CN1332045A - 一种冷轧带肋钢筋母材和冷轧带肋钢筋的生产工艺 - Google Patents
一种冷轧带肋钢筋母材和冷轧带肋钢筋的生产工艺 Download PDFInfo
- Publication number
- CN1332045A CN1332045A CN01127012A CN01127012A CN1332045A CN 1332045 A CN1332045 A CN 1332045A CN 01127012 A CN01127012 A CN 01127012A CN 01127012 A CN01127012 A CN 01127012A CN 1332045 A CN1332045 A CN 1332045A
- Authority
- CN
- China
- Prior art keywords
- rolling
- temperature
- mother metal
- steel bar
- cold rolled
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
级别代号 | 钢种 | 化学成分(%) | |||||
C | Si | Mn | Ti | P | S | ||
CRB800 | 24MnTi | 0.19-0.27 | 0.17-0.37 | 1.2-1.6 | 0.01-0.05 | ≤0.045 | ≤0.045 |
20MnSi | 0.17-0.25 | 0.40-0.80 | 1.2-1.6 | ≤0.045 | ≤0.045 |
钢种 | 开轧温度℃ | BGV入口温度℃ | 吐丝温度℃ | 斯太尔摩冷却线风机 | 辊道速度rmp |
CRB800母材 | 1100±30 | ≤980 | 960±20 | 1-2#开85% | 70 |
钢种 | 抗拉强度σbMpa | 伸长率δ5% | 冷弯试验180°,d=3ad=弯心直径a=试样直径 |
CRB800母材 | ≥6 50 | ≥22 | 无裂纹 |
元素 | C | Mn | P | S | Si | Nb | Ceq |
含量(%) | 0.18-0.22 | 1.3-1.51 | 0.018-0.032 | 0.018-0.030 | 0.49-0.62 | 0.018-0.025 | 0.4-0.48 |
项目 | σs(N/mm2) | σb(N/mm2) | δ5(%) |
母材的力学性能 | 485-555 | 670-755 | 24-30 |
项目 | σ0.2(N/mm2) | σb(N/mm2) | δ100(%) | 冷弯试验180°,d=3ad=弯心直径a=试样直径 |
抽检的产品性能 | 645-740 | 810-865 | 6-7 | 无裂纹 |
国家标准 | ≥640 | ≥800 | ≥4 | 无裂纹 |
来样编号/试样编号 | 276-1/OW139 | 276-20/OW1396 | 277/OW1397 | |
松弛性能 | 标准值 | 实测值 | ||
10h测定时间内松弛率% | ≤5 | 3.6 | 3.9 | |
100h测定时间内松弛率% | 4.8 | 5.0 | 3.6 | |
1000h松弛率% | ≤8 | 5.9* | 5.8 | |
备注 | *:5.9为推算1000h松弛率。 | |||
初负荷为相邻试样最大负荷的70%,其中试样编号为OW1397试样的初负荷为相邻试样最大负荷的72.8%。 |
Claims (3)