CN1644795A - Acrylic acid emulsion gloss, oil, its production and use - Google Patents
Acrylic acid emulsion gloss, oil, its production and use Download PDFInfo
- Publication number
- CN1644795A CN1644795A CN 200410052497 CN200410052497A CN1644795A CN 1644795 A CN1644795 A CN 1644795A CN 200410052497 CN200410052497 CN 200410052497 CN 200410052497 A CN200410052497 A CN 200410052497A CN 1644795 A CN1644795 A CN 1644795A
- Authority
- CN
- China
- Prior art keywords
- water
- acrylic emulsion
- gloss oil
- emulsifying agent
- initator
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A polishing oil for the printed refractory thermoviscose PVC wall paper is prepared from the emulsion of modified styrene-acrylate polymer and pigments. Its advantages are high resistance to high temp (180-200 deg.C), high toughness, natural and soft lustre, and high durability.
Description
Technical field
The present invention relates to the fine chemicals field, specifically relate to a kind of heat sticky resistance and print PVC wallpaper acrylic emulsion gloss oil, the invention still further relates to the preparation method and the application on printing PVC wallpaper thereof of this gloss oil.
Background technology
The PVC plastic wall paper be a kind of be base material with paper, be surface layer with the polyvinyl chloride plastic film, through a kind of new decorative material compound, that seal closes, operations such as stamp, embossing are made.The PVC wallpaper is owing to have preferably anti-flammability and be used widely, but because it can discharge hydrogen chloride gas, infringement human body health, and for giving a large amount of plasticizer that the PVC film has certain flexibility to add, in use separate out easily, easily being clamminess in the surface, also dust suction is dirty, defectives such as ABRASION RESISTANCE reduction.For having overcome defective, making it range of application enlarges, the Lacquer finish sealing is carried out on the PVC top layer, suppress on the one hand effectively the release of hydrogen chloride gas and prevent that the micromolecule migration of plasticizer from separating out, on the other hand by gloss oil is added pigment and filler, and process such as adopting process processing embossing printing, play the wallpaper decoration beautification function.Require to print the PVC wallpaper and have following feature with gloss oil: 1, compliance with environmental protection requirements, organic solvent-free discharges, and content of formaldehyde does not exceed standard; 2, heat sticky resistance can be good, can be not hot sticky under 180 ~ 200 ℃; 3, PVC is had excellent adhesive force and permeability, the densification of filming can suppress separating out of interior micromolecule plasticizer of PVC plastics and hydrogen chloride gas; 4, coating gloss, richness height have excellent decoration and protective effect etc.
Marthe etc. (United States Patent (USP) 4772518) have synthesized the water soluble paint that can be used for the PVC surface layer, can effectively improve the shortcoming that the PVC surface layer exists, and improve its gloss, but because this system adopts the solution polymerization process preparation, organic solvent content is higher relatively, does not meet the environmental requirement of " zero " VOC of increasingly stringent; Xuzhou plastic molding and processing plant has also carried out top finishing research to the PVC surface layer, has studied water and milk PVC gloss oil.Though these acrylic emulsion types PVC finishing oil of being studied at present is a water-based system, VOC content is lower, basic compliance with environmental protection requirements, but easily " hot sticky cold crisp ", can not satisfy the not hot sticky requirement of embossing under 180 ~ 200 ℃ of conditions, and the wetting adhesive property to pigment, pearl essence is not good, is unsuitable for the inline process operation of industrial printing wallpaper.Develop a kind of heat sticky resistance and print the PVC wallpaper, both satisfied heat sticky resistance and the PVC ground is had requirements such as excellent adhesive attraction, reduce organic solvent and hydrogen chloride gas again, avoid infringement human body with high-performance acrylic acid emulsion gloss oil.
Summary of the invention
One object of the present invention is to exist at existing acrylic resin the shortcoming of hot sticky cold crisp, and a kind of acrylic emulsion gloss oil of heat sticky resistance is provided.
Another object of the present invention is to provide the preparation method of this emulsion gloss oil.
A further object of the invention provides this emulsion gloss oil in the application of printing on the PVC wallpaper.
For achieving the above object, the present invention has taked following technical scheme:
A kind of acrylic emulsion gloss oil, form by the material of following percentage by weight:
Acrylic emulsion 40～65
Coalescents 4～10
Thickener 1～3
Pearl essence 0～12
Mill base 0.3～0.5
Dispersant 0.5～0.8
Defoamer 0.1～0.4
Volatility conditioning agent 8～15
Deionized water 10～20;
Described coalescents is ethylene glycol ethyl ether, butyl glycol ether, N-Methyl pyrrolidone, 2,2,4-TMPD mono isobutyrate, diethylene glycol ether, the diethylene glycol butyl ether, dipropylene glycol ether, the mixture of one or more in the dipropylene glycol butyl ether; Described thickener is nonionic polyurethane thickener, anionic property acrylic acid thickener or its mixture; Described dispersant is polyacrylic acid sodium salt DP-512, ammonium polyacrylate salt DP-518, straight chain non-ionic surfactant DP-18 etc.; Described defoamer is non-silicone organosilane ester and hydrocarbon mixtures, polyether-modified polysiloxane solution stone Na base mineral oil and contain the mixture etc. of organosilyl hydrophobic components; Described volatility conditioning agent is: ethanol, butanols etc.;
Acrylic emulsion in the technique scheme is made up of the material of following percentage by weight:
Butyl acrylate 5～12
Methyl methacrylate 20～30
Styrene 3～8
Methacrylic acid 0.5～2
Contain amido vinyl unsaturated monomer 0～4
Hydroxyl unsaturated vinyl monomer 0～4
Emulsifying agent 1.5～3
Initator 0.2～1
Sodium bicarbonate 0.1～0.5
Ammoniacal liquor 0～0.4
Water 35～55
Wherein, forming the amido vinyl unsaturated monomer that contains described in the acrylic emulsion is acrylamide, N hydroxymethyl acrylamide or its mixture; Described initator is azodiisobutyronitrile, benzoyl peroxide, ammonium persulfate or potassium peroxydisulfate; Described emulsifying agent is by anionic emulsifier and cationic emulsifier is composite forms, anionic emulsifier is one or more the mixture in neopelex, lauryl sodium sulfate, disodium 4-dodecyl-2,4 '-oxydibenzenesulfonate, the ethoxy alcohol disodium sulfosuccinate, non-ionic emulsifier is Nonyl pheno (10～a 40) ether, octyl phenol polyoxy ethene (10～40) ether or its mixture, the composite ratio of anionic emulsifier and cationic emulsifier weight is 2: 1～1: 2.
The preparation method of described heat sticky resistance acrylic emulsion is characterized in that may further comprise the steps:
The preparation method of acrylic emulsion gloss oil may further comprise the steps:
(1) preparation of acrylic emulsion;
(a) in the four-hole boiling flask of loading onto agitator, thermometer and condensed water by the acrylic emulsion prescription add the water, the sodium bicarbonate that account for water gross weight 40～60%, the compound emulsifying agent that accounts for emulsifying agent gross weight 5～50% is as still liquid, is warming up to 70～85 ℃ with water-bath in the time of stirring;
(b) take by weighing 5～30% the acrylic monomers that accounts for total monomer weight and account for the emulsifying agent of emulsifying agent gross weight 5～30% and account for the water of water gross weight 2～5%, carry out pre-emulsification;
(c) take by weighing 70～95% the acrylic monomers that accounts for total monomer weight and account for 30～65% emulsifying agent of emulsifying agent gross weight and account for the water of water gross weight 20～30%, pre-emulsification 20～30min;
(d) still liquid refluxes stablely in the question response still, after adding the initator that accounts for initator total amount 30～50% and accounting for the mixed solution of water of water gross mass 2～5%, begins to add the pre-emulsion that step (b) is prepared, and is incubated then to blue streak to occur in 70～85 ℃;
(e) drip step (c) pre-emulsion and initator that accounts for initator total amount 50～70% and the water that accounts for water gross mass 10～20%, the dropping time is at 0.5h～3h;
(f) behind the insulation 1h, be warming up to 85 ℃～90 ℃ and be incubated 1h again; Be cooled to below 45 ℃, ammoniacal liquor is regulated about pH value to 7, and discharging is filtered in further cooling.
(2) deionized water is pressed acrylic emulsion gloss oil formula ratio and added in the dispersion machine, add dispersant, pearl essence and the mill base of formula ratio successively, mix;
(3) acrylic emulsion that step (1) is made is inserted in the container by formula ratio, and low whipping speed is a high speed dispersion under 700～900rpm, presses formula ratio simultaneously and adds coalescents, volatility conditioning agent and the prepared component of step (2), disperses 15～20 minutes.
(4) turn down speed of agitator to the 200～300rpm of dispersion liquid in (3) step, add defoamer, thickener, the water of formula ratio, adjust to viscosity 50～300s (use is coated with 4 glasss of measurements), the packing discharging.
The acrylic emulsion gloss oil that said method makes can be used for the printing of PVC wallpaper and uses.
Compared with the prior art, the present invention has following beneficial effect:
1, high temperature resistant, not hot sticky under 180～200 ℃;
2, the color additive of Jia Ruing is gone through the years baptism even assumed appearance pool is bright and clean naturally, soft, and is also lasting in the same old way as newly;
3, select modified phenylethylene-acrylic polymer emulsion allotment for use, have very strong toughness, can resist frequent scouring easily and a bit can't harm;
4, through the macromolecule of special treatment PVC is had excellent adhesive force and permeability, can prevent the infiltration of PVC plasticizer and separating out of hydrogen chloride gas, make paint film strong stick to wallpaper, never come off;
5, coating gloss, richness height have excellent decoration and protective effect.
The specific embodiment
The present invention is further illustrated below in conjunction with specific embodiment.
Embodiment 1
The preparation 1 of heat sticky resistance acrylic emulsion
(1) in the four-hole boiling flask of loading onto agitator, thermometer and condensed water, adds entry 30g, sodium bicarbonate 0.1g, compound emulsifying agent 0.2g, in the time of stirring, be warming up to 75 ℃ as still liquid.
(2) take by weighing methyl methacrylate 10g, styrene 5g and respective amount emulsifying agent 1.0g thereof and water 3g, pre-emulsification, standby.
(3) take by weighing methyl methacrylate 15g, styrene 2g, butyl acrylate 12g contains amido vinyl unsaturated monomer 4g, hydroxyl vinyl insatiable hunger 3g, methacrylic acid 1g and monomer and emulsifying agent 1.8g and water 7g, pre-emulsification, standby.
(4) backflow of still liquid is stable in the question response still, adds initator 0.1g and H
2Behind the mixed solution of O2g, begin to add the part pre-emulsion that step 2 is prepared, be incubated to blue streak at 75 ℃ then and occur.
(5) drip step 3 pre-emulsion and initator 0.3g and water 8g simultaneously, this dropping time is at .5h～3h.
(6) dropwise, behind 75 ℃ of insulation 1h, be warming up to 85 ℃～90 ℃ and be incubated 1h again.Be cooled to below 45 ℃, ammoniacal liquor is regulated about pH value to 7, and discharging is filtered in further cooling.
Embodiment 2
The preparation 2 of heat sticky resistance acrylic emulsion
(1) in the four-hole boiling flask of loading onto agitator, thermometer and condensed water, adds entry 20g, sodium bicarbonate 0.3g, compound emulsifying agent 0.5g, in the time of stirring, be warming up to 75 ℃ as still liquid.
(2) take by weighing methyl methacrylate 4g, styrene 4g, butyl acrylate 2g and respective amount emulsifying agent 0.5g thereof and water 5g, pre-emulsification, standby.
(3) take by weighing methyl methacrylate 21g, styrene 4g, butyl acrylate 5g contains amido vinyl unsaturated monomer 3g, hydroxyl vinyl insatiable hunger 2g, methacrylic acid 2g and monomer and emulsifying agent 1.5g and water 15g, pre-emulsification, standby.
(4) backflow of still liquid is stable in the question response still, adds initator 0.2g and H
2Behind the mixed solution of O2g, begin to add the part pre-emulsion that step 2 is prepared, be incubated to blue streak at 75 ℃ then and occur.
(5) drip step 3 pre-emulsion and initator 0.3g and water 8g simultaneously, this dropping time is at .5h～3h.
(6) dropwise, behind 75 ℃ of insulation 1h, be warming up to 85 ℃～90 ℃ and be incubated 1h again.Be cooled to below 45 ℃, ammoniacal liquor is regulated about pH value to 7, and discharging is filtered in further cooling.
Embodiment 3
The preparation 3 of heat sticky resistance acrylic emulsion
(1) in the four-hole boiling flask of loading onto agitator, thermometer and condensed water, adds entry 25g, sodium bicarbonate 0.5g, compound emulsifying agent 0.8g, in the time of stirring, be warming up to 75 ℃ as still liquid.
(2) take by weighing methyl methacrylate 1g, styrene 3g and respective amount emulsifying agent 0.2g thereof and water 5g, pre-emulsification, standby.
(3) take by weighing methyl methacrylate 26g, styrene 2g, butyl acrylate 5g contains amido vinyl unsaturated monomer 2g, hydroxyl vinyl insatiable hunger 1g, methacrylic acid 2g and monomer and emulsifying agent 0.6g and water 15g, pre-emulsification, standby.
(4) backflow of still liquid is stable in the question response still, adds initator 0.4g and H
2Behind the mixed solution of O2g, begin to add the part pre-emulsion that step 2 is prepared, be incubated to blue streak at 75 ℃ then and occur.
(5) drip step 3 pre-emulsion and initator 0.6g and water 8g simultaneously, this dropping time is at .5h～3h.
(6) dropwise, behind 75 ℃ of insulation 1h, be warming up to 85 ℃～90 ℃ and be incubated 1h again.Be cooled to below 45 ℃, ammoniacal liquor is regulated about pH value to 7, and discharging is filtered in further cooling.
Embodiment 4
The preparation 1 of gloss oil
(1) earlier deionized water 7g is put into high speed dispersor, under high-speed condition, add dispersant 0.7g, pearl essence 15g, mill base 1.3g successively, mix, standby.
(2) will synthesize heat sticky resistance acrylic emulsion 45g inserts in the container, low whipping speed is high speed dispersion under 700～900rpm condition, add coalescents 3.5g, volatility conditioning agent 10g simultaneously,, water 8g and the prepared component of (1) step, fully disperseed then 15～20 minutes.
(3) turn down speed of agitator to the 200～300rpm of dispersion liquid in (2) step, add defoamer, thickener, water, adjust to suitable viscosity, the packing discharging.
Embodiment 5
The preparation 2 of gloss oil
(1) will synthesize heat sticky resistance acrylic emulsion 50g inserts in the container, low whipping speed is high speed dispersion under 700～900rpm condition, add coalescents 3g, volatility conditioning agent 8g simultaneously,, water 26g, dispersant 0.8g, fully disperseed then 15～20 minutes.
(2), in the component that dispersant 0.2g adding step (1) is prepared, mix with aqueous color paste 2g.
(3) turn down speed of agitator to the 200～300rpm of dispersion liquid in (2) step, add defoamer, thickener, water, adjust to suitable viscosity, the packing discharging.
Embodiment 6
The commodity that heat sticky resistance acrylic emulsion gloss oil that embodiment 4 and 5 is made and existing market are sold print that the PVC wallpaper carries out performance with the acrylic emulsion gloss oil and the PVC wallpaper is printed the experiment comparison, the result is: 1, gained heat sticky resistance acrylic emulsion gloss oil of the present invention is high temperature resistant, and is not hot sticky under 180～200 ℃; 2, the film forming agent consumption of this gloss oil is low, does not contain formaldehyde, compliance with environmental protection requirements.3, PVC is had excellent wettability, adhesive force and permeability, can prevent the infiltration of PVC plasticizer and separating out of hydrogen chloride gas, make paint film strong stick to wallpaper, never come off.4, have very strong toughness, can resist frequent scouring easily and a bit can't harm.5, coating gloss, richness height have excellent decoration and protective effect.
Claims (9)
1, acrylic emulsion gloss oil is characterized in that being made up of the material of following percentage by weight:
Acrylic emulsion 40～65
Coalescents 6～10
Thickener 1～3
Pearl essence 0～12
Mill base 0.3～0.5
Dispersant 0.5～0.8
Defoamer 0.1～0.4
Volatility conditioning agent 8～15
Deionized water 10～20.
2, acrylic emulsion gloss oil according to claim 1, it is characterized in that described coalescents is ethylene glycol ethyl ether, butyl glycol ether, N-Methyl pyrrolidone, 2,2, the mixture of one or more in 4-TMPD mono isobutyrate, diethylene glycol ether, diethylene glycol butyl ether, dipropylene glycol ether, the dipropylene glycol butyl ether.
3, acrylic emulsion gloss oil according to claim 1 is characterized in that described thickener is nonionic polyurethane thickener, anionic property acrylic acid thickener or both mixtures.
4, acrylic emulsion gloss oil according to claim 1 is characterized in that described dispersant is polyacrylic acid sodium salt DP-512, ammonium polyacrylate salt DP-518 or straight chain non-ionic surfactant DP-18.
5, acrylic emulsion gloss oil according to claim 1 is characterized in that described defoamer is non-silicone organosilane ester and hydrocarbon mixtures, polyether-modified polysiloxane solution paraffin wax base mineral oil or the mixture that contains organosilyl hydrophobic components.
6, acrylic emulsion gloss oil according to claim 1 is characterized in that described volatility conditioning agent is ethanol or butanols.
7, acrylic emulsion gloss oil according to claim 1 is characterized in that described acrylic emulsion is made up of the material of following percentage by weight:
Butyl acrylate 5～12
Methyl methacrylate 20～30
Styrene 3～8
Methacrylic acid 0.5～2
Contain amido vinyl unsaturated monomer 0～4
Hydroxyl unsaturated vinyl monomer 0～4
Emulsifying agent 1.5～3
Initator 0.2～1
Sodium bicarbonate 0.1～0.5
Ammoniacal liquor 0～0.4
Water 35～55
Wherein, forming the amido vinyl unsaturated monomer that contains described in the acrylic emulsion is acrylamide, N hydroxymethyl acrylamide or its mixture; Described initator is azodiisobutyronitrile, benzoyl peroxide, ammonium persulfate or potassium peroxydisulfate; Described emulsifying agent is by anionic emulsifier and cationic emulsifier is composite forms, anionic emulsifier is one or more the mixture in neopelex, lauryl sodium sulfate, disodium 4-dodecyl-2,4 '-oxydibenzenesulfonate, the ethoxy alcohol disodium sulfosuccinate, non-ionic emulsifier is Nonyl pheno (10～a 40) ether, octyl phenol polyoxy ethene (10～40) ether or its mixture, the composite ratio of anionic emulsifier and cationic emulsifier weight is 2: 1～1: 2.
8, the method for preparing the described acrylic emulsion gloss oil of claim 1 is characterized in that comprising the steps:
(1) preparation of acrylic emulsion;
(a) in the four-hole boiling flask of loading onto agitator, thermometer and condensed water by the acrylic emulsion prescription add the water, the sodium bicarbonate that account for water gross weight 40～60%, the compound emulsifying agent that accounts for emulsifying agent gross weight 5～50% is as still liquid, is warming up to 70～85 ℃ with water-bath in the time of stirring;
(b) take by weighing 5～30% the acrylic monomers that accounts for total monomer weight and account for the emulsifying agent of emulsifying agent gross weight 5～30% and account for the water of water gross weight 2～5%, carry out pre-emulsification;
(c) take by weighing 70～95% the acrylic monomers that accounts for total monomer weight and account for 30～65% emulsifying agent of emulsifying agent gross weight and account for the water of water gross weight 20～30%, pre-emulsification 20min～30min;
(d) still liquid refluxes stablely in the question response still, after adding the initator that accounts for initator total amount 30～50% and accounting for the mixed solution of water of water gross mass 2～5%, begins to add the pre-emulsion that step (b) is prepared, and is incubated then to blue streak to occur in 70～85 ℃;
(e) drip step (c) pre-emulsion and initator that accounts for initator total amount 50～70% and the water that accounts for water gross mass 10～20%, the dropping time is at 0.5h～3h;
(f) behind the insulation 1h, be warming up to 85 ℃～90 ℃ and be incubated 1h again; Be cooled to below 45 ℃, ammoniacal liquor is regulated about pH value to 7, and discharging is filtered in further cooling;
(2) deionized water is pressed acrylic emulsion gloss oil formula ratio and added in the dispersion machine, add dispersant, pearl essence and the mill base of formula ratio successively, mix;
(3) acrylic emulsion that step (1) is made is inserted in the container by formula ratio, and low whipping speed is a high speed dispersion under 700～900rpm, presses formula ratio simultaneously and adds coalescents, volatility conditioning agent and the prepared component of step (2), disperses 15～20 minutes;
(4) turn down speed of agitator to the 200～300rpm of dispersion liquid in (3) step, add defoamer, thickener, the water of formula ratio, adjust to viscosity 50～300s, the packing discharging.
9, the application of the described acrylic emulsion gloss oil of claim 1 on printing PVC wallpaper, the especially application on 180～200 ℃ high temperature printing PVC wallpaper.