CN1536182A - 纤维增强硅酸钙复合夹芯轻质隔墙条板 - Google Patents
纤维增强硅酸钙复合夹芯轻质隔墙条板 Download PDFInfo
- Publication number
- CN1536182A CN1536182A CNA031141579A CN03114157A CN1536182A CN 1536182 A CN1536182 A CN 1536182A CN A031141579 A CNA031141579 A CN A031141579A CN 03114157 A CN03114157 A CN 03114157A CN 1536182 A CN1536182 A CN 1536182A
- Authority
- CN
- China
- Prior art keywords
- portions
- calcium silicate
- flyash
- light partition
- sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种纤维增强硅酸钙复合夹芯轻质隔墙条板,涉及纤维增强硅酸钙复合夹芯轻质墙板相关技术。本技术墙板及芯体材料组成;面板为粉煤灰硅酸钙板,芯体材料各成分质量份数为:水泥:200,粉煤灰:0~70,砂:150~300,废料:0~40,聚苯乙烯:7~12,缓凝减水剂:0~4,表面活性剂:5~10,水:100~150。其生产工艺为:将上述物料按比例选取并计量经充分搅拌,注入插有硅酸钙板的模框内,经模内养护、脱模、磨边、养护库养护即可。本技术原材料来源广泛,成本低,隔音、隔热,质轻,抗冲击性能好,可钉可锯。用于建筑内隔墙体,施工速度快,干法作业,板墙平整,增大建筑使用面积,符合国家墙改政策。
Description
技术领域
本发明涉及建筑材料领域,特别涉及纤维增强硅酸钙复合墙板相关技术。
背景技术
目前,各种新型隔墙条板种类很多,如纤维增强水泥混凝土空心隔墙条板,工业灰渣混凝土空心隔墙条板,钢丝网架聚苯乙烯轻质墙板,蒸压加气混凝土条板,氯氧镁水泥薄板复合夹芯轻质隔墙条板等,其性能各有特点,也分别存在不足,作为房屋的内隔墙新型板材,具有轻质,施工工期短,建筑使用率高等共同特点。
技术内容
本发明目的是设计一种原材料来源广泛,成本低,隔音、隔热、质轻、抗冲击性能好,抗弯破坏荷载大,可钉可锯的轻质隔墙条板。
本发明目的可通过以下技术方案实现。
以纤维增强粉煤灰硅酸钙板作为面板材料,并以快硬铁铝酸盐水泥作胶凝材料,以聚苯乙烯发泡珠、砂作为骨料辅以其它外加剂,外掺料而组成的轻质混凝土作芯体材料,面板与芯体有机复合而成。其芯体材料的配方中各成份的质量份数为:
水泥:200
粉煤灰:0~70
砂:150~300
废料:0~40
聚苯乙烯:7~12
缓凝减水剂:0~4
表面活性剂:5~10
水:100~150
以上的配方中所述水泥选用525号快硬铁铝酸盐水泥;所述聚苯乙烯为经蒸汽发泡成泡珠,发泡容重为13.5~15g/l,胶粒半径在1.2~1.6mm;所述废料为生产、施工过程中的废墙板经破碎而成,粒径为小于30mm;所述缓凝减水剂为聚羧酸钠水溶液;所选的粉煤灰为三级以上灰,0.045mm筛余45%;所选取的砂为中砂,模数为3.0~2.3。纤维增强硅酸钙复合夹芯轻质隔墙板所采用的面板为纤维增强粉煤灰硅酸钙板,厚度为3-5mm,纵向抗折强度≥13MPa,横向抗折强度≥20MPa。其它性能符合国家建材工业行业标准JC/T564-2000要求。纤维增强硅酸钙复合夹芯轻质隔墙板的生产工艺,其特征在于所述工艺包括以下步骤:
①按比例选取上述物料;
②将上述处理好的物料在搅拌机中充分搅拌,得混凝土拌合料;
③在模框的两侧***硅酸钙板;
④将充分搅拌的拌合料以混凝土输送泵泵入插有硅酸钙板的模框中;
⑤墙板端头平面修整;
⑥模内自然状态下养护8小时以上;
⑦脱去模框;
⑧脱模后的复合墙板湿法磨出接缝槽边;
⑨自然状态下养护14天以上,包装为成品。
本发明技术进步在于原材料易得,成本低,所制造的板材隔音、隔热、防火性能好,可钉可锯。用于建筑内隔墙体,安装施工速度快,干法施工,板墙平整,增大建筑使用面积,符合国家墙改政策。
具体实施方法
一种纤维增强硅酸钙复合夹芯轻质隔墙板的配方,所述实施实例如规格为610×75(mm)(宽×厚)的墙板芯体材料配方中各成份的重量百份比为:
525号快硬铁铝酸盐水泥:33%
三级粉煤灰:10%
模数为3.0~2.3的中砂:40%
粉碎至3cm以下的废墙板:3.3%
聚苯乙烯发泡珠(发泡容重13.5~15g/l):1.4%
缓凝减水剂聚羧酸钠水溶液:0.3%
表面活性剂聚乙烯醇缩甲醛:1.2%
水灰比:0.46
规格为610×75(mm)(宽×厚)的墙板的生产工艺如下:
①将上述处理好的物料在搅拌机中充分搅拌,得拌合料;
②在模框的两侧***硅酸钙板;
③将充分搅拌的拌合料以混凝土输送泵泵入插有硅酸钙板的模框中;
④对墙板端头平面进行修整;
⑤模内自然状态下养护8小时以上;
⑥脱去模框;
⑦脱模3天后的复合墙板湿法磨出接缝槽边;
⑧自然状态下养护14天以上,包装为成品。
Claims (4)
1、一种纤维增强硅酸钙复合夹芯轻质隔墙条板,其特征在于:所述隔墙条板由面板及芯体材料组成,面板采用粉煤灰硅酸钙板,芯体材料配方中各成份的质量份数为:
水泥:200
粉煤灰:0~70
砂:150~300
废料:0~40
聚苯乙烯:7~12
缓凝减水剂:0~4
表面活性剂:5~10
水:100~150
2、根据权利要求1所述的纤维增强硅酸钙复合夹芯轻质隔墙条板,其特征在于:所采用面板为纤维增强粉煤灰硅酸钙板,厚度为3~5mm,纵向抗折强度≥13MPa,横向抗折强度≥20MPa。
3、根据权利要求1所述的纤维增强硅酸钙复合夹芯轻质隔墙条板,其特征在于:水泥选用525号快硬铁铝酸盐水泥,所述缓凝减水剂为聚羧酸钠水溶液,所选的粉煤灰为三级以上灰,0.045mm筛余45%,所选取的砂为中砂,模数为3.0~2.3,所选的废料为经破碎为小于30mm的废墙板;所述聚苯乙烯为经蒸汽发泡成泡珠,发泡容重为13.5~15g/L,胶粒半径在1.2~1.6mm,所述表面活性剂为聚乙烯醇缩甲醛。
4、一种纤维增强硅酸钙复合夹芯轻质隔条板的生产工艺,其特征在于,所述工艺包括以下步骤:
①按比例选取上述物料;
②将上述处理好的物料在搅拌机中充分搅拌,得到拌合料;
③在模框的两侧***硅酸钙板;
④将充分搅拌的拌合料以混凝土输送泵泵入插有硅酸钙板的模框;
⑤墙板端头平面修整;
⑥模内自然状态下养护8小时以上;
⑦脱去模框;
⑧脱模后的复合墙板湿法磨出接缝槽边;
⑨自然状态下养护14天以上,包装为成品。