CN1472161A - 一种水泥混凝土用表面增强密封剂 - Google Patents
一种水泥混凝土用表面增强密封剂 Download PDFInfo
- Publication number
- CN1472161A CN1472161A CNA031167942A CN03116794A CN1472161A CN 1472161 A CN1472161 A CN 1472161A CN A031167942 A CNA031167942 A CN A031167942A CN 03116794 A CN03116794 A CN 03116794A CN 1472161 A CN1472161 A CN 1472161A
- Authority
- CN
- China
- Prior art keywords
- concrete
- water
- cement concrete
- cement
- sealing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明为一种水泥混凝土用表面增强密封剂,由氟硅酸镁、硅氧烷乳液、硫酸铝、水按一定的重量配比组成。使用该材料可以提高混凝土表面的强度、抗钢筋锈蚀、抗碳化、耐磨性和防水性。该增强密封剂可广泛用于桥梁、隧道、高速公路、建筑物等混凝土建筑物或构筑物。
Description
技术领域
本发明涉及一种水泥混凝土用表面增强密封剂,可以提高混凝土表面的强度、抗钢筋锈蚀、抗碳化、耐磨性与防水能力。
技术背景
结构构筑物在服役过程中,受到周围环境的物理、化学、生物作用,如微生物侵蚀、镁盐、酸雨、二氧化碳、氯盐侵蚀等,混凝土内的某些成分发生反应、溶解、膨胀,从而造成混凝土结构的劣化、破坏。
综合混凝土劣化机理来看,混凝土劣化过程(物理、化学和生物的)和钢筋或预应力钢筋混凝土发生劣化的主要原因有冻融循环、碱骨料反应、硫酸盐侵蚀、收缩开裂和钢筋锈蚀等。对其任何一种劣化而言,膨胀和开裂的原因都与水有关,同时水也是侵蚀性介质(如氯盐、硫酸盐等)迁移进入混凝土内的载体。水既是破坏物质的传递介质,又是破坏发生的必要条件和许多失效机理与模型建立的基础。综合分析混凝土结构各种劣化机理可知,几乎所有影响混凝土结构耐久性的化学和物理过程都涉及两个主要的影响因素,即水及其在混凝土孔隙和裂缝中的迁移。因此,加强对混凝土进行有效的保护措施以提高混凝土结构的密实性,降低水渗透性,对提高混凝土的使用寿命,保证混凝土安全性具有重量的现实意义。研制一种能提高混凝土表面强度、密实度与防水性的表面增强密封剂也十分迫切。
发明内容
本发明的目的在于提供一种可以提高混凝土表面的强度、抗钢筋锈蚀、抗碳化和防水能力的水泥混凝土表面用增强密封剂。
本发明提出的水泥混凝土表面用增强密封剂,由氟硅酸镁、硅氧烷乳液、硫酸铝、水组成,各组分重量百分比为:
氟硅酸镁 100
硅氧烷乳液(固含量) 12-200
硫酸铝 0-160
水 100-700
各组分较佳重量比例为:
氟硅酸镁 100
硅氧烷乳液(固含量) 40-60
硫酸铝 15-30
水 200-250。
本发明是一种水泥混凝土用水性硅酸盐类复合表面处理剂。它既具有较好的增强、密实作用,又有防水密封作用。
当本发明应用在水泥混凝土表面时,氟硅酸镁能渗入硬化水泥混凝土表面孔隙和微裂缝中后,与水泥水化产物氢氧化钙发生反应,生成二氧化硅凝胶与氟化物,填充混凝土表面以及内部毛细孔隙,减少水泥混凝土表面的原生缺陷,改善表层的孔结构,使水泥混凝土表面强度提高、耐磨性比未处理前提高一倍以上。同时组分中低聚合度的硅氧烷也会渗透到混凝土内部而水解或与水泥水化产物反应形成憎水性薄膜或产物,具有较好的憎水、防水效果。
本发明是一种白色乳液,会产生化学反应、水溶性的封堵剂,它可以渗入混凝土、重质混凝土砖、水泥砂浆、石膏、洗石子、磨石子及任何砂、石子、水泥之混合物中,并提供永久保护与增强作用。可以广泛用于桥梁、隧道、高速公路、建筑物等混凝土表面的增强和密封。
本发明制备容易控制,首先将一定量的氟硅酸镁溶解在水中,然后与规定比例的硅氧烷乳液进行混合,得到匀质的白色液体即可。
本发明的独特优点有:
(1)具有较高的增强性能,因为本发明配方原料成份能与水泥反应生产产物,紧密结合一起,增加混凝土面之密度、强度及硬度,这硬化的过程可防止水泥地面不够密实而产生的破坏。
(2)具有较好的填充、密实作用,本发明深入渗透至混凝土表面5mm,产生一种锁住混凝土内部空隙之化学反应,对各种形式之混凝土表面提供深远永久的封堵。形成一个坚强无孔洞的实体表面层;
(3)具有较好的防水、密封作用,本发明配方中硅氧烷会渗透到混凝土内部而水解或与水泥水化产物反应形成憎水性薄膜或产物,具有较好的憎水、防水效果;
(4)具有较高的抗环境侵蚀能力,尤其可提高抗碳化、抗钢筋锈蚀和粘结能力。由于消除表面不利结合之混凝土盐类和杂质,且表面增强与密实,使得混凝土二氧化碳的渗透性大大降低;
(5)具有较好的透气性,经本发明处理后的密封剂,既可阻止水分子的渗入,又可以把混凝土中的水蒸气透过皮肤似的涂膜而透出。使封闭在混凝土内的湿气可以及时透出;
(6)长效性效果:只须使用本发明一次,水泥混凝土表面便永久具有良好的增强、高耐久性、防水与密封性。
具体实施方式
本发明水泥混凝土用表面增强密封剂由氟硅酸镁、硅氧烷乳液、硫酸铝、水组成,尤其组分之间的相互促进作用,使得性能得到充分体现。在具体实施过程中,可优先考虑以下方案。
实施例1
水泥混凝土表面用增强密封剂按氟硅酸镁25%(重量百分比,下同)、硅氧烷乳液12%、水63%的比例配制而成,产品具有良好的增强、密实、防水与密封性能,可以广泛用于各类建筑物、桥梁等各类混凝土的表面保护。
实施例2
水泥混凝土表面用增强密封剂按氟硅酸镁25%、硅氧烷乳液12%、硫酸铝5%、水58%的比例配制而成,产品不仅具有较好的防水、密封性能,更具有高效的增强密实作用,可以广泛用于各类普通混凝土、高孔隙率混凝土、或表面不密实的混凝土的表面保护,特别适合于贫混凝土的表面防护。
实施例3
水泥混凝土表面用增强密封剂按氟硅酸镁22%、硅氧烷乳液20%、硫酸铝4%、水54%的比例配制而成,产品不仅具有良好的增强、密实作用,还具有非常优良的防水、密封性能,特别适合于浪尖区、海潮区等受到水气反复侵蚀的混凝土结构的表面保护。
Claims (2)
1、一种水泥混凝土用表面增强密封剂,其特征在于由氟硅酸镁、硅氧烷乳液、硫酸铝、水组成,各组分重量百分比为:
氟硅酸镁 100
硅氧烷乳液(固含量) 12-200
硫酸铝 0-160
水 100-700
2、根据权利要求1所述的表面增强密封剂,其特征在于各组分的重量比为:
氟硅酸镁 100
硅氧烷乳液(固含量) 40-60
硫酸铝 15-30
水 200-250。