CN1629235A - Formulation for vehicle paint - Google Patents
Formulation for vehicle paint Download PDFInfo
- Publication number
- CN1629235A CN1629235A CN 200310109519 CN200310109519A CN1629235A CN 1629235 A CN1629235 A CN 1629235A CN 200310109519 CN200310109519 CN 200310109519 CN 200310109519 A CN200310109519 A CN 200310109519A CN 1629235 A CN1629235 A CN 1629235A
- Authority
- CN
- China
- Prior art keywords
- vibrin
- vehicle paint
- byk
- paint
- require
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a formulation for vehicle paint, which comprises resin, anti sagging resin, pigment powder, adjuvant, and solvent. The prepared paint can meet the ultraviolet ray artificial aging requirement of 1600 hours and vertical construction dried film thickness of over 40 um.
Description
One. technical field:
The prescription of a kind of vehicle paint of the present invention relates to the formulation for coating material technical field, particularly automobile packaged paint formula technique field.
Two. background technology:
Compare product on the existing market, the defective that exists is because the combination of the quality of the chemical structure of the matrix resin of vehicle paint and pigment and various compositions is not good enough, the accelerated aging test time of causing ultraviolet resistance xenon lamp temper(ing) instrument to carry out be lower than 1200 hours with vertical coating decoration after build less than 40 μ m.
Three. summary of the invention:
The prescription purpose of a kind of vehicle paint of the present invention is to overcome above-mentioned defective, improves the ultraviolet aging resistance performance of vehicle paint and has sag resistance when the vertical surface application simultaneously.It is characterized in that: the prescription of coating (calculating by weight 100%)
The sag prevention vibrin 8-12% that contains polyamide wax
Vibrin 24-36%
Aminoresin 28-32%
Pigment dyestuff 8-28%
Auxiliary agent 0-6%
Solvent 3-8%
Amount to 100%
Wherein, 91703 sag prevention vibrin can be the sag prevention vibrin of other Aksu companies;
1703 vibrin can be the cooperation vibrin of other Aksu companies;
2310 white TiO 2 pigment powder can be E.I.Du Pont Company's 706 titanium dioxides;
The above raw material is commercially available.
The obvious advantage of implementing after this technology is: can tolerate 1600 hours ultraviolet temper(ing) and require to have reached the international most advanced level of original-pack vehicle plain color lacquer with more than the build of vertical construction reaches 40 μ m, economic results in society are obvious.
Four. embodiment:
Below produce the vehicle paint of 100 kilograms prescription, the present invention is further described;
Embodiment 1
1) white paint prescription
The name % that weighs
91703 sag prevention vibrin 10
4815 vibrin 12
1703 vibrin 14
683 aminoresin 16
2310 white TiO 2 pigment powder 28
4920 iron oxide yellow powder 0.12
The goth black powder 0.02 of M-100
BYK-310 auxiliary agent 0.1
BYKP-104 auxiliary agent 0.9
BYK-161 auxiliary agent 3.4
433 auxiliary agents 0.25
CAC 7.51
DAA 2.3
Butyl glycol ether 2.3
N-BUTYL ACETATE 1.5
#100 solvent 0.8
Butanols 0.8
2) its technology is:
CAC and BYK-161, BYK-PIO4 were stirred 30 minutes with 400 rev/mins with the 3F-22 high speed dispersor in container, then, add titanium dioxide, iron oxide yellow, goth black pigment, stirred 30 minutes, add 4815 resins again, be ground to fineness on the SK-50 sand mill and meet≤after 10 μ m require;
The above-mentioned white slurry that makes is poured in the paint still, add 91703 resins, 1703 resins, 683 resins, BYK-310,433, DAA, butyl glycol ether, N-BUTYL ACETATE, #100 solvent and butanols, stirred 2 hours, through after the assay was approved, check, discharging, boiler, filtration, packing.
Embodiment 2
1) blue colored paint prescription
The name % that weighs
91703 sag prevention vibrin 10
4815 vibrin 7.54
1703 vibrin 29.71
683 aminoresin 18
2310 white TiO 2 pigment powder 13.5
BS4303 phthalocyanine blue 1.36
Permanent violet 0.03
The goth black powder 0.1 of M-100
BYK-310 auxiliary agent 0.1
BYKP-104 auxiliary agent 0.9
BYK-161 auxiliary agent 3.4
433 auxiliary agents 0.25
CAC 7.51
DAA 2.3
Butyl glycol ether 2.3
N-BUTYL ACETATE 1.5
#100 solvent 0.8
Butanols 0.8
2) its technology is:
CAC and BYK-161, BYK-PIO4 were stirred 30 minutes with 400 rev/mins with the 3F-22 high speed dispersor in container, then, add titanium dioxide, phthalocyanine blue and violet pigment, stirred 30 minutes, add 4815 resins again, be ground to fineness on the SK-50 sand mill and meet≤after 10 μ m require;
The above-mentioned white slurry that makes is poured in the paint still, add 91703 resins, 1703 resins, 683 resins, BYK-310,433, DAA, butyl glycol ether, N-BUTYL ACETATE, #100 solvent and butanols, stirred 2 hours, through after the assay was approved, check, discharging, boiler, filtration, packing.
Embodiment 3
1) red paint prescription
The name % that weighs
91703 sag prevention vibrin 10
4815 vibrin 13
1703 vibrin 27
683 aminoresin 18.84
DPP-TR rouge and powder 1.8
AAH-3-SQ molybdenum red powder 9.5
BYK-310 auxiliary agent 0.1
BYKP-104 auxiliary agent 0.9
BYK-161 auxiliary agent 3.4
433 auxiliary agents 0.25
CAC 7.51
DAA 2.3
Butyl glycol ether 2.3
N-BUTYL ACETATE 1.5
#100 solvent 0.8
Butanols 0.8
2) its technology is:
CAC and BYK-161, BYK-PIO4 were stirred 30 minutes with 400 rev/mins with the 3F-22 high speed dispersor in container, then, add DPP-TR rouge and powder and AAH-3-SQ molybdenum red powder pigment, stirred 30 minutes, add 4815 resins again, be ground to fineness on the SK-50 sand mill and meet≤after 15 μ m require;
The above-mentioned white slurry that makes is poured in the paint still, add 91703 resins, 1703 resins, 683 resins, BYK-310,433, DAA, butyl glycol ether, N-BUTYL ACETATE, #100 solvent and butanols, stirred 2 hours, through after the assay was approved, check, discharging, boiler, filtration, packing.
Embodiment 4
1) black paint prescription
The name % that weighs
91703 sag prevention vibrin 10
4815 vibrin 13
1703 vibrin 27
683 aminoresin 18.84
#6-goth black 4.5
BYK-310 auxiliary agent 0.1
BYKP-104 auxiliary agent 0.9
BYK-161 auxiliary agent 3.4
433 auxiliary agents 0.25
CAC 14.31
DAA 2.3
Butyl glycol ether 2.3
N-BUTYL ACETATE 1.5
#100 solvent 0.8
Butanols 0.8
2) its technology is:
CAC and BYK-161, BYK-PIO4 were stirred 30 minutes with 400 rev/mins with the 3F-22 high speed dispersor in container, then, add the goth black pigment of #6-, stirred 30 minutes, add 4815 resins again, be ground to fineness on the SK-50 sand mill and meet≤after 15 μ m require;
The above-mentioned white slurry that makes is poured in the paint still, add 91703 resins, 1703 resins, 683 resins, BYK-310,433, DAA, butyl glycol ether, N-BUTYL ACETATE, #100 solvent and butanols, stirred 2 hours, through after the assay was approved, check, discharging, boiler, filtration, packing.
Claims (4)
1. the prescription of a kind of vehicle paint of the present invention, its feature exists: the formula technique of vehicle paint (calculating by 100% weight)
The sag prevention vibrin 8-12% that contains polyamide wax
Vibrin 24-36%
Aminoresin 28-32%
Pigment dyestuff 8-28%
Auxiliary agent 0-6%
Solvent 3-8%
Above raw material is the commercially available prod.
2. require 1 described a kind of vehicle paint prescription according to aforesaid right, it is characterized in that: 91703 sag prevention vibrin can be the sag prevention vibrin of other Aksu companies.
3. require 1 described a kind of vehicle paint prescription according to aforesaid right, it is characterized in that: 1703 vibrin can be the cooperation vibrin of other Aksu companies.
4. require 1 described a kind of vehicle paint prescription according to aforesaid right, it is characterized in that: 2310 white TiO 2 pigment powder can be E.I.Du Pont Company's 706 titanium dioxides.