CN1347137A - Filmforming method and device - Google Patents
Filmforming method and device Download PDFInfo
- Publication number
- CN1347137A CN1347137A CN 01140673 CN01140673A CN1347137A CN 1347137 A CN1347137 A CN 1347137A CN 01140673 CN01140673 CN 01140673 CN 01140673 A CN01140673 A CN 01140673A CN 1347137 A CN1347137 A CN 1347137A
- Authority
- CN
- China
- Prior art keywords
- aforementioned
- processed substrate
- film
- suction nozzle
- aqueous film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a film forming method and device. A liquid film formation section is composed of a resist dropping nozzle 102, a nozzle movement mechanism not shown in a figure that moves the resist dropping nozzle 102 in a y direction (a horizontal direction on page space), and the movement rest of the substrate 110 to be treated not shown in the figure where the substrate 110 to be treated having a diameter of 200 mm is installed and is moved in an x direction. A liquid film drying section is composed of a suction nozzle 101, and a vacuum pump 103 connected to the suction nozzle 101. Also, the movement rest of the substrate to be treated is also one of the components of the liquid film drying section. The invention is able to suppress the generation of film thickness distribution in an application film, and at the same time to shorten time for forming the application film.
Description
Technical field
The present invention relates to make in semiconductor (single-chip technology (ウ エ Ha エ journey), exposure mask preparation technology), the liquid crystal apparatus technology of preparing film build method and the film formation device that use in filming.
Background technology
The method of spin coating that always used before in lithography technology, owing to be that with residual a few percent film forming, the liquid waste of use is big beyond the most of discharge of the liquid substrate that will drip on the substrate, because the soup of discharging is a lot, also can produce ill effect to environment.In addition, on square substrate or the heavy caliber circular substrate more than the 300mm,, be created in the problem of these part membrane thickness unevenness in substrate peripheral part branch turbulization.
As not wasting soup comprehensive method of homogeneous coating on substrate, the spy opens and has put down in writing in the flat 2-220428 communique by a plurality of nozzles that the are configured to row diaphragm (resist) that drips, and from its rear the liquid film forming face being blown obtains the method for homogeneous film.In addition, the spy opens to have put down in writing in the flat 6-151295 communique a plurality of nozzles is set on rod, diaphragm is dripped to the technology that obtains the homogeneous film on the substrate by it.In addition, the spy opens in the flat 7-321001 communique, has put down in writing the method that use spray head (a plurality of film formed squit holes of spraying protection that are are arranged on this spray head) and substrate relatively move and be coated with.
In above-mentioned all apparatus for coating, all be that a plurality of dropping liquids or spray nozzle landscape configuration are listed one, make it obtain the homogeneous film along substrate surface scanning.In addition, except these uses have the coating process of device of a plurality of nozzles, also have the nozzle that uses ejection one post liquid, scanning forms the method for liquid film on processed substrate.
With filming that these methods are made, can produce problem from coating beginning side to the thick distribution of coating end of a period side form.This be because the stand-by time of medicine liquid droplet when down the back is to dried in coating beginning portion and coating end of a period portion oversize (drying regime of soup).In addition, up to the present, aqueous film forms technology and drying process all carries out respectively independently, and therefore, filming to final formation need the expensive time.
Summary of the invention
As mentioned above, if after scan nozzle forms aqueous film on the processed substrate, carry out dried, then can produce film thickness distribution problem from coating beginning portion to coating end of a period portion.The problem of expensive time when in addition, also exist forming final filming.
The film build method and the film formation device of the purpose of this invention is to provide when the generation film thickness distribution is filmed in inhibition, formation time is filmed in shortening.
The present invention has following formation for achieving the above object.
(1) the present invention's (claim 1) is, comprising that aqueous film formation technology is (promptly relative with processed substrate, on substrate, be adjusted to a certain amount of expansion, drip from the dropping liquid nozzle and solvent, to have added the soup that solid formation divides, aforementioned dropping liquid nozzle and aforementioned processed substrate are relatively moved, on whole of aforementioned processed substrate, form the technology of aqueous film) and remove in the film build method of the drying process that the solvent formation in the aforementioned aqueous film films, the aforementioned drying process that carries out is to dispose suction nozzle with this discontiguous distance in aqueous film surface on aforementioned processed substrate, this suction nozzle and this processed substrate are relatively moved, and the solvent atmosphere gas under the aforementioned suction nozzle is sucked away from the air entry of this suction nozzle simultaneously.
The preferred embodiment of the invention is as described below.
After the aqueous film planarization on the aforementioned processed substrate, and before forming aqueous film all sidedly on the aforementioned processed substrate, form technology Yi Bian carry out aforementioned aqueous film, Yi Bian carry out aforementioned drying process.
By this processed substrate and aforementioned suction nozzle are relatively moved, carry out dried for several times repeatedly to whole of aforementioned processed substrate.
According to the drying regime of the aforementioned aqueous film after the dried last time, change the distance between the aforementioned suction nozzle and this aqueous film surface in the dried next time.
Aforementioned drying process is to use the air feed mouth that links to each other with the outer gas stream feedway, and the aqueous film that the air entry by aforementioned suction nozzle is siphoned away on the processed substrate of solvent atmosphere gas is supplied with air-flow.
From the place ahead with respect to the direction that relatively moves of the aforementioned suction nozzle of aforementioned processed substrate, the aqueous film on processed substrate is supplied with air-flow.
(2) film formation device, it is characterized in that possessing following parts, dropping liquid nozzle with the supply of chemical of the relative configuration of aforementioned processed substrate, with with relative configuration of aforementioned processed substrate, siphon away by suction nozzle from the solvent atmosphere gas of aforementioned dropping liquid nozzle supply of chemical on the aqueous film that aforementioned processed substrate forms, with the 1st moving part that aforementioned processed substrate and aforementioned dropping liquid nozzle are relatively moved and the 2nd moving part that aforementioned processed substrate and suction nozzle are relatively moved.
The preferred embodiments of the invention are as described below.
Further possess with aforementioned suction nozzle integrally formedly, the aqueous film on the aforementioned processed substrate is supplied with the air feed mouth of air-flow.
The air entry of aforementioned suction nozzle length longitudinally is more than the aforementioned processed substrate.
The present invention has following effect, effect by above formation.
Can cancel the aqueous film formation time difference that scanning coating causes and carry out dried, in addition, can carry out simultaneously that aqueous film forms and dry, making changing in short-term of coating process is possible.At this moment, can carry out the drying process of aqueous film according to the planarization time.
By when aqueous film is supplied with air-flow, carrying out drying drying efficiency is improved.In addition, can reach the homogenization of filming by adjusting flowing of air-flow.
By carrying out dried repeatedly for several times, can make aqueous film slowly dry, can prevent that the solid formation branch in the aqueous film is attracted, reach the thickness homogeneity.In addition,, carry out each time scanning, can improve drying efficiency and thickness homogeneity in only distance according to the drying regime of aqueous film.The scheme that invention is implemented
With reference to the accompanying drawings embodiment of the present invention are described.
[the 1st embodiment]
Fig. 1 is the concise and to the point formation schematic diagram of film formation device in the present invention's the 1st embodiment.Fig. 1 (a) is the plane graph of film formation device, and Fig. 1 (b) is a cutaway view.This film formation device can carry out aqueous film simultaneously and form technology and drying process.
At first describe carrying out aqueous film formed structure in the film formation device.As Fig. 1 (a); (b) shown in; by diaphragm dropping liquid nozzle 102 with this diaphragm dropping liquid nozzle 102 is provided with along the processed substrate 110 of mobile nozzle moving mechanism (not shown) of y direction (paper transverse direction) and diameter 200mm, processed substrate 110 is constituted along the processed substrate travelling carriage (not shown) that the x direction moves.
Then, the device formation of carrying out drying process is described.As shown in Figure 1, constitute with the vacuum pump 103 that is connected with suction nozzle 101 by suction nozzle 101.In addition, as what use in aqueous film formation technology, the processed substrate travelling carriage that has been illustrated also is the part that the drying process device constitutes.
The shape of the air entry 101a of suction nozzle 101 is 2 * 220mm, and the longitudinal length of air entry 101a (220mm) is more than the diameter (200mm) of processed substrate 110.The moving direction orthogonal configuration of the vertical and processed substrate of the air entry 101a of suction nozzle 101.Because the longitudinal length of air entry 101a is more than the diameter of processed substrate, the moving direction orthogonal configuration of the vertical and processed substrate of air entry 101a, so be accompanied by moving of processed substrate 110, processed substrate 110 can be scanned by suction nozzle 101 comprehensively.
Below, aqueous film formation and the drying process that uses this film formation device described.At first, the formation to aqueous film describes.With diaphragm dropping liquid nozzle 102 in of the speed reciprocating motion of processed substrate 110 upper edge y directions with 1 meter per second.If diaphragm dropping liquid nozzle 102 moves on to beyond the processed substrate 110, can processed substrate 110 be moved along the x direction in turn by processed substrate travelling carriage.From processed substrate 110+x side (coating starting position) is to-x side (coating ultimate position), uses chemical amplification type DUV diaphragm (M20G:JSR system) to drip in turn with wire (shape of unicursal), forms the thick aqueous film 111 of 40 μ m on substrate.
Below, drying is described.Through 30 seconds, the suction nozzle 101 of the position configuration that has by the flat portions that becomes with a certain distance from the aqueous film 111 that drips began processed substrate 110 is carried out drying after beginning from dropping liquid.By suction nozzle 101 the solvent atmosphere aspiration on the aqueous film 111 is walked, formed diaphragm (filming) 112.
Owing in advance diaphragm dropping liquid nozzle 102 and suction nozzle 101 are kept certain configuration space, be accompanied by moving of processed substrate 110, in processed real estate, can carry out aqueous film simultaneously and form technology and solvent seasoning technology.
According to this embodiment, carry out drying process after the soup planarization of dripping immediately, can shorten the formation time of final diaphragm.In addition, beginning not rely on the position of dripping to carrying out dry stand-by time from the soup that drips, almost is certain, therefore, to coating end of a period side film thickness distribution does not take place from coating beginning side.
In the film build method of the present embodiment, the configuration space between the distance of the size of suction nozzle, suction nozzle and processed substrate surface, suction nozzle 101 and the diaphragm dropping liquid nozzle 102, the speed of diaphragm dropping liquid nozzle 101 are respectively but are not limited to 2 * 220mm, 1mm, 50mm, 1 meter per second.In addition,, be not limited to this method, can use slit-type diaphragm nozzle, can carry out the meniscus coating as aqueous film formation method.In addition, aqueous film formation technology and drying process carry out in real estate simultaneously in this method, but also can carry out separately respectively.Soup used herein can be according to the technology appropriate change.
In addition; the present embodiment is to use the width slit-type suction nozzle bigger than processed substrate to operate in a direction; as shown in Figure 2; also can use the suction nozzle littler than processed substrate; the same when dripping with diaphragm; when suction nozzle is carried out shuttle-scanning, from dropping liquid begin side to the end the processed substrate of side shifting carry out drying.
[the 2nd embodiment]
It is identical with the device shown in Figure 1 that illustrates in the 1st embodiment that the device of the present embodiment constitutes, so omit the device explanation.Describe with regard to drying process.
At first, identical with the 1st embodiment, the soup that drips on processed substrate 110 begins to form aqueous film 111.
Be accompanied by moving of processed substrate 110, the air entry of the suction nozzle 101 that links to each other with vacuum pump 103 attracts the solvent atmosphere gas on the aqueous film 111 on the processed substrate 110, begins the 1st dried.
Even suction nozzle 101 by 111 whole of aqueous films after, from+x side (coating beginning side) to-x side (being coated with the end of a period side), the dissolvent residual in the aqueous film 111 still a lot, the thickness of aqueous film 111 is 10 μ m (Fig. 3 (a)).
As the 2nd dried, from+x side (coating beginning side) to-x side (being coated with the end of a period side), attract the solvent atmosphere gas on the aqueous film 111 in turn once more, carry out the 2nd dried.Aqueous film 111 thickness after the 2nd dried become 5 μ m.This dried amounts to repeatable operation 8 times, and the solvent in the aqueous film 111 is completely dried, finally forms the homogeneous diaphragm 112 (Fig. 3 (b)) of 300nm.
According to the present embodiment, by carrying out for several times dried repeatedly, aqueous film 111 has been prevented that by slowly dry solid formation branch in the aqueous film 111 is attracted, and can guarantee the homogeneity of thickness.
In the film build method of the present embodiment, the distance between the size of suction nozzle 101, suction nozzle 101 and processed substrate 110 surfaces, the speed of diaphragm dropping liquid nozzle are respectively but are not limited to 2 * 220mm, 2mm, 1m/ second.In addition,, be not limited to this method, can use the diaphragm of the slit-type nozzle that spues, can carry out the meniscus coating as aqueous film formation method.In addition, in the method, be not limited to carry out 5 times with the scanning of suction nozzle 101.Soup used herein can be according to the technology appropriate change.
The present embodiment is carried out the 1st dried and liquid film formation simultaneously, but is not limited thereto, and also can begin to carry out dried after substrate forms liquid film comprehensively.
[the 3rd embodiment]
It is identical with the device shown in Figure 1 that illustrates in the 1st embodiment that the device of the present embodiment constitutes, so omit the device explanation.Describe with regard to drying process.
At first, identical with the 1st embodiment, the soup that drips on processed substrate 110 begins to form aqueous film 111.But, in the present embodiment,, on substrate, form the thick aqueous film 111 of 40 μ m with wire (shape of the unicursal) interlayer dielectric (LKD21:JSR system) that drips in turn comprehensively.
Be accompanied by moving of processed substrate 110, the suction nozzle 101 that links to each other with vacuum pump 103 covers on the processed substrate 110, siphon away solvent atmosphere gas on the aqueous film 111 from air entry, begin the 1st dried from+x side (coating beginning side) to-x side (coating end of a period side).Even behind 111 whole of aqueous films, the dissolvent residual in the aqueous film 111 is still a lot, the thickness of aqueous film 111 is 10 μ m.In addition, at this moment, aqueous film thickness distributes from attracting the beginning side to attracting the end of a period side to demonstrate the tendency (Fig. 4 (a)) of thickening.
Therefore, as the 2nd dried,, siphon away the solvent atmosphere gas on the aqueous film 111 in turn from-x side (coating end of a period side) to+reverse the carrying out of x side (coating begins side).Aqueous film 111 thickness after the 2nd dried become 6 μ m, and aqueous film 111 thickness distribution flatten all smooth.By this repeatedly dried amount to 8 times (4 back and forth), the solvent in the aqueous film 111 is completely dried, finally forms the homogeneous diaphragm 112 (Fig. 4 (b)) of 500nm.
That is, in the present embodiment, the inferior mobile route of the mobile route of the aforementioned suction nozzle 101 relative with aforementioned processed substrate 110 and odd number is opposite in the dried of even number time.
In the present embodiment, owing to used more liquid soup, adopt two-way attraction so that do not produce to the thickness distribution tendency that attracts direction, reach the thickness planarization.
In the film build method of the present embodiment, the distance between the size of suction nozzle 101, suction nozzle 101 and processed substrate 110 surfaces, the speed of diaphragm dropping liquid nozzle, the substrate translational speed is respectively but be not limited to 2 * 220mm, 2mm, 1m/ second, 1.6mm/ second.In addition,, be not limited to this method, can use the diaphragm nozzle of slit-type, can carry out the meniscus coating as aqueous film formation method.In addition, in the method, be not limited to carry out (4 back and forth) 8 times with the shuttle-scanning of suction nozzle 101.Soup used herein can be according to the technology appropriate change.
The present embodiment is carried out the 1st dried and liquid film formation simultaneously, but is not limited thereto, and also can begin to carry out dried after substrate forms liquid film comprehensively.
[the 4th embodiment]
It is identical with the device shown in Figure 1 that illustrates in the 1st embodiment that the device of the present embodiment constitutes, so omit the device explanation.Describe with regard to drying process.
At first, identical with the 1st embodiment, the soup that drips on the processed substrate of cleaning 110 begins to form aqueous film 111.But, in the present embodiment,, on substrate, form the thick aqueous film 111 of 40 μ m with wire (shape of the unicursal) interlayer dielectric (LKD21:JSR system) that drips in turn comprehensively.
Be accompanied by moving of processed substrate 110, the air entry of the suction nozzle 101 that links to each other with vacuum pump 103 covers on the processed substrate 110, siphon away the solvent atmosphere gas on the aqueous film 111, begin the 1st dried from+x side (coating beginning side) to-x side (coating end of a period side).In addition, processed here substrate 110 surfaces are identical with the 1st embodiment with distance between the suction nozzle 101, are 2mm.
Even behind 111 whole of aqueous films, the dissolvent residual in the aqueous film 111 is still a lot, the thickness of aqueous film 111a is 10 μ m (Fig. 5 (a)).
Therefore, as the 2nd dried, processed substrate 110 surfaces and distance setting between the suction nozzle 101 be 1.5mm after, from+x side (coating beginning side) to-x side (being coated with the end of a period side), siphon away the solvent atmosphere gas on the aqueous film 111 in turn.Aqueous film 111 thickness after the 2nd dried become 1 μ m.
Then, as the 3rd dried, processed substrate 110 surfaces and distance setting between the suction nozzle 101 be 1mm after, from+x side (coating beginning side) to-x side (being coated with the end of a period side), siphon away the solvent atmosphere gas on the aqueous film 111 in turn.By this processing, aqueous film 111 thickness become 500nm.
Then, as the 4th dried, processed substrate 110 surfaces and distance setting between the suction nozzle 101 be 0.5mm after, from+x side (coating beginning side) to-x side (being coated with the end of a period side), siphon away the solvent atmosphere gas on the aqueous film 111 in turn.By above 4 steps processing, the solvent in the aqueous film 111 is completely dried, finally forms the diaphragm 112 (Fig. 5 (b)) of 300nm homogeneous.
In the present embodiment, according to the thickness of aqueous film 111,, improve drying efficiency by the distance between processed substrate 110 surfaces and the suction nozzle 101 is shifted near, form the high diaphragm 112 of homogeneity.
In the film build method of the present embodiment, distance, the substrate translational speed between the size of suction nozzle 101, suction nozzle 101 and processed substrate 110 surfaces is respectively but is not limited to 2 * 220mm, 2mm → 1.5mm → 1mm → 0.5mm, 1.6mm/ second.In addition,, be not limited to this method, can use the diaphragm of the slit-type nozzle that spues, can carry out the meniscus coating as aqueous film formation method.In addition, in the method, carry out 4 times slowly asymptotic the time, but carry out more than 4 times also passablely, also can below 4 times with the scanning of suction nozzle 101.In addition, this method is the scanning of carrying out according to a direction, and shuttle-scanning also can.Soup used herein can be according to the technology appropriate change.
The present embodiment is carried out the 1st dried and liquid film formation simultaneously, but is not limited thereto, and also can begin to carry out dried after substrate forms liquid film comprehensively.
[the 5th embodiment]
The device shown in Figure 1 that illustrates in device formation of the present embodiment and the 1st embodiment is basic identical, therefore omits the device explanation.But because the structure difference of suction nozzle 101, therefore the structure to suction nozzle 101 describes.
Fig. 6 is the organigram of suction nozzle 101 in the present invention's the 5th embodiment.In addition, in Fig. 6, the part identical with Fig. 1 represents that with prosign it illustrates omission.
As shown in Figure 6, the air entry that links to each other with vacuum pump 103 is that (2 * 220mm) suction nozzle 101, relative with this suction nozzle to be connected with forced draft fan (air-flow feeder) 602 air outlets that link to each other be the spray nozzle of the gas supply 601 of slit-type to slit-type.In addition, below suction nozzle 101 and spray nozzle of the gas supply are collectively referred to as the dry nozzle 600 of using of aqueous film.
As shown in Figure 6, dispose aqueous film drying and make spray nozzle of the gas supply 601 at aqueous film formed upstream side with nozzle 600, suction nozzle 101 is at downstream side.In addition, the dry nozzle 600 of aqueous film with the distance on processed substrate 110 surfaces is and aqueous film 111 discontiguous 1mm.
Below, the formation and the drying process of the aqueous film 111 that uses this film formation device described.Formation to aqueous film 111 describes.Diaphragm dropping liquid nozzle is moved back and forth in the speed of processed substrate 110 upper edge y directions with 1m/ second.If diaphragm dropping liquid nozzle moves on to beyond the processed substrate 110, processed substrate 110 can be moved along the x direction in turn.From processed substrate 110+x side (coating starting position) is to-x side (coating ultimate position); use chemical amplification type DUV diaphragm (M20G:JSR system) to drip in turn, on processed substrate 110, form the thick aqueous film 111 of 40 μ m all sidedly with wire (shape of unicursal).
After forming aqueous film 111a all sidedly on the processed substrate 110, nozzle is relative scans from coating beginning side to coating end of a period side with aforementioned aqueous film drying with processed substrate 110.At this moment; 601 couples of aqueous film 111b supply with air-flow from spray nozzle of the gas supply; by this air-flow that contains solvent that attracts on the aqueous film 111 with suction nozzle 101; by between the air entry of the air outlet of spray nozzle of the gas supply 601 on the aqueous film 111 and suction nozzle 101, producing air current flow; make the solvent seasoning in the aqueous film 111, form the homogeneous diaphragm 112 of thickness 300nm.
In the present embodiment,, can improve drying efficiency by increasing air current flow.In addition, use when having the soup of high flowability in the method, control the drying regime of aqueous film 111, can prevent that suction nozzle 101 from directly siphoning away soup by supplying with air-flow in advance.
In the present embodiment, aqueous film forms and dried is independently carried out respectively, but also can carry out simultaneously with the official hour difference as the 1st embodiment.In addition, also can resemble carry out the 2nd~the 4th embodiment several handle (folk prescription to, back and forth).In addition, in the present embodiment, use to be a side form the device of one as spray nozzle of the gas supply, a side as suction nozzle 101, also can use shown in Fig. 7 (a), in the both sides of air entry 700a air outlet 700b is set, the aqueous film that suction nozzle and air feed mouth become one is dry with nozzle 700.In addition, also can use shown in Fig. 7 (b), in the both sides of air outlet 700b air entry 700a is set, the aqueous film that suction nozzle and air feed mouth become one is dry with nozzle 700.In addition, in Fig. 7, the 103rd, vacuum pump, the 603rd, forced draft fan.
In the film build method of the present embodiment, the size of suction nozzle 101, the distance between suction nozzle 101 and processed substrate 110 surfaces, the diaphragm nozzle velocity is respectively but is not limited to 2 * 220mm, 1mm, 1m/ second.In addition,, be not limited to this method, can use the diaphragm nozzle of slit-type, can carry out the meniscus coating as aqueous film formation method.The soup that these membrance casting conditions are used can be according to the technology appropriate change.
In addition, the present invention is not limited to above-mentioned embodiment, and it all is possible carrying out various distortion enforcements in the scope that does not break away from its main idea.The effect of invention
As mentioned above, according to the present invention, the thickness uneven phenomenon that can suppress to film shortens to form and films the required time.
Brief description of drawings
[Fig. 1]
The concise and to the point formation schematic diagram of the film formation device that relates in the 1st embodiment.
[Fig. 2]
The concise and to the point formation schematic diagram of the variation of the film formation device that relates in the 1st embodiment.
[Fig. 3]
The film build method key diagram that relates in the 2nd embodiment.
[Fig. 4]
The film build method key diagram that relates in the 3rd embodiment.
[Fig. 5]
The film build method key diagram that relates in the 4th embodiment.
[Fig. 6]
The dry concise and to the point formation schematic diagram of using the variation of nozzle of the aqueous film of the film formation device that relates in the 5th embodiment.
[Fig. 7]
The concise and to the point formation schematic diagram of the film formation device that relates in the 5th embodiment.
Claims (11)
1, a kind of film build method, comprise that aqueous film forms technology and drying process, it is relative with processed substrate that aqueous film wherein forms technology, on substrate, be adjusted to a certain amount of expansion, drip from the dropping liquid nozzle and solvent, to have added the soup that solid formation divides, aforementioned dropping liquid nozzle and aforementioned processed substrate are relatively moved, on whole of aforementioned processed substrate, form the technology of aqueous film, drying process wherein is to form the technology of filming for the solvent of removing in the aforementioned aqueous film, wherein, aforementioned drying process be on aforementioned processed substrate with should be aqueous the discontiguous distance in film surface dispose suction nozzle, this suction nozzle relatively moves with this processed substrate, and the solvent atmosphere gas under the aforementioned suction nozzle is sucked away from the air entry of this suction nozzle simultaneously.
2, the film build method of record in the claim 1, it is characterized in that, after the aqueous film planarization on the aforementioned processed substrate, and before forming aqueous film all sidedly on the aforementioned processed substrate, carry out aforementioned aqueous film on one side and form technology, Yi Bian carry out aforementioned drying process.
3, the film build method of record in the claim 1 is characterized in that, relatively moves by making this processed substrate and aforementioned suction nozzle, carries out the dried to whole of aforementioned processed substrate for several times repeatedly.
4, the film build method of record in the claim 3 is characterized in that in the dried of aforementioned several, the mobile route of the aforementioned suction nozzle relative with aforementioned processed substrate is identical.
5, the film build method of record in the claim 3 is characterized in that, in the dried of aforementioned several, the inferior mobile route of the mobile route of the aforementioned suction nozzle relative with aforementioned processed substrate and odd number is opposite in the dried of even number time.
6, the film build method of record in the claim 3 is characterized in that, according to the drying regime of the aforementioned aqueous film after the dried last time, changes the distance between the aforementioned suction nozzle and this aqueous film surface in the dried next time.
7, the film build method of record in the claim 1, it is characterized in that, in aforementioned drying process, use the air feed mouth link to each other with the outer gas stream feedway, siphon away the aqueous film supply air-flow on the processed substrate of solvent atmosphere gas to air entry by aforementioned suction nozzle.
8, the film build method of record in the claim 1 is characterized in that, from the place ahead with respect to the direction that relatively moves of the aforementioned suction nozzle of aforementioned processed substrate, the aqueous film on processed substrate is supplied with air-flow.
9, film formation device is characterized in that, this device possesses following parts:
With the dropping liquid nozzle of the supply of chemical of the relative configuration of aforementioned processed substrate,
With relative configuration of aforementioned processed substrate, siphon away by from aforementioned dropping liquid nozzle supply of chemical and the suction nozzle of the solvent atmosphere gas on the aqueous film that aforementioned processed substrate forms,
Make the 1st moving part that aforementioned processed substrate and aforementioned dropping liquid nozzle relatively move and
The 2nd moving part that aforementioned processed substrate and suction nozzle are relatively moved.
10, the film formation device of record in the claim 9 is characterized in that, further possesses the air feed mouth of the aqueous film supply air-flow on aforementioned processed substrate.
11, the film formation device of record in the claim 9 is characterized in that the air entry of aforementioned suction nozzle length longitudinally is more than the aforementioned processed substrate.