CN1450018A - 环保型透水砖 - Google Patents

环保型透水砖 Download PDF

Info

Publication number
CN1450018A
CN1450018A CN 03126168 CN03126168A CN1450018A CN 1450018 A CN1450018 A CN 1450018A CN 03126168 CN03126168 CN 03126168 CN 03126168 A CN03126168 A CN 03126168A CN 1450018 A CN1450018 A CN 1450018A
Authority
CN
China
Prior art keywords
permeable brick
bauxitic clay
environment
particulate material
granularity
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 03126168
Other languages
English (en)
Other versions
CN1169741C (zh
Inventor
曹正茂
曹旭东
曹东辉
方春红
Original Assignee
曹正茂
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 曹正茂 filed Critical 曹正茂
Priority to CNB03126168XA priority Critical patent/CN1169741C/zh
Publication of CN1450018A publication Critical patent/CN1450018A/zh
Application granted granted Critical
Publication of CN1169741C publication Critical patent/CN1169741C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

一种环保型透水砖，其特征在于：各组份的重量份数比如下：粒度为6－35目的铝矾土颗粒料75％－85％，250－300目的粘土细粉7％－10％，滑石粉3％－6％，膨润土4％－8％。由于本发明的透水砖是采用6－35目的铝矾土颗粒料为主，经高温烧制而成，这就使得本发明的产品除具有高强度、高硬度、承载能力强和防滑、抗冻、吸光的特点，更主要的是它还具有良好的透水性能(经实测，其透水速率可达21mm/s)。即，使用本发明的地面砖不仅可解决因路面积水影响行人行走的问题，还可很好解决城市地下水源的补充问题，为调节城市环境和市区绿化植物的生长提供了有利条件。

Description

环保型透水砖
(一)技术领域
本发明涉及一种用于铺设人行道的地面砖，特别涉及一种环保型透水砖。
(二)背景技术
目前城市人行道板的路面硬化，多是采用铺设大理石、釉面砖、水泥砖的方法来实现。采用上述材料铺设出的路面虽具有整洁美观和防尘的作用，但也存在一些不足：
1、由于其透水性极差，直接阻断了雨水的渗透，其结果是导致城市地下水源得不到补充，加重了城市的干旱现象；
2、路面阳光的反射极大的增加了城市的热岛效应；
3、对市区的环保、植保极为有害，直接影响到花草树木的生长。
(三)发明内容
本发明的目的就在于克服上述现有技术中的不足之处而提供一种具有良好透水性能、且不反射光线的环保型透水砖。
本发明的目的可通过以下措施来实现：
本环保型透水砖的各组份重量份数比如下：粒度为6-35目的铝矾土颗粒料75％-85％，250-300目的粘土细粉7％-10％，滑石粉3％-6％，膨润土4％-8％。
本发明中所述粒度为6-35目的铝矾土颗粒料，是将铝矾土直接经破碎机破碎后，再通过振动筛筛选而成；它是用来生产地面砖的主要原料。
本发明中所述的粒度为6-35目的铝矾土颗粒料，是由250-300目的铝矾土粉90％-96％加入4％-8％色彩染料添加剂，经混合、成型、烘干、煅烧后，再破碎而成，它是用来生产彩色地面砖的辅料；所述色彩添加剂的具体颜色可根据用户需求来选择；所述铝矾土含AI2O370％-80％。
由于本发明的透水砖是采用6-35目的铝矾土颗粒料为主，经高温烧制而成，这就使得本发明的产品除具有高强度、高硬度、承载能力强和防滑、抗冻、吸光的特点，更主要的是它还具有良好的透水性能(经实测，其透水速率可达21mm/s)。即，使用本发明的地面砖不仅可解决因路面积水影响行人行走的问题，还可很好解决城市地下水源的补充问题，调节城市环境，为市区绿化植物的生长提供有利条件。
(四)具体实施方式
本发明以下将结合实施例作进一步详述：
实施例1：
a、按重量份数比取粒度为15目的铝矾土颗粒料80％(将含AI2O370％-80％的铝矾土经破碎机、对辊机破碎后，再通过振动筛筛选而成)、250-300目的粘土细粉7％、滑石粉6％、膨润土7％，加入上述总重量5％-8％的水进行充分的搅拌，时间在30分钟左右；
b、将搅拌好的混合料放入模型中在500-800吨的压力条件下进行振压成型，时间控制在10-15秒；
c、把成形后的砖坯送入烘干房中进行烘干：
d、将烘干后的砖坯进行装窑煅烧，温度控制在1250-1280℃之间，保持100-120分钟即可。
本实施例所生产出的产品为不带色彩的普通地面砖。
实施例2：
a、按重量份数比取粒度为300目的铝矾土粉90％-96％加入4％-8％草绿色染料添加剂，加入上述总重量4％-8％的水进行充分的搅拌，经混合后入模成型，并按传统工艺进行烘干、煅烧后，再破碎制成20目左右的草绿色铝矾土颗粒料；
b、按重量份数比取草绿色铝矾土颗粒料80％、250-300目的粘土细粉7％、滑石粉6％、膨润土7％，加入上述总重量5％-8％的水进行充分的搅拌，时间在30分钟左右；
c、按重量份数比取粒度为15目的铝矾土颗粒料80％(将含AI2O370％-80％的铝矾土经破碎机、对辊机破碎后，再通过振动筛筛选而成)、250-300目的粘土细粉7％、滑石粉6％、膨润土7％，加入上述总重量5％-8％的水进行充分的搅拌，时间在30分钟左右；
d、按重量份数比取70％的c放入模型的下部，再取30％的b以覆盖在c上方的方式放入模型中，在500-800吨的压力条件下进行振压成型，时间控制在10-15秒；
e、把成形后的砖坯送入烘干房中进行烘干：
f、将烘干后的砖坯进行装窑煅烧，温度控制在1250-1280℃之间，保持100-120分钟即可。
本实施例所生产出的产品为彩色地面砖。

Claims (4)

1、一种环保型透水砖，其特征在于：各组份的重量份数比如下：粒度为6-35目的铝矾土颗粒料75％-85％，250-300目的粘土细粉7％-10％，滑石粉3％-6％，膨润土4％-8％。
2、根据权利要求1所述的环保型透水砖，其特征在于：所述粒度为6-35目的铝矾土颗粒料，是将铝矾土直接经破碎机破碎后，再通过振动筛筛选而成。
3、根据权利要求1所述的环保型透水砖，其特征在于：所述粒度为6-35目的铝矾土颗粒料，是由250-300目的铝矾土粉90％96％加入4％-8％色彩染料添加剂，经混合、成型、烘干、煅烧后，再破碎而成。
4、根据权利要求1或2或3所述的环保型透水砖，其特征在于：所述铝矾土含AI2O370％-80％。
CNB03126168XA 2003-05-14 2003-05-14 环保型透水砖 Expired - Fee Related CN1169741C (zh)