CN1504540A - Catalyst for preparing low carbon olefin by petroleum hydrocarbon cracking - Google Patents
Catalyst for preparing low carbon olefin by petroleum hydrocarbon cracking Download PDFInfo
- Publication number
- CN1504540A CN1504540A CNA021533741A CN02153374A CN1504540A CN 1504540 A CN1504540 A CN 1504540A CN A021533741 A CNA021533741 A CN A021533741A CN 02153374 A CN02153374 A CN 02153374A CN 1504540 A CN1504540 A CN 1504540A
- Authority
- CN
- China
- Prior art keywords
- zeolite
- catalyzer
- catalyst
- mfi
- sio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a catalyst for preparing lower carbon number hydrocarbon olefin through petroleum hydrocarbon decomposition, which comprises (catalyst weight as benchmark) 0-70% clay, 5-99% inorganic oxide compound and 1-50% zeolite, wherein the zeolite is 25-100 wt% MFI structure zeolite and 0-75 wt% Y-type zeolite, characterized by that, the MFI structure zeolite contains phosphor and transient metal M. the catalyst can improve the cracking capability for heavy oil macromolecule and conversion rate of reaction.
Description
Technical field
The invention relates to a kind of petroleum hydrocarbon cracking and produce the catalyzer of low-carbon alkene, further say so and produce the catalyzer of low-carbon alkene about a kind of petroleum hydrocarbon cracking that contains the five-ring supersiliceous zeolite.
Background technology
Low-carbon alkene is important petrochemical materials, and generally the preparation method of Cai Yonging is to be the steam cracking of raw material with the Sweet natural gas; With petroleum naphtha or solar oil is the pyrolysis in tubular furnace of raw material; The heat carrier cracking of heavy hydrocarbon and with the method for low-carbon alcohol catalyzed conversion.Conventional catalytic cracking unit also by-product low-carbon alkene when producing gasoline and solar oil, its productive rate accounts for below the 15 heavy % of stock oil.
With the petroleum hydrocarbon be raw material when adopting cracking or cleavage method to produce low-carbon alkene employed catalyzer three classes are roughly arranged: a class is to be the metal load type catalyst of carrier with the oxide compound, and their carrier can be SiO
2, Al
2O
3Or other oxide compound, mostly the metallic element of institute's load is to belong to IIB, VB, VIIB and VIIIB family element (USP3541179, USP3647682, DD225135, SU1214726).When using this class catalyzer because the dehydrogenation of institute's loaded metal, the also corresponding quickening of polymerization coking reaction when carrying out cracking reaction, therefore, generally can only use boiling range when adopting this type of catalyzer is<220 ℃ lightweight material.
The employed second class catalyzer is composite oxides.As with ZrO
2And/or HfO
2Catalyzer for main component is aided with Al
2O
3, Cr
2O
3, MnO and/or Fe
2O
3And basic metal or alkaline earth metal oxide (USP3725495, USP3839485); Be catalyzer and for example with potassium vanadate, potassium stannate or potassium niobate, can be about after the naphtha cracking low-carbon alkene of 56 heavy %, the therein ethylene productive rate can reach 36.5 heavy %, productivity of propylene is 12.5 heavy % (SU523133, SU487927, SU410073); Contain small amount of Fe for another example
2O
3, TiO
2, CaO, MgO, Na
2O, K
2The SiO of O
2Al
2O
3Catalyzer is used for the cracking (SU550173, SU559946) of various hydrocarbon-fractions.Composite oxides commonly used are amorphous Si O
2Al
2O
3, disclosed among the DD152356 with amorphous Si O
2Al
2O
3Being catalyzer, is raw material with liquid hydrocarbon or various hydrocarbon-fraction (comprising gasoline, kerosene, gas oil or vacuum distillate), produces the process of low-carbon alkene under 600~800 ℃ temperature of reaction, C
2 =~C
4 =Productive rate can reach 40~55m% (accounting for raw material).
Along with zeolite increasingly extensive application in petrochemical complex and refining of petroleum field, a large amount of reported in literature the 3rd class catalyzer, promptly contain the catalyzer of zeolite, particularly contain have the MFI structural zeolite catalyzer of (five-ring supersiliceous zeolite).This class catalyzer both can use separately, also can be used as additive and introduced in catalytic cracking unit or the cracking catalyst.
For example, having disclosed with ZSM one 5 zeolites among the JP60-224428 is active ingredient, Al
2O
3Be the catalyzer of carrier, under 600~750 ℃ to C
5~C
25The paraffinic hydrocarbon raw material carry out catalytic cracking, C
2 =~C
4 =Productive rate is about 30m%.
Having disclosed among the USP3758403 with ZSM-5 zeolite and large pore zeolite (as X type, Y type) is that the catalyzer of active ingredient (ratio of the two is 1: 10~3: 1) can make (C in the gasoline octane rating in improving product
3 =+ C
4 =) productive rate increase to about 10 heavy %.
Employing large pore zeolite and SiO have been reported among the USP5318696
2/ Al
2O
3The catalyzer of<30 the zeolite with MFI structure can be produced high-octane gasoline, also can improve low-carbon alkene, especially C simultaneously
3 =Productive rate.
The mixture that has disclosed among the CN1004878B with ZSM-5 zeolite and y-type zeolite is the catalyzer of active ingredient, under 500~650 ℃ temperature of reaction, can improve C when improving the product gasoline octane rating
2 =~C
4 =Productive rate, and wherein with C
3 =And C
4 =Be primary product.
Many methods that zeolite with five-membered ring structure is carried out the modification processing have also been reported in the document, to improve the selectivity of reaction product.As introducing phosphorus in the zeolite that has five-membered ring structure at ZSM-5 etc. or/and metal ion, absorption and catalytic performance that can the modulation zeolite.
Reported among the U.S. Pat P4365104 with the method for P and Mg modified zsm-5 zeolite, its objective is that the molecular sieve with modification is used for xylene isomerization, to improve the selectivity of p-Xylol, introducing P and Mg mainly is in order to strengthen the shape selectivity energy of molecular sieve; But then, the reactive behavior of the acidity of molecular sieve and the hydrocarbon conversion then reduces after the modification.
Reported at SiO among the USP5236880
2/ Al
2O
3The paraffinic hydrocarbon cracking catalyst that adds VIIIB family metal component, preferred nickel in>5 the zeolite with MFI or MEL structure, this catalyzer can improve the paraffinic hydrocarbon conversion of raw material, increase the aromatic component in the gasoline fraction, improve the octane value and the gasoline yield of gasoline.
It is the catalyzer of active ingredient that USP5380690 and CN1093101A have disclosed with phosphorous and five-ring supersiliceous zeolite rare earth.This catalyzer hydro-thermal activity stability height under 580 ℃ reaction conditions, is high 4~7 units of catalyzer transformation efficiency of active ingredient with the HZSM-5 zeolite, C
2 =~C
4 =High 4~5 units of productive rate.
It is the catalyzer of active ingredient that CN1117518A has disclosed with phosphorous and five-ring supersiliceous zeolite and y-type zeolite mixture rare earth.Particularly propylene, iso-butylene and the high characteristics of isopentene productive rate of low-carbon alkene in this catalyzer hydro-thermal activity stability height, transformation efficiency height, the product.
Summary of the invention
It is higher to the purpose of this invention is to provide a kind of petroleum hydrocarbon cracking transformation efficiency, C in the product
2 =~C
4 =The catalyzer that low-carbon alkene, particularly productivity of propylene are high.
Catalyzer provided by the invention has following composition: the clay, 5~99% inorganic oxide and 1~50% the zeolite that in the catalyst weight are benchmark 0~70%, the y-type zeolite of the zeolite of the MFI structure that wherein said zeolite is 25~100 heavy % and 0~75 heavy %, it is characterized in that the phosphorous and transition metal M of said MFI structural zeolite, its anhydrous chemical expression is counted (0~0.3) Na with the quality of oxide compound
2O (0.3~5) Al
2O
3(1.0~10) P
2O
5(0.7~15) M
xO
y(0~10) RE
2O
3(70~98) SiO
2, wherein, M is selected from one or both transition metal among Fe, Co, Ni, Cu, Zn, Mo or the Mn, and RE represents rare earth, x is the valency of oxygen, and y is the valency of transition metal, wherein when if the valency of transition metal is even number, x is 1, y be the transition metal compound valency divided by 2.
In the catalyzer provided by the present invention, said clay can be natural or synthetic, through or without various chemistry and or the various clays that are used as cracking catalyst carrier usually handled of physical method, as kaolin and halloysite etc.
In the catalyzer provided by the present invention, said inorganic oxide is selected from amorphous Si O
2Al
2O
3, Al
2O
3Or/and SiO
2
In the catalyzer provided by the present invention, said zeolite is made up of MFI structural zeolite and Y zeolite.
Said y-type zeolite prepares with various chemistry and/or physical method, for example hydrothermal method, method of chemical treatment (EDTA acidic treatment, ammonium silicofluoride aluminium-eliminating and silicon-replenishing method and SiCl
4Vapor phase process) or combine with chemical treatment method preparation of hydro-thermal, can contain or not contain rare earth; The y-type zeolite that wherein contains rare earth is Rare Earth Y (REY) or rare earth hydrogen Y (REHY).
Catalyzer provided by the invention is characterized in that phosphorous and transition metal M in the said MFI structural zeolite, and the quality in oxide compound is preferably (0~0.2) Na
2O (0.9~5) Al
2O
3(1.5~7) P
2O
5(0.9~10) M
xO
y(82~92) SiO
2Perhaps be (0~0.2) Na
2O (0.9~5) Al
2O
3(1.5~7) P
2O
5(0.9~10) M
xO
y(0.5~10) RE
2O
3(82~92) SiO
2
Transition metal M wherein has dehydrogenation functionality, is selected from one or both metals among Fe, Co, Ni, Cu, Zn, Mo or the Mn, one or both among preferred Fe, Co or the Ni, more preferably Fe and/or Ni.
Described MFI structural zeolite, its preparation process comprises ammonia exchange, phosphorus modification, metal-modified and calcination process step usually.
The exchange of described ammonia be with the na-pretreated zeolite that contains or do not contain rare earth of conventional crystallization gained with MFI structure according to zeolite: ammonia salt: H
2O=1: (0.1~1): the weight ratio of (5~10) is at room temperature to 100 ℃ 0.3~1 hour after-filtration of exchange down, and na-pretreated zeolite wherein is if adopt organic formwork agent synthetic words, at first removed template method.Described ammonium salt can be selected from one of ammonium chloride, ammonium sulfate or ammonium nitrate or their mixture for inorganic ammonium salt commonly used.
Described with the phosphorus modification and metal-modified be to adopt the mode of dipping or ion-exchange to carry out.
Wherein said dipping can adopt following three kinds of modes again:
A. the filter cake after the ammonia exchange and the P contained compound aqueous solution of calculated amount are evenly dried in room temperature to 95 a ℃ making beating, after roasting under 400~800 ℃ of conditions, ℃ mix, dry in room temperature to 95 with the compound water solution that contains transition metal M of calculated amount again.
B. the P contained compound aqueous solution of filter cake after the ammonia exchange and calculated amount is evenly dried in room temperature to 95 a ℃ making beating, ℃ mix oven dry with the compound water solution that contains transition metal M of calculated amount in room temperature to 95 again, wherein reversed order that also can the above-mentioned two kinds of solution of dipping.
C. the mixed aqueous solution of the P contained compound of the filter cake after the ammonia exchange and calculated amount and the compound of transition metal M ℃ is mixed afterwards in room temperature to 95 and dry.
Wherein said ion-exchange is: the P contained compound aqueous solution of filter cake after the ammonia exchange and calculated amount is evenly dried in room temperature to 95 a ℃ making beating, after roasting under 400~800 ℃ of conditions, again with the compound water solution that contains transition metal M of calculated amount by 1: after the solid-to-liquid ratio of (5~20) mixes, at 80~95 ℃, pH=4~7 time 2~3 hours after-filtration of stirring, but repeated exchanged repeatedly, and exchange back gained samples with water is washed repeatedly, and oven dry gets final product.
Described P contained compound is selected from one of phosphoric acid, aluminum phosphate, ammonium hydrogen phosphate, primary ammonium phosphate or ammonium phosphate or its mixture.The compound of described transition metal M is selected from their water-soluble salt, said water-soluble salt is selected from muriate, nitrate, vitriol or carbonate, for example ferric sulfate, ferrous sulfate, iron nitrate, iron(ic) chloride, iron protochloride, rose vitriol, Xiao Suangu, cobalt chloride, single nickel salt, nickelous nitrate or nickelous chloride.
Catalyzer provided by the invention, its preparation process is as follows: with the precursor of inorganic oxide, as pseudo-boehmite, aluminium colloidal sol, silicon sol or its mixture and silicon-aluminum sol or gel, mix by preset blending ratio with halloysite, and it is mixed with the slurries that solid content is 10~50 heavy % with decationized Y sieve water, stir, use the mineral acid example hydrochloric acid, nitric acid, phosphoric acid or sulfuric acid transfer to 2~4 with slurries PH, keep this pH value, add aluminium colloidal sol after leaving standstill aging 0~2 hour under 20~80 ℃, stirred 0.5~1.5 hour, the MFI structural zeolite and the y-type zeolite that add predetermined amount, homogeneous, spraying drying, the flush away free sodium ion, drying.
Contain two zeolite activity components in the catalyzer provided by the invention, a kind of zeolite is to have the zeolite of MFI structure through P and transition metal modified making, another kind of zeolite is to contain y-type zeolite an amount of rare earth or that do not contain rare earth, this catalyzer can strengthen the macromolecular cracking ability of heavy oil, improve reaction conversion ratio, higher C in the product
2 =~C
4 =Productive rate, particularly C
3 =Productive rate.
Embodiment
Following example will give further instruction to the present invention.
In each example and Comparative Examples, Na in the zeolite
2O, Fe
2O
3, NiO, Al
2O
3, SiO
2Content measure (referring to " petrochemical complex analytical procedure (RIPP experimental technique) ", volumes such as Yang Cuiding, Science Press, nineteen ninety publishes) with x-ray fluorescence method.
Example 1~9 illustrates the preparation process of the MFI structural zeolite of phosphorous and transition metal M.
Example 1
With 20gNH
4Cl is dissolved in the 1000g water, and (the Qilu Petrochemical catalyst plant is produced, SiO to add 100g (butt) crystallization product ZRP-1 zeolite in this solution
2/ Al
2O
3=30, content of rare earth RE
2O
3=4.0 heavy %), behind 90 ℃ of exchange 0.5h, filter filter cake; Add 4.0gH
3PO
4(concentration 85%) and 4.8gFe (NO
3)
3Be dissolved in the 90g water, dry with the filter cake hybrid infusion; The gained sample was 550 ℃ of calcination process 2 hours.Its elementary analytical chemistry consists of 0.1Na
2O4.9Al
2O
32.4P
2O
51.5Fe
2O
33.8RE
2O
387.3SiO
2
Example 2
With 50gNH
4Cl is dissolved in the 1000g water, adds 100g (butt) crystallization product ZRP-1 in this solution, 85 ℃ the exchange 0.5h after, filter filter cake; With 8.0gNH
4H
2PO
4Be dissolved in the 60g water, with filter cake hybrid infusion oven dry, through 550 ℃ of calcination process 2 hours; 's 5% Fe (NO with above-mentioned sample in 5: 1 ratio of solid-to-liquid ratio and concentration
3)
3Solution filters 80~90 ℃ of down exchanges 2 hours, exchanges several times again, until reaching aim parameter, again 550 ℃ of calcination process 2 hours.Elementary analytical chemistry consists of 0.03Na
2O4.7Al
2O
34.5P
2O
53.0Fe
2O
33.7RE
2O
384.1SiO
2
Example 3
With 20gNH
4Cl is dissolved in the 1000g water, and (the Qilu Petrochemical catalyst plant is produced, SiO to add 100g (butt) crystallization product ZRP-5 in this solution
2/ Al
2O
3=60), 90 ℃ the exchange 0.5h after, filter filter cake; Add 3.8gH
3PO
4(concentration 85%) and 34.2gFe (NO
3)
3Be dissolved in the 90g water, dry with the filter cake hybrid infusion; The gained sample was 550 ℃ of calcination process 2 hours.Elementary analytical chemistry consists of 0.1Na
2O2.4Al
2O
32.0P
2O
510Fe
2O
385.5SiO
2
Example 4
With 80gNH
4Cl is dissolved in the 1000g water, adds 100g (butt) crystallization product ZRP-5 molecular sieve in this solution, 85 ℃ the exchange 0.5h after, filter filter cake; With 8.9gNH
4H
2PO
4Be dissolved in the 60g water, with filter cake hybrid infusion, oven dry; With 5.2gFeSO
46H
2O is dissolved in the 90g water, with above-mentioned sample mix dipping, oven dry, again 600 ℃ of calcination process 2 hours.Elementary analytical chemistry consists of 0.1Na
2O2.6Al
2O
35.1P
2O
51.5Fe
2O
390.7SiO
2
Example 5
With 80gNH
4Cl is dissolved in the 1000g water, and (the Qilu Petrochemical catalyst plant is produced, SiO to add 100g (butt) crystallization product ZRP-5 molecular sieve in this solution
2/ Al
2O
3=70), 85 ℃ the exchange 0.5h after, filter filter cake; With 8.9gNH4H
2PO
4Be dissolved in the 60g water, with filter cake hybrid infusion, oven dry; With 3.5gFeSO
46H
2O is dissolved in the 90g water, with above-mentioned sample mix dipping, oven dry, again 600 ℃ of calcination process 2 hours.Elementary analytical chemistry consists of 0.1Na
2O2.2Al
2O
35.1P
2O
51.0Fe
2O
391.6SiO
2
Example 6
With 80gNH
4Cl is dissolved in the 1000g water, adds 100g (butt) crystallization product ZRP-5 in this solution, 85 ℃ the exchange 0.5h after, filter filter cake; With 9.0g (NH
4)
2HPO
4Be dissolved in the 60g water, dry with the filter cake hybrid infusion; Add 8.3gNi (NO again
3)
26H
2O is dissolved in the 90g water, with the oven dry of above-mentioned sample mix dipping; The gained sample was 600 ℃ of calcination process 2 hours.Elementary analytical chemistry consists of 0.1Na
2O2.6Al
2O
34.5P
2O
52.0NiO90.8SiO
2
Example 7
With 80gNH
4Cl is dissolved in the 1000g water, adds 100g (butt) crystallization product ZRP-1 in this solution, 85 ℃ the exchange 0.5h after, filter filter cake; With 8.4g (NH
4)
2HPO
4Be dissolved in the 60g water, dry with the filter cake hybrid infusion; Add 3.9gNi (NO again
3)
26H
2O is dissolved in the 90g water, with the oven dry of above-mentioned sample mix dipping; The gained sample was 600 ℃ of calcination process 2 hours.Elementary analytical chemistry consists of 0.1Na
2O4.9Al
2O
34.1P
2O
51.0NiO3.8RE
2O
386.1SiO
2
Example 8
With 80gNH
4Cl is dissolved in the 1000g water, adds 100g (butt) crystallization product ZRP-5 in this solution, 85 ℃ the exchange 0.5h after, filter filter cake; With 8.8g (NH
4)
2HPO
4Be dissolved in the 60g water, dry with the filter cake hybrid infusion; Add 4.2gNi (NO again
3)
26H
2O and 3.3gFe (NO
3)
3Be dissolved in the 90g water, with the oven dry of above-mentioned sample mix dipping; The gained sample was 600 ℃ of calcination process 2 hours.Elementary analytical chemistry consists of 0.08Na
2O2.6Al
2O
34.4P
2O
51.0NiO1.0Fe
2O
390.9SiO
2
Example 9
With 80gNH
4Cl is dissolved in the 1000g water, adds 100g (butt) crystallization product ZRP-5 in this solution, 85 ℃ the exchange 0.5h after, filter filter cake; With 8.9gNH
4H
2PO
4Be dissolved in the 60g water, with filter cake hybrid infusion, oven dry; With 10.6gFeSO
46H
2O is dissolved in the 90g water, with above-mentioned sample mix dipping, oven dry, and again 600 ℃ of calcination process 2 hours, molecular sieve promptly provided by the invention.Elementary analytical chemistry consists of 0.07Na
2O2.5Al
2O
35.0P
2O
53.0Fe
2O
389.4SiO
2
Example 10
With 250Kg decationized Y sieve water with 75.4Kg halloysite (Suzhou china clay company Industrial products, solid content 71.6m%) making beating, add 54.8Kg pseudo-boehmite (Shandong Aluminum Plant's Industrial products, solid content 63m%) again, its PH is transferred to 2~4 with hydrochloric acid, stir, left standstill under 60~70 ℃ aging 1 hour, keeping PH is 2~4, cools the temperature to below 60 ℃, add 41.5Kg aluminium colloidal sol (Qilu Petrochemical company catalyst plant product, Al
2O
3Content is 21.7m%), stirred 40 minutes, (Qilu Petrochemical catalyst plant Industrial products, lattice constant is 2.445~2.448nm, contains RE for the MFI structural zeolite (butt is 22.5Kg) of adding example 1 preparation and DASY zeolite
2O
3Be 2.0m%, butt is 30Kg) mix slurry 165Kg, stir, spray drying forming, with ammonium dihydrogen phosphate (phosphorus content is 1m%) washing, the flush away Na that dissociates
+, be drying to obtain catalyst sample A.
Example 11
With 250Kg decationized Y sieve water the 75.4Kg halloysite is pulled an oar, add the 54.8Kg pseudo-boehmite again, with hydrochloric acid its PH is transferred to 2~4, stir, under 60~70 ℃, left standstill aging 1 hour, keeping PH is 2~4, cool the temperature to below 60 ℃, add 41.5Kg aluminium colloidal sol, stirred 40 minutes, add the MFI structural zeolite (butt is 22.5Kg) of example 1 preparation and the mix slurry 165Kg of DASY zeolite, stir, spray drying forming, with ammonium dihydrogen phosphate (phosphorus content is 1m%) washing, the flush away Na that dissociates
+, be drying to obtain catalyst sample B.
Example 12
With 250 Kg decationized Y sieve water the 75.4Kg halloysite is pulled an oar, add the 54.8Kg pseudo-boehmite again, with hydrochloric acid its PH is transferred to 2~4, stir, left standstill under 60~70 ℃ aging 1 hour, keeping PH is 2~4, cools the temperature to below 60 ℃, add 41.5Kg aluminium colloidal sol, stirred 40 minutes.Add the MFI structural zeolite (butt is 22.5Kg) and DASY molecular sieve (butt is 30Kg) mix slurry 165Kg of example 7 preparations, stir, spray drying forming washs with ammonium dihydrogen phosphate (phosphorus content is 1m%), the flush away Na that dissociates
+, be drying to obtain catalyst sample C.
Comparative Examples 1
This Comparative Examples is the contrast medium of describing according to CN1117518A.
With 250Kg decationized Y sieve water the 75.4Kg halloysite is pulled an oar, add the 54.8Kg pseudo-boehmite again, with hydrochloric acid its PH is transferred to 2~4, stir, left standstill under 60~70 ℃ aging 1 hour, keeping PH is 2~4, cools the temperature to below 60 ℃, add 41.5Kg aluminium colloidal sol, stirred 40 minutes.Add ZRP-1 and DASY zeolite mixture slurries 165Kg, stir, spray drying forming washs with ammonium dihydrogen phosphate (phosphorus content is 1m%), the flush away Na that dissociates
+, be drying to obtain Comparative Examples agent DB-1.
Table 1 is listed the composition of catalyst A, B, C and DB-1.
On the small fixed flowing bed device, be that raw material is estimated catalyst sample with 30m% residual oil+70m% wax oil (character sees Table 2), temperature of reaction is 515 ℃, and agent-oil ratio is 8, and weight space velocity is 10h
-1Catalyst sample is in advance through 790 ℃, and 100% steam-treated 14 hours, loading amount are 180 grams, and evaluation result sees Table 3.
Table 1
Catalyzer | ????A | ????B | ????C | ????DB-1 |
Form heavy % kaolin pseudo-boehmite aluminium colloidal sol MFI structural zeolite DASY | ????36 ????23 ????6 ????15 ????20 | ????36 ????23 ????6 ????15 ????20 | ????36 ????23 ????6 ????15 ????20 | ????36 ????23 ????6 ????15 ????20 |
??Fe 2O 3 | ????1.5 | ????3.0 | ||
??NiO | ????1.0 |
Table 2
Density (20 ℃), g/cm 3Carbon residue, heavy % alkali nitrogen, ppm boiling range, ℃ characterization factor | ????0.8658 ????2.47 ????630 ????>293 ????12.3 |
Table 3
Catalyzer | ????A | ????B | ????C | ????DB-1 |
Transformation efficiency, the m% product distributes, m% dry gas liquefied gas gasoline (C 5~221 ℃) coke is wherein for diesel oil (221~330 ℃) heavy oil (>330 ℃), gas yield, m% H 2?C 2 =?C 3 =?C 4 =?C 2 =+C 3 =+C 4 = | ????85.35 ????4.6 ????41.93 ????32.41 ????9.04 ????5.59 ????6.41 ????0.1 ????3.06 ????16.94 ????10.82 ????30.82 | ????85.63 ????4.72 ????42.13 ????32.49 ????8.91 ????5.44 ????6.3 ????0.15 ????3.06 ????17.03 ????11.43 ????31.52 | ????85.32 ????4.36 ????41.13 ????33.63 ????9.14 ????5.51 ????6.22 ????0.11 ????2.89 ????16.88 ????11.16 ????30.93 | ????85.27 ????4.12 ????39.71 ????35.1 ????9.18 ????5.53 ????6.34 ????0.11 ????2.63 ????15.63 ????11.09 ????29.35 |
In the gas, C 3 =Concentration, m% olefinicity, m% | ????36.4 ????66.22 | ????36.33 ????67.26 | ????37.1 ????67.97 | ????35.65 ????66.93 |
As shown in Table 3, when MFI structural zeolite content was identical in the catalyzer, catalyst A provided by the invention and B and DB-1 had close transformation efficiency, and C
3 =Productive rate is than high about 1.5 centivals of DB-1, C
2 =~C
4 =Productive rate than high about 1.5~2 centivals of DB-1.As seen after MFI structural zeolite is wherein handled through the iron modification, help increasing C
2 =And C
3 =Productive rate, and do not influence product selectivity.
Catalyzer C is than the C of DB-1
3 =Productive rate has improved 1 centival, C
2 =~C
4 =High 1.5 centivals of productive rate, C in liquefied gas yield and the gas
3 =Concentration all improved about 1.5 centivals, and hydrogen and coke yield do not change basically.Illustrate that a large amount of dehydrogenation reactions does not take place the catalyzer that contains the MFI structural zeolite after the nickel modification is handled, but increased the cracking to gasoline component, this helps increasing C
3 =Productive rate.
Example 13
With 250Kg decationized Y sieve water the 75.4Kg halloysite is pulled an oar, add the 54.8Kg pseudo-boehmite again, with hydrochloric acid its PH is transferred to 2~4, stir, under 60~70 ℃, left standstill aging 1 hour, keeping PH is 2~4, cools the temperature to below 60 ℃, adds 41.5Kg aluminium colloidal sol, stirred 40 minutes, add the MFI structural zeolite (butt is 22.5Kg) of example 5 preparations and the mix slurry 165Kg of USY zeolite (Qilu Petrochemical Zhou village catalyst plant Industrial products, lattice constant are 2.445~2.448nm, and butt is 30Kg), stir, spray drying forming, with ammonium dihydrogen phosphate (phosphorus content is 1m%) washing, the flush away Na that dissociates
+, be drying to obtain catalyst sample D.
Example 14
With 250Kg decationized Y sieve water the 75.4Kg halloysite is pulled an oar, add the 54.8Kg pseudo-boehmite again, with hydrochloric acid its PH is transferred to 2~4, stir, under 60~70 ℃, left standstill aging 1 hour, keeping PH is 2~4, cool the temperature to below 60 ℃, add 41.5Kg aluminium colloidal sol, stirred 40 minutes, (Qilu Petrochemical Zhou village catalyst plant Industrial products contain RE for the MFI structural zeolite (butt is 22.5Kg) of adding example 5 preparations and REHY zeolite
2O
3Be 7.0%, butt is 30Kg) mix slurry 165Kg, stir, spray drying forming, with ammonium dihydrogen phosphate (phosphorus content is 1m%) washing, the flush away Na that dissociates
+, be drying to obtain catalyst sample E.
Comparative Examples 2
Be mixed into active ingredient with ZRP-5 zeolite and USY zeolite, the preparation method according to Comparative Examples 1 prepares contrast medium, numbering DB-2.
With 30m% residual oil+70m% wax oil is raw material, on the small fixed flowing bed device above-mentioned catalyst sample D, E and contrast medium DB-2 is estimated, and temperature of reaction is 505 ℃, and agent-oil ratio is 10.Evaluation result is listed in table 5.
Table 4
Catalyzer | ????D | ????E | ????DB-2 |
Form heavy % kaolin pseudo-boehmite aluminium colloidal sol MFI structural zeolite Y zeolite REHY USY | ????36 ????23 ????6 ????20 ????15 | ????36 ????23 ????6 ????20 ????15 | ????36 ????23 ????6 ????20 ????15 |
??Fe 2O 3 | ????1.0 | ????1.0 |
Table 5
Catalyzer | ????D | ????E | ????DB-2 |
Transformation efficiency, the m% product distributes, m% dry gas liquefied gas gasoline (C 5~221 ℃) coke is wherein for diesel oil (221~330 ℃) heavy oil (>330 ℃), gas yield, m% H 2??C 2 =??C 3 =??C 4 =??C 2 =+C 3 =+C 4 = | ????85.55 ????3.11 ????39.67 ????36.46 ????9.04 ????5.57 ????6.31 ????0.11 ????1.89 ????17.84 ????10.99 ????30.72 | ????85.68 ????3.18 ????38.76 ????37.52 ????8.98 ????5.34 ????6.22 ????0.11 ????1.68 ????15.78 ????10.63 ????28.09 | ????85.04 ????2.98 ????37.56 ????38.84 ????9.44 ????5.52 ????5.67 ????0.08 ????1.6 ????15.11 ????10.89 ????27.60 |
As can be seen from Table 5, the zeolite with MFI structure through P and Fe modification processing can improve C
3 =Productive rate.
Example 15
With 250Kg decationized Y sieve water the 75.4Kg halloysite is pulled an oar, add the 54.8Kg pseudo-boehmite again, with hydrochloric acid its PH is transferred to 2~4, stir, under 60~70 ℃, left standstill aging 1 hour, keeping PH is 2~4, cool the temperature to below 60 ℃, add 41.5Kg aluminium colloidal sol, stirred 40 minutes, add the MFI structural zeolite (butt is 22.5kg) of example 4 preparations and the mix slurry 165Kg of DASY zeolite (butt is 30kg), stir, spray drying forming, with ammonium dihydrogen phosphate (phosphorus content is 1m%) washing, the flush away Na that dissociates
+, be drying to obtain catalyst sample F.
Example 16
Preparation process is identical with example 13, and difference is to adopt the MFI structural zeolite of example 9 preparations.Catalyzer is numbered G.
Comparative Examples 3
Preparation process is identical with Comparative Examples 2, and difference is that Y zeolite is DASY.Contrast medium is numbered DB-3.
Form and list in table 6
Table 6
Catalyzer | ????F | ????G | ????DB-3 |
Form heavy % kaolin pseudo-boehmite aluminium colloidal sol MFI structural zeolite (not containing rare earth) Y zeolite (DASY) | ????36 ????23 ????6 ????15 ????20 | ????36 ????23 ????6 ????15 ????20 | ????36 ????23 ????6 ????15 ????20 |
??Fe 2O 3 | ????1.5 | ????3.0 |
With 30m% residual oil+70m% wax oil is raw material, on the small fixed flowing bed device above-mentioned catalyst sample F, G and DB-3 is estimated, and temperature of reaction is 525 ℃, and agent-oil ratio is 6, and weight space velocity is 10h
-1Catalyst sample is in advance through 790 ℃, and 100% steam-treated 14 hours, loading amount are 180 grams.The results are shown in table 7
Table 7
Catalyzer | ????F | ????G | ????DB-3 |
Transformation efficiency, the m% product distributes, m% dry gas liquefied gas gasoline (C 5~221 ℃) coke is wherein for diesel oil (221~330 ℃) heavy oil (>330 ℃), gas yield, m% H 2??C 2 =??C 3 =??C 4 =??C 2 =+C 3 =+C 4 = | ????86.41 ????3.31 ????39.45 ????37.21 ????8.47 ????5.12 ????6.44 ????0.14 ????1.8 ????16.61 ????11.55 ????29.96 | ????85.88 ????3.33 ????38.66 ????37.44 ????8.8 ????5.32 ????6.44 ????0.2 ????1.73 ????16.1 ????11.61 ????29.44 | ????83.69 ????3.01 ????37.76 ????37.04 ????9.95 ????6.36 ????5.87 ????0.08 ????1.73 ????15.6 ????11.04 ????28.37 |
As can be seen from Table 7, catalyzer has improved about 2.2~2.7 centivals than the reaction conversion ratio of contrast medium DB-3, and the scission reaction that helps raw material is described.C in the catalyzer F product
3 =Productive rate is than high 1 centival of DB-3.Catalyzer G is than the C of contrast medium DB-3
2 =~C
4 =Productive rate has improved about 1 centival.
Example 17
With the making beating of 94.3Kg halloysite, add the 71.5Kg pseudo-boehmite with 280Kg decationized Y sieve water again, with hydrochloric acid its PH is transferred to 2~4, stir, left standstill under 60~70 ℃ aging 1 hour, keeping PH is 2~4, cools the temperature to below 60 ℃.Add the zeolite with MFI structure and the DASY molecular sieve mixture slurries 118Kg of example 1 preparation, the zeolite butt that wherein has the MFI structure is 15kg; The DASY butt is 22.5Kg.Stir spray drying forming, the flush away Na that dissociates
+, be drying to obtain catalyst sample H.
Comparative Examples 4
Press described in the example 2 of CN1117518, the preparation comparative catalyst, note is made DB-4.Form and see Table 8.
Table 8
Catalyzer | ????H | ????DB-4 |
Form heavy % kaolin pseudo-boehmite MFI structural zeolite DASY | ????45 ????30 ????10 ????15 | ????45 ????30 ????10 ????15 |
??Fe 2O 3 | ????1.5 |
With 30% residual oil+70% wax oil is raw material, on the small fixed flowing bed device sample H and DB-4 is estimated, and temperature of reaction is 530 ℃, and agent-oil ratio is 6, and air speed is 8h
-1The results are shown in table 9.
Table 9
Catalyzer | ????H | ????DB-4 |
Transformation efficiency, the m% product distributes, m% dry gas liquefied gas gasoline (C 5~221 ℃) coke is wherein for diesel oil (221~330 ℃) heavy oil (>330 ℃), gas yield, m% H 2??C 2 =??C 3 =??C 4 =??C 2 =+C 3 =+C 4 = | ????84.58 ????3.79 ????40.01 ????34.87 ????9.65 ????5.77 ????5.91 ????0.12 ????2.35 ????16.77 ????11.29 ????30.41 | ????82.54 ????2.68 ????36.46 ????37.73 ????10.58 ????6.88 ????5.67 ????0.08 ????1.5 ????15.21 ????10.59 ????27.3 |
As can be seen from Table 9, catalyzer H of the present invention compares with contrast medium DB-4, has higher C
2 =~C
4 =Productive rate particularly has higher C
3 =Productive rate.
Example 18
In the aluminium colloidal sol of 218Kg, add the 147Kg halloysite, stirs and added MFI zeolite and the 54Kg decationized Y sieve water that 36Kg (butt) example 5 prepares in 1.5 hours again, homogeneous, spray drying forming, the flush away Na that dissociates
+, be drying to obtain catalyst sample I.
Comparative Examples 5
According to the preparation comparative catalyst described in the example 1 of CN1093101A, note is made DB-5.
The composition of catalyst sample I and DB-5 is listed in table 10.
Table 10
Catalyzer | ????I | ????DB-5 |
Form heavy % kaolin aluminium colloidal sol MFI structural zeolite | ????57.4 ????24.6 ????18 | ????57.4 ????24.6 ????18 |
??Fe 2O 3 | ????1.0 |
With intermediate base wax oil (character sees Table 11) is raw material, on the small fixed flowing bed device sample I and DB-5 is estimated.Reaction conditions is: 580 ℃ of temperature of reaction, agent-oil ratio are 5, and air speed is 1h
-1,, through 760 ℃ and 100% steam treatment 6 hours, its loading amount was 180 grams to catalyst sample in advance.Evaluation result is listed in table 12.
Table 11
Density (20 ℃), g/cm 3Carbon residue, heavy % alkali nitrogen, ppm boiling range, ℃ characterization factor | ????0.8808 ????0.1 ????537 ????256~545 ????12.0 |
Table 12
Catalyzer | ????I | ????DB-5 |
Transformation efficiency, the m% product distributes, m% reacted gas gasoline (C 5~221 ℃) coke is wherein for diesel oil (221~330 ℃) heavy oil (>330 ℃), olefins yield, m% C 2 =??C 3 =??C 4 =??C 2 =+C 3 =+C 4 = | ????76.95 ????51.3 ????20.31 ????8.02 ????15.03 ????5.34 ????7.05 ????19.94 ????14.87 ????41.86 | ????75.61 ????49.48 ????21.09 ????8.29 ????16.1 ????5.04 ????6.31 ????18.91 ????14.29 ????39.51 |
As can be seen from Table 12, under 580 ℃ temperature of reaction, through the zeolite with MFI structure of iron modification, can be than the C of contrast medium DB-5
3 =Productive rate improves a centival.
Example 19
Preparation process is with example 1, and difference is to adopt the MFI zeolite of example 6 preparations, and catalyzer is numbered J.Form and see Table 13.
Example 20
Preparation process is with example 1, and difference is to adopt the MFI zeolite of example 8 preparations, and catalyzer is numbered K.Form and see Table 13.
Example 21
Preparation process is with example 1, and difference is to adopt the MFI zeolite of example 3 preparations, and catalyzer is numbered L.Form and see Table 13.
Table 13
Catalyzer | ????J | ????K | ????L |
Form heavy % kaolin pseudo-boehmite aluminium colloidal sol MFI structural zeolite Y zeolite (DASY) | ????36 ????23 ????6 ????15 ????20 | ????36 ????23 ????6 ????15 ????20 | ????36 ????23 ????6 ????15 ????20 |
??Fe 2O 3 | ????1.0 | ????10 | |
??NiO | ????2.0 | ????1.0 |
On the small fixed flowing bed device above-mentioned sample is estimated, appreciation condition is with example 15, and evaluation result is listed in table 14.
Table 14
Catalyzer | ????J | ????K | ????L | ????DB-3 |
Transformation efficiency, the m% product distributes, m% dry gas liquefied gas gasoline (C 5~221 ℃) coke is wherein for diesel oil (221~330 ℃) heavy oil (>330 ℃), gas yield, m% H 2??C 2 =??C 3 =??C 4 =??C 2 =+C 3 =+C 4 = | ????86.24 ????3.38 ????39.53 ????37.18 ????8.43 ????5.33 ????6.15 ????0.14 ????1.85 ????16.41 ????11.46 ????29.72 | ????86.00 ????3.46 ????39.75 ????36.56 ????8.53 ????5.47 ????6.23 ????0.24 ????1.91 ????16.75 ????11.78 ????30.44 | ????84.1 ????4.29 ????37.17 ????36.27 ????8.7 ????7.2 ????6.37 ????0.35 ????2.0 ????15.92 ????11.23 ????29.15 | ????83.69 ????3.01 ????37.76 ????37.04 ????9.95 ????6.36 ????5.87 ????0.08 ????1.73 ????15.6 ????11.04 ????28.37 |
As can be seen from Table 14, catalyzer provided by the invention contains that (content is the zeolite of the MFI structure handled of the modification of 1m%~10m%), can improve C through phosphorus and a kind of (or two kinds) transition metal
2 =~C
4 =Productive rate.
Claims (10)
1, the catalyzer of low-carbon alkene is produced in a kind of petroleum hydrocarbon cracking, have in the catalyst weight is clay, 5~99% inorganic oxide and 1~50% the zeolite of benchmark 0~70%, the y-type zeolite of the zeolite of the MFI structure that wherein said zeolite is 25~100 heavy % and 0~75 heavy %, it is characterized in that the phosphorous and transition metal M of said MFI structural zeolite, its anhydrous chemical expression is counted (0~0.3) Na with the quality of oxide compound
2O (0.3~5) Al
2O
3(1.0~10) P
2O
5(0.7~15) M
xO
y(0~10) RE
2O
3(70~98) SiO
2, wherein, M is selected from one or both transition metal among Fe, Co, Ni, Cu, Zn, Mo or the Mn, and x is the valency of oxygen, and y is the valency of transition metal.
2, according to the said catalyzer of claim 1, it is characterized in that said clay is natural or synthetic, through or the various clays that are used as cracking catalyst carrier usually handled without various chemistry and/or physical method.
3,, it is characterized in that said clay is kaolin or halloysite according to the said catalyzer of claim 1.
4,, it is characterized in that said inorganic oxide is selected from amorphous Si O according to the said catalyzer of claim 1
2Al
2O
3, Al
2O
3And/or SiO
2
5, according to the said catalyzer of claim 1, it is characterized in that the anhydrous chemical expression of said MFI structural zeolite, count (0~0.2) Na with the quality of oxide compound
2O (0.9~5) Al
2O
3(1.5~7) P
2O
5(0.9~10) M
xO
y(0.5~10) RE
2O
3(82~92) SiO
2
6, according to the said catalyzer of claim 1, it is characterized in that the anhydrous chemical expression of said MFI structural zeolite, count (0~0.2) Na with the quality of oxide compound
2O (0.9~5) Al
2O
3(1.5~7) P
2O
5(0.9~10) M
xO
y(82~92) SiO
2
7,, it is characterized in that M is selected from one or both among Fe, Co or the Ni according to the said catalyzer of claim 1.
8,, it is characterized in that M is Fe and/or Ni according to the said catalyzer of claim 7.
9,, it is characterized in that said y-type zeolite contains or do not contain rare earth according to the said catalyzer of claim 1.
10,, it is characterized in that the said rare earth exchanged Y zeolite that contains is REY or REHY according to the said catalyzer of claim 9.