CN1388160A - New tyre facing rubber material for retreading tyre of giant mining engineering machinery - Google Patents
New tyre facing rubber material for retreading tyre of giant mining engineering machinery Download PDFInfo
- Publication number
- CN1388160A CN1388160A CN 02121282 CN02121282A CN1388160A CN 1388160 A CN1388160 A CN 1388160A CN 02121282 CN02121282 CN 02121282 CN 02121282 A CN02121282 A CN 02121282A CN 1388160 A CN1388160 A CN 1388160A
- Authority
- CN
- China
- Prior art keywords
- antioxidant
- tyre
- carbon black
- cyclohexyl
- rubber material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The rubber material for retreading tyre facing is compounded with the material including natural rubber, zinc oxide, stearic acid, carbon black, white carbon black, Si-69, antiager A, antiager 4010NA, antiager H, dimorphiline disulfide, N-cyclohexyl-2-benzothiazole sulfenamide, sulfur powder, oil insoluble sulfur, modified alkylphenol resin, N-cyclohexyl thiophthalimide and aromatic oil. The retreaded tyre with the said rubber material has better cutting and pricking resistance.
Description
Technical field
The present invention relates to a kind of new tyre facing rubber material for retreading tyre of giant mining engineering machinery, this tread mix is used for the tyre surface of renovated tyre, and the tyre surface when being mainly used in the 3600R51 tyre rebuilding is handled.
Background technology
The continuous increase of modern bargh traffic capacity, impel the mine carrier vehicle to develop to the direction that maximizes, the vehicle load tonnage is increasing, and the road conditions in mine is more abominable, thereby the tyre surface position of tire very easily is subjected to cutting and puncture and cause heel and toe wear to damage, and has higher requirement with regard to the tread mix of giving this tire for this reason.Chinese patent ZL01104025.4 discloses a kind of high trans-1, the high-speed and energy-saving tire tread compound of 4-polyisoprene and high vinyl polybutadiene and usefulness, it is characterized in that, in the tread mix prescription, used high trans-1 simultaneously, 4-polyisoprene (being called for short TPI) and high vinyl polybutadiene (being called for short HVBR), and with other tire rubber commonly used such as natural rubber (NR); styrene-butadiene rubber(SBR) (SBR; comprise the poly-butadiene-styrene rubber ESBR of breast; solution polymerized butylbenzene glue SSBR and oil-filled butadiene-styrene rubber etc.); cis-1,4-polybutadiene rubber at least a blend such as (BR); covulcanization; what make both has low-rolling-resistance and low dynamic heat build up, a rubber tyre that has high wet road-traction (high wet-sliding resistant performance) again.Cooperate the preparation of blend covulcanization with other conventional rubber.For example, the natural gum of prescription employing 20-25 mass parts TPI and 20-25 mass parts HVBR replacement equivalent or butadiene-styrene rubber or cis-butadiene cement etc. are as the sizing material of tyre surface, can reduce tire drag 15-20%, save fuel oil about 2.5%, be a kind of more satisfactory tread mix.But this tread mix lacks higher wear resistance and anti-puncture, therefore, needs to propose a kind of the have excellent anti-cutting and the tread mix of anti-puncture performance.
Summary of the invention
The new tyre facing rubber material for retreading tyre that the purpose of this invention is to provide a kind of giant mining engineering machinery, this tread mix can further improve the anti-cutting and the anti-puncture performance of tread rubber under the prerequisite that satisfies tire use over-all properties.
The objective of the invention is to be realized by following technical scheme: a kind of new tyre facing rubber material for retreading tyre of giant mining engineering machinery is characterized in that: formulated by weight by following raw material:
Natural rubber 100
Zinc oxide 5
Stearic acid 2.5
Carbon black 30-50
White carbon black 5-20
Bis(3-triethoxy silylpropyl)tetrasulfide 0.2-1
Antioxidant A 1-2
Antioxidant 4010NA 1-3
Antioxidant H 0.1-0.3
Dithiodimorpholine 0.5-2.0
N cyclohexyl 2 benzothiazole sulfenamide 0.5-2.5
SULPHUR POWDER 0.5-2.5
Oil-filled insoluble sulfur 0.5-2.5
Modification alkyl phenol resin 1-3
N-cyclohexyl thio phthalimide 0.1-0.3
Fragrance hydrocarbon ils 4-8.
Know-why of the present invention is to adopt the most excellent super abrasion resistant carbon black (code name N110) and the precipitated silica of reinforcing property to make an addition in the best natural rubber of over-all properties, make the sizing material that recaps, can solve anti-cutting of tread rubber and anti-puncture problem preferably.
Embodiment
Embodiment one:
Natural rubber (code name SCR5) 100
Zinc oxide 5
Stearic acid 2.5
Carbon black (code name N110) 35
White carbon black (precipitated silica) 15
Bis(3-triethoxy silylpropyl)tetrasulfide (code name Si-69) 0.4
Antioxidant A 1.3
Antioxidant 4010NA 1.5
Antioxidant H 0.2
Dithiodimorpholine (code name DTDM) 1.5
N cyclohexyl 2 benzothiazole sulfenamide (code name CZ) 1.4
SULPHUR POWDER (code name S) 0.8
Oil-filled insoluble sulfur (code name IS-6005) 0.8
Modification alkyl phenol resin (code name TKM-M) 2
N-cyclohexyl thio phthalimide (code name CTP) 0.1
Fragrance hydrocarbon ils 6.
In the present embodiment, described antioxidant A is the N-phenyl-a-naphthylamine, and described antioxidant 4010NA is N-sec.-propyl-N '-diphenyl-para-phenylene diamine, and described antioxidant H is N, N '-diphenyl-para-phenylene diamine.
In the present embodiment, the calendering process of tread rubber is taked conventional technology, but white carbon black and Si-69 need be carried out the premix processing.
The performance test data of the tread mix that the use present embodiment is made is as follows:
Tensile strength/Mpa 26.8
300% stress at definite elongation/Mpa 12.1
Tensile yield/% 525
Shao Er A type hardness tester/degree 67
Akron abrasion loss/m
3≤ 0.3
Tear strength/KN/m 142
The renovated tyre that use present embodiment to make are used for the 3600R51 tire and carry out 38126 km mine pavement tests to have anti-preferably cutting and anti-puncture performance.
Embodiment two:
Natural rubber 100
Zinc oxide 5
Stearic acid 2.5
Carbon black 30
White carbon black 20
Bis(3-triethoxy silylpropyl)tetrasulfide 0.6
Antioxidant A 1.5
Antioxidant 4010NA 1.5
Antioxidant H 0.3
Dithiodimorpholine 2.0
N cyclohexyl 2 benzothiazole sulfenamide 1.8
SULPHUR POWDER 0.7
Oil-filled insoluble sulfur 1.0
Modification alkyl phenol resin 3
N-cyclohexyl thio phthalimide 0.2
Fragrance hydrocarbon ils 8.
In the present embodiment, described antioxidant A is the N-phenyl-a-naphthylamine, and described antioxidant 4010NA is N-sec.-propyl-N '-diphenyl-para-phenylene diamine, and described antioxidant H is N, N '-diphenyl-para-phenylene diamine.
Embodiment three:
Natural rubber 100
Zinc oxide 5
Stearic acid 2.5
Carbon black 40
White carbon black 10
Bis(3-triethoxy silylpropyl)tetrasulfide 0.4
Antioxidant A 1.5
Antioxidant 4010NA 2
Antioxidant H 0.2
Dithiodimorpholine 1.5
N cyclohexyl 2 benzothiazole sulfenamide 1.2
SULPHUR POWDER 1.1
Oil-filled insoluble sulfur 1.1
Modification alkyl phenol resin 2
N-cyclohexyl thio phthalimide 0.2
Fragrance hydrocarbon ils 6.
In the present embodiment, described antioxidant A is the N-phenyl-a-naphthylamine, and described antioxidant 4010NA is N-sec.-propyl-N '-diphenyl-para-phenylene diamine, and described antioxidant H is N, N '-diphenyl-para-phenylene diamine.
Claims (3)
1, a kind of new tyre facing rubber material for retreading tyre of giant mining engineering machinery is characterized in that: formulated by weight by following raw material:
Natural rubber 100
Zinc oxide 5
Stearic acid 2.5
Carbon black 30-50
White carbon black 5-20
Bis(3-triethoxy silylpropyl)tetrasulfide 0.2-1
Antioxidant A 1-2
Antioxidant 4010NA 1-3
Antioxidant H 0.1-0.3
Dithiodimorpholine 0.5-2.0
N cyclohexyl 2 benzothiazole sulfenamide 0.5-2.5
SULPHUR POWDER 0.5-2.5
Oil-filled insoluble sulfur 0.5-2.5
Modification alkyl phenol resin 1-3
N-cyclohexyl thio phthalimide 0.1-0.3
Fragrance hydrocarbon ils 4-8.
2, tread mix according to claim 1 is characterized in that: formulated by weight by following raw material:
Natural rubber 100
Zinc oxide 5
Stearic acid 2.5
Carbon black 40
White carbon black 10
Bis(3-triethoxy silylpropyl)tetrasulfide 0.4
Antioxidant A 1.5
Antioxidant 4010NA 2
Antioxidant H 0.2
Dithiodimorpholine 1.5
N cyclohexyl 2 benzothiazole sulfenamide 1.2
SULPHUR POWDER 1.1
Oil-filled insoluble sulfur 1.1
Modification alkyl phenol resin 2
N-cyclohexyl thio phthalimide 0.2
Fragrance hydrocarbon ils 6.
3, tread mix according to claim 1 and 2 is characterized in that: described antioxidant A is the N-phenyl-a-naphthylamine, and described antioxidant 4010NA is N-sec.-propyl-N '-diphenyl-para-phenylene diamine, and described antioxidant H is N, N '-diphenyl-para-phenylene diamine.