CN1515383A - Steel ball grinding abrasive wheel binder and its production method - Google Patents
Steel ball grinding abrasive wheel binder and its production method Download PDFInfo
- Publication number
- CN1515383A CN1515383A CNA031528244A CN03152824A CN1515383A CN 1515383 A CN1515383 A CN 1515383A CN A031528244 A CNA031528244 A CN A031528244A CN 03152824 A CN03152824 A CN 03152824A CN 1515383 A CN1515383 A CN 1515383A
- Authority
- CN
- China
- Prior art keywords
- oxide
- production method
- feldspar
- bond according
- total amount
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention belongs to the field of ball-grinding abrasive-disk anchoring agent technology. Its effective chemical components are: (wt%) silicon oxide 56.1%-60.3%, aluminium oxide 23.5%-26.7%, iron oxide less than 1.0%, calcium oxide less than 0.5%, potassium oxide+sodium oxide 7.0%-9.0%, boron oxide, 1.46%-2.20% and manganese oxide 3.25%-5.2%. The production method of said anchoring agent includes the following steps: respectively weighing clay, feldspar, boron glass and metal oxide, mixing them, pulverizing and sieving by means of 240-mesh sieve. The anchoring agent has high heat resistance and wear resistance.
Description
Technical field
The invention belongs to abrasive wheel for abrasion of steel ball bond technical field.
Background technology
Existing abrasive wheel for abrasion of steel ball bond is made up of clay-feldspar-boron glass, owing to adopt greatly in conjunction with dosage, the big high briquetting pressure of compact density etc. are in the hope of high volume density, and emery wheel easily cracks, aliquation, and percent defective is higher.
Summary of the invention
The object of the invention is to provide a kind of hear resistance height, and wearability is good, in roasting process with the high abrasive wheel for abrasion of steel ball bond of yield rate.
Abrasive wheel for abrasion of steel ball bond of the present invention, effectively chemical analysis is: silica 56.1%~60.3%, aluminium oxide 23.5%~26.7%, iron oxide<1.0%, calcium oxide<0.5%, potassium oxide+sodium oxide molybdena 7.0%~9.0%, boron oxide 1.46%~2.20%, manganese oxide 3.25%~5.2%.
The present invention makes bond hear resistance height owing to add metal oxide, particularly manganese oxide, and wearability is good, can improve product percent of pass 16~18%, cuts down the consumption of energy 30%~36%.
The present invention also provides a kind of method of producing bond: take by weighing clay, feldspar, boron glass, metal oxide respectively, mix, pulverize, sieve by 240 eye mesh screens.
20~40% of described clay comprises total amount; Feldspar accounts for 45~60% of total amount; Boron glass accounts for 5~20% of total amount; Metal oxide accounts for 5~20% of total amount.
The Main Ingredients and Appearance of clay is Al
2O
32SiO
22H
2O; The Main Ingredients and Appearance of feldspar is K
2OAl
2O
36SiO
2The Main Ingredients and Appearance of boron glass is NaB
4O
710H
2O; Metal oxide is MnO
2
Magnetic thing<0.15% of bond of the present invention, 1260~1320 ℃ of refractoriness, plasticity 〉=50 second, free moisture content<0.1%.
Description of drawings
Accompanying drawing is a process chart of the present invention.
Specific embodiment
Get the raw materials ready:
Al is produced in Suzhou, clay Jiangsu
2O
32SiO
22H
2O
The feldspar yueyang, hunan produces K
2OAl
2O
36SiO
2
Boron glass borax glass NaB
4O
710H
2O;
Metal oxide MnO
2
The preparation method of abrasive wheel for abrasion of steel ball bond of the present invention is by the weighing of component proportioning with clay powder, feldspar powder, boron glass powder and oxidate powder, relative error is no more than 0.5%, mix through the double helix conical mixer, greater than 99.5%, being coarser than 80 purpose each component particles is 0 by 240 eye mesh screens.
Check: measure refractoriness, granularmetric composition, the uniformity for every batch, the selective examination chemical analysis is checked water content before going into operation.
Claims (7)
1, a kind of bond of abrasive wheel for abrasion of steel ball, it is characterized in that its effective chemical analysis (percentage by weight) is: silica 56.1%~60.3%, aluminium oxide 23.5%~26.7%, iron oxide<1.0%, calcium oxide<0.5%, potassium oxide+sodium oxide molybdena 7.0%~9.0%, boron oxide 1.46%~2.20%, manganese oxide 3.25%~5.2%.
2, the production method of bond according to claim 1 is characterized in that taking by weighing respectively clay, feldspar, boron glass, metal oxide, mixes, and pulverizes, and sieves by 240 eye mesh screens.
3, the production method of bond according to claim 2 is characterized in that 20~40% of described clay comprises total amount; Feldspar accounts for 45~60% of total amount; Boron glass accounts for 5~20% of total amount; Metal oxide accounts for 5~20% of total amount.
4, the production method of bond according to claim 3, the main composition that it is characterized in that clay is Al
2O
32SiO
22H
2O.
5, the production method of bond according to claim 3, the main composition that it is characterized in that feldspar is K
2OAl
2O
36SiO
2
6, the production method of bond according to claim 3, the main composition that it is characterized in that boron glass is NaB
4O
710H
2O.
7, the production method of bond according to claim 3 is characterized in that metal oxide is MnO
2