dry heat-setting rates after handling 1 minute, and PSW is illustrated under elongation 100% and the damp and hot condition with 60 minutes and is warming up to after 130 ℃ continuously in damp and hot 130 ℃ of processing wet heat setting rates after 60 minutes down from 40 ℃).
4. the elastomer of record is characterized in that in the above-mentioned the 1st, contains the moist particulate of high suction of organic class and/or mineral-type.
5. the elastomer of record in the above-mentioned the 1st, it is characterized in that, the moist particulate of high suction that contains organic class and/or mineral-type, and the average grain diameter of the moist particulate of this high suction is below 20 μ m, swelling capacity below 200% and the regain under the 20 ℃ * 65%RH more than 30%, contain the moist particulate of this high suction of 0.2~50 weight % with respect to fibre weight.
6. the elastomer of record in the above-mentioned the 1st, it is characterized in that, the moist particulate of high suction that contains organic class and/or mineral-type, at least a kind is particulate as described below in the moist particulate of this high suction, promptly, on the vinyl cyanide polymer that contains the above acrylonitrile of 50 weight %, handle the importing cross-linked structure by hydrazine, divinylbenzene or triallyl isocyanuric acid ester, be residual itrile group chemical conversion salt type carboxyl by hydrolysis again, and contain the moist organic fine particles of high suction of the above salt type of 1.0mmol/g carboxyl.
7. a braided fabric is characterized in that, has used the elastomer of record in the above-mentioned the 1st to small part.
8. high scalability knitted fabric, be the high scalability knitted fabric that constitutes by elastomer and non-elastic fiber, it is characterized in that permanent load elongation is more than 50%, permanent load elongation recovery rate is more than 50%, and the surface temperature ascending amount of knitted fabric is more than 3 ℃ during moisture absorption.
9. the high scalability knitted fabric of record is characterized in that in the above-mentioned the 8th, and elastomer is the elastomer of record in the above-mentioned the 1st.
10. the high scalability knitted fabric of record is characterized in that in the above-mentioned the 8th, and elastomer is the elastomer of record in the above-mentioned the 4th.
11. the manufacture method of a high scalability knitted fabric is characterized in that, with the drawing-off limit, elastomer limit and the synthetic thread of record in the above-mentioned the 1st compound after, this compound silk is independent or reinstate circular knitter with other long filaments one and interweave.
12. the manufacture method of a high scalability knitted fabric is characterized in that, the naked silk of the elastomer of record in the above-mentioned the 1st is used for the back sley bar, synthetic thread is used for the most preceding sley bar, adopts warp knitting machine to weave.
13. flexible knitted fabrics, it is characterized in that, it is the knitted fabric that contains the flexible knitted fabrics that is made of non-elastic fiber and elastic yarn to small part, be to show that when moisture absorption programming rate shows the knitted fabric of heat-absorbing action when being heating effect more than 5 ℃/minute and hydrofuge, before the washing of this knitted fabric and the difference of the moisture absorption exothermic temperature after the washing 10 times less than 1 ℃.
14. the flexible knitted fabrics of record is characterized in that in the above-mentioned the 13rd, elastic yarn is made of the elastomer of record in the above-mentioned the 1st.
15. the flexible knitted fabrics of record is characterized in that in the above-mentioned the 13rd, elastic yarn is made of the elastomer of record in the above-mentioned the 4th.
16. the flexible knitted fabrics of record is characterized in that non-elastic fiber is the fiber more than a kind that is selected from polyester fiber, polyamide-based fiber, the cellulosic fibre in the above-mentioned the 13rd.
17. the flexible knitted fabrics of record is characterized in that having antibiotic, deodoriging properties in the above-mentioned the 13rd.18. the flexible knitted fabrics of record is characterized in that in the above-mentioned the 13rd, elastic yarn is naked silk or its composite elastic silk of polyurethane.
19. a underwear is characterized in that, requires the flexible knitted fabrics of record in 13 to small part right to use profit.
20. a stocking is characterized in that, it is the stocking that contains elastic yarn and synthetic fibres to small part, shows the heating effect more than 7 ℃/minute during moisture absorption, shows heat-absorbing action during hydrofuge, before the washing and the moisture absorption exothermic temperature difference after the washing 10 times less than 1 ℃.
21. the stocking of record is characterized in that in the above-mentioned the 20th, elastic yarn is made of the elastomer of record in the above-mentioned the 1st.
22. the stocking of record is characterized in that in the above-mentioned the 20th, elastic yarn is made of the elastomer of record in the above-mentioned the 4th.
23. the stocking of record is characterized in that having antibiotic, deodoriging properties in the above-mentioned the 20th.
24. the stocking of record is characterized in that the deodorizing rate of ammonia is more than 70% in the above-mentioned the 20th.
25. the stocking of record is characterized in that the deodorizing rate of acetic acid is more than 70% in the above-mentioned the 20th.
26. the stocking of record is characterized in that the deodorizing rate of isovaleric acid is more than 70% in the above-mentioned the 20th.
27. the stocking of record is characterized in that in the above-mentioned the 20th, with respect to being selected from ammonia, acetic acid, the isovaleric acid a kind or multiple, before the washing and the deodorizing rate after the washing all more than 70%.
28. the stocking of record is characterized in that frictional static voltage is below 2500V in the above-mentioned the 20th.
29. the stocking of record is characterized in that in the above-mentioned the 20th, the half-life in the half-life mensuration of JIS-L-1094 antistatic behaviour is below 50 seconds.
30. the stocking of record in the above-mentioned the 20th, it is characterized in that, the main body of positive and negative that constitutes the knitted fabric of stocking is synthesized fiber and covers, there is not the moist particulate of high suction on this synthetic fiber surface in fact, the elastic yarn that constitutes stocking contains the moist particulate of high suction of 0.2~50 weight %, and this elastic yarn is extremely constituted more than the 20 weight % of knitted fabric by compound.
31. a fabric is the fabric that contains the compound silk of non-elastic fiber and elastomer, permanent load elongation is more than 15%, and permanent load elongation recovery rate is more than 35%, and the fabric face ascending temperature is more than 1 ℃ during moisture absorption.
32. the fabric of record is characterized in that in the above-mentioned the 31st, elastomer is the elastomer of record in the above-mentioned the 1st.
33. the fabric of record is characterized in that in the above-mentioned the 31st, elastomer is the elastomer of record in the above-mentioned the 4th.
34. the fabric of record in the above-mentioned the 31st, the non-elastic fiber and/or the fiber beyond the compound silk that wherein constitute the compound silk of fabric are the silks that is made of polyesters long filament and/or polyamide-based long filament.
35. the fabric of record in the above-mentioned the 31st, the non-elastic fiber and/or the compound silk fiber in addition that wherein constitute the compound silk of fabric are bulky yarns.
36. the fabric of record in the above-mentioned the 31st, the non-elastic fiber and/or the compound silk fiber in addition that wherein constitute the compound silk of fabric are potential filament length difference mixed filaments.
37. contain the clothes of the fabric of record in the above-mentioned the 31st to small part.
38. the clothes of record is characterized in that in the above-mentioned the 37th, is any in sportswear, underwear, general clothes, winter protection lining or the winter liner (liner).
39. a fabric is the fabric that contains the compound silk of non-elastic fiber and elastomer, permanent load elongation is more than 15%, and permanent load elongation recovery rate is more than 35%, and the fabric face ascending temperature is more than 0.5 ℃ during moisture absorption, on the cloth surface with 10/cm
2Above density contains the filoplume of length more than 1mm.
40. the fabric of record is characterized in that in the above-mentioned the 39th, elastomer is the elastomer of record in the above-mentioned the 1st.
41. the fabric of record is characterized in that in the above-mentioned the 39th, elastomer is the elastomer of record in the above-mentioned the 4th.
42. the fabric of record is characterized in that in the above-mentioned the 39th, constituting the non-elastic fiber of compound silk and/or the compound silk fiber in addition of formation fabric is the silk that contains staple fibre.
43. the fabric of record is characterized in that in the above-mentioned the 39th, constituting the non-elastic fiber of compound silk and/or the compound silk fiber in addition of formation fabric is the silk that contains staple fibre, and the silk that contains this staple fibre is cotton yarn or silk/cotton blended yarn.
44. contain the clothes of the fabric of record in the above-mentioned the 39th to small part.
45. the clothes of record is characterized in that in the above-mentioned the 44th, is any in the clothes of Work Clothes, office uniform, health clothes, Work Clothes style or the general underpants' (being through between underwear and the coat).
Specifically describe the present invention below.
At first the invention at elastomer describes.The maximum temperature ascending amount of the elastomer that relates among the present invention when moisture absorption and/or suction is preferably more than 2 ℃.More preferably more than 3 ℃.This is thin and can give cloth high heat insulating ability because have an elastomer of described characteristic.If but the maximum temperature ascending amount in moisture absorption and/or when suction is too high, then the fracture of wire when throwing can increase, in addition, when in actual braided fabric, using, can cause that unnecessary too high temperature rises, therefore not preferred, the maximum temperature ascending amount of elastomer can be below about 10 ℃ usually.
Moreover the elastomer described in the present invention preferably has above-mentioned exothermicity, and the hydroscopicity under 20 ℃ * 65%RH is more than 0.5%, and the hydroscopicity under 20 ℃ * 95%RH is more than 1.5%.More preferably the hydroscopicity under 20 ℃ * 65%RH is 1.0~5.0%, and the hydroscopicity under 20 ℃ * 95%RH is 2.0~15.0%.Elastomer with above-mentioned feature except can also absorbing sweat effectively with having the cloth attenuation of certain heat insulating ability, even therefore health warms and perspires and also can not feel sense of discomfort, can be given warm and not sultry high comfortableness.Also can eliminate the sense of feeling cold when perspiring back sweat cooling in addition.
The difference of the hydroscopicity of elastomer of the present invention under 20 ℃ * 65%RH and 20 ℃ * 95%RH is preferably more than 1.0%, more preferably more than 2.0%.This numeric representation absorbs the ability of sweat, and this numerical value is big more represents that then its absorbing sweat ability is high more.
Secondly, the heat resistance to polyurethanes elastomer of the present invention describes.At first, with regard to the dry heat-setting of polyurethanes elastomer of the present invention, the PSD (elongation 100% and the dry heat-setting rate after handling 1 minute under 190 ℃ of dry heat conditions) that measures by the aftermentioned assay method is preferably more than 60%.When this numerical value less than 60% the time, the DIMENSIONAL STABILITY of grey cloth can variation in the preboarding operation, and is not preferred.
Also have, with regard to the wet heat setting of polyurethanes elastomer of the present invention, the PSW that measures by the aftermentioned assay method (being warming up to after 130 ℃ continuous in the wet heat setting rate of damp and hot 130 ℃ of following heat treatments after 60 minutes with 60 minutes from 40 ℃ under elongation 100% and damp and hot condition) is preferably below 75%.Heat resistance in this numeric representation dyeing process, the big more heat resistance of then representing of this numerical value is good more.That is to say, if PSW greater than 75% with the difficulty that becomes interweaving of the polyester fiber that needs high-temperature pressure dyeing, elastic return reduction simultaneously, therefore not preferred.
Dress material is with in the cloth, elastomer is not exposed to usually on the surface of cloth and is present in its inside, if therefore described elastomer heat release then be equivalent to by the inner heat release of cloth, with cover radiator body with heat-insulating material and have same effect, thereby can be incubated and obtain accumulation of heat effectively, can also obtain higher comfortableness in addition.Under the situation of giving the non-elastic fiber exothermicity that is exposed to the cloth surface, be exposed to the fast cooling of part of an opposite side, so efficient is low with human body, when the part heat release of human body one side, comfortableness can reduce sometimes, so not too preferred in addition.
In addition, the reagent of heat release is attracted on the cloth surface or makes it to be comprised in the method that is exposed in the surperficial fiber when making moisture absorption by the method for using bonding agent pad dyeing (padding), except feel is damaged easily, washing resistance becomes insufficient easily in pad dyeing etc., and is therefore not too preferred.
Elastomer seldom is exposed to the cloth surface in common using method, therefore has the advantage that can not damage feel.We can say that the reagent that contains moisture absorption and heat release in the inside of elastomer is preferred mode.
At first, effectively in the raw polymer of elastomer, add and mix the moist particulate of high suction, carry out spinning afterwards as giving hygroscopic method.As the typical example of elastomer, can enumerate the polyurethanes elastomer.Spinning can be implemented by any method in dry spinning, wet type spinning, the melt spinning.As the moist particulate of high suction, can use the material of organic class and/or mineral-type, for example can enumerate polyacrylic polymer particulate, polyethylene based polymers particulate, polyamide polymers particulate, polyurethane polymer particulate, porous silica particulate, hydrophily silicon dioxide microparticle etc., in order to prevent the rerum natura reduction and to make spinning operation good with the processing trafficability characteristic, particle diameter is below the 20 μ m, preferably below 10 μ m, more preferably below 5 μ m, most preferably below 2 μ m.This is because in order to achieve the above object, needs to make the moist microparticulate of high suction in spinning process in fiber.If segregation can take place greater than 20 μ m then add mixing the back particle in particle diameter, ooze out into fiber surface simultaneously, therefore become the spinning broken end or the reason of the fracture of wire that causes by absorption scum silica frost in the processing of back.If but average grain diameter is too small, then cause aggegation between particulate easily, the dispersiveness in the polyurethanes elastomer is variation on the contrary, therefore preferably more than 0.1 μ m.In addition, the shape of particulate limits especially, can be ball shape, flat a little any shape such as spherical, amorphous.
The moist particulate of high suction with respect to the content of polyurethanes elastomer preferably more than 0.2 weight %, more preferably more than 0.5 weight %.If less than 0.2 weight % then lack hygroscopicity and not preferred.If the stringiness but content is excessive in the spinning stage can descend, it is many that fracture of wire also becomes, therefore preferably below 50 weight %, more preferably below 48 weight %.
The swelling capacity of the moist particulate of high suction that uses among the present invention is preferably below 200%, more preferably below 100%.If swelling capacity surpasses 200%, then therefore polyurethanes elastomer itself becomes in bag core or the braiding owing to the absorption scum silica frost causes fracture of wire or reason off quality owing to moisture produces swelling.The swelling capacity of the moist particulate of high suction is the smaller the better.In polyurethanes elastomer of the present invention, the swelling that is caused by moisture absorption only takes place in the moist particulate of high suction slightly, and the polyurethane polymer that forms fiber can cause swelling owing to moisture absorption hardly, and therefore fracture of wire or the problem of the aspect of processing afterwards that waits off quality that occurs because of absorption scum silica frost on the guide is less.
The moist particulate of high suction that uses among the present invention, consider from its regain size under 20 ℃, 65%RH, be preferably the moist organic fine particles of high suction of abiotic base polymer, particularly preferred chemical composition as described later, the regain of the moist organic fine particles of high suction under 20 ℃ * 65%RH is preferably more than 30%, more preferably more than 35%, most preferably more than 40%.At present in hygroscopic particulate is arranged, be considered to hygroscopicity the highest be wool powder and gelatin powder, but its regain under 20 ℃ * 65%RH at the most just 15%.In addition, polysaccharide particulate such as starch and cellulose, silk, collagen and protide particulate are littler than above-mentioned wool powder and gelatin powder, are 8~12%.Other also have the powder of urea resin class and melamine resin class, but consider regain under 20 ℃ * 65%RH far less than 30%, so not too preferred.
In addition, for the rerum natura that prevents elastomer reduces and makes spinning operation and processing trafficability characteristic good, the particle diameter of the moist particulate of high suction is below the 20 μ m, preferably below 10 μ m, more preferably below 5 μ m, most preferably below 2 μ m, its content is preferably 0.2~50 weight % with respect to fiber.This is then can not obtain effect of sufficient because if content is lower than this scope, takes place if be higher than this scope then produce rough sledding such as bringing out fracture of wire when making elastomer.
In elastomer of the present invention, contain under the situation of the moist organic fine particles of forming by abiotic base polymer of high suction, the hydrophilic radical that contains as the moist organic fine particles of this high suction, can be salt type carboxyl, salt type sulfonic group, salt type phosphate, salt type phosphonate group etc., as salt can be alkali metal such as Li, Na, K, alkaline-earth metals such as Mg, Ca, Ba, other metals such as Cu, Ag, Mn, the salt of organic cation such as ammonium, amine etc., but the group of acid type except the salt type, also can be contained.The moist particulate of high suction is by after hydrazine, divinylbenzene or the triallyl isocyanuric acid ester processing importing cross-linked structure in the vinyl cyanide polymer that contains the above acrylonitrile of 50 weight %, be the particulate that salt type carboxyl forms by hydrolysis with residual itrile group chemical conversion again, especially preferably contain the particulate of the above salt type of 1.0mmol/g carboxyl.Do not limit especially, but more specifically can enumerate (a) and in the vinyl cyanide polymer that contains the above acrylonitrile of 85 weight %, make that by hydrazine processing importing cross-linked structure being increased to after 1.0~15.0 of nitrogen content is that salt type carboxyl forms by hydrolysis with residual itrile group chemical conversion again, the acrylic compounds metal transition particle that contains the above salt type of 1.0mmol/g carboxyl, (b) importing cross-linked structure by divinylbenzene or triallyl isocyanuric acid ester and containing in the vinyl cyanide polymer of the above acrylonitrile of 50 weight %, is the acrylic compounds metal transition particle etc. that salt type carboxyl formed and contained the above salt type of 2.0mmol/g carboxyl by hydrolysis with residual itrile group chemical conversion.Salt type carboxyl amount is 4.0~10.0mmol/g more preferably.As the manufacture method of the moist organic fine particles of high suction, can open the method manufacturing of putting down in writing in the flat 8-225610 communique by for example Japanese Patent Application Publication spy.The moisture absorption exothermic effects of elastomer of the present invention is mainly from its salt type carboxyl, and the concentration of particulate makes the amassing of particle concentration (weight %) in salt type carboxyl concentration (mmol/g) and the fiber be generally about 40~80, particularly about 45~75 in the therefore preferred regulation fiber.If the fraction of particle in the elastomer is in above-mentioned scope, health can fully feel warm, simultaneously can not cause difficulty in spinning because of fracture of wire etc., and is therefore preferred.
These metal transition particles are cross-linked acrylic acid base polymer particulates, in its primary particle is in the vinyl cyanide polymer, as the monomer that uses simultaneously with acrylonitrile, specifiable is monomer and the salt thereof, the monomer that contains carboxylic acids such as acrylic acid and the salt thereof that contain sulfonic acid such as vinyl halides, ethylidene halide, acrylate, methacrylate, p styrene sulfonic acid, acrylamide, styrene, vinylacetate etc.
The elastomer that contains the moist organic fine particles of this high suction has good exothermicity and hygroscopicity concurrently.Compare with the situation in the non-elastic fiber that is added into ester or nylon, under the situation of the moist organic fine particles of this high suction in being added into polyurethane elastomeric fiber, can demonstrate significant heat release and hygroscopicity, the rerum naturas such as strength and elongation of polyurethane elastomeric fiber reduce also extremely small on the other hand.Its reason it be unclear that, but can infer owing to be exuded to fiber surface easily.Moreover the moist organic fine particles of this high suction also shows good antibiotic property and deodorization, particularly provides extra value to the elastomer of the present invention that is used for stocking and underwear etc.
Elastomer among the present invention is meant that society generally thinks the fiber that shows the caoutchouc elasticity characteristic in idea, and specifiable is the fiber etc. that for example can extend more than 50% at least, more preferably can extend more than 100% and have 20% above recovery rate.The recovery rate here is meant the length of recovery contraction and the ratio of whole elongated portion branch.Typical example is the polyurethanes elastomer with good retractility.
The polyether polyols with reduced unsaturation that can be used for elastomer of the present invention, it also can be the polymer that obtains by following operation, that is to say, two ends that will be made of the diisocyanate cpd of polyalcohol and superfluous molar weight are that the intermediate polymer of isocyanate group is dissolved in N, in the inert organic solvents such as N '-dimethylacetylamide, methyl-sulfoxide and make it the polymer that obtains with diamine compound reaction.
As the restriction especially of above-mentioned polyalcohol, specifiable is polymer diol etc. for example.Specifically can be selected from the polyoxygenated ethylidene glycol, the polyoxygenated trimethylene glycol, polyoxygenated fourth support glycol, PTMEGs such as polyoxy pentamethylene two pure and mild polyoxypropylene fourth support glycol, by adipic acid, decanedioic acid, maleic acid, furoate clothing, in the binary acid such as azelaic acid and malonic acid more than a kind or 2 kinds and ethylene glycol, 1, the 2-propylene glycol, 1, ammediol, 2,2-dimethyl-1, ammediol, 1, the 4-butanediol, 2, the 3-butanediol, the polyester-diol that obtains more than a kind or 2 kinds in the glycol such as hexamethylene two pure and mild diethylene glycol (DEG)s, polylactone glycol such as poly epsilon caprolactone lactone and poly-valerolactone, the polyesteramide glycol, the polyether ester glycol, PCDL etc.
As diisocyanate cpd, so long as aliphatic, alicyclic and aromatic diisocyanate cpd just are not particularly limited.Specifiable is for example methylene-two (4-phenyl isocyanate), methylene-two (3-methyl-4-phenyl isocyanate), 1,4-toluene support vulcabond, 2,6-toluene support vulcabond, and to phenylene diisocyanate, and terephthaldehyde's group diisocyanate, methylene-two (4-cyclohexyl isocyanate), 1,3-and 1,4-cyclohexalene vulcabond, trimethylene diisocyanate, fourth support vulcabond, hexamethylene vulcabond, isophorone diisocyanate etc.
Diamine compound as chain extender is not particularly limited, and specifiable is ethylenediamine, 1 for example, 2-propane diamine, 1,3-propane diamine, 1,6-hexamethylene diamine, 1,2-cyclohexanediamine, 1,3-cyclohexanediamine, 1,4-cyclohexanediamine and hydrazine etc.
Elastomer among the present invention also can be used for cladded yarn and false twist yarn.This is because above-mentioned composite elastic silk becomes the state that is coated by elastomer, therefore can provide long and high heat insulation effect and comfortableness.
Moreover the elastomer among the present invention also can be used for pantyhose.This be because since this purposes when paying attention to wear aesthetic feeling and to require be thin cloth, so can bring into play effect of the present invention especially.
The material that interweaves of the elastomer among the present invention can be any in thermoplastic synthetic fiber, natural fabric, the regenerated fiber, but when being the thermoplastic synthetic fiber, wish to adopt any in polyester fiber, the polyamide fiber, when being natural fabric, adopt cotton or wool, when being regenerated fiber, adopt Pori's nosik (polynosic) viscose.
When the raw material of correspondence and elastomer of the present invention are interweaved, be not subjected to special restriction, but when for example under situation about interweaving, covering elastomer, generally polyester fiber etc. be coated on the elastomer, and be used as warp thread and/or weft yarn with corresponding raw material.In addition with situation that corresponding raw material interweave under, both can be directly with corresponding raw material doubling and enroll, also can enroll with bag core silk.
About the dyeing processing of the retractility braided fabric that obtains, can adopt general manufacturing procedure, that is, grey cloth is carried out preboarding after lax, concise, dye, dry, feel handles, and implements the extreme trace setting afterwards again.
Below, describe at the invention that relates to knitted fabric of the present invention.
Knitted fabric of the present invention is the high scalability knitted fabric that is made of above-mentioned elastic yarn and non-resilient silk, and said non-elastic fiber is meant the fiber of elongation at break less than 100% in the synthetic thread of natural fabric such as wool, cotton, silk and nylon, polyester etc. among the present invention.Non-resilient silk does not contain moisture absorption exothermicity organic fine particles in fact, and the positive and negative of knitted fabric is preferably covered by non-elastic fiber.The hygroscopicity organic fine particles that do not contain in fact described here is meant the above particle of amount that does not contain influential knitted fabric hydroscopicity, can contain on a small quantity.
The rate of using with of elastic yarn in the knitted fabric of the present invention is considered to be preferably institute and is constituted more than the 20 quality % of knitted fabric from obtaining moisture absorption heating effect aspect, and preferred less than 50 quality % are considered in the good property of lining cloth aspect when maintenance is worn.Elastic yarn among the present invention is compared with wool fibre with cotton fiber, the wet speed of suction is slow, and reach the level height of moisture absorption, therefore has the gentle and long-time feature that continues of heating and heat release, particularly slower in the decrease speed of the back fiber temperature that stops to perspire, have that can suppress moves and stop the effect of the sense of feeling cold that the back occurs.Salt type carboxyl is except having the moisture absorption exothermal effect in addition, also has deodorizing, bacteriostasis antibiosis, pH buffering, various effects such as antistatic, as warm-up clothes, is the goods that possess ideal performance.Do not have bacterial reproduction even dry in the shade in addition yet, therefore be suitable as swimsuit yet.
The surface temperature ascending amount of knitted fabric of the present invention knitted fabric when moisture absorption is more than 3 ℃.Heat release during this moisture absorption is that dry knitted fabric is being put into the drier temperature adjustment of silica gel more than 8 hours again after 2 hours under 70 ℃, in being adjusted into 32 ℃, the atmosphere of 70%RH, measured surface temperature in continuous 5 minutes in knitted surfaces afterwards by thermography, the instrumentation maximum temperature and with the difference of itself and 32 ℃ as ascending temperature.If 3 ℃ of this temperature less thaies then lack body sense effect, ascending temperature is high more then good more, reaches about about 10 ℃ and gets final product.
The elongation characteristics of knitted fabric is an important factor, be close to the clothes that does not damage motility in order to improve heat insulating ability and to make as much as possible with health, knitted fabric need have the permanent load elongation more than 50%, preferably has permanent load elongation and be 60~100% extensibility.In addition, in order to keep and the adaptation of health, restorative good and do not damage appearance, the elongation of wishing to have permanent load elongation recovery rate and being more than 50% is restorative.More preferably 60~95%.
When using elastic yarn and non-elastic fiber with, can adopt the method that is made as the method for knitted fabric again after the compound silk and interweaves elastic yarn and non-resilient silk of making.But under situation about interweaving, preferably accomplishing does not have elastic yarn directly to come out at the positive and negative of knitted fabric.This is because can cause the water absorbent fiber surfaces of tacky after the moisture absorption, thereby with the non-elastic fiber of non-hygroscopic in fact volume moisture, can avoid the skin sense of feeling to be clamminess.
As the method for making compound silk, can enumerate the method for making composite spinning or cladded yarn.As the object lesson of the method for making composite spinning, can enumerate in the roving-drafting district of the spinning operation of non-elastic fiber and to supply with suitable drawing-off multiplying power and make the method for core-skin compound silk.As the object lesson of the method for making cladded yarn, can enumerate with the method for suitable drawing-off multiplying power elasticity of supply silk and the non-resilient silk of reeling thereon etc.In the previous case, can use wool, cotton, fiber crops and polyester staple fiber, nylon short fibre as non-elastic fiber.Under latter event, can use the short fibre yarn of silk, polyester filament, Tynex, cotton and wool.Also can be used as the composit false twisting yarn in addition under the situation of polyester filament, Tynex uses.
These compound silks can use separately, also can be woven into circular knitted fabric with other filaments and use, and circular knitted fabric has the advantage that can increase percentage elongation.As long as percentage elongation can satisfy necessary condition, it is just organized be not particularly limited.
Making under the situation of knitted fabric, as long as after the sley bar of supplying with the non-resilient long filament that forms coil, even then in which sley bar, use elastic yarn, all can become knitted fabric with non-resilient long filament parcel elastic yarn, therefore can use naked silk as elastic yarn.At this moment, non-resilient silk also can use staple fibre yarn, but in order to suppress because burr and flyings cause the reduction of operability, preferably use long filament.
Knitted fabric of the present invention goes for underwear.The feature that goes for the knitted fabric of underwear is the effect that has wettability power and have heat release, heat when moisture absorption.We can say that this point also is like this in the invention that relates to stocking described later.At first the damp-warm syndrome degree when wearing knitted fabric of the present invention changes and narrates.Damp-warm syndrome degree among the present invention is meant the damp-warm syndrome degree of the air that comprises in the tissue of underskirt knitted fabric, and this changes the decision comfortableness.Because stimulations such as motion cause body temperature to rise, and then in order to cool off body temperature, sweat is released from skin surface, the temperature of the gas phase that contains in the knitted fabric, humidity also rise simultaneously, thereby do not feel well sense in dress.If at this moment knitted fabric has hygroscopicity, then can suppress gas phase humidity and make it lower, thereby can suppress uncomfortable degree.The moisture of moisture absorption by the fiber surface hydrofuge to external environment condition.If heat release is heated when moisture absorption, then, have only temperature to rise to some extent owing to amount of moisture in the gas phase is identical, so the relative humidity reduction, promote skin to perspire, the result can suppress body temperature and rise.This phenomenon can continue several minutes until the moisture equilibrium at dry side state that reaches underwear.Soon hygroscopic capacity and hydrofuge amount reach balance, and heating effect stops.At this moment the temperature of underwear descends, and reaches equilibrium temperature.If stop motion then perspire stops, only carrying out hydrofuge, just can return to initial conditions soon.
The elastic yarn that uses in the knitted fabric of the present invention is compared with wool fibre with cotton fiber, the wet speed of suction is slow and reach the level height of moisture absorption, therefore heating and heat release are than gentle and long-time continuing, underspeeding of fiber temperature after particularly stopping to perspire is slow, has the effect that can suppress the sense of feeling cold that occurs after the stop motion.
Inventors etc. are by changing the concentration of hygroscopicity particulate in the elastic yarn, and the heating effect during to the moisture absorption that can feel in wearing test is studied, and it is that intensification ability more than 5 ℃/minute is necessary that results verification goes out programming rate.Be preferably more than 7 ℃/minute.This value also is subjected to the influence of external environment condition, and the low more required intensification ability of outer usually temperature is high more.
Conduct can be applicable to the knitted fabric of underwear among the present invention, use the flexible knitted fabrics of forming as the elastic yarn and the non-elastic fibers such as polyester fiber, polyamide-based fiber and cellulosic fibre of representative by with above-mentioned polyurethanes elastomer, but make the knitted fabric of thin and create an aesthetic feeling, the long filament of preferred polyester fibrid, polyamide-based fiber in order to use thin raw yarn.With regard to knitting technology weave, if it is circular knitting, then can be that plain stitch, double rib are knitting, rib stitch, positive and negative tissue and these variation knitted fabric, if can be Te Like (tricot) knitted fabric, La Sheer (raschel) warp-knitted fabric etc., be not particularly limited through knitting.As knitting technology weave, if section's knitted fabric in the spy, can illustratively have through suede-warp plain stitch, vicarious menstruation suede-warp plain stitch, two sley bar warp plain stitch, two sley bar satin, if the La Sheer knitted fabric can illustratively have elastic force mesh warp-knitted fabric, half elastic force mesh warp-knitted fabric, hair weft sateen (サ テ Application ネ Star ト), knitted net ocular hair fabric etc.
Elastic yarn and non-elastic fiber both can be used as compound silks such as cladded yarn and twisted filament, composite spinning and had used, the naked silk of also can interweave non-elastic fiber and elastic polyurethane silk.Compound silk and non-resilient silk as required also can interweave.In order to reduce processing charges, more preferably interweave with naked silk.The sense of being clamminess during in addition for the sense of touch of the rubber like that reduces knitted fabric and moisture absorption, the top layer of knitted fabric preferably covers with non-elastic fiber.At this moment, from giving full play to the telescopicing performance aspect of moisture absorption heat release, hydrofuge, antibiotic, deodoriging properties and knitted fabric, the containing ratio of elastomer is preferably more than 10 quality %.20~50 quality % more preferably.If surpass 50 quality %, then not only unfavorable from the economy aspect, and also can cause sometimes feel like jelly, the decline of texture such as expansion, therefore not too preferred.
1 ℃ of the temperature difference less than of moisture absorption exothermic character after the initial stage of knitted fabric of the present invention and the washing 10 times, 1 ℃ of expression of less than has washing resistance, washs also to keep the moisture absorption exothermic character that can feel after 10 times.
Right fabric of the present invention is suitable for underwear, owing in above-mentioned elastic resin, contain above-mentioned high-hygroscopicity organic fine particles, therefore can make except high scalability can and performances comfortable and easy to wear such as moisture absorption heat release, hydrofuge heat absorption, antistatic behaviour also possess by the sanitation performance of deodorizing antibiotic effect generation, by the multi-functional flexible knitted fabrics of the performance of keeping humidity of pH shock-absorbing capacity generation.The present invention comprises the invention of underwear.
Then describe at the invention that relates to stocking among the present invention.
Stocking of the present invention is characterised in that to have moisture pick-up properties, has heat release and heating effect in addition during moisture absorption.Damp-warm syndrome degree when at first, wearing stocking of the present invention changes and can be applicable to that the knitted fabric of underwear is basic identical.
Inventors etc. are by changing the concentration of the moist particulate of high suction in the elastic yarn, and the heating effect when wear the moisture absorption that stocking can feel in testing is studied, and found that the intensification ability that preferably has more than 7 ℃/minute.More preferably more than 9 ℃/minute.Also be subjected to external environment influence, the low more required intensification ability of outer temperature is high more.
From the restorative aspect of thin and thick, intensity, extensibility and elongation, the compound silk that stocking of the present invention is preferably by elastic yarn and synthetic fibres constitutes, perhaps the MIXED FABRIC of the false twist yarn of this compound silk and synthetic fibres.Elastic yarn is preferably elastic filament, and synthetic fibres is preferably synthetic thread.Preferably the positive and negative of stocking is synthesized the long filament covering in fact.This is directly to contact the lubricity of also improving thus with skin surface with skin for fear of elastic yarn, satisfies the preferred characteristics as stocking.If the compound silk both sides are made long filament, be preferred then for improving the transparency and improving intensity and improve wear thus, synthetic thread is preferably polyester or nylon.From the viewpoint of hygroscopicity and durability, synthetic thread is Tynex more preferably.The total fiber number of this compound silk is preferably 30 dtexs~80 dtexs when partly using as pants in actual applications, divide as shank to be preferably 10 dtexs~50 dtexs when using.
Initial stage and the moisture absorption exothermic character difference of washing after 10 times are represented washing resistance, and 1 ℃ of less than is meant can also keep the moisture absorption exothermic character that can feel after the washing 10 times.Washing described in the present invention is meant with the washing as benchmark of the JIS-0217-103 method of the standard wash agent of using estimation of fibres technological associations.
The elastic yarn that contains the moist organic fine particles of high suction preferably contains more than the 20 weight % of the fabric that constitutes to some extent, if at this with next suction moisture performance deficiency, therefore not preferred.The fastening sense of stocking is also not enough, therefore not preferred in addition.More preferably 25~40%.Under the situation of pantyhose, the pants part is made of different silks respectively with the shank branch is general.It is also no problem that both constitute with identical silk, if only there is use among the side to contain the elastic yarn of this hygroscopicity organic fine particles, then only refers to contain in the knitted fabric in this section the component ratio of the elastic yarn of this hygroscopicity organic fine particles.
As mentioned above, by dividing the knitted fabric that uses respectively arbitrarily according to environmental change repetition moisture absorption heat release and hydrofuge heat-absorbing action, can design the pantyhose that are adapted to season and environment in pants part and shank.For example in the stocking of using summer by only divide adopting the elastic yarn that contains heat release hygroscopicity organic fine particles at shank, can obtain having the nice and cool stocking of smooth sense, preferably divide all uses as the time spent in winter in pants part and shank.
Stocking of the present invention preferably has following feature, and the deodorizing rate that promptly is selected from least a material in ammonia, acetic acid and the isovaleric acid is more than 70%.These compositions are as the stink composition defined of bad smell of perspiration as the estimation of fibres technological associations of civic organization, as long as have the performance of eliminating these compositions, particularly all has deodoriging properties for any composition in above-mentioned 3 kinds, then think to have the performance of removing the back stink of perspiring easily, and this performance should be more than 70%.If thereby less than 70% then its performance is insufficient, not talkative have a deodoriging properties.Preferably deodoriging properties is more than 85%, more preferably more than 90%.
Stocking of the present invention for be selected from deodorizing rate at least a in ammonia, acetic acid and the isovaleric acid before washing and washing back amount to and be preferably more than 70%.Commercially available stocking is the so-called back processed goods that adheres to the deodorizing composition after making product mostly at present, and its washing resistance is poor, even therefore have deodoriging properties at first, its deodoriging properties of washing back also can deterioration.The preferred elastic yarn that adopts in the stocking of the present invention, owing to become one with fiber at its fiber surface and inside, also hardly can deterioration even therefore wash its performance.The more preferably scope of washing back deodorizing rate is more than 80%, more preferably more than 85%.
The frictional static voltage of stocking of the present invention is preferably below 2500V.If frictional static voltage surpasses 2500V, then when wearing skirt, twine easily, sense does not easily particularly feel well when wearing the winter of low humidity.Preferred range is below the 2000V, more preferably below the 1500V.
The half-life of the electrostatic potential of stocking of the present invention is preferably below 50 seconds.Identical with frictional static voltage, the half-life of this electrostatic potential also is to estimate a parameter of twining easness, if this value is below 50 seconds, even since with about stocking and the friction of the outside of skirt etc. cause static, very fast because of the minimizing speed of electrostatic potential, therefore go out to be difficult to feel sense of discomfort.If surpass 50 seconds, particularly when wearing the winter of low humidity, do not feel well easily.Preferably below 30 seconds, more preferably below 15 seconds.
Secondly, describe at the fabric that the present invention relates to.At first be primarily aimed at and relate to the invention that contains a large amount of long stapled fabrics (hereinafter referred to as the long fiber fabric) and describe.
Long fiber fabric of the present invention is the fabric that contains the compound silk of non-elastic fiber and above-mentioned elastomer, preferably permanent load elongation more than 15%, permanent load elongation recovery rate at fabric face ascending temperature more than 35%, during moisture absorption at the fabric more than 1 ℃.
In the present invention, the fabric face ascending temperature is the value of measuring by the aftermentioned method respectively when permanent load elongation, permanent load restoration rate and moisture absorption.
The elongation characteristics of long fiber fabric is to the clothes desired key property of sweat shirt particularly.For the clothes that obtains to be easy to move, the permanent load elongation of fabric of the present invention is more than 15%, preferably more than 20%.For fear of reducing conformality and extending restoratively, the upper limit of permanent load elongation is preferably about 40%.
Attractive in appearance for fear of damaging in addition, the perseverance load elongation recovery rate of long fiber fabric of the present invention is more than 35%, preferably more than 60%.The upper limit of permanent load elongation recovery rate is not particularly limited, and is about 95%.
Fabric face ascending temperature during the moisture absorption of long fiber fabric of the present invention in addition is more than 1 ℃, preferably more than 2 ℃.The fabric face ascending temperature is high more good more during moisture absorption, but just enough to about 5 ℃ usually.If the fabric face ascending temperature can be felt warm in above-mentioned scope during moisture absorption when then wearing.
When containing the compound silk of above-mentioned non-elastic fiber and elastomer permanent load elongation 15% or more, permanent load extends recovery rate and can make by the following method at the fabric more than 1 ℃ at fabric face ascending temperature more than 35%, during moisture absorption.The content of promptly making the non-elastic fiber and the compound silk of the elastomer that contains the moist particulate of high suction is the above fabrics of 5 weight %, and pass through suitable degree of draft, knit stitches and the count of regulating when making compound silk, can obtain the fabric of above-mentioned number range.
Permanent load elongation and perseverance load elongation recovery rate, the content of compound silk improves or reduces in degree of draft, knit stitches and count in the time of can passing through to adjust the making compound silk and the fabric.The ascending temperature of fabric face during moisture absorption in addition, the content of compound silk improves or reduces in content that can be by regulating particulate in the elastic yarn and the fabric.
The fiber number of the silk that is constituted, still as the fiber number of elastic yarn, is generally about 20~100dtex with purposes and different with the kind of constituent material, is preferably 30~50dtex especially.If in above-mentioned scope, the elongation characteristics of the fabric that then obtains, recovery characteristics will become good.
In long fiber fabric of the present invention, so-called non-elastic fiber is meant that the elongation at break of regulation among the JIS L1013 (2000) (test of isodromicing elongation's shape) is the fiber below 100%.The kind of non-elastic fiber does not limit especially, can use known fiber.As so known non-elastic fiber, specifiable is the synthetic fiber of polyamide (nylon etc.), polyester, polyvinyl, acrylonitrile, polyethylene, polypropylene and so on; The regenerated fiber of artificial silk, cuprammonium rayon and so on; The semisynthetic fibre of acetate, general sieve Mick silk and so on; The natural fabric of silk and so on etc.
From satisfying the desired intensity of sweat shirt aspect, the especially preferred long filament that constitutes by polyester, polyamide (nylon etc.).Non-elastic fiber can mix use separately more than a kind or 2 kinds.
By non-elastic fiber constitute the silk fiber number be generally about 10~100dtex, be preferably about 20~50dtex especially.
Bulk from obtaining, as to expand sense, warm up and feel aspect, non-elastic fiber is preferably and carries out bulk manufactured fiber, more preferably false twisting bulky yarn.
The form of compound silk can be used ad lib as the known form of elastomer complex form.As the known compound silk of this class, specifiable is with suitable drawing-off multiplying power elasticity of supply fiber and the bag core yarn of non-elastic fiber or complexing of reeling in the above, perhaps with suitable drawing-off multiplying power elasticity of supply fiber and with the state of non-elastic fiber doubling twisting and the twine that obtains etc. down.Especially preferably wrap the core yarn.From covering property that can improve non-elastic fiber and the cut-out of avoiding owing to elastomer that causes of exposing, can reduce the aspect of the friction between the cloth simultaneously, the coiling bag core yarn (single core yarn that wraps) that more preferably uses hollow spindle formula coating machine to make.
The twisting count of compound silk can be about 500~1200T/m, to be preferably about 600~1200T/m.If twisting count in above-mentioned scope, can satisfy the elongation recovery characteristics of compound silk, and can reduce " the order system キ " problem that causes to the elastomer surface owing to exposing.
The usage rate of elastomer and non-elastic fiber is in the weight ratio elastomer: the ratio of non-elastic fiber is generally 1: 2~and about 1: 8, preferred especially about 1: 3~1: 5.
In order to obtain sufficient moisture absorption exothermal effect in actual applications, in long fiber fabric of the present invention, preferably contain above-mentioned compound silk more than the 5 weight %.Particularly contain more than the 20 weight %, more preferably contain more than the 25 weight %.Can use 100% this compound silk as silk in the fabric, but the aspect of the comfortableness when keeping wearing is preferably about 30 weight %.If the ratio of compound silk in above-mentioned scope, is then felt the moisture absorption exothermal effect easily when wearing.
Under the situation of the fiber that has the formation long fiber fabric beyond the above-mentioned compound silk, its material is not particularly limited, can use any in synthetic fiber, semisynthetic fibre, regenerated fiber, the natural fabric.In addition, Si form also can be long filament or short fibre yarn.Fiber beyond the compound silk both can be that non-elastic fiber also can be an elastomer, but from feel and sense of touch aspect, preferably used the long fiber of non-elastic fiber.Fiber beyond the compound silk can be independent a kind or make up more than 2 kinds and use.
Fiber beyond the above-mentioned compound silk under the situation of making the fabric that sportswear uses, is preferably polyesters and/or polyamide-based long filament (particularly non-resilient silk).Under the situation of making thin and the ganoid cloth of cloth, can use flat yarn, but can become the poor slightly cloth of elastic force under this situation.Under the situation of and the cloth that percentage elongation is big thick a little at needs, the silk as beyond the above-mentioned compound silk preferably uses bulky yarn.Especially preferably use the false twist yarn (particularly 1 grade of processing yarn) of polyesters long filament or polyamide-based long filament.
Requiring under the situation of aesthetic feeling in addition, the silk as beyond the above-mentioned compound silk preferably uses potential filament length difference mixed filament, more preferably uses the potential filament length difference mixed filament that is made of polyester filament.Using under the situation of potential filament length difference mixed filament, the fabric after making is being carried out decrement processing, can improve soft hand feeling and drapability by using NaOH etc.As potential filament length difference mixed filament, can use and mix that to have knitted the long filament more than 2 kinds with thermal contraction difference be so-called different contraction mixed filament, perhaps mix and knitted the long filament that shrinks by heat treatment and the long filament of elongation is a so-called spontaneous elongation mixed filament etc.
In addition under the situation of making the fabric that underwear and general clothes use, as the basic silk beyond the compound silk, the preferred flat yarn of forming by polyester or nylon of using.
Springy compound filaments can perhaps also can be made a side of warp thread or weft yarn the silk of being made up of springy compound filaments with warp thread and weft yarn both sides and mutual the arrangement, and the opposing party makes the silk of being made up of non-resilient silk.Can obtain 2 road stockinettes under the previous case, can obtain 1 road bullet under the latter event and exhale fabric.
Therefore long fiber fabric of the present invention is suitable as the lining or the winter liner uses such as (wearing off lining cloth freely) of sportswear, underwear, general clothes, insulated cold wear owing to have the character and the retractility of moisture absorption heat release concurrently.
Use the kind of the clothes of long fiber fabric of the present invention to limit especially, but owing to have the character and the retractility of moisture absorption heat release concurrently, so sportswear, underwear, winter liner, the lining of insulated cold wear, general clothes etc. are suitable.Be used under the situation of sportswear, becoming and be particularly suitable for outside the room the warm-up clothes of motion.
Specifically, specifiable as sportswear be tennis togs, golf jersey, anorak, jog clothes etc. upper garment or trousers; Skirt etc.In the middle of these, be fit to the fabric that springy compound filaments and inelastic polyester false twist yarn have for example been made up in use.
As general clothes specifiable be shirt or blouse and so on underpants, trousers, skirt, go out with the upper garment of jacket and so on etc.In the middle of these, be fit to use the fabric (middle robe use etc.) of the fine-titred silk that has made up silk or constituted by special long filament with absorption of perspiration, made up the fabric (upper garment use etc.) of springy compound filaments and inelastic polyester flat yarn, and made up springy compound filaments and different contraction and mixed the fabric of knitting silk (upper garment use etc.) etc.Having made up the mixed fabric of knitting silk of springy compound filaments and different contraction not only can be as the upper garment of going out with the general clothes of jacket and so on, and the type games that can also be used for tennis jacket, golf jacket is used extensive uses such as clothing.
Can enumerate shirt and pants etc. as underwear.In the middle of these, be fit to use the fabric of the fine-titred silk that has made up silk or constituted by special long filament etc. with absorption of perspiration.
In the lining and winter liner with upper garment and so on insulated cold wear, the long fiber fabric of springy compound filaments and inelastic polyester flat yarn has been made up in suitable use at overcoat and skiing.
Then be described at the fabric (hereinafter referred to as spun fabric) that mainly contains a large amount of staple fibres among the present invention.Wherein elastomer is preferably long fiber.
Spun fabric of the present invention is the fabric that contains the compound silk of non-elastic fiber and above-mentioned elastomer, preferably permanent load elongation is more than 15%, permanent load elongation recovery rate is more than 35%, and the fabric face ascending temperature is more than 0.5 ℃ during moisture absorption, and contains 10/cm on the cloth surface
2Fabric with the filoplume more than the length 1mm of upper density.
The filoplume density on fabric face ascending temperature and cloth surface was the value of measuring by the aftermentioned method respectively when in the present invention, permanent load elongation, perseverance were loaded elongation recovery rate, moisture absorption.
The elongation characteristics of spun fabric is to the clothes desired key property of sweat shirt particularly.In order to obtain the clothes of motion easily, the permanent load elongation of spun fabric of the present invention is more than 15%, preferably more than 20%.In order to make conformality and extend and restoratively do not reduce, the upper limit of permanent load elongation is preferably about 40%.
Attractive in appearance in order not damage in addition, the perseverance load elongation recovery rate of spun fabric of the present invention is more than 35%, preferably more than 60%.The upper limit of permanent load elongation recovery rate is not particularly limited, and is about 95%.
In addition during the moisture absorption of spun fabric of the present invention the fabric face ascending temperature more than 0.5 ℃, preferably more than 2 ℃.The fabric face ascending temperature is high more good more during moisture absorption, but just enough to about 5 ℃ usually.If in above-mentioned scope, can feel because the heat release that moisture absorption produces, and can obtain forming the clothes of comfort by heating.
Spun fabric of the present invention in addition contains 10/cm on the cloth surface
2With the filoplume more than the length 1mm of upper density.This filoplume density is preferably 20/cm
2More than.The upper limit of this filoplume density does not limit especially, but usually at 30/cm
2About.If this filoplume density in above-mentioned scope, can obtain sensation warm and nature making under the situation of fabric.
Permanent load elongation 15% or more, permanent load extends recovery rate and containing 10/cm more than 0.5 ℃ and on the cloth surface at fabric face ascending temperature more than 35%, during moisture absorption
2Spun fabric with the filoplume more than the length 1mm of upper density can obtain by the following method.Promptly, suitable is will be by non-elastic fiber and the elastomer that contains the moist particulate of the high suction of 0.2~50 weight % a compound silk of forming and a fabric that interweaves that contains staple fibre, in the fabric more than this compound silk content is 5 weight %, degree of draft, knit stitches and count when making compound silk by suitable adjusting, and optimize the fibre length of the twist factor and the staple fibre of compound silk simultaneously, can obtain the fabric of above-mentioned number range.
Permanent load elongation and permanent load elongation recovery rate, degree of draft, knit stitches and the count in the time of can making compound silk by adjustment and the content of compound silk improve or reduce.The ascending temperature of fabric face during moisture absorption in addition, the content that can be by regulating particulate and the content of compound silk improve or reduce.The filoplume density on cloth surface can improve or reduce by the twist factor of optimization compound silk and the fibre length of staple fibre.
The fiber number of silk that constitutes spun fabric of the present invention, still as the fiber number of elastic yarn, is generally about 20~100dtex with purposes and different with the kind of constituent material, is preferably about 30~50dtex especially.If in above-mentioned scope, the elongation characteristics of the fabric that then obtains, recovery characteristics will become good.
In the invention that relates to spun fabric, so-called non-elastic fiber is meant that the elongation at break of regulation among the JISL1013 (2000) (test of isodromicing elongation's shape) is the fiber below 100%.Can use known non-elastic fiber as non-elastic fiber.As so known non-elastic fiber, specifiable is the synthetic fiber of polyesters, nylon-type, acrylic compounds, polyvinyl class, polyethylene kind, polypropylene type and so on; The regenerated fiber of artificial silk, cuprammonium rayon and so on; The staple fibre of forming by the semisynthetic fibre of acetate, general sieve Mick silk and so on; Cotton, numb and so on natural fabric etc.
Under the situation of the few clothes purposes of the washing times of the uniform and so on that is used for for example handling official business, also can use hair (wool, goats hair, camel hair, mohair, alpaca fibre, an Angora etc.).
The Work Clothes of moisture absorption when being used to pay attention to wearing and absorbing sweat performance; The general underpants of shirt, blouse and so on; The clothes of Work Clothes style; Under the situation of the purposes of health clothes, suitable is cotton fiber.
Non-elastic fiber can be independent a kind or make up more than 2 kinds and use.
The fibre diameter of non-elastic fiber is generally about 12~22 μ m, is preferably especially about 14~17 μ m.
Compound silk can be made as the known form of complex form of elastomer.As such known forms, specifiable is with suitable drawing-off multiplying power elastomer to be supplied with the spinning zone of non-elastic fiber and rolled the composite spinning that obtains by twisting, or twists with the fingers the twisted union yarn line obtain etc. with suitable drawing-off multiplying power elasticity of supply silk and by handing over the stiff short fibre yarn of other manufacturing.
From the covering property that can improve non-elastic fiber and avoid since elastomer expose the cut-out that causes, can reduce the friction aspect between the cloth simultaneously, preferred composite spinning.
(TW is twisting count [returning/2.54cm], when N is english cotton counts, uses the twist factor of compound silk
Expression) for can being for example about 3~5, preferred about 3.8~4.5 under the situation of composite spinning silk.If twist factor in above-mentioned scope, can obtain required short fibre yarn fabric feeling, and when weaving, it can obtain the suitable inclusion power of composite spinning.
The usage rate of elastomer and non-elastic fiber by weight, elastomer: the ratio of non-elastic fiber is generally 1: 2~about 1: 8, preferred especially about 1: 3~1: 5.
In order to obtain sufficient moisture absorption exothermal effect in actual applications, in spun fabric of the present invention, contain the above-mentioned compound silk more than the 5 weight %.Particularly contain more than the 20 weight %, more preferably contain more than the 25 weight %.The upper limit that contains ratio of compound silk can be according to the desired characteristic of different purposes (for example elastic force etc.) decision.
Silk beyond the above-mentioned compound silk is preferably the silk that contains staple fibre, more preferably the silk that is made of staple fibre.The kind of staple fibre limits especially, also can use any in synthetic fiber, semisynthetic fibre, regenerated fiber, the natural fabric.The silk that is made of staple fibre both can be the silk that is made of a kind of fiber, also can be the blended yarn that is made of the fiber more than 2 kinds.
As the silk that constitutes by staple fibre beyond the above-mentioned compound silk, be fit to use non-resilient silk in addition.
Preferred especially cotton yarn, contain the blended yarn of cotton fiber.Specifically, in interweaving, use the close plain cloth of knitting of the cotton yarn of 40~50 english cotton counts, can utilize the moist and moisture absorption heat release of suction imitate-really, to be applicable in underpants' purposes of shirt, blouse and so on.In interweaving, use the plain weave or the TWILL CLOTH of the cotton yarn of 20~40 english cotton counts in addition, can utilize antibiotic, antibacterial, deodorizing effect, suction is moist and the moisture absorption exothermal effect, can be used as the medical clothes of white frock and operating coat and so on.In the usefulness that interweaves, use the positive TWILL CLOTH of the cotton yarn of 10~30 english cotton counts in addition, can utilize the moist and moisture absorption exothermal effect of suction, be applicable to the clothes that Work Clothes and COARSE DRILL are fabric.In either case, feature all is easy because of having elastic operation, and has comfortableness when wearing.
Hair in the natural fabric (wool etc.) is suitable for making the situation of the general underpants of shirt, blouse and so on, office uniform that washing times is few.By using hair, can make the cloth of the soft and warm sense of touch that has sedate gloss and bring by filoplume, can obtain the clothes of directly on skin, wearing easily.Specifically,, can obtain the elastic force cloth that also has aesthetic feeling and wrinkle resistance the moist and moisture absorption exothermal effect except suction, be suitable for the office uniform for example by using hair short fibre yarn or wool blended yarn as warp thread.
These short fibre yarns can use warp thread and weft yarn alternately to arrange, and perhaps also a side of warp thread or weft yarn can be made the silk of being made up of springy compound filaments, and the opposing party makes the silk of being made up of short fibre yarn.2 road stockinettes can be obtained under the previous case, 1 road stockinette can be obtained under the latter event.
Owing to have characteristic that filoplume is arranged on character, retractility and the surface of moisture absorption heat release (sense naturally of warm, sense of touch, outward appearance) concurrently, therefore fabric of the present invention is suitable as the clothes of Work Clothes, office uniform, health clothes, Work Clothes style, generally uses such as underpants.
Clothes of the present invention is the main clothes that uses spun fabric in the invention described above.The kind of clothes does not limit especially, but is suitably for Work Clothes; The office uniform; The health clothes of white frock, operating coat, lab-gown and so on; The clothes of the Work Clothes style of the fabric trousers of COARSE DRILL, bawneen, overalls and so on for example; The general underpants of shirt, blouse and so on etc.
The specific embodiment
Specifically describe the present invention by the following examples.Be meant parts by mass with what part was represented among the embodiment.Assay method, evaluation method etc. are following described in addition.
(A) exothermicity of elastomer (maximum temperature rising)
Use circular cyiinder knitting machine to make the naked braiding grey tube cloth sample of 10g elastomer.To weave the grey tube cloth sample is contained in temperature sensor and (is wound on the 540K MD-5 type with bar-shaped test side that the upright gauge (strain) of peace makes, and make it to be close to as far as possible, by the test side front end turn back remaining braiding grey tube cloth sample end and cling with glass paper tape or annular natural gum etc.) on, after under 70 ℃ dry 2 hours, put into the drier (the about 5%RH of drier) that silica gel is housed, placed 24 hours down at 32 ℃.To adorn the temperature sensor and temperature recorder (for example upright gauge (strain) manufacturing of peace of sample then fast; DATA COLLECTOR AM-7052 type) connect, (for example potassium sulfate saturated aqueous solution drier) instrumentation under the environment of 32 ℃ * 70%RH is because the variations in temperature that the moisture absorption heat release produces.The maximum temperature data that calculate (℃) and initial temperature (32 ℃) is poor, try to achieve maximum temperature rise (℃).
(B) hydroscopicity of elastomer
After the 5g elastomer cleaned with the 100ml benzinum, measure the weight W under the absolute dry condition
1(g).After placing 24 hours under the atmosphere of 20 ℃ * 65%RH, measure its weight W
2(g), by following formula (3), try to achieve the hydroscopicity under 20 ℃ * 65%RH.
20 ℃ * 65%RH, hydroscopicity (%)={ (W
2-W
1)/W
1} * 100...... (3)
Also have, under the atmosphere of 20 ℃ * 95%RH, placed 24 hours, measure the weight W of this moment
3(g), by following formula (4), try to achieve the hydroscopicity under 20 ℃ * 95%RH.
20 ℃ * 95%RH, hydroscopicity (%)={ (W
3-W
1)/W
1} * 100...... (4)
(C) swelling capacity of particulate
About 1g adiabatic drying sample after 24 hours in being set at 105 ℃ drier is put into the 10ml helix tube, keep vertical, make the level of keeping as far as possible above the sample, read the volume V of this moment by scale
1(ml).Add pure water in helix tube, its amount also is higher than amount above the sample for the suction back water surface, vertically place 6 hours after, read volume V above the sample by scale
2(ml).The swelling capacity of particulate is tried to achieve by following formula (5).
Swelling capacity (%)={ (V
2-V
1)/V
1} * 100...... (5)
(D) regain of particulate
With cleaning and absolutely dry culture dish is got about 2g sample, cover the aluminium foil of reserving the part aperture, be careful and do not allow particulate disperse, put into the Constant Temperature and Humidity Chambers that is set at 20 ℃ * 65%RH, after 24 hours, the weight W of mensuration culture dish
4Put into the drying machine that is set at 105 ℃ then after dry 24 hours, measure the weight W of culture dish
5(g).The regain of particulate is tried to achieve by following formula (6) under 20 ℃ * 65%RH.
Regain (%)={ (W
4-W
5)/W
5} * 100...... (6)
(E) average grain diameter of particulate
The ELS-800 pattern of using light scattering photometer (Da mound electronics corporation to make), try to achieve the average grain diameter of particulate according to the subsidiary specification of photometer.
(F) dry heat-setting rate (PSD)
The elastomer that with initial length is 22.5cm (L1) under the condition of elongation 100%, in 190 ℃ carry out 1 minute dry heat treatment after, at room temperature place cooling in 10 minutes after, measure filament length (L2), calculate by following formula (7).
PSD(%)={(L2-L1)/L1}×100......(7)
(G) wet heat setting rate (PSW)
With initial length be 9.5cm (L3) elastomer under the condition of elongation 100% in damp and hot be warming up to 130 ℃ with 60 minutes from 40 ℃ down after, handled 60 minutes down at damp and hot 130 ℃ continuously again, at room temperature place cooling in 10 minutes afterwards, measure filament length (L4) then, calculate by following formula (8).
PSW(%)={(L4-L3)/L3}×100......(8)
(H) the salt type carboxyl concentration in the particulate
Smart claim about 1g intensive drying for examination particulate (X (g)), after wherein adding 200g water, add the 1N aqueous hydrochloric acid solution while heat to 50 ℃, adjusting pH is 2, then uses the 0.1N caustic soda aqueous solution to try to achieve titration curve according to conventional method.Try to achieve the sodium hydrate aqueous solution consumption (Y (cc)) that is consumed by carboxyl by this titration curve, calculate carboxyl concentration by following formula (9).
Carboxyl concentration=0.1 * Y/X...... (9)
Not adding 1N aqueous hydrochloric acid solution adjusting pH in addition in above-mentioned carboxyl quantitative determination operation is 2, and directly similarly tries to achieve titration curve and obtain the carboxylic acid concentration.Calculate salt type carboxyl concentration by these results by following formula (10).
Salt type carboxyl concentration=carboxyl concentration-carboxylic acid concentration ... (10)
(I) the permanent load elongation of knitted fabric and permanent load elongation recovery rate
Method according to record in " standardization of hand valuation and parsing " (Japanese fibre machinery association compile) IV chapter " mensuration of the mechanical characteristic of cloth " is measured.The size of measuring sample is wide 20cm, long 5cm, gathers respectively at the warp-wise and the broadwise of cloth.To measure sample alongst with 4.00 * 10
-3It is 500gf/cm that the constant speed of/second stretches until peak load, measures the percentage elongation (%) of this moment, and the mean value of calculating warp-wise and broadwise is as permanent load elongation (%).In addition, its elongation is returned to the load vanishing that puts on sample, and will this moment with the percentage elongation be zero point be the percentage elongation of benchmark as B (%), 500gf/cm load percentage elongation down is as under the situation of (A), recovery rate is represented with following formula (11).
Recovery rate (%)=(A-B)/mean value of the recovery rate of A} * 100...... (11) warp-wise and broadwise is as perseverance load elongation recovery rate (%).
(J) mensuration of the moisture absorption exothermic character of knitted fabric
In 70 ℃ cylinders (tumbler) drying machine, the sample knitted fabric after dry 2 hours, is put into the drier that silica gel is housed, in temperature adjustment under the environment of 32 ℃ * 70%RH more than 8 hours.Then, under the environment of 32 ℃ * 70%RH, from drier, take out, took the temperature of instrumentation knitted surfaces every 20 seconds with the hot pursuit device.Reach the highest temperature and time by this data setting, calculate programming rate by following formula (12).
Programming rate={ (being up to Da Wendu)-(32 ℃) }/time of advent (minute) ... (12) the moisture absorption exothermic temperature difference before and after the washing is relatively to be up to Da Wendu.
(K) anti-microbial property of knitted fabric or stocking
Use staphylococcus aureus as test organisms, test, use the bacteriostatic activity value representation according to the SEK uniform tests method of estimation of fibres technological associations regulation.If this value is more than 1.6 then can judge to have anti-microbial property.
(L) deodoriging properties of the knitted fabric beyond the stocking
The foul smell of 3 liters of normal concentrations enclosed together with the knitted fabric of the amount that is equivalent to contain the 1g elastic yarn in 5 liters the Tedler sack, measuring the foul smell composition slip (%) after 30 minutes under the room temperature with gas Tekes (ガ ス テ ッ Network ス) detector tube, is qualified more than 70%.Also have, the odor concentration of different odor sources is set as follows.
Ammonia: 100ppm, acetic acid: 100ppm, isovaleric acid: 60ppm repeats 3 times and measures, and gets its mean value.
(M) containing ratio of elastic yarn in the knitted fabric beyond the stocking
Give silk speed and fiber number by elastic yarn and non-resilient silk are calculated by following formula (13).Under situation, use guide wheel (runner) length to replace to silk speed through compiling.
The containing ratio of elastic yarn (quality %)=(elastic yarn give silk a speed * fiber number) ÷ { (elastic yarn give a silk speed * fiber number)+(non-resilient silk give a silk speed * fiber number) } * 100...... (13)
(N) the moisture absorption exothermic character of stocking
The part (about 30cm) of stocking after dry 2 hours, is put into the drier that silica gel is housed in 70 ℃ roller drier, under the environment of 32 ℃ * 70%RH with the drier temperature adjustment more than 8 hours.Then, under the environment of 32 ℃ * 70%RH, from drier, take out, took the temperature on instrumentation stocking surface every 20 seconds with the hot pursuit device.Reach the highest temperature and time by this data setting, calculate programming rate by following formula (14).
Programming rate (℃/minute)={ (being up to Da Wendu ℃)-(32 ℃) }/time of advent (minute) ... (14) the moisture absorption exothermic temperature of 10 front and back of washing is poor, is relatively to be up to Da Wendu.
(O) mensuration of stocking deodoriging properties
Equipment evaluation method according to estimation of fibres technological associations is measured.Ammonia and acetic acid are measured according to the detector tube method, and isovalerate is according to gas chromatography determination.
(P) frictional static voltage
Frictional static voltage determination method according to JIS-L-1094 is measured.
(Q) half-life
Half-life determination method according to JIS-L-1094 is measured.
(R) the permanent load elongation of fabric and permanent load elongation recovery rate
Method according to record in " standardization of hand valuation and parsing " (Japanese fibre machinery association compile) IV chapter " mensuration of the mechanical characteristic of cloth " is measured.Promptly from fabric, get the sample of wide 20cm, long 5cm.Under the situation that is 2 road stockinettes, on the warp-wise of cloth and broadwise, respectively get 1 respectively, under the situation that is 1 road stockinette, only get the sample that direction of extension is a length direction.
Then, with each sample alongst with 4.00 * 10
-3The peak load that the constant speed of/second is stretched to per unit width is 500gf/cm, and the percentage elongation (%) of this moment is permanent load elongation (%).In addition, its elongation is returned to the load vanishing that puts on sample, and will this moment be that zero point is that the percentage elongation of benchmark is as B (%) with the percentage elongation, under the situation of permanent load elongation as A (%), permanent load elongation recovery rate is the value of following formula (15) expression.
Permanent load elongation recovery rate=(A-B)/A} * 100...... (15)
No matter be to measure permanent load elongation or permanent load elongation recovery rate, the mean value of the measured value of the measured value of the warp-wise of employing cloth and broadwise under the situation that is 1 road stockinette, only adopts the measured value of direction of extension under the situation that is 2 road stockinettes.
(S) fabric face ascending temperature during moisture absorption
In 70 ℃ roller drier fabric drying after 2 hours, is put into the drier that silica gel is housed, temperature adjustment is more than 8 hours under the environment of 32 ℃ of temperature, relative humidity 70%RH.Then, under the environment of 32 ℃ of temperature, relative humidity 70%RH, from drier, take out fabric, by taking the temperature of instrumentation fabric face 5 minutes with hot pursuit device (NEC Japanese electric apparatus three flourish societies make the TH3102 pattern) every 20 seconds.The ascending temperature of fabric face during as moisture absorption with the difference that is up to Da Wendu and 32 ℃.
(T) deodoriging properties of fabric test
The foul smell of 3 liters of normal concentrations being enclosed together with the fabric of the amount that is equivalent to contain the 1g elastic yarn in 5 liters the Tedler sack, measure under the room temperature through the foul smell composition slip after 30 minutes with gas Tekes detector tube, is qualified more than 50%.The odor concentration of each odor source is set as follows.Repeat 3 times and measure, get its mean value.
Ammonia: 100ppm, acetic acid: 100ppm
Use embodiment and comparative example to specify the present invention below, but the present invention is not limited by these.
(embodiment 1)
The main embodiment that records and narrates about elastomer.
Making 200 parts of molecular weight under 80 ℃ is 1800 poly tetramethylene oxide two pure and mild 45 parts of methylenes-two (4-phenyl isocyanate) reaction 3 hours, obtains two and terminally is the intermediate polymer of isocyanate group.After intermediate polymer is cooled to 40 ℃, adds 375 parts of N,N-dimethylacetamide and be cooled to 10 ℃.Be ready to 4.0 parts of ethylenediamines, 0.4 part of diethylamine are dissolved in 147.6 parts of N, the diethylamine solution of N-dimethylacetylamide, once add diethylamine solution in the intermediate polymer solution of high-speed stirred, obtaining solution concentration is that 32.2 weight %, viscosity are the polyether polyols with reduced unsaturation solution of 2500 pools (30 ℃).
In the polyether polyols with reduced unsaturation solution that obtains thus, add and mix 4% n-butylamine/N, polymer, benzotriazole compound, the hindered phenol compound of N-dimethylhydrazine endcapped.
Then, the feed particles aqueous dispersion that to form by acrylonitrile, methyl acrylate, sodium p styrene sulfonate and water with the crosslinked back of hydrazine with the NaOH hydrolysis process, average grain diameter is that 0.5 μ m (measuring with light scattering photometer), swelling capacity are that regain under 80%, the 20 ℃ * 65%RH is 45% the moist organic fine particles of high suction (sodium-salt type carboxyl amount is 5.4mmol/g), in the above-mentioned polyether polyols with reduced unsaturation solution of 5 weight %, add, mixed 3 hours with mixer, make spinning solution.
After the spinning solution deaeration, from being the spinning head of 0.5mm, the aperture spues, in having flowed into 235 ℃ the spinning tube that adds hot-air, push, add the finish of 5%OWF and reel with 550m/ minute speed.The strand that obtains 40 ℃ of following heat treated 72 hours, the 22dtex of back processing, the polyurethane elastomeric fiber of 2 long filaments have been obtained supplying with.The exothermic maximum amount of the polyurethane elastomeric fiber that obtains is 3 ℃, and the hydroscopicity under the 20 ℃ * 65%RH is that the hydroscopicity under 2.0%, the 20 ℃ * 95%RH is 4.4%, and PSD is 62%, and PSW is 63%.
Use the common drawn yarn 8dtex of nylon 6, the strand of 5fil as winder in the elastomer that obtains, the core filament drafting when setting the bag core respectively is 3.3, and the first twist twisting count is 2900 times/m, and the retwist twisting count is 2450 times/m, makes the dual packet heart yarn.
Above-mentioned cladded yarn is supplied with 4 mouthfuls of pantyhose braiding machines (4 inches of bores, 400 of knitting needle radicals) braiding, carry out preboarding, cutting again, a series of back such as make, dye processing, finalization etc. processes, and obtains pantyhose.
In the winter time, with the pantyhose that make 20 testers have been carried out wear test.The result answers warm and comfortable for 17 in 20 testees.In above-mentioned wear test, answering the shank that not only exposes has the also cold and uncomfortable people of heat insulating ability, belly to have 8.
(comparative example 1)
The main comparative example that relates to elastomer of recording and narrating.
Except the addition with heat release hygroscopicity organic fine particles changes into 0.1%, adopt method similarly to Example 1 to obtain pantyhose.The exothermic maximum amount of the polyurethane elastomeric fiber that obtains is 0.6 ℃, and the hydroscopicity under the 20 ℃ * 65%RH is that the hydroscopicity under 1.5%, the 20 ℃ * 95%RH is 1.8%, and PSD is 61%, and PSW is 62%.Allow 20 testers wear the pantyhose that make similarly to Example 1.As a result, answer have 16 that do not have difference with common pantyhose, answer is warmed up a little but is had 4 inadequately fully.
Main embodiment and the comparative example that relates to knitted fabric of recording and narrating in embodiment 2,3 and the comparative example 2.
(embodiment 2)
Making 200 parts of molecular weight under 80 ℃ is 1800 poly tetramethylene oxide two pure and mild 45 parts of methylenes-two (4-phenyl isocyanate) reaction 3 hours, obtains two and terminally is the intermediate polymer of isocyanate group.After intermediate polymer is cooled to 40 ℃, adds 375 parts of N,N-dimethylacetamide and be cooled to 10 ℃.Be ready to 4.0 parts of ethylenediamines, 0.4 part of diethylamine are dissolved in 147.6 parts of N, the diethylamine solution of N-dimethylacetylamide, once add diethylamine solution in the intermediate polymer solution of high-speed stirred, obtaining solution concentration is that 32.2 weight %, viscosity are the polyether polyols with reduced unsaturation solution of 2500 pools (30 ℃).
In the polyether polyols with reduced unsaturation solution that obtains thus, add and mix 4% n-butylamine/N, polymer, benzotriazole compound, the hindered phenol compound of N-dimethylhydrazine endcapped.
Then add in polyether polyols with reduced unsaturation solution that to mix 13 quality % average grain diameters be that 0.5 μ m (measuring with light scattering photometer), swelling capacity are that 80% the moist organic fine particles of high suction (will be by the feed particles aqueous dispersion of acrylonitrile, methyl acrylate, sodium p styrene sulfonate copolymerization with the material of the crosslinked back of hydrazine with the NaOH hydrolysis process.Wherein keep carboxylic acid sodium and sodium sulfonate as hydrophilic radical), make spinning solution.
After the spinning solution deaeration, from being the spinning head of 0.5mm, the aperture spues, in having flowed into 235 ℃ the spinning tube that adds hot-air, push, add the finish of 5%omf and reel with 550m/ minute speed.The strand that obtains 40 ℃ of following heat treated 72 hours, is obtained the polyurethane elastomeric fiber of 44dtex, 4 long filaments.
On the sley bar of back, use the elastic polyurethane silk obtain, the polyester filament 56dtex36 long filament that on preceding sley bar, uses cation normal-pressure to dye, with the tricot warp knitting machine of 28 leaf gauges obtain half organize through knitted fabric (containing ratio of elastomer is 25 quality %).Utilize conventional method to implement concise, preboarding, normal temperature dyeing, finalization with what obtain through knitted fabric, obtain row (course) density and be 102C/2.54cm, wale (wale) density and be 62W/2.54cm, order and pay and be 200g/m
2The finished product knitted fabric.The elongation characteristics of this knitted fabric, moisture absorption exothermic character are as shown in table 1.
Make this knitted fabric and make leotard and spat, obtain following evaluation when wearing as netman's underwear in the gymnasium in the winter time: imperceptible initial cold, the 10 minutes time of half when usefulness is not worn approximately warms up and just health can be adjusted to the state that can race, does not also have feeling of oppression and heat.
(embodiment 3)
3.3 times of the elastic yarn 78dtex drawing-offs that will obtain on one side according to method similarly to Example 2, on one side with nylon 6 long filament 77dtex24 long filament doublings, carry out 1 grade of false twisting processing with 2500T/m, reel again after before coiling, interweaving with about 60/m.
Use this false twisting compound silk, the circular knitter of employing 28G obtains the knitted fabric of plain stitch.Utilize conventional method to implement concise, dyeing, setting the knitted fabric that obtains, make order and pay and be 150g/m
2And the containing ratio of elastic yarn is the refining knitted fabric of 25 quality %.The elongation characteristics of this knitted fabric, moisture absorption exothermic character are as shown in table 1.In addition, make tights by refining knitted fabric.Allow cinder specialists wear this tights, and make it to estimate its wearing feeling when warm-up, the result is that body temperature rises rapid and do not have feeling of oppression and heat.
(comparative example 2)
Except not containing high moisture absorption organic fine particles, make tights according to method similarly to Example 3.The elongation characteristics of this knitted fabric, moisture absorption exothermic character are as shown in table 1.The result who estimates according to method similarly to Example 3 is in addition, and the warm-up vigorous exercise that needs feels sultry when perspiring, after the stop motion, just feel cold soon.
Table 1
Permanent load elongation | Permanent load elongation recovery rate | Cloth surface ascending temperature | |
Embodiment 2 | ????62% | ????75% | ????5℃ |
Embodiment 3 | ????57% | ????64% | ????6℃ |
Comparative example 2 | ????58% | ????62% | ????2℃ |
Embodiment 4~9, comparative example 3 expressions relate generally to the knitted fabric that is suitable for underwear and the embodiment and the comparative example of underwear.
(embodiment 4)
Making 200 parts of molecular weight under 80 ℃ is 1800 poly tetramethylene oxide two pure and mild 45 parts of methylenes-two (4-phenyl isocyanate) reaction 3 hours, obtains two and terminally is the intermediate polymer of isocyanate group.After intermediate polymer is cooled to 40 ℃, adds 375 parts of N,N-dimethylacetamide and be cooled to 10 ℃.Be ready to 4.0 parts of ethylenediamines, 0.4 part of diethylamine are dissolved in 147.6 parts of N, the diethylamine solution of N-dimethylacetylamide, once add diethylamine solution in the intermediate polymer solution of high-speed stirred, obtaining solution concentration is the polyether polyols with reduced unsaturation solution of 32.2 weight %, viscosity 2500 pools (30 ℃).
In the polyether polyols with reduced unsaturation solution that obtains, add and mix 4% n-butylamine/N, the N '-polymer of dimethylhydrazine endcapped, benzotriazole compound, hindered phenol compound.
Then adding mixing 13 quality % average grain diameters in polyether polyols with reduced unsaturation solution is that 0.5 μ m (measuring with light scattering photometer), swelling capacity are 80% the moist organic fine particles of the high suction (material that will be obtained with the NaOH hydrolysis process with the crosslinked back of hydrazine by the feed particles aqueous dispersion of acrylonitrile, methyl acrylate and sodium p styrene sulfonate copolymerization.Keep carboxylic acid sodium and sodium sulfonate as hydrophilic radical), make spinning solution.
After the spinning solution deaeration, from being the spinning head of 0.5mm, the aperture spues, in having flowed into 235 ℃ the spinning tube that adds hot-air, push, add the finish of 5%omf and reel with 550m/ minute speed.The strand that obtains 40 ℃ of following heat treated 72 hours, is obtained the polyurethane elastomeric fiber of 44dtex, 4 long filaments.
With the 56dtex-24 long filament combination of silk and the nylon 6 of the elastic polyurethane silk 44dtex that obtains, the circular knitter (XL-3A/38 inch diameter 28 leaf gauges) that uses the former smart machine of good fortune society to make is made into the grey cloth of ベ ア plain stitch (partly using the fabric of Polyester Filament in the plain stitch).Carry out the refining processing of common dyeing for this grey cloth, obtaining through density is that 100C/2.54cm, weft density are the grey cloth of 54W/2.54cm.The elastic yarn containing ratio of this knitted fabric is 24 quality %.Use this grey cloth to make underskirt as dress material.The performance of this knitted fabric is as shown in table 2.Wearing this underskirt under 10 ℃, 40%RH environment, was that unit repeats 2 walkings and peace and quiet are taken one's seat with 10 minutes, have warm when evaluation result is walking and do not have the wearing feeling of feeling of oppression and heat, and walking stops the initial stage sense of not feeling cold.
(embodiment 5)
With the 56dtex-24 long filament combination of silk and the polyester of the elastic polyurethane silk 44dtex that obtains among the embodiment 4, use the circular knitter (XL-3A/38 inch diameter 28 leaf gauges) of the former smart machine of good fortune society manufacturing to be made into the grey cloth of ベ ア plain stitch.Carry out the refining processing of common dyeing for this grey cloth, obtaining through density is that 100C/2.54cm, weft density are the grey cloth of 54W/2.54cm.The elastic yarn containing ratio of this knitted fabric is 28 quality %.Use this grey cloth to make underskirt similarly to Example 1 as dress material.The performance of this knitted fabric is as shown in table 2.Wearing this underskirt under 10 ℃, 40%RH environment, was that unit repeats 2 walkings and peace and quiet are taken one's seat with 10 minutes, have warm when evaluation result is walking and do not have the wearing feeling of feeling of oppression and heat, and walking stops the initial stage sense of not feeling cold, and also had smooth sense of touch.
(embodiment 6)
The silk of the elastic polyurethane silk 44dtex that will obtain according to the method identical with embodiment 4 and the 56dtex-24 long filament combination of nylon 6, the tricot warp knitting machine (wide 28 leaf gauges of HKS2/180 inch) that uses カ one Le マ ィ ャ-society to make is made into the grey cloths of half tissue 2 tunnel through volume.Carry out the refining processing of common dyeing for this grey cloth, obtaining through density is that 100C/2.54cm, weft density are the grey cloth of 58W/2.54cm.The elastic yarn containing ratio of this knitted fabric is 21 quality %.Use this grey cloth to make pants as dress material.The performance of this knitted fabric is as shown in table 2.Wearing this pants under 10 ℃, 40%RH environment, was that unit repeats 2 walkings and peace and quiet are taken one's seat with 10 minutes, have warm when evaluation result is walking and do not have the wearing feeling of feeling of oppression and heat, and walking stops the initial stage sense of not feeling cold, and also had smooth sense of touch.
(embodiment 7)
The silk of the elastic polyurethane silk 22dtex that will obtain according to the method identical with embodiment 4 and the 33dtex-12 long filament combination of nylon 6, the tricot warp knitting machine (wide 28 leaf gauges of HKS2/180 inch) that uses カ-Le マ ィ ャ-society to make is made into the grey cloths of half tissue 2 tunnel through volume.Carry out the refining processing of common dyeing for this grey cloth, obtaining through density is that 110C/2.54cm, weft density are the grey cloth of 57W/2.54cm.The elastic yarn containing ratio of this knitted fabric is 17 quality %.Use this grey cloth to make pants similarly to Example 6 as dress material.The performance of this knitted fabric is as shown in table 2.Wearing this pants under 10 ℃, 40%RH environment, was that unit repeats 2 walkings and peace and quiet are taken one's seat with 10 minutes, have warm when evaluation result is walking and do not have the wearing feeling of feeling of oppression and heat, and walking stops the initial stage sense of not feeling cold, and also had smooth sense of touch.
(embodiment 8)
To use the Raschel looms (wide 28 leaf gauges of RSE-4N/130 inch) of カ-Le マ ィ ャ-society's manufacturing to be made into the grey cloth of 4C warp plain stitch according to the 55dtex-12 long filament combination of silk and the nylon 6 of the elastic polyurethane silk 235dtex that obtains with embodiment 4 same procedure.Carry out the refining processing of common dyeing for this grey cloth, obtaining through density is that 118C/2.54cm, weft density are the grey cloth of 39W/2.54cm.The elastic yarn containing ratio of this knitted fabric is 22 quality %.Use this grey cloth to make and tie up tripe as dress material.The performance of this knitted fabric is as shown in table 2.Wearing this and tie up tripe under 10 ℃, 40%RH environment, was that unit repeats 2 walkings and peace and quiet are taken one's seat with 10 minutes, have warm when evaluation result is walking and do not have the wearing feeling of feeling of oppression and heat, and walking stops the initial stage sense of not feeling cold, and also had smooth sense of touch.
(embodiment 9)
To use the Raschel looms (wide 28 leaf gauges of RSE-4N/130 inch) of カ-Le マ ィ ャ-society's manufacturing to be made into the grey cloth of 6C elastic force mesh warp knitting fabrics according to the 78dtex-24 long filament combination of silk and the nylon 6 of the elastic polyurethane silk 310dtex that obtains with embodiment 4 same procedure.Carry out the refining processing of common dyeing for this grey cloth, obtaining through density is that 53C/2.54cm, weft density are the grey cloth of 33W/2.54cm.The elastic yarn containing ratio of this knitted fabric is 25 quality %.Use this dress material to make grey cloth in the side.The performance of this knitted fabric is as shown in table 2.Wearing this brassiere under 10 ℃, 40%RH environment, was that unit repeats 2 walkings and peace and quiet are taken one's seat with 10 minutes, have warm when evaluation result is walking and do not have the wearing feeling of feeling of oppression and heat, and walking stops the initial stage sense of not feeling cold, and also had smooth sense of touch.
(comparative example 3)
The elastic polyurethane silk 44dtex that use obtains according to similarly to Example 4 method except not adding the high-hygroscopicity organic fine particles, adopt method similarly to Example 4 to obtain knitted fabric, use this grey cloth to make underskirt similarly to Example 4 as dress material.The elastic yarn containing ratio of this knitted fabric is 25 quality %.The performance of this knitted fabric is as shown in table 2.Wearing this underwear under 10 ℃, 40%RH environment, was that unit repeats 2 walkings and peace and quiet are taken one's seat with 10 minutes, and evaluation result is to feel cold at the walking initial stage, and the later stage is sultry, and stopping the initial stage in walking has the sense of feeling cold, unsatisfactory.
Table 2
Exothermic peak temperature | Programming rate (℃/minute) | Antibiotic property | Deodorization | ||||
Before the washing | After the washing | Ammonia | Acetic acid | Isovaleric acid | |||
Embodiment 4 | ??37℃ | ??37℃ | ????15 | ??3.1 | ??82% | ??81% | ??90% |
Embodiment 5 | ??36℃ | ??36℃ | ????9 | ??2.7 | ??78% | ??79% | ??85% |
Embodiment 6 | ??37℃ | ??37℃ | ????12 | ??2.9 | ??80% | ??80% | ??88% |
Embodiment 7 | ??36℃ | ??36℃ | ????10 | ??2.5 | ??72% | ??74% | ??82% |
Embodiment 8 | ??37℃ | ??37℃ | ????12 | ??3.0 | ??81% | ??79% | ??86% |
Embodiment 9 | ??37℃ | ??37℃ | ????14 | ??3.2 | ??83% | ??80% | ??92% |
Comparative example 3 | ??33℃ | ??33℃ | ????3 | ??0.3 | ??10% | ??2% | ??3% |
Embodiment 10,11 and comparative example 4~6 main embodiment and the comparative examples that relate to stocking of recording and narrating.
(embodiment 10)
Making 200 parts of molecular weight under 80 ℃ is 1800 poly tetramethylene oxide two pure and mild 45 parts of methylenes-two (4-phenyl isocyanate) reaction 3 hours, obtains two and terminally is the intermediate polymer of isocyanate group.After intermediate polymer is cooled to 40 ℃, adds 375 parts of N,N-dimethylacetamide and be cooled to 10 ℃.Be ready to 4.0 parts of ethylenediamines, 0.4 part of diethylamine are dissolved in 147.6 parts of N, the diethylamine solution of N-dimethylacetylamide, once add diethylamine solution in the intermediate polymer solution of high-speed stirred, obtaining solution concentration is the polyether polyols with reduced unsaturation solution of 32.2 weight %, viscosity 2500 pools (30 ℃).
In the polyether polyols with reduced unsaturation solution that obtains thus, add and mix 4% n-butylamine/N, polymer, benzotriazole compound, the hindered phenol compound of N-dimethylhydrazine endcapped.
Then in above-mentioned polyether polyols with reduced unsaturation solution, add mix feed particles aqueous dispersion that 13 weight % will be made up of acrylonitrile, methyl acrylate, sodium p styrene sulfonate and water with hydrazine crosslinked afterwards with the NaOH hydrolysis process, average grain diameter is that 0.5 μ m (measuring with light scattering photometer), swelling capacity are 80% the moist organic fine particles of high suction, makes spinning solution.
After the spinning solution deaeration, from being the spinning head of 0.5mm, the aperture spues, in having flowed into 235 ℃ the spinning tube that adds hot-air, push, add the finish of 5%OWF and reel with 550m/ minute speed.The strand that obtains 40 ℃ of following heat treated 72 hours, is obtained supplying with the 22dtex of back processing, the polyurethane elastomeric fiber of 2 long filaments.The exothermic maximum amount of the elastic polyurethane silk that obtains is 3 ℃, and the hydroscopicity under the 20 ℃ * 65%RH is that the hydroscopicity under 4.8%, the 20 ℃ * 95%RH is 6.4%.
The strand of common drawn yarn 8dtex, 5fil that uses nylon 6 on the elastic yarn that obtains is as winder, and the core filament drafting when setting the bag core respectively is 3.3, and the first twist twisting count is 2900 times/m, and the retwist twisting count is 2450 times/m, makes the dual packet heart yarn.
Above-mentioned cladded yarn is supplied with 4 mouthfuls of pantyhose braiding machines (4 inches of bores, 400 of knitting needle radicals) braiding, carry out preboarding, cutting again, a series of backs such as the processing of making, dye, setting at last process, and obtain pantyhose.The evaluation result of the half-life of the moisture absorption exothermic character of this stocking, anti-microbial property, deodoriging properties, frictional static voltage, electrostatic potential is as shown in table 3.Use these pantyhose to repeat this wearing test 2 times with 10 minutes units under the condition of the walking and the posture of keeping quite under 20 ℃, the environment of 65%RH, 10 testers of evaluation result all feel more comfortable than the pantyhose that obtain in the comparative example 4.
(embodiment 11)
Except nylon 6 false twist yarns of the cladded yarn that will obtain among the embodiment 10 and 22dtex, 6fil are configured in per 1 row (course), adopt method similarly to Example 10 to obtain pantyhose.The evaluation result of the half-life of the moisture absorption exothermic character of this stocking, anti-microbial property, deodoriging properties, frictional static voltage, electrostatic potential is as shown in table 3.Use these pantyhose to carry out walking under 20 ℃, the environment of 65%RH and the posture each 10 minutes of keeping quite, repeat 2 times this wearing test, evaluation result is to compare with the pantyhose that obtain in the comparative example 4, and 9 feel comfortably cool among 10 testers.
(comparative example 4)
Except making the spinning solution that does not add the moist organic fine particles of high suction, adopt with embodiment 10 identical methods and obtain pantyhose.The evaluation result of the half-life of the moisture absorption exothermic character of this stocking, anti-microbial property, deodoriging properties, frictional static voltage, electrostatic potential is as shown in table 3.Use these pantyhose walking and the posture each 10 minutes of keeping quite under 20 ℃, the environment of 65%RH, repeat 2 times this wearing test, evaluation result is to compare with the pantyhose that obtain among the embodiment 10, and 10 all do not feel well among 10 testers.
(comparative example 5)
Except the moist organic fine particles of the interpolation high suction of mixing in the above-mentioned polyether polyols with reduced unsaturation solution of 3 weight % is made spinning solution, adopt with embodiment 10 identical methods and obtain pantyhose.The evaluation result of the half-life of the moisture absorption exothermic character of this stocking, anti-microbial property, deodoriging properties, frictional static voltage, electrostatic potential is as shown in table 3.Use these pantyhose walking and the posture each 10 minutes of keeping quite under 20 ℃, the environment of 65%RH, repeat 2 times this wearing test, evaluation result is to compare with the pantyhose that obtain among the embodiment 10, and 8 do not feel well among 10 testers.
(comparative example 6)
Employing is rolled the baking method with the moist organic fine particles of high suction, soluble polyurethane (the ェ ラ ス ト ロ Application W-33 that use among the embodiment 10; The first industrial drugmaker makes solid constituent 30%) and catalyst (キ ャ シ ス ト 64; The mixed liquor of 200: 33: 10 the ratio manufacturing of the first industrial drugmaker) anchors in the pantyhose that obtain in the comparative example 4, makes the moist organic fine particles of high suction reach 5 weight %.The evaluation result of the half-life of the moisture absorption exothermic character of this stocking, anti-microbial property, deodoriging properties, frictional static voltage, electrostatic potential is as shown in table 3.Moisture absorption exothermic character before the washing shows good performance, but the performance behind the repeated washing 10 times extremely descends.Adopt method similarly to Example 10 that stocking before washing is carried out wearing test in addition, 10 philtrums of participating in test have 3 people to feel at the volley to be clamminess.
Table 3
Embodiment 10 | Embodiment 11 | Comparative example 4 | Comparative example 5 | Comparative example 6 | |||
Exothermic peak temperature | Before the washing | ??37℃ | ??35℃ | ????33℃ | ??34℃ | ??38℃ | |
After the washing | ??37℃ | ??35℃ | ????33℃ | ??34℃ | ??34℃ | ||
Programming rate (℃/minute) | ??15 | ??9 | ????3 | ??6 | ??18 | ||
Antibiotic property (bacteriostatic activity value) | ??3.1 | ??2.7 | ????0.3 | ??1.2 | ??3.0 | ||
Deodorization (before the washing) | Ammonia | ??94% | ??92% | ????10% | ??65% | ??83% | |
Acetic acid | ??93% | ??92% | ????2% | ??68% | ??84% | ||
Isovaleric acid | ??97% | ??90% | ????3% | ??70% | ??89% | ||
Deodorization (washing back) | Ammonia | ??94% | ??92% | ????10% | ??65% | ??83% | |
Acetic acid | ??92% | ??90% | ????2% | ??68% | ??84% | ||
Isovaleric acid | ??90% | ??88% | ????3% | ??70% | ??89% | ||
Frictional static voltage (V) | ??900 | ??1270 | ????5900 | ??3320 | ??880 | ||
Half-life (second) | ??11.8 | ??20.3 | ????171.8 | ??130.8 | ??16.8 |
Embodiment 12,13 and comparative example 7 main records relate to embodiment and the comparative example that contains a large amount of long stapled fabrics.
(embodiment 12)
Making 200 parts of molecular weight under 80 ℃ is 1800 poly tetramethylene oxide two pure and mild 45 parts of methylenes-two (4-phenyl isocyanate) reaction 3 hours, obtains two and terminally is the intermediate polymer of isocyanate group.After intermediate polymer is cooled to 40 ℃, adds 375 parts of N,N-dimethylacetamide and be cooled to 10 ℃.Be ready to 4.0 parts of ethylenediamines, 0.4 part of diethylamine are dissolved in 147.6 parts of N, the diethylamine solution of N-dimethylacetylamide, once add this diethylamine solution in the intermediate polymer solution of high-speed stirred, obtaining solution concentration is the polyether polyols with reduced unsaturation solution of 32.2 weight %, viscosity 2500 pools (30 ℃).
In the polyether polyols with reduced unsaturation solution that obtains thus, add and mix 4 weight % n-butylamine/N, polymer, benzotriazole compound and the hindered phenol compound of N-dimethylhydrazine endcapped.
In the autoclave of 21 capacity, pack into 490 parts by weight of acrylonitrile, 16 weight portion sodium p styrene sulfonates and 1181 weight parts waters, it is airtight behind the polymerization initiator di-tert-butyl peroxide of 0.5 weight % adding with respect to the monomer total amount again, then stir and 150 ℃ temperature under polymerization 23 minutes.After reaction finishes, be cooled to about 90 ℃, obtain the aqueous dispersion that average grain diameter is the feed particles of 0.2 μ m while continue to stir.
Concentration reached 35 weight % during the adding hydrazine made and bathes in the aqueous dispersion of feed particles, carried out 2.5 hours crosslinking Treatment under 102 ℃.
Then add NaOH make to bathe in concentration reach 10 weight %, after carrying out 5 hours hydrolysis process under 102 ℃, put into fibre pipe, in 1 week of dialysis desalting under flowing water, obtain the aqueous dispersion of object moisture absorption heat release particulate.The particulate that obtains 105 ℃ of following dryings.
The salt type carboxyl concentration of the particulate that obtains thus is 4.5mmol/g, and average grain diameter is 0.5 μ m.And be that swelling capacity is 80% high moisture absorption particulate.
Adding the polyether polyols with reduced unsaturation solution that mixes with respect to above-mentioned gained is the particulate that obtains in above-mentioned operation of 13 weight %, makes spinning solution.
After this spinning solution deaeration, from being the spinning head of 0.5mm, the aperture spues, in having flowed into 235 ℃ the spinning tube that adds hot-air, push, add the finish of 5%OWF and reel with 550m/ minute speed.The strand that obtains 40 ℃ of following heat treated 72 hours, is obtained supplying with the 44dtex of back processing, the polyurethane elastomeric fiber of 4 long filaments.
On one side,, make the elasticity cladded yarn on one side with 1 grade of false twist yarn 84dtex of 800T/m coiling polyester, 36 long filaments with 3 times of the elastic yarn drawing-offs that obtain.The rate of using with of elastic polyurethane silk is 13.7 weight %.
As density configuration spontaneous elongation mixed filament 55dtex, 36 long filaments of warp thread with 286/2.54cm, is the composite elastic silk that in unit alternate configurations operation (c) obtain and 1 grade false twist yarn of polyester filament with the density of 100/2.54cm with 1 as weft yarn, obtains the fabric through the face satin weave.
Use the lax collator of becate with this fabric after lax 90 seconds under 130 ℃ of dry heat conditions, use liquid-flow dyeing machine to carry out the destarch refining processing, use stenter 195 ℃ of 30 seconds of setting down.Handled this cloth 45 minutes, decrement 12% by the sodium hydrate aqueous solution that uses 30g/L down at 95 ℃.Then dyeed 50 minutes down at 120 ℃ with the white dyestuff of fluorescence.
The fabric that obtains be rich in whiteness, have rich tool retractility on soft sense of touch, the transverse direction, the restorative fabric that feeling of high class is arranged.Owing to these reasons, this fabric is applicable to jacket.
(embodiment 13)
The 78dtex elastic polyurethane filament drafting that will obtain according to method similarly to Example 12 is 3.3 times on one side, with retwist twisting count covering polyester false twist yarn 165dtex, 48 long filaments of 800T/m also reel on one side, obtain the elasticity cladded yarn.
As the regular polyester false twist yarn of 116/2.54cm of warp thread configuration and mixed filament 165dtex, 48 long filaments of cation dyeable polyester processing silk,, obtain the fabric of 3/1 twill-weave as this elasticity cladded yarn of 55/2.54cm of weft yarn configuration.
Carry out concise, preboarding, dispersion dyeing, finalization by conventional method, obtain fabric.The cloth that obtains is at the cloth that can stretch on broadwise with pattern accent outward appearance.
(comparative example 7)
Except not containing particulate, obtain the fabric of twill-weave according to method similarly to Example 13.
The measurement result of fabric face ascending temperature is as shown in table 4 below when the permanent load elongation of the fabric that obtains by embodiment 12,13 and comparative example 7, permanent load elongation recovery rate, moisture absorption.
Table 4
Permanent load elongation | Permanent load elongation recovery rate | Cloth surface ascending temperature | |
Embodiment 12 | ????35% | ????85% | ????3℃ |
Embodiment 13 | ????25% | ????92% | ????1.5℃ |
Comparative example 7 | ????25% | ????95% | ????0.5℃ |
The fabric that use is obtained by embodiment 12 is made the warm-up upper garment of the usefulness that plays tennis, and when wearing in the gymnasium winter, initial warm-up effect is remarkable.Do not have feeling of oppression and heat afterwards yet and can cosily warm up.Do not find because the dewfall that moisture causes in the clothes the inside, back of undressing in addition.
When the fabric that use is obtained by embodiment 13 is made slacks, can make the slacks of the usefulness that is suitable for playing golf.Feel warm morning when wearing these slacks and play golf early winter, also not sultry when the temperature rises in the afternoon, shown comfortable wearing feeling.
Use is made slacks by the fabric that comparative example 7 obtains.When wearing these slacks and play golf early winter, slight chill in the air when begin morning feels sultry when perspire daytime, promptly feel cold after having beaten soon.
By above result as can be seen, during 1 ℃ of fabric face ascending temperature less than, relatively poor when not containing particulate of the present invention and moisture absorption as the warm-up clothes comfortableness outside the room.
In contrast, permanent as can be seen load elongation more than 15%, permanent load elongation recovery rate at fabric face ascending temperature more than 35%, during moisture absorption at the fabric of the present invention more than 1 ℃, warm and also not sultry or dewfall can be made comfortable clothes when moving outside the room of cold.
Embodiment 14,15 and comparative example 8 main embodiment and the comparative examples that relate to the fabric that contains a large amount of staple fibres of recording and narrating.
(embodiment 14)
Making 200 parts of molecular weight under 80 ℃ is 1800 poly tetramethylene oxide two pure and mild 45 parts of methylenes-two (4-phenyl isocyanate) reaction 3 hours, obtains two and terminally is the intermediate polymer of isocyanate group.After intermediate polymer is cooled to 40 ℃, adds 375 parts of N,N-dimethylacetamide and be cooled to 10 ℃.Be ready to 4.0 parts of ethylenediamines, 0.4 part of diethylamine are dissolved in 147.6 parts of N, the diethylamine solution of N-dimethylacetylamide, once add this diethylamine solution in the intermediate polymer solution of high-speed stirred, obtaining solution concentration is the polyether polyols with reduced unsaturation solution of 32.2 weight %, viscosity 2500 pools (30 ℃).
In the polyether polyols with reduced unsaturation solution that obtains thus, add and mix 4 weight % n-butylamine/N, polymer, benzotriazole compound and the hindered phenol compound of N-dimethylhydrazine endcapped.
In the autoclave of 21 capacity, pack into 490 parts by weight of acrylonitrile, 16 weight portion sodium p styrene sulfonates and 1181 weight parts waters, it is airtight behind the polymerization initiator di-tert-butyl peroxide of 0.5 weight % adding with respect to the monomer total amount again, then stir and 150 ℃ temperature under polymerization 23 minutes.After reaction finishes, be cooled to about 90 ℃, obtain the aqueous dispersion that average grain diameter is the feed particles of 0.2 μ m while continue to stir.
Concentration reached 35 weight % during the adding hydrazine made and bathes in the aqueous dispersion of feed particles, carried out 2.5 hours crosslinking Treatment under 102 ℃.
Then add NaOH make to bathe in concentration reach 10 weight %, after carrying out 5 hours hydrolysis process under 102 ℃, put into fibre pipe, in 1 week of dialysis desalting under flowing water, obtain the aqueous dispersion of object moisture absorption heat release particulate.The particulate that obtains 105 ℃ of following dryings.
The salt type carboxyl concentration of the particulate that obtains thus is 4.5mmol/g, and average grain diameter is 0.5 μ m.And be that swelling capacity is 80% high moisture absorption particulate.
Add mixing with respect to the particulate that in above-mentioned operation, obtains that the above-mentioned polyether polyols with reduced unsaturation solution that obtains is 13 weight %, make spinning solution.
After this spinning solution deaeration, from being the spinning head of 0.5mm, the aperture spues, in having flowed into 235 ℃ the spinning tube that adds hot-air, push, add the finish of 5%OWF and reel with 550m/ minute speed.The strand that obtains 40 ℃ of following heat treated 72 hours, is obtained supplying with the 44dtex of back processing, the polyurethane elastomeric fiber of 4 long filaments.
Between preliminary roller and back roller, will be 48 times of the roving-draftings formed of the cotton fiber of 26mm by average fiber length, simultaneously with above-mentioned elastic polyurethane silk 44dtex, 3.5 times of 4 filament drawings and supply with preliminary roller, twist factor is made as 4.2 and reel on spinning cop, obtain the core-sheath-type composite spinning of 40 cotton numbers.The rate of using with of polyurethane elastomeric fiber is 8.6%.
As density configuration cotton yarn 40 numbers of warp thread,, obtain the fabric of plain weave as the composite spinning that obtains in the density configuration (c) of weft yarn with 70/2.54cm with 90/2.54cm.
Adopt common continuous treating operation, to this cloth singe, destarch, concise, bleaching, mercerising processing, on 170 ℃ of following widths, extend 3% again, classical prescription is upwards extended 5% and is formalized.Carry out mulberry width of cloth mechanical shrinkproof (sanforize) processing at last.Use 35% aqueous hydrogen peroxide solution (25g/L) under 95 ℃, to carry out during bleaching 40 minutes.
The fabric that obtains is rich tool whiteness, have rich tool retractility on soft sense of touch, the transverse direction, restorative and the fabric of feeling of high class arranged.
(embodiment 15)
Preliminary roller is supplied with on 3.3 times of one side of 78dtex elastic polyurethane filament drafting that will obtain according to method similarly to Example 14 on one side, and twist factor is made as 4.2 and reel on spinning cop, obtain the core-sheath-type composite spinning of 30 cotton numbers.The rate of using with of this elastomer is 12.0%.
With the density of 65/2.54cm configuration cotton yarn, 20 numbers, dispose above-mentioned composite spinning with the density of 60/2.54cm as warp thread, obtain the fabric of twill-weave as weft yarn.
Adopt common continuous treating operation, this cloth is carried out destarch, concise, bleaching, mercerising processing, extend 3% again on 170 ℃ of following widths, classical prescription is upwards extended 5% and is formalized.Carry out the processing of mulberry width of cloth mechanical shrinkproof at last.Use 35% aqueous hydrogen peroxide solution (25g/L) under 95 ℃, to carry out during bleaching 40 minutes.The fabric that obtains is rich tool whiteness, have rich tool retractility on soft sense of touch, the transverse direction, restorative and the fabric of feeling of high class arranged.
(comparative example 8)
Except not containing particulate, make the fabric of plain weave, carry out refinement treatment according to method similarly to Example 14 according to the method identical with embodiment 14.
The measurement result of fabric face ascending temperature and the filoplume density more than the fabric face length 1mm is as shown in table 5 below when the permanent load elongation of the fabric that obtains by embodiment 14,15 and comparative example 8, permanent load elongation recovery rate, moisture absorption.
Table 5
Permanent load elongation | Permanent load elongation recovery rate | Cloth surface ascending temperature | Cloth surface hairiness density | |
Embodiment 14 | ????25% | ????45% | ????1℃ | 12/cm 2 |
Embodiment 15 | ????18% | ????48% | ????0.7℃ | 43/cm 2 |
Comparative example 8 | ????18% | ????49% | ????0.0℃ | 16/cm 2 |
When using the fabric that obtains by embodiment 14 to make dress shirt, the shirt of can obtain being rich in gloss, retractility is good and dress is felt good.
When using the fabric that obtains by embodiment 15 to make white frock, nurse's clothes of can obtain being rich in gloss, retractility is good and dress is felt good.
At this fabric, when estimating anti-microbial property according to the SEK uniform tests method of fibre health processing association regulation with the bacteriostatic activity value, anti-microbial property is 1.8.In addition, confirm that according to the method described above the result of deodoriging properties is, every 1g fabric sample for the deodorizing rate of foul gas 3L is, ammonia is 68%, and acetic acid is 72%.
When using the fabric that is obtained by comparative example 8 to make dress shirt, wearing feeling is comfortable usually, but has felt slight chill in the air after going out hidrosis during inertia.
The clothes that use the fabric of embodiment 14,15 to make in addition can be felt soft sense of touch and warm sense, and can obtain feeling naturally of outward appearance.
Industrial utilizability
According to the present invention, can provide the elastomer that to make unfertile land light weight, heat insulating ability height and have the retractility cloth of comfortableness, aesthetic feeling.In addition, can provide back processing trafficability characteristic steam good, that perspiration produces when having excellent heat resistance and motion evaporation and not sultry elastic garment from skin fast.
Relate in the invention of knitted fabric, can provide hygroscopicity not only good and also have the heat release heating effect at the moisture absorption initial stage, promoted warm-up effect, perspire can not occur after stopping since the rich tool comfortableness of the sense of being clamminess that chilling causes be most suited to knitted fabric in the warm-up clothes, this knitted fabric also is simultaneously that the height that has both sanitation performance such as antibiotic property, deodorization, pH resiliency and antistatic property shrinks knitted fabric.
In the invention that relates to stocking, can provide hygroscopicity good and have the heat release heating effect at the moisture absorption initial stage, can not occur after stopping to perspire because the sense and be rich in the also good stocking of washing resistance of comfortableness of being clamminess that chilling causes, the stocking of sanitation performances such as also having both antibiotic, deodoriging properties, pH shock-absorbing capacity and antistatic property can be provided in addition.
In the invention of fabric, can provide having heat effect time easily motion clothes and be applicable to wherein Woven stretch fabric.Also have antibacterial action, deodorization, pH cushioning effect, antistatic property in addition.Fabric has the character of moisture absorption heat release, has the character that moisture is seen through simultaneously.This fabric is compared with COTTON FABRIC or wool fabric, slow, the moisture absorption level height of the wet speed of suction, and the result can prevent be clamminess sense and the dewfall in the clothes, can stably continue heat release for a long time simultaneously.
Of the present inventionly mainly contain a large amount of long stapled fabrics and be suitable as sportswear, winter raw material with underwear etc.
On the other hand, with regard to the fabric that mainly contains a large amount of staple fibres, except character,, can obtain the warm sense that exists filoplume to bring owing to the surface, its soft-touch and have the outward appearance of nature because of also containing staple fibre outside the elastic yarn with above-mentioned fabrics.The fabric that the present invention contains a large amount of staple fibres has both these character, therefore is suitable as the raw material of Work Clothes, office uniform, health clothes, the clothes of Work Clothes style, general underpants etc.
Claims (45)
1. an elastomer is characterized in that, the maximum temperature ascending amount when moisture absorption and/or suction is more than 2 ℃.
2. the elastomer described in claim 1 is characterized in that, the hydroscopicity under 20 ℃ * 65%RH is more than 0.5%, and the hydroscopicity under the 20 ℃ * 95%RH is more than 1.5%.
3. the elastomer described in claim 1 is characterized in that, satisfies following formula (1) and (2),
PSD(%)≥60%………………………………………(1)
PSW(%)≤75%………………………………………(2)
Wherein, PSD is illustrated under elongation 100% and the xeothermic condition 190 ℃ of dry heat-setting rates after handling 1 minute, PSW be illustrated under elongation 100% and the damp and hot condition with 60 minutes from 40 ℃ be warming up to after 130 ℃ continuously under the wet heat condition in the wet heat setting rate of 130 ℃ of processing after 60 minutes.
4. the elastomer described in claim 1 is characterized in that, contains the moist particulate of high suction of organic class and/or mineral-type.
5. the elastomer described in claim 1, it is characterized in that, the moist particulate of high suction that contains organic class and/or mineral-type, and the average grain diameter of the moist particulate of this high suction is below 20 μ m, swelling capacity is below 200%, and the regain under the 20 ℃ * 65%RH contains the moist particulate of this high suction of 0.2~50 weight % more than 30% with respect to fibre weight.
6. the elastomer described in claim 1, it is characterized in that, the moist particulate of high suction that contains organic class and/or mineral-type, at least a kind is particulate as described below in the moist particulate of this high suction, promptly, on the vinyl cyanide polymer that contains the above acrylonitrile of 50 weight %, handle the importing cross-linked structure by hydrazine, divinylbenzene or triallyl isocyanuric acid ester, be residual itrile group chemical conversion salt type carboxyl by hydrolysis again, and contain the moist organic fine particles of high suction of the above salt type of 1.0mmol/g carboxyl.
7. a braided fabric is characterized in that, has used the elastomer described in the claim 1 to small part.
8. high scalability knitted fabric, be the high scalability knitted fabric that constitutes by elastomer and non-elastic fiber, it is characterized in that permanent load elongation is more than 50%, permanent load elongation recovery rate is more than 50%, and the surface temperature ascending amount of knitted fabric is more than 3 ℃ during moisture absorption.
9. the high scalability knitted fabric described in claim 8 is characterized in that, elastomer is the elastomer described in the claim 1.
10. the high scalability knitted fabric described in claim 8 is characterized in that, elastomer is the elastomer described in the claim 4.
11. the manufacture method of a high scalability knitted fabric is characterized in that, with the drawing-off limit, elastomer limit described in the claim 1 and synthetic thread compound after, with this compound silk separately or reinstate circular knitter with other long filaments one and interweave.
12. the manufacture method of a high scalability knitted fabric is characterized in that, the naked silk of the elastomer described in the claim 1 is used in the back sley bar, and synthetic thread is used in the most preceding sley bar, adopts warp knitting machine to weave.
13. flexible knitted fabrics, it is characterized in that, it is the knitted fabric that contains the flexible knitted fabrics that is made of non-elastic fiber and elastic yarn to small part, be to show that when moisture absorption programming rate shows the knitted fabric of heat-absorbing action when being heating effect more than 5 ℃/minute and hydrofuge, before the washing of this knitted fabric and the difference of the moisture absorption exothermic temperature after the washing 10 times less than 1 ℃.
14. the flexible knitted fabrics described in claim 13 is characterized in that, elastic yarn is made of the elastomer described in the claim 1.
15. the flexible knitted fabrics described in claim 13 is characterized in that, elastic yarn is made of the elastomer described in the claim 4.
16. the flexible knitted fabrics described in claim 13 is characterized in that, non-elastic fiber is the fiber more than a kind that is selected from polyester fiber, polyamide-based fiber, the cellulosic fibre.
17. the flexible knitted fabrics described in claim 13 is characterized in that, has antibiotic, deodoriging properties.
18. the flexible knitted fabrics described in claim 13 is characterized in that, elastic yarn is naked silk or its composite elastic silk of polyurethane.
19. a underwear is characterized in that, requires the flexible knitted fabrics described in 13 to small part right to use profit.
20. a stocking is characterized in that, it is the stocking that contains elastic yarn and synthetic fibres to small part, shows the heating effect more than 7 ℃/minute during moisture absorption, shows heat-absorbing action during hydrofuge, before the washing and the moisture absorption exothermic temperature difference after the washing 10 times less than 1 ℃.
21. the stocking described in claim 20 is characterized in that, elastic yarn is made of the elastomer described in the claim 1.
22. the stocking described in claim 20 is characterized in that, elastic yarn is made of the elastomer described in the claim 4.
23. the stocking described in claim 20 is characterized in that, has antibiotic, deodoriging properties.
24. the stocking described in claim 20 is characterized in that, the deodorizing rate of ammonia is more than 70%.
25. the stocking described in claim 20 is characterized in that, the deodorizing rate of acetic acid is more than 70%.
26. the stocking described in claim 20 is characterized in that, the deodorizing rate of isovaleric acid is more than 70%.
27. the stocking described in claim 20 is characterized in that, with respect to being selected from ammonia, acetic acid, the isovaleric acid a kind or multiple, before the washing and the deodorizing rate after the washing all more than 70%.
28. the stocking described in claim 20 is characterized in that, frictional static voltage is below 2500V.
29. the stocking described in claim 20 is characterized in that, the half-life in the half-life mensuration of JIS-L-1094 antistatic behaviour is below 50 seconds.
30. the stocking described in claim 20, it is characterized in that, the positive and negative that constitutes the knitted fabric of stocking mainly is synthesized fiber and covers, there is not the moist particulate of high suction on this synthetic fiber surface in fact, the elastic yarn that constitutes stocking contains the moist particulate of high suction of 0.2~50 weight %, and this elastic yarn is extremely constituted more than the 20 weight % of knitted fabric by compound.
31. a fabric is the fabric that contains the compound silk of non-elastic fiber and elastomer, it is characterized in that, permanent load elongation is more than 15%, and permanent load elongation recovery rate is more than 35%, and the fabric face ascending temperature is more than 1 ℃ during moisture absorption.
32. the fabric described in claim 31 is characterized in that, elastomer is the elastomer described in the claim 1.
33. the fabric described in claim 31 is characterized in that, elastomer is the elastomer described in the claim 4.
34. the fabric described in claim 31, the non-elastic fiber and/or the fiber beyond the compound silk that wherein constitute the compound silk of fabric are the silks that is made of polyesters long filament and/or polyamide-based long filament.
35. the fabric described in claim 31, the non-elastic fiber and/or the compound silk fiber in addition that wherein constitute the compound silk of fabric are bulky yarns.
36. the fabric described in claim 31, the non-elastic fiber and/or the compound silk fiber in addition that wherein constitute the compound silk of fabric are potential filament length difference mixed filaments.
37. contain the clothes of the fabric described in the claim 31 to small part.
38. the clothes described in claim 37 is characterized in that, is any in sportswear, underwear, general clothes, winter protection lining or the winter liner.
39. a fabric is the fabric that contains the compound silk of non-elastic fiber and elastomer, permanent load elongation is more than 15%, and permanent load elongation recovery rate is more than 35%, and the fabric face ascending temperature is more than 0.5 ℃ during moisture absorption, on the cloth surface with 10/cm
2Above density contains the filoplume of length more than 1mm.
40. the fabric described in claim 39 is characterized in that, elastomer is the elastomer described in the claim 1.
41. the fabric described in claim 39 is characterized in that, elastomer is the elastomer described in the claim 4.
42. the fabric described in claim 39 is characterized in that, constituting the non-elastic fiber of compound silk and/or the compound silk fiber in addition of formation fabric is the silk that contains staple fibre.
43. the fabric described in claim 39 is characterized in that, constituting the non-elastic fiber of compound silk and/or the compound silk fiber in addition of formation fabric is the silk that contains staple fibre, and the silk that contains this staple fibre is cotton yarn or silk/cotton blended yarn.
44. contain the clothes of the fabric described in the claim 39 to small part.
45. the clothes described in claim 44 is characterized in that, is any in the clothes of Work Clothes, office uniform, health clothes, Work Clothes style or the general underpants.