CN1590605A - High strength viscose long filament spinning technology and equipment - Google Patents
High strength viscose long filament spinning technology and equipment Download PDFInfo
- Publication number
- CN1590605A CN1590605A CN 200410012725 CN200410012725A CN1590605A CN 1590605 A CN1590605 A CN 1590605A CN 200410012725 CN200410012725 CN 200410012725 CN 200410012725 A CN200410012725 A CN 200410012725A CN 1590605 A CN1590605 A CN 1590605A
- Authority
- CN
- China
- Prior art keywords
- spinning
- viscose
- strand
- equipment
- disc
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A technology for spinning high-strength viscose filament includes conveying viscose, metering, filtering, spinning by spinneret, coagulating in bath, drafting, solidifying in the another bath, water washing, applying oil, baking and winding. Its apparatus is also disclosed.
Description
One, technical field: the present invention relates to field of textiles, specifically the present invention relates to high-strength viscose continuous yarn spinning technology and spinning machine.
Two, prior art: existing viscose filament yarn manufacturing technique has: centrifugally spin, semicontinuously three kinds of technologies such as spin and spin continuously.Centrifugal spin with semicontinuous spinning process in, viscose glue is expressed in the coagulating bath from shower nozzle and is shaped, the strand that solidifies by the bath face of drawing after after solidifying on the roller further regeneration, carry out wet concentration to the washing roller and handle, be shaped to spinning cake through tophan box; In continuous spinning process, viscose glue is shaped in the spinning glass tube through spinning head is extruded after, and the strand that solidifies wet concentration to the treatment tube is handled after coiling and molding is silk tin.The tradition viscose filament yarn is a kind of multifilament, and its filament number generally is not less than 2dtex, and Denier range is generally 44-666dtex; Because the fine content of first was all about 9% during the viscose glue of these three kinds of technologies was formed, all have only about 6% and contain alkali, it adopts single bath process to be shaped, zinc sulfate concentration is lower in the coagulating bath, because the characteristics of these spinning techniques and device layout, determine the fiber solidification forming too violent, caused the fibre section to form tangible zigzag skin-core structure; It is low to show as fibre strength, and fatigue performance is poor, is difficult to satisfy special requirement.
Three, Fa Ming purpose, in order to overcome the shortcoming of existing viscose filament yarn Processes and apparatus, the objective of the invention is to: a kind of new viscose rayon filament spinning skill is provided and implements the high-strength viscose continuous yarn spinning equipment of this method, to improve the quality of spinning, make the viscose filament yarn fiber have good intensity and fatigue performance, to satisfy special requirement.
Four, summary of the invention: the objective of the invention is to be implemented by following technical scheme: a kind of high-strength viscose long filament continuous spinning process and equipment, its spinning technique is realized by one roller multifibres continous mode viscose filament yarn spinning machine.Spinning machine partly is made up of viscose glue induction system, measuring pump, candle filter, spinning head, spin duct, spinning disc, washing roller, two baths, washing pipe, oil bath, drier roll and electric ingot system etc.
Viscose glue is by the viscose glue induction system, after the measuring pump metering, spin preceding filtration by candle filter, extrude by spinning head and to form the viscose glue thread, be configured as nascent strand with the coagulating bath effect in the level vial of viscose glue thread in immersing coagulating bath, nascent strand enters second coagulating bath and regenerates after carrying out first drawing-off between the spinning disc and second spinning disc, one or more strand through regeneration is washed processing to treatment tube after by the 3rd spinning disc drawing-off, after strand after washing is handled oils by oil bath, through drier roll oven dry back winding shaping.
Main technique feature of the present invention has been compared very big with traditional handicraft be high, its advantage is: (one), the process that adopts traditional viscose filament yarn to produce, in the viscose filament yarn production process, because fibre forming is too violent, causes the fibre section to be tangible zigzag skin-core structure (as shown in Figure 3); Viscose filament yarn of the present invention cross section is the full cortex construction (as shown in Figure 2) that is close to circle; (2), traditional viscose filament yarn is a kind of multifilament, its filament number generally is not less than 2dtex, its filament number of viscose filament yarn of the present invention can be low to moderate 0.8dtex; (3), traditional viscose filament yarn Denier range is generally 44-666dtex, viscose filament yarn Denier range of the present invention is 44-2200dtex; (4), traditional viscose filament yarn adopts single bath process to be shaped, the present invention adopts two-bath process to be shaped; (5), the present invention adopts a rhizoid bar or multi-filament bar to handle on a pair of washing roller; (6) one or more strand is dried on a pair of drier roll, and divides bull to reel.(7), the spinning glue that adopts of the present invention forms and is starkly lower than traditional viscose, the fine content of first is 5-7% in the viscose glue; (8), its sulfuric acid of coagulating bath, the sodium sulfate concentration of the present invention's employing are starkly lower than traditional viscose filament yarn coagulation bath composition, zinc sulfate concentration is apparently higher than traditional viscose filament yarn coagulation bath composition, and sulfuric acid concentration is that 60-80g/l, sodium sulfate concentration are that 150-180g/l, zinc sulfate concentration are 75-90g/l.
Five, description of drawings
Below in conjunction with drawings and Examples the present invention is further described,
Fig. 1 is a spinning machine structural principle schematic diagram of the present invention.
Fig. 2 is a high-strength viscose long filament sectional view of the present invention.
Fig. 3 for existing centrifugally spin, semicontinuous spunbond glue long filament sectional view.
Fig. 4 is a high-strength viscose continuous yarn spinning process chart of the present invention.
In Fig. 1, measuring pump 1, candle filter 2, spinning head 3, spin duct 4, the 3rd spinning disc 5, washing roller 6, second spinning disc 7, two baths 8, washing roller 9, washing pipe 10, oil bath 11, drier roll 12, spinning tube 13, drip tray 14.
Six, embodiment
With reference to Fig. 1, Fig. 4, realize its spinning technique of the present invention by its spinning machine, high-strength viscose continuous yarn spinning of the present invention technological process is: viscose glue is by the viscose glue induction system, through measuring pump, spin front filter, spinning glass tube, spinning head, spinning drawing-off dish, the second spinning drawing-off dish, coagulating bath regeneration, the 3rd spinning drawing-off dish drawing-off, washing is handled, is oiled, dries, spinning process such as last silk tube winding shaping, classification packing.
With reference to Fig. 1, viscose glue is by the viscose glue induction system, after measuring pump 1 metering, spin preceding filtration by candle filter 2, extrude by spinning head 3 and to form the viscose glue thread, after preliminary chemical reaction is carried out in viscose glue thread glue of being extruded by spinning head and acid bath, the strand epidermis is shaped rapidly, strand with spinning bath together with certain speed by spinning glass tube 4, in pipe, continue neutralization, a series of one-tenth shaped reactions such as dehydration, be configured as nascent strand with the coagulating bath effect in the level vial 4 in immersing coagulating bath, nascent strand enters second coagulating bath and regenerates after spinning drawing-off dish and second 7 on the spinning drawing-off dish carry out first drawing-off, one or more strand through regeneration is washed processing to water treatment roller 9 after by 5 drawing-offs of the 3rd spinning disc, after strand after washing is handled oils by oil groove 11, go up silk tube winding shaping through drier roll 12 oven dry backs
Main technologic parameters:
1, spinning glue is formed: the fine 5-7% of first
NaOH 5-7%
2, first coagulation bath composition: sulfuric acid concentration 60-80g/l
Sodium sulfate concentration 150-180g/l
Zinc sulfate concentration 70-90g/l
Temperature 45-60 ℃
3, second coagulation bath composition: acid concentration 0-70g/l
Temperature 90-99 ℃
4, total draft rate 45-80%
The product leading indicator
Intensity 〉=4.55cn/dtex
Elongation 12-20%
Claims (5)
1, the present invention relates to a kind of high-strength viscose continuous yarn spinning technology and spinning equipment, its spinning technique is to use a roller multifibres continuous spinning equipment, by the viscose glue induction system, measuring pump, candle filter, spinning head, spinning glass tube, spinning disc, the washing roller, two baths, oil bath, drier roll, and electric ingot control system etc. partly forms, and it is characterized in that: viscose glue is by the viscose glue induction system, through measuring pump, spin front filter, the spinning glass tube, spinning head, spinning disc, enter second coagulating bath regeneration behind second spinning disc, one or more oils by handling after the 3rd spinning disc drawing-off through the strand of regeneration, oven dry, last silk tube winding shaping.
2, the rayon spinning technology of using in a kind of high-strength viscose spinning technique according to claim 1 and the spinning equipment, it is characterized in that: be configured as nascent strand with the coagulating bath effect in the spinning glass tube 4 in immersing coagulating bath, nascent strand enters second coagulating bath and regenerates after carrying out first drawing-off between spinning drawing-off dish, the second spinning drawing-off dish, strand after the regeneration is washed processing after 5 drawing-offs of the 3rd spinning disc, after strand oiled by oil groove 11, drying roller flood was done and is gone up silk tube winding shaping.
3, according to claim 1,2 described a kind of high-strength viscose continuous yarn spinning technology and spinning equipments, it is characterized in that: the viscose filament yarn fiber number is 44-2200dtex, spin speed and be one or the multifibres technology of (29-66) mm/min, its first coagulation bath composition is sulfuric acid (60-80) ± 0.5g/l, and second coagulation bath composition is: sulfuric acid concentration (40-70) ± 0.3g/l; Temperature 90-99 ℃
4, a kind of high-strength viscose continuous yarn spinning technology according to claim 1 and spinning equipment, it is characterized in that: spinning machine equipment is by the viscose glue induction system, measuring pump, candle filter, spinning head, drawing-off dish, the spinning glass tube, the washing roller, two baths, drier roll spinning tube, electric ingot control system are formed.
5, a kind of high-strength viscose continuous yarn spinning technology according to claim 1 and spinning equipment, it is characterized in that: one or more treated strand is dried on a pair of drier roll.