CN1404084A - Spring touch finger for high-voltage switch and its manufacture - Google Patents
Spring touch finger for high-voltage switch and its manufacture Download PDFInfo
- Publication number
- CN1404084A CN1404084A CN 01128127 CN01128127A CN1404084A CN 1404084 A CN1404084 A CN 1404084A CN 01128127 CN01128127 CN 01128127 CN 01128127 A CN01128127 A CN 01128127A CN 1404084 A CN1404084 A CN 1404084A
- Authority
- CN
- China
- Prior art keywords
- spring
- touch finger
- voltage switch
- section
- beryllium copper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The spring touch finger for high-voltage switch is ring spring with elliptic section and made of beryllium copper and the major axis is in the direction of the ring spring axis. The manufacture includes softening treatment of beryllium copper wire at 750-800 deg.c for 0.5-2 hr; winding spiral spring wire on one rod model with elliptic section with the length of the spring wire being 0.1-0.2 mm longer than that of final spring product; welding the two ends together to form closed spring with the welding spot being at major axis end of the elliptic section; setting in a setting model with the same shape as the final product and maintaining at 600-650 deg.c for 1-3 hr. The structure of the present invention ensure the relatively larger contact surface and less contact resistance between the spring touch finger and the rigid touch finger of the static contact.
Description
Technical field:
The present invention relates to high-voltage switch gear, the switch spring touch finger of the electric pressure (220～500 kilovolts) in a kind of power transmission and transformation line is provided especially.
Background technology:
High-voltage switch gear is generally used for switching on and off the circuit under zero load, normal load or the short-circuit condition, usually by the galvanic circle, can divide several parts such as contact, arc-control device, transmission mechanism, operating mechanism to form.The galvanic circle is used for loaded current; Arc-control device is used for promptly reliably that extinguish arcs finally disconnects circuit, and high voltage isolator is not provided with special arc-control device usually; Can divide contact is the executive component that makes circuit connection or disjunction, constitute by moving contact, fixed contact, have spring and rubber-like fingertip on the fixed contact, high-voltage switch gear is when the combined floodgate tram, and fingertip is compressing or straining and be used for guaranteeing with contact enough contact pressures and less contact resistance are arranged by spring fully.
It shown in the accompanying drawing 1 a kind of divided structure of contact terminal of novel Lw series high voltage switch, constitute by fixed contact 1, moving contact 2, spring touch finger 3, the fingertip of fixed contact 1 is a rigidity, moving contact is provided with cannelure, the spring touch finger 3 of annular overlaps thereon, and moving contact can move up and down until disengaging in fixed contact.Operation principle is: moving contact is with after fixed contact contacts, rely on the strain of spring touch finger that both are closely contacted, electric current flows through from spring touch finger, because electric current flows through through each circle spring, the heating of each circle all can cause elasticity to change and the contact pressure of regulating dynamic/static contact automatically.And the spring touch finger surface area is big, and radiating surface is big, and every circle very easily cools off, and (as 3000～4000A), temperature rising amplitude is controlled easily when big current work.The design of this kind series high voltage switch has changed high-voltage switch gear complex structure in the past, and materials are many, and difficulty of processing is big, and the parts heaviness is assembled complicated shortcoming, can reduce the production cost of high-voltage switch gear greatly.The key problem in technology of this kind high-voltage switch gear is a spring touch finger, require it must possess better elastic, to guarantee that moving contact is in folding and motion, with fixed contact good compatible the contact arranged, make electric current each circle spring wire of flowing through equably, do not raise and do not produce local temperature, thereby whole element temperature rise is in the scope of design.Specifically, require each circle spring wire all accurate shape will be arranged exactly, total number of turns is wanted strict control, the weld bond of spring wire joint must be avoided contacting with fixed contact, solder joint must be smooth smooth, must not macroscopic difference be arranged with spring diameter, cause damage to avoid the electrion under the high pressure.
Summary of the invention:
In order to make the possibility that is designed to of above-mentioned new structure Lw series high voltage switch, the invention provides a kind of spring touch finger for high-voltage switch, it is characterized in that this spring touch finger is the ring spring structure of oval cross section, the major axis of oval cross section is axial along ring spring, is the beryllium copper material.
Because spring touch finger of the present invention has adopted a kind of special design, be that spring is the ring spring structure of oval cross section, the major axis of oval cross section is axial along ring spring, thereby guaranteed to have bigger contact-making surface between the rigidity fingertip of spring touch finger and fixed contact, to guarantee to have less contact resistance.Simultaneously,, guaranteed the satisfactory electrical conductivity of himself, and the function of automatic arc extinguishing has been arranged, do not produced electric spark because spring touch finger of the present invention adopts the beryllium copper material.At present, the ring spring technology of preparing of circular cross-section is comparatively ripe, but because the anisotropy of oval cross section structure, the preparation of occluded ellipse cross section ring spring does not still have report.
The present invention also provides the preparation method of above-mentioned spring touch finger for high-voltage switch, it is characterized in that process is:
---the beryllium copper silk is softened processing, 75～800 ℃ of temperature, 0.5～2 hour time;
---the beryllium copper silk after will softening is wound in the helical spring silk on the bar-shaped mold of cross section for ellipse, the length of spring wire is than the long 0.1～0.2mm of the girth of final ring spring;
---above-mentioned spring wire two ends are welded together, form the closed ring spring, solder joint is in the longitudinal end of oval cross section;
---above-mentioned ring spring is put into the typing mold consistent with the final products shape, under 600～650 ℃ of conditions, be incubated 1～3 hour.
Among the preparation method of spring touch finger for high-voltage switch of the present invention, the welding of spring wire two ends can adopt the method for electron beam, laser or argon arc welding to carry out.
Among the preparation method of spring touch finger for high-voltage switch of the present invention, nickel plating or silver-plated processing can also be carried out in timeliness rear spring surface.
Description of drawings:
Accompanying drawing 1 is the divided structure of contact terminal signal of Lw series high voltage switch;
Accompanying drawing 2 is the structural representation of spring wire molding fetal;
Accompanying drawing 3 shows for spring wire molding fetal A-A cuts open;
Accompanying drawing 4 is the signal of typing positioner structure;
Accompanying drawing 5 is typing mold cut-away view.
Embodiment:
The silk of beryllium copper described in the present invention raw material can form by alloy melting, moulding by casting, extruding wire drawing, also can directly buy from the market, all needs to soften processing during use.
Embodiment 1
The QBe2 beryllium copper silk of the φ 1.5mm that market is buied softens processing, 800 ℃ of temperature, 0.5 hour time was wound in the helical spring silk with the beryllium copper silk after softening on the bar-shaped mold of cross section for ellipse, the major axis of oval cross section is 13mm, minor axis is 11mm, and the length of spring wire is 90 circles; The spring wire two ends are welded together with argon arc welding, form the closed ring spring, solder joint is in the longitudinal end of oval cross section; Ring spring is put into the typing mold, and the internal diameter of mold is φ 90 ± 1mm, and external diameter is φ 110 ± 1.5mm, and the cross section is identical with bar-shaped mold cross section.Under 620 ± 10 ℃ of conditions, be incubated 2 hours; Finally obtaining spring touch finger adheres to specification.
The QBe1.9 beryllium copper silk of the φ 1.6mm that market is buied, soften processing, 800 ℃ of temperature, 0.5 hour time, beryllium copper silk after softening is wound in the helical spring silk on the bar-shaped mold of cross section for ellipse, the major axis of oval cross section is 12.7mm, and minor axis is 10.5mm, and the length of spring wire is 138 circles; The spring wire two ends are welded together with argon arc welding, form the closed ring spring, solder joint is in the longitudinal end of oval cross section; Ring spring is put into the typing mold, and the internal diameter of mold is φ 125 ± 1mm, and external diameter is φ 150+2mm, and the cross section is identical with bar-shaped mold cross section.Under 620 ± 10 ℃ of conditions, be incubated 2 hours; Finally obtaining spring touch finger adheres to specification.
Embodiment 3
The QBe1.9 beryllium copper silk of the φ 1.59mm that market is buied, soften processing, 800 ℃ of temperature, 0.5 hour time, beryllium copper silk after softening is wound in the helical spring silk on the bar-shaped mold of cross section for ellipse, the major axis of oval cross section is 13mm, and minor axis is 11mm, and the length of spring wire is 159 circles; The spring wire two ends are welded together with argon arc welding, form the closed ring spring, solder joint is in the longitudinal end of oval cross section; Ring spring is put into the typing mold, and the internal diameter of mold is φ 145 ± 1mm, and external diameter is φ 165 ± 2mm, and the cross section is identical with bar-shaped mold cross section.Under 620 ± 10 ℃ of conditions, be incubated 2 hours; Finally obtaining spring touch finger adheres to specification.
Claims (4)
1, a kind of spring touch finger for high-voltage switch is characterized in that this spring touch finger is the ring spring structure of oval cross section, and the major axis of oval cross section is axial along ring spring, is the beryllium copper material.
2, the preparation method of the described spring touch finger for high-voltage switch of a kind of claim 1 is characterized in that process is:
---the beryllium copper silk is softened processing, 750～800 ℃ of temperature, 0.5～2 hour time;
---the beryllium copper silk after will softening is wound in the helical spring silk on the bar-shaped mold of cross section for ellipse, the length of spring wire is than the long 0.1～0.2mm of the girth of final ring spring;
---above-mentioned spring wire two ends are welded together, form the closed ring spring, solder joint is in the longitudinal end of oval cross section;
---above-mentioned ring spring is put into the typing mold consistent with the final products shape, under 600～650 ℃ of conditions, be incubated 1～3 hour;
---under 260～380 ℃ of conditions, timeliness 0.2～1 hour obtains spring touch finger for high-voltage switch with the spring after the above-mentioned typing.
3, according to the preparation method of the described spring touch finger for high-voltage switch of claim 2, it is characterized in that: adopt the method for electron beam, laser or argon arc welding to weld.
4, according to the preparation method of the described spring touch finger for high-voltage switch of claim 2, it is characterized in that: nickel plating or silver-plated processing are carried out in timeliness rear spring surface.