CN1552796A - Semi-dry method gun mix for coal oven reparing - Google Patents
Semi-dry method gun mix for coal oven reparing Download PDFInfo
- Publication number
- CN1552796A CN1552796A CNA031289886A CN03128988A CN1552796A CN 1552796 A CN1552796 A CN 1552796A CN A031289886 A CNA031289886 A CN A031289886A CN 03128988 A CN03128988 A CN 03128988A CN 1552796 A CN1552796 A CN 1552796A
- Authority
- CN
- China
- Prior art keywords
- coke oven
- repaired
- semi dry
- dry gunning
- alumina
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A reparing material for reparing the coke oven by spraying the semi-dried it is prepared from the raw Al-Si material chosen from mullite, high-Al alumine, etc. high-Al cement or calcium aluminate cement, soft clay, kyanite, Al2O3 and/or SiO2 powder, and naphthalenesulfonic acid-formaldehyde condensate. Its advantages are high adhesion, strength, heat shock resistance and antiwear performance, and low cost.
Description
Technical field
The present invention relates to a kind of coke oven and repair the semi dry gunning material of usefulness, belong to refractory materials manufacturing technology field.
Background technology
Coke oven is the main equipment of coking, and its effect is coking coal to be carried out destructive distillation obtain coke and other byproducts in coking chamber.Coke oven is operated the effects such as thermal stress, mechanical stress and chemical corrosion that cause continuously owing to coalingging, pluck door, coke pushing etc. after operation, each position of body of heater is changed gradually.Therefore coke oven in use damages year by year, especially carbonization chamber and burner position.Domestic having only traditional wet method repairing technique aspect the coking furnace shaft maintenance technique, wet method is repaired and can be made hot furnace wall be subjected to rapid refrigerative impact on the one hand, makes the surface tissue of silica brick be subjected to certain damage, shortens converter life.Because the pug water content is more, when contacting with furnace wall violent vaporization can take place, influence cohesive strength and bridging time on the other hand.Be a kind of repairing means that comparatively fall behind, eliminated traditional wet method already at western developed country and repaired, generally adopted methods such as semi dry gunning to carry out the routine maintenance of coke oven.
Introduced a kind of traditional wet spraying mode on " unshape refractory " (P365 page or leaf, metallurgical industry press, 1994), its coke oven end Gunning refractory is to adopt phosphoric acid high alumina matter gun-mix refractory to carry out hot gunning.This material is by bauxite chamotte particle 45~60%, zircon grain 5~10%, and high alumina fine powder 25~40%, concentration is 42.5% phosphoric acid 28~35%.The furnishing muddy is in the nitrogen jar spraying machine of packing into, with defeated material of pressurized air and spraying.600 ℃ of folding strength 3MPa of material, 800 ℃ of 4.3MPa, 1100 ℃ is 2.1MPa.
Application No. US3360594 discloses a kind of Gunning refractory, it consists of: flint clay grog 60~80%,<4 orders, fat clay 3~8%, cement material 20~40%, cement can be portland cement or aluminous cement, for reducing rebound degree, add 1~5% fibrous magnesium silicate.Add water 3% during use earlier, spray repair adds surplus water again, and rebound degree is 7.5~21%, and use temperature can be at 1500 ℃.Because environmental protection requirement, fibrous magnesium silicate bans use of at present.
Summary of the invention
The purpose of this invention is to provide the semi dry gunning material that is fit to carbonizing chamber of coke oven and burner position repairing usefulness, make that this Gunning refractory has that adhesive rate height, coking property are good, good thermal shock stability, characteristics such as wear-resistant, can be fine repairing coke oven liner produce peel off, corrode, fall brick position and crack, thereby prolong coke oven work-ing life.
Coke oven of the present invention is repaired and is used the semi dry gunning material, and its component and weight percentages of components are:
Alumina-silica raw material 55~78%
Wedding agent 10~25%
Agglutinant and plasticizer 3~5%
Swelling agent 3~7%
Al
2O
3Micro mist is or/and SiO
2Micro mist 5~10%.
Gunning refractory of the present invention also is added with admixture, add-on be total amount+0.1~1.0%.
Further, described alumina-silica raw material can be more than in flint clay, mullite or the alumine one or more.
Wherein, Al in the described alumina-silica raw material
2O
3〉=45%;
The particle of described alumina-silica raw material can be divided into 3~1mm and two grades of 1~0mm.
Described wedding agent is high-alumina cement or pure calcium aluminate cement.
Wherein, described high-alumina cement accounts for the Gunning refractory total amount and is no less than 5%;
Al in the described high-alumina cement
2O
3〉=46%, CaO≤40%;
Al in the described pure calcium aluminate cement
2O
3〉=69%, CaO≤25%.
Described agglutinant and plasticizer are soft clay.
Described swelling agent is a kyanite; The granularity of swelling agent≤100 orders.
SiO wherein
2Micro mist is no less than 3%.
Described admixture is a naphthalene sulfonic acidformaldehyde condensation product.
Aluminium siliceous raw material of the present invention is a main raw material, can be flint clay, mullite or alumine, can be according to coke oven working conditions and different cost requirements respectively or be used.About 1200 ℃ of carbonizing chamber of coke oven use temperature, coke oven sharply descends in the back temperature of the discharging of the coke, and Gunning refractory must have good spalling resistance.Coke constantly advances from the carbonization chamber and releases, so Gunning refractory also must have good wearability.Adopting the alumina-silica raw material is main raw material, because such raw material host is mullite and corundum mutually, fire performance, thermal shock resistance and wear resistance is preferably arranged.Particle can be divided into 3~1mm and two grades of 1~0mm.Its chemical ingredients requires Al
2O
3〉=45%, TiO
2<2.0%, R
2O<0.5%, particle water-intake rate≤5%; Be to strengthen matrix, improve erosion resistance, the heat-shock resistance of Gunning refractory, fine powder is selected refractoriness, mullite or alumine that purity is higher for use, and fineness is<0.088mm, requires Al
2O
3〉=60%, TiO
2<2.0%, R
2O<0.5% is 55~78% with the add-on of the little main raw material of alumina-silica raw material.
Gunning refractory of the present invention has adopted the wedding agent that is different from traditional hot Gunning refractory, and having adopted aluminate cement is wedding agent, can be high-alumina cement and pure calcium aluminate cement.High-alumina cement is to be the cement of essential mineral with aluminic acid-calcium (CA), and CA has very high hydraulically active, and sclerosis is the early strong important mineralogical composition of cement rapidly.The pure calcium aluminate cement essential mineral is calcium dialuminate (CA mutually
2), CA
2Hydration and hardening is slower, the low and later stage intensity height of early strength.Both are used, and not only can make material that suitable setting rate is arranged, and make material in each stage higher intensity and fire performance be arranged all, and this also is one of characteristic of the present invention.Require employed high-alumina cement Al
2O
3〉=46%, CaO≤40%, SiO
2≤ 10%; Pure calcium aluminate cement Al
2O
3〉=69%, CaO≤25%, SiO
2≤ 1%.Think by experimental study to be controlled at 10~25% in conjunction with dosage, and high-alumina cement is no less than 5%, Gunning refractory has optimum properties.
The agglutinant and the plasticizer that adopt are soft clay.Because Gunning refractory is in about hot spray repair more than 500 ℃, about 1200 ℃ of the medial temperature of life-time service needs material under existing temperature condition good sintering character to be arranged.So added 3~5% soft clay, acceleration of sintering improves medium temperature intensity.Soft clay can improve the plasticity-of Gunning refractory simultaneously, improves the adhesive rate of material.Also play simultaneously certain ceramic keying action.But add too much, can make the material at high temperature degradation, crackle appears too greatly in contraction.Few acceleration of sintering of add-on and plasticity-effect are not obvious.
Because Gunning refractory is compared with mould material, the construction water yield is more relatively, and void content is many.At high temperature shrinkage crack can appear in life-time service, and the spray repair layer peels off easily in use.Therefore, add demi-inflation agent kyanite 3~7% among the present invention, for keeping having suitable swelling property for a long time, the kyanite of adding is unsuitable meticulous, is generally≤100 orders.
For further strengthening matrix, improve coking property, the high-temperature behavior of Gunning refractory, in matrix, added Al
2O
3Micro mist and SiO
2Micro mist, this also is the present invention and traditional Gunning refractory difference.Total amount is 5~10%, wherein SiO
2Micro mist is no less than 3%.SiO
2After the micro mist aquation is solidified, form the Si-OH base (silanol) of larger amt on the surface, the dehydration post polymerization forms the network-like micro mist chain of Si-O-Si bonded, make the spray repair layer have higher intensity, this structure does not improve with temperature and weakens, in use, and the SiO that reactive behavior is very high
2Micro mist and Al
2O
3Micro mist can react and generate the mullite crystalline phase, helps improving thermal shock resistance and hot strength, adds the reactive sintering effect of micro mist, further promotes dense structureization, thereby has improved the wearing quality of material.
By determining the research trial repeatedly of additive, think that naphthalene sulfonic acidformaldehyde condensation product can be fit to this Gunning refractory well, this is different from the poly-phosphate dispersion agent of common employing, the semi dry gunning material does not need very good flowability, otherwise the spray repair layer down drops down easily, but need additive that certain water reducing ability is arranged, promote the wetting ability and the quick humidification of material.And the naphthalene sulfonic acidformaldehyde condensation product molecular structure that adopts exists naphthalene nucleus and sulfonate radical simultaneously.When conjugated system in the naphthalene nucleus and cement granules meet, be adsorbed on its surface easily; Sulfonate radical then is easy to form hydrogen bond and produce association with water.Both coefficient results have formed stable moisture film at cement particle surface, and the flowability of grout and suspension are improved.Gunning refractory key property when construction is a wetting ability in addition.The introducing of sulfonate radical can make the surface tension of solution significantly reduce, and can make the very fast wetting well Gunning refractory of water, forms hydration layer and fine micelle, helps workability.The employing naphthalene sulfonic acidformaldehyde condensation product is an additive, is one of characteristics of the present invention, and add-on is better in+0.1~1.0% effect.
Embodiment
The proportioning of embodiments of the invention and comparative example is referring to table 1.Table 2 be semi dry gunning material of the present invention with the performance contrast of comparative example.
The required water content of Gunning refractory of the present invention construction is few, is about 11~15%, is significantly less than conventional wet spray repair (amount of water about 20%), destructive little to hot furnace wall, and the void content of repairing layer is low, and the bridging time is long, can reach more than 6 months, and cost is lower.Adhesive rate 〉=85%, the spray repair layer used 4 months, cracking do not occur, peel off and wore and tore, and estimated that work-ing life can be above 6 months.
The cost and the over-all properties of material have been taken into full account in an embodiment, carry out reasonably combined on the material, in the thermal shock performance test, at first carried out the thermal treatment of 500 ℃ * 5h, carry out again 1200 ℃ ← → water-cooled test, having obtained 22 materials of continuous circulation does not have the destructive good result.Hot strength also has high value, can bear periodic abrasive action.
Comparative example 1 has all adopted the high aluminous cement of alumina content, and preferable performance is arranged when 1400 ℃ of high temperature, but intensity is not high when low temperature, middle temperature, does not have advantage under the coke oven use temperature, and intensity forms slowly during construction, and can increase material cost.Comparative example 2 does not adopt micro mist, has influenced each temperature section intensity of Gunning refractory, and to shrink also be maximum, influences the use properties of material equally.Have only embodiment to embody better comprehensive performance, be fit to use under the coke oven condition.
The proportioning (wt%) of table 1 semi dry gunning material
Raw material specification | Embodiment | Comparative example | |||
????1 | ????2 | ????3 | ????1 | ????2 | |
Flint clay particle≤3mm | ????50 | ????- | ????- | ????50 | ????- |
Mullite particle≤3mm | ????- | ????55 | ????53 | ????- | ????51 |
Mullite fine powder≤0.088mm alumina fine powder≤0.088mm | ????5 | ????10 | ????22 | ????8 | ????17 |
High-alumina cement | ????5 | ????10 | ????5 | ????- | ????10 |
Aluminous cement | ????20 | ????10 | ????5 | ????20 | ????10 |
Kyanite | ????7 | ????5 | ????3 | ????7 | ????7 |
SiO 2Micro mist | ????5 | ????3 | ????5 | ????5 | ????0 |
Al 2O 3Micro mist | ????5 | ????2 | ????4 | ????5 | ????0 |
Soft clay | ????3 | ????5 | ????3 | ????5 | ????5 |
Naphthalene sulfonic acidformaldehyde condensation product | ????+1.0 | ????+0.5 | ????+0.3 | ????+0.3 | ????+0.7 |
The performance of table 2 semi dry gunning material
Project | Embodiment 1 | Embodiment 2 | Embodiment 3 | Comparative example 1 | Comparative example 2 | |
110℃× 24h | Folding strength, MPa | ????7.5 | ????7.3 | ????6.5 | ????4.9 | ????5.3 |
Compressive strength, MPa | ????38.1 | ????39.1 | ????33.4 | ????30.5 | ????32.3 | |
Volume density, g/cm 3 | ????2.08 | ????2.14 | ????2.21 | ????2.12 | ????2.18 | |
1200℃× 3h | Folding strength, MPa | ????5.0 | ????7.3 | ????5.5 | ????3.7 | ????3.2 |
Compressive strength, MPa | ????25.6 | ????28.2 | ????27.4 | ????20.3 | ????20.1 | |
The line velocity of variation, % | ????-0.4 | ????-0.3 | ????-0.37 | ????-0.3 | ????-0.6 | |
Volume density, g/cm 3 | ????2.05 | ????2.09 | ????2.12 | ????2.08 | ????2.05 | |
The hot anti-folding of 1200 ℃ * 1h, MPa | ????5.0 | ????5.4 | ????5.7 | ????2.7 | ????3.0 | |
The hot anti-folding of 1400 ℃ * 1h, MPa | ????1.9 | ????2.1 | ????2.0 | ????2.3 | ????0.9 |
Claims (14)
1. coke oven is repaired and is used the semi dry gunning material, and its component and weight percentages of components are:
Alumina-silica raw material 55~78%
Wedding agent 10~25%
Agglutinant and plasticizer 3~5%
Swelling agent 3~7%
Al
2O
3Micro mist is or/and SiO
2Micro mist 5~10%.
2. coke oven as claimed in claim 1 is repaired and is used the semi dry gunning material, it is characterized in that, also is added with admixture, add-on be total amount+0.1~1.0%.
3. coke oven as claimed in claim 1 is repaired and is used the semi dry gunning material, it is characterized in that, described alumina-silica raw material can be more than in flint clay, mullite or the alumine one or more.
4. coke oven as claimed in claim 1 is repaired and is used the semi dry gunning material, it is characterized in that Al in the described alumina-silica raw material
2O
3〉=45%.
5. use the semi dry gunning material as claim 1 or 4 described coke ovens repairings, it is characterized in that the particle of described alumina-silica raw material can be divided into 3~1mm and two grades of 1~0mm.
6. coke oven as claimed in claim 1 is repaired and is used the semi dry gunning material, it is characterized in that described wedding agent is high-alumina cement or pure calcium aluminate cement.
7. coke oven as claimed in claim 6 is repaired and is used the semi dry gunning material, it is characterized in that described high-alumina cement accounts for the Gunning refractory total amount and is no less than 5%.
8. use the semi dry gunning material as claim 6 or 7 described coke ovens repairings, it is characterized in that Al in the described high-alumina cement
2O
3〉=46%, CaO≤40%.
9. coke oven as claimed in claim 6 is repaired and is used the semi dry gunning material, it is characterized in that Al in the described pure calcium aluminate cement
2O
3〉=69%, CaO≤25%.
10. coke oven as claimed in claim 1 is repaired and is used the semi dry gunning material, it is characterized in that described agglutinant and plasticizer are soft clay.
11. coke oven as claimed in claim 1 is repaired and is used the semi dry gunning material, it is characterized in that described swelling agent is a kyanite.
12. use the semi dry gunning material as claim 1 or 11 described coke ovens repairings, it is characterized in that the granularity of described swelling agent≤100 orders.
13. coke oven as claimed in claim 1 is repaired and is used the semi dry gunning material, it is characterized in that, wherein SiO
2Micro mist is no less than 3%.
14. coke oven as claimed in claim 1 is repaired and is used the semi dry gunning material, it is characterized in that described admixture is a naphthalene sulfonic acidformaldehyde condensation product.