CN1417153A - 一种预拌混凝土制品及其制造方法 - Google Patents
一种预拌混凝土制品及其制造方法 Download PDFInfo
- Publication number
- CN1417153A CN1417153A CN01132040A CN01132040A CN1417153A CN 1417153 A CN1417153 A CN 1417153A CN 01132040 A CN01132040 A CN 01132040A CN 01132040 A CN01132040 A CN 01132040A CN 1417153 A CN1417153 A CN 1417153A
- Authority
- CN
- China
- Prior art keywords
- cement
- concrete
- mixed concrete
- admixture
- concrete product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
编号 | 胶结料kg/m3 | 胶结料组成% | 外加剂FTH-2C | 水灰比W/C | 坍落度保留值mm | 抗压强度(MPa) | 拌和物和易性 | ||||||
P.O | F | 0h | 0.5h | 1.0h | R3 | R7 | R28 | R60 | |||||
P.O1 | 500 | 50 | 50 | 9.00 | 0.37 | 200 | 130 | 110 | 24.3 | 38.2 | 57.8 | 61.0 | 一般 |
P.O2 | 500 | 60 | 40 | 9.00 | 0.37 | 190 | 150 | 130 | 26.1 | 40.9 | 59.6 | 63.0 | 好 |
P.O3 | 500 | 70 | 30 | 9.00 | 0.37 | 200 | 165 | 150 | 28.5 | 43.1 | 62.4 | 65.7 | 好 |
P.O4 | 500 | 80 | 20 | 9.00 | 0.37 | 200 | 175 | 145 | 30.5 | 45.1 | 63.7 | 65.8 | 好 |
P.O5 | 500 | 100 | 0 | 9.00 | 0.37 | 190 | 180 | 160 | 38.5 | 56.4 | 65.4 | 67.0 | 好 |
编号 | 胶结料kg/m3 | 胶结料组成% | 外加剂FTH-2C | 水灰比W/C | 坍落度保留值mm | 抗压强度(MPa) | 拌和物和易性 | ||||||
P.II | F | 0h | 0.5h | 1.0h | R3 | R7 | R28 | R60 | |||||
P.II1 | 400 | 50 | 50 | 6.0 | 0.45 | 150 | 120 | 90 | 13.9 | 21.2 | 42.1 | 52.0 | 好 |
P.II2 | 400 | 60 | 40 | 6.0 | 0.45 | 180 | 150 | 110 | 15.2 | 25.3 | 48.6 | 55.2 | 好 |
P.II3 | 400 | 70 | 30 | 6.0 | 0.45 | 175 | 140 | 120 | 17.3 | 27.3 | 47.4 | 54.4 | 好 |
P.II4 | 400 | 80 | 20 | 6.0 | 0.45 | 180 | 175 | 150 | 20.5 | 30.8 | 46.7 | 56.2 | 好 |
P.II5 | 400 | 100 | 0 | 6.0 | 0.45 | 195 | 180 | 145 | 30.5 | 39.1 | 50.4 | 58.8 | 较好 |
P.II1 | 500 | 50 | 50 | 9.0 | 0.35 | 170 | 120 | 105 | 25.4 | 44.1 | 51.6 | 60.4 | 一般 |
P.II2 | 500 | 60 | 40 | 9.0 | 0.35 | 180 | 150 | 120 | 31.3 | 44.1 | 60.4 | 65.0 | 好 |
P.II3 | 500 | 70 | 30 | 9.0 | 0.35 | 200 | 160 | 145 | 34.8 | 48.6 | 62.0 | 67.1 | 好 |
P.II4 | 500 | 80 | 20 | 9.0 | 0.35 | 200 | 170 | 165 | 38.4 | 56.9 | 65.1 | 68.5 | 好 |
P.II5 | 500 | 100 | 0 | 9.0 | 0.35 | 210 | 185 | 170 | 42.2 | 58.9 | 69.8 | 73.8 | 较好 |
编号 | 胶结料kg/m3 | 掺量% | 胶结料组成% | 外加剂FTH-2C | 水灰比W/C | 坍落度保留值mm | 抗压强度(MPa) | 拌和物和易性 | |||||||
P.O | F | KF | 0h | 0.5h | 1.0h | R3 | R7 | R28 | R60 | ||||||
P.O1 | 430 | 28 | 72 | 28 | 0 | 6.4 | 0.42 | 205 | 190 | 170 | 20.9 | 23.2 | 42.1 | 51.2 | 好 |
P.O2 | 430 | 49 | 51 | 28 | 21 | 6.4 | 0.42 | 200 | 195 | 185 | 19.4 | 21.0 | 39.4 | 52.4 | 好 |
P.O3 | 460 | 25 | 75 | 25 | 0 | 8.3 | 0.39 | 195 | 185 | 170 | 23.1 | 34.9 | 52.6 | 57.0 | 好 |
P.O4 | 460 | 48 | 52 | 25 | 23 | 8.3 | 0.39 | 190 | 170 | 165 | 22.5 | 33.1 | 51.4 | 56.7 | 好 |
P.O5 | 500 | 22 | 78 | 22 | 0 | 10.0 | 0.36 | 205 | 190 | 175 | 25.5 | 40.1 | 60.4 | 62.8 | 好 |
P.O6 | 500 | 46 | 54 | 22 | 24 | 10.0 | 0.36 | 210 | 195 | 180 | 24.6 | 37.8 | 58.6 | 67.0 | 好 |
编号 | 胶结料kg/m3 | 掺量% | 胶结料组成% | 外加剂FTH-2C | 水灰比W/C | 坍落度保留值mm | 抗压强度(MPa) | 拌和物和易性 | |||||||
P.II | F | KF | 0h | 0.5h | 1.0h | R3 | R7 | R28 | R60 | ||||||
P.II1 | 400 | 40 | 60 | 40 | 0 | 6.4 | 0.45 | 185 | 175 | 155 | 17.2 | 27.8 | 40.5 | 47.3 | 好 |
P.II2 | 400 | 58 | 42 | 40 | 18 | 6.4 | 0.45 | 180 | 170 | 165 | 16.1 | 25.3 | 38.4 | 48.2 | 好 |
P.II3 | 430 | 30 | 70 | 30 | 0 | 7.7 | 0.42 | 175 | 165 | 150 | 21.4 | 33.0 | 53.2 | 58.3 | 好 |
P.II4 | 430 | 55 | 45 | 30 | 25 | 7.7 | 0.42 | 175 | 170 | 165 | 19.1 | 30.3 | 54.4 | 60.5 | 好 |
P.II5 | 480 | 20 | 80 | 20 | 0 | 10.0 | 0.38 | 190 | 175 | 160 | 26.1 | 36.5 | 57.5 | 63.3 | 好 |
P.II6 | 480 | 46 | 54 | 20 | 26 | 10.0 | 0.38 | 195 | 180 | 170 | 23.6 | 35.3 | 55.9 | 59.1 | 好 |
序号 | 强度等级 | 外加剂牌号 | 配合比(kg/m3) | 掺合比例% | ||||||
水 | 水泥 | 黄砂 | 碎石 | 粉煤灰 | 矿渣微粉 | 外加剂 | ||||
1 | C20 | EA-1 | 180 | 145 | 820 | 1030 | 80 | 80 | 1.35 | 52.4 |
2 | C20 | EA-1 | 180 | 160 | 820 | 1030 | 80 | 65 | 1.35 | 47.5 |
3 | C25 | EA-1 | 185 | 175 | 803 | 1017 | 70 | 90 | 1.59 | 47.8 |
4 | C25 | EA-1 | 185 | 202 | 803 | 1017 | 70 | 63 | 1.59 | 39.7 |
5 | C30 | EA-1 | 186 | 206 | 771 | 1027 | 80 | 91 | 1.77 | 45.3 |
6 | C30 | EA-1 | 186 | 236 | 771 | 1027 | 80 | 61 | 1.77 | 37.4 |
7 | C35 | EA-1 | 186 | 231 | 737 | 1024 | 81 | 101 | 1.98 | 44.0 |
8 | C35 | EA-1 | 186 | 261 | 737 | 1024 | 81 | 61 | 1.98 | 35.2 |
9 | C40 | EA-1 | 191 | 256 | 696 | 1028 | 80 | 111 | 2.19 | 42.7 |
10 | C40 | EA-1 | 191 | 291 | 696 | 1028 | 80 | 76 | 2.19 | 34.9 |
11 | C50 | FTH-2C | 171 | 307 | 715 | 1027 | 60 | 120 | 8.50 | 36.9 |
12 | C50 | FTH-2C | 171 | 332 | 715 | 1027 | 60 | 95 | 8.50 | 31.8 |
13 | C55 | FTH-2C | 172 | 343 | 686 | 1029 | 60 | 120 | 11.04 | 34.4 |
14 | C55 | FTH-2C | 172 | 363 | 686 | 1029 | 60 | 100 | 11.04 | 30.5 |
15 | C60 | FTH-2C | 172 | 392 | 652 | 1024 | 50 | 120 | 12.28 | 30.0 |
16 | C60 | FTH-2C | 172 | 432 | 652 | 1024 | 50 | 80 | 12.28 | 23.1 |
序号 | 强度等级 | 新拌混凝土性能 | 混凝土凝结时间(h:min) | 混凝土抗压强度(MPa) | |||
和易性 | 坍落度损失水泥 | 初凝时间 | 终凝时间 | 3天 | 28天 | ||
1 | C20 | 好 | 145/130/110 | 6:20 | 10:30 | 16.7 | 30.1 |
2 | C20 | 好 | 150/120/100 | 6:45 | 10:40 | 15.8 | 31.2 |
3 | C25 | 较好 | 150/140/130 | 7:08 | 10:56 | 18.3 | 32.1 |
4 | C25 | 较好 | 145/130/120 | 6:50 | 10:47 | 19.2 | 33.6 |
5 | C30 | 较好 | 150/120/115 | 6:47 | 11:20 | 21.4 | 35.6 |
6 | C30 | 较好 | 155/130/110 | 7:22 | 11:56 | 20.6 | 36.1 |
7 | C35 | 好 | 150/140/120 | 7:18 | 11:02 | 25.1 | 42.2 |
8 | C35 | 好 | 150/130/115 | 7:25 | 11:15 | 23.9 | 44.6 |
9 | C40 | 好 | 145/110/90 | 8:30 | 11:32 | 29.1 | 47.1 |
10 | C40 | 好 | 150/120/95 | 8:15 | 10:42 | 27.9 | 48.5 |
11 | C50 | 好 | 185/165/135 | 8:30 | 11:26 | 38.4 | 60.2 |
12 | C50 | 好 | 180/160/150 | 8:10 | 10:47 | 36.1 | 61.5 |
13 | C55 | 好 | 180/170/150 | 8:21 | 11:27 | 46.6 | 65.6 |
14 | C55 | 好 | 185/170/145 | 8:40 | 11:51 | 47.2 | 63.2 |
15 | C60 | 好 | 190/180/165 | 8:56 | 12:18 | 52.1 | 68.2 |
16 | C60 | 好 | 200/190/165 | 8:37 | 11:45 | 49.2 | 70.1 |
混凝土等级 | 每立方米混凝土原材料用量(kg) | ||||||
水 | 水泥 | 矿渣微粉 | 粉煤灰 | 黄砂 | 碎石 | 外加剂 | |
C30 | 186 | 206 | 80 | 91 | 771 | 1027 | 1.77 |
经时坍落度(mm) | 混凝土凝结时间(h:min) | 混凝土含气量 | 混凝土和易性 | |||
出机时 | 0.5h | 1.0h | 初凝 | 终凝 | ||
160 | 145 | 120 | 7:16 | 11:43 | 1.6% | 好 |
混凝土试块龄期 | 3天 | 7天 | 28天 | 60天 |
混凝土抗压强度 | 14.3 | 26.6 | 37.2 | 43.4 |
序号 | 指标名称 | 单位 | 试验结果 |
1 | 劈裂抗拉强度 | MPa | 3.5 |
2 | 抗折强度 | MPa | 6.9 |
3 | 轴心抗压强度 | MPa | 27.5 |
4 | 弹性模量 | MPa | 3.5×104 |
混凝土强度等级 | 抗渗等级(S) | 抗冻性能 | |
D100重量损失率(%) | D100强度损失率(%) | ||
C30 | S>6 | 1.5 | 6.5 |
强度等级 | 混凝土不同龄期收缩值ε×10-6 | ||||||||
1天 | 3天 | 7天 | 14天 | 28天 | 45天 | 60天 | 90天 | 120天 | |
C30 | 25 | 66 | 102 | 187 | 252 | 276 | 329 | 371 | 426 |
混凝土强度等级 | 快速碳化龄期(天) | 相当碳化自然年限(年) | 碳化后试件平均碳化深度(mm) |
28 | 50 | 7.8 | |
C30 | 56 | 100 | 12.5 |
注:混凝土人工碳化试验条件:温度:20±5℃,相对湿度70±5%,CO2浓度20±3% |
Claims (6)