CN1583630A - Manufacturing method for luminescent glass mosaic bricks - Google Patents
Manufacturing method for luminescent glass mosaic bricks Download PDFInfo
- Publication number
- CN1583630A CN1583630A CN 200410027570 CN200410027570A CN1583630A CN 1583630 A CN1583630 A CN 1583630A CN 200410027570 CN200410027570 CN 200410027570 CN 200410027570 A CN200410027570 A CN 200410027570A CN 1583630 A CN1583630 A CN 1583630A
- Authority
- CN
- China
- Prior art keywords
- glass
- cover
- solvent layer
- water
- bonding solvent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The materials is normal transparent colourless glass and colored glass processed into needed size. First, clear up glass materials with alcohol and dry to a 0-5% level of percent moisture content. Second, cover a water miscible solvent layer on the down surface and dry to a 0-10% level of percent moisture content. Then cover a fluorescent material with the grain size of 30-800 description and dry to a 0-8% level of percent moistre content. Clear the surface of cover. Finally, melting at 800deg.C -1300deg.C and cool down. Trimming effect is vivid at night. Illuminated scale is convenience and safe. Production cycle is shot. It can automatic large scale produce.
Description
Technical field
The present invention relates to the field of glass decoration building materials, particularly can self luminous glass Mosaic brick.
Background technology
Along with people's improving constantly to the decorative effect requirement, the glass Mosaic decorative block enters people's life again, and changes the design of single, the single look of tradition, and the glass Mosaic brick is with multicolour combination, collocation, multiple shape effects occurs, and produces the decoration design requirement thereby enrich people.But regrettably, these colorful mosaic bricks can only be by day or are embodied its decorative effect well-lighted the time at present, and when one to evening or insufficient light, mosaic brick can't embody it and decorate true qualities.
The development and use of current social various new forms of energy, novel material make that the luminous world is more and more abundanter, luminous source based on electric energy can not satisfy modern life demand fully, and the modern life is to the demand of light, also no longer rest on basic illumination functions, wish that also light more can beautify the living environment, in view of the building glass mosaic accounts for critical positions in decorating the design life, how the luminescent material with new technology combines with traditional product, expand new kink characteristics, the decorative effect of mosaic product, just the inventor's research emphasis.
Summary of the invention
The objective of the invention is to propose a kind of manufacture method that can self luminous over a long time fluorescent glass mosaic brick after being subjected to illumination or absorbing luminous energy, make the decorate properties of mosaic brick, especially the decorate properties at night fully manifests, and can produce low illumination to surrounding environment simultaneously.
The objective of the invention is to be achieved through the following technical solutions: a kind of manufacture method of fluorescent glass mosaic brick, with known, conventional glass is made raw material, the block glass that cuts into required size and shape by processing is matrix, glass basis must be the vitreum of water white transparency or colored transparent, at first glass basis is cleaned with the alcohol decontamination, be dried to water ratio 0-5%, cover the bonding solvent layer of one deck at its lower surface then, be dried to water ratio 0-10%, on bonding solvent layer, cover again and adhere to one deck particle diameter 30-800 purpose fluorescent material, be dried to water ratio 0-8%, clean cover surface with alcohol, put into kiln at last and fire, get finished product after the cooling 800-1300 ℃ of temperature.Further, fluorescent material can pass through spray gun, is 0.3-2.5Mpa with pressure, and gas velocity is 0.2-0.5m
3/ s direct injection is attached to the surface of the water-soluble bonding solvent layer on the glass basis.Perhaps, fluorescent material can directly print by screen printing apparatus and be attached on the water-soluble bonding solvent layer.
The present invention is based on the new and high technology luminescent material and combines with traditional processing technology, through experiment in a large number, in the utilization again of the luminous energy new breakthrough is arranged, and develops ultra-long afterglow, holds light, luminous glass Mosaic brick.Its absorbs visible luminous energy such as natural light, light, holds after light 10-29 minute in the dark place luminous, can be luminous whole night, lasting luminous more than 13 hours, extinction has recyclability to luminous, and authenticates through national authority department, product is nontoxic, harmless, meets international environmental protection standard.
Embodiment
Embodiment one:
The manufacture method of fluorescent glass mosaic brick adopts the crystal of known routine or transparent glass to make raw material.Glass cutting is become the square glass basis of required size specification by machinery, remove glass basis dirty long-pending with alcohol wash, be dried to water ratio 5% then, first water-soluble bonding solvent covering surfaces with a kind of being commonly called as " water glass " (the general chemical shop is on sale), stamp with automatic stamp-pad ink machine, it is combined with the glass basis surface, the lower surface of general cover glass matrix, upper surface does not cover, in order to absorb luminous energy, be dried to water ratio 8%, use compressor again, pressurized gas, to have pressure is 0.3-2.5Mpa, the spray gun that has high-speed gas 0.2-0.5m/s is as specific equipment, with the particle diameter is that 600-800 purpose fluorescent material particle is as blasting materials, fluorescent material is sprayed in the distance of 0.05-0.5m by spray gun, clash into to the bonding solvent layer of glass basis surface, fluorescent material particle is attached on the bonding solvent layer preferably, be dried to water ratio 6%, use the alcohol wash surface, put into the roller-way cellar for storing things at last and be warming up to 1300 ℃ of high-temperature firings, but become luminous mosaic brick product after cooling.
Embodiment two:
By with artificial or mechanical, large-area colored transparent glass cutting is become required toroidal glass block, with glass alcohol wash decontamination, make glass block be dried to water ratio 1%, earlier by hand with " water glass " bonding solvent coating in the lower surface of glass basis, it is combined with glass basis, be dried to water ratio 2%, use screen printing apparatus again, be particle diameter the particle of 30-60 purpose fluorescent material, printing is attached to the surface of bonding solvent layer, uses the alcohol wash surface.At last with the roller kiln high-temperature firing in 800 ℃ that heats up, but become luminous mosaic brick product after cooling.
Certainly, only enumerated several preferred implementation here, other is equal to the protection domain that roughly the same structure all should belong to this patent, repeats no more here.
Claims (3)
1, a kind of manufacture method of fluorescent glass mosaic brick, with known, conventional glass is made raw material, the block glass that cuts into required size and shape by processing is matrix, it is characterized in that: glass basis must be the vitreum of water white transparency or colored transparent, at first glass basis is cleaned with the alcohol decontamination, be dried to water ratio 0-5%, cover the bonding solvent layer of one deck at its lower surface then, be dried to water ratio 0-10%, on bonding solvent layer, cover again and adhere to one deck particle diameter 30-800 purpose fluorescent material, be dried to water ratio 0-8%, clean cover surface with alcohol, put into kiln at last and fire, get finished product after the cooling 800-1300 ℃ of temperature.
2, manufacture method according to claim 1 is characterized in that fluorescent material can pass through spray gun, is 0.3-2.5Mpa with pressure, and gas velocity is 0.2-0.5m
3/ s direct injection is attached to the surface of the water-soluble bonding solvent layer on the glass basis.
3, manufacture method according to claim 1 is characterized in that fluorescent material can be attached on the water-soluble bonding solvent layer by the direct printing of screen printing apparatus.