Summary of the invention
It is good to the objective of the invention is to propose a kind of material mechanical performance, and resistance toheat and processing characteristics have the polyvinyl chloride nano matrix material of raising again.
The polyvinyl chloride nano matrix material that the present invention proposes is to be prepared from organically modified montmorillonite clay intercalation polyvinyl chloride (PVC), and its starting material component proportioning by weight is as follows:
Polyvinyl chloride 100
Masterbatch 10.5-15.5
Stablizer 2-5
Processing aid 1
The present invention used polyvinyl chloride model can be WS-1000.
Organically modified montmorillonite clay of the present invention (0-MMT) is that its sheet interlayer spacing is 2nm-4nm through the montmorillonite of cationite 16-18 carbon alkylammonium salt, the modification of two 16-18 carbon alkylammonium salt.The montmorillonite particle diameter is generally 20-100 μ m.
Intercalation masterbatch prescription of the present invention following (weight part):
Intercalation resin 100
Organically modified montmorillonite clay (0-MMT) 10-50
Stablizer 2-5
Among the present invention, the intercalation resin that is adopted can be a kind of of vinyl chloride-vinyl acetate copolymer (VP), anti-impact type acrylate (ACR).The stablizer that is adopted can be a kind of of lead salt, organotin, calcium stearate, barium stearate.The processing aid that is adopted is a conventional material.The chlorinity of the polyvinyl chloride that adopts is 35-37%.
Because the present invention is compound organically modified montmorillonite clay in PVC, so also claim that this material is polyvinyl chloride/montmorillonite nano-composite material.
Polyvinyl chloride of the present invention/montmorillonite nano-composite material adopts the preparation of mother material fusion intercalation, and concrete steps are as follows:
(1) described intercalation resin, organically modified montmorillonite clay and stablizer are put into homogenizer by weight ratio and mix, with twin-roll plastic mixing mill or forcing machine or Banbury mixer melt blending, processing temperature is 110-130 ℃, obtains the intercalation masterbatch.
(2) again polyvinyl chloride and intercalation masterbatch, stablizer, processing aid are put into homogenizer by weight ratio and mixed, with twin-roll plastic mixing mill or forcing machine or Banbury mixer melt blending, processing temperature is 140-160 ℃, promptly obtains polyvinyl chloride/montmorillonite nano-composite material.
In the prepared polyvinyl chloride/montmorillonite nano-composite material of the present invention, organically modified montmorillonite clay reaches the nano-dispersed level in the polyvinyl chloride matrix, formed intercalation configuration, and matrix material has the good comprehensive performance, and its shock strength increases substantially.For example, mechanical property of material (intensity, toughness) and thermotolerance can improve simultaneously, and processing fluidity makes moderate progress.Like this, for the PVC door and window profile material, just can improve the physical and mechanical property index of section bar; Or keeping reducing the wall thickness of section bar on section bar drop impact performance and the rigid foundation, thus reduce every square metre of section bar consumption of door and window, improved the market competitiveness of plastic door-window.In addition,, can change and traditional improve its stable on heating method of modifying (processing of this method goods is difficulty especially),, both can improve heat resisting temperature, can improve its processing fluidity again with stratiform montmorillonite modified PVC with CPVC for heat-resistant PVC electric power tubing.In addition, this material is because the adding of laminated clay, can make it have good flame retardancy and puts out certainly.
Embodiment
The invention is further illustrated by the following examples.
With 100g vinyl chloride-vinyl acetate copolymer and 3 gram stablizer blend, with twin-roll plastic mixing mill or forcing machine or Banbury mixer fusion intercalation, processing temperature is 110 ℃, gets intercalation masterbatch 1;
100g vinyl chloride-vinyl acetate copolymer and 10 gram O-MMT, 3 are restrained the blend of stablizer lead salt, and with twin-roll plastic mixing mill or forcing machine or Banbury mixer fusion intercalation, processing temperature is 130 ℃, gets intercalation masterbatch 2;
100g vinyl chloride-vinyl acetate copolymer and 20 gram O-MMT, 3 are restrained the blend of stablizer lead salt, and with twin-roll plastic mixing mill or forcing machine or Banbury mixer fusion intercalation, processing temperature is 120 ℃, gets intercalation masterbatch 3;
100g vinyl chloride-vinyl acetate copolymer and 30 gram O-MMT, 3 are restrained the blend of stablizer organotin, and with twin-roll plastic mixing mill or forcing machine or Banbury mixer fusion intercalation, processing temperature is 125 ℃, gets intercalation masterbatch 4;
100g vinyl chloride-vinyl acetate copolymer and 40 gram O-MMT, 3 are restrained the blend of stablizer organotin, and with twin-roll plastic mixing mill or forcing machine or Banbury mixer fusion intercalation, processing temperature is 110 ℃, gets intercalation masterbatch 5;
100g vinyl chloride-vinyl acetate copolymer and 50 gram O-MMT, 3 are restrained the blend of stablizer calcium stearate, and with twin-roll plastic mixing mill or forcing machine or Banbury mixer fusion intercalation, processing temperature is 130 ℃, gets intercalation masterbatch 6.
With 100g anti-impact type ACR and 3 gram stablizer calcium stearate blend, with twin-roll plastic mixing mill or forcing machine or Banbury mixer fusion intercalation, processing temperature is 110 ℃, gets intercalation masterbatch 7.
Restrain the blend of stablizer barium stearate with 100g anti-impact type ACR with 10 gram O-MMT, 3, with twin-roll plastic mixing mill or forcing machine or Banbury mixer fusion intercalation, processing temperature is 130 ℃, gets intercalation masterbatch 8.
Restrain the blend of stablizer barium stearate with 100g anti-impact type ACR with 20 gram O-MMT, 3, with twin-roll plastic mixing mill or forcing machine or Banbury mixer fusion intercalation, processing temperature is 125 ℃, gets intercalation masterbatch 9.
Restrain the blend of stablizer organotin with 100g anti-impact type ACR with 30 gram O-MMT, 3, with twin-roll plastic mixing mill or forcing machine or Banbury mixer fusion intercalation, processing temperature is 120 ℃, gets intercalation masterbatch 10.
Restrain the blend of stablizer organotin with 100g anti-impact type ACR with 40 gram O-MMT, 3, with twin-roll plastic mixing mill or forcing machine or Banbury mixer fusion intercalation, processing temperature is 110 ℃, gets intercalation masterbatch 11.
Restrain the blend of stablizer lead salt with 100g anti-impact type ACR with 50 gram O-MMT, 3, with twin-roll plastic mixing mill or forcing machine or Banbury mixer fusion intercalation, processing temperature is 130 ℃, gets intercalation masterbatch 12.
Embodiment 1
With 100g polyvinyl chloride, 2-5g stablizer and the blend of 1g processing aid, stir with homogenizer, with twin-roll plastic mixing mill or forcing machine or Banbury mixer fusion intercalation, processing temperature is 140-160 ℃, obtains the blank material of polyvinyl chloride, its performance sees Table 1.
Embodiment 2
With 100g polyvinyl chloride, 2-5g stablizer and the blend of 1g processing aid, stir with homogenizer, mix with 10.5g masterbatch 1 then, with twin-roll plastic mixing mill or forcing machine or Banbury mixer fusion intercalation, processing temperature is 140-160 ℃, obtain polyvinyl chloride/montmorillonite nano-composite material, its performance sees Table 1.
Embodiment 3
With 100g polyvinyl chloride, 2-5g stablizer and the blend of 1g processing aid, stir with homogenizer, mix with 11.5g masterbatch 2 then, with twin-roll plastic mixing mill or forcing machine or Banbury mixer fusion intercalation, processing temperature is 140-160 ℃, obtain polyvinyl chloride/montmorillonite nano-composite material, its performance sees Table 1.
Embodiment 4
With 100g polyvinyl chloride, 2-5g stablizer and the blend of 1g processing aid, stir with homogenizer, mix with 12.5g masterbatch 3 then, with twin-roll plastic mixing mill or forcing machine or Banbury mixer fusion intercalation, processing temperature is 140-160 ℃, obtain polyvinyl chloride/montmorillonite nano-composite material, its performance sees Table 1.
Embodiment 5
With 100g polyvinyl chloride, 2-5g stablizer and the blend of 1g processing aid, stir with homogenizer, mix with 13.5g masterbatch 4 then, with twin-roll plastic mixing mill or forcing machine or Banbury mixer fusion intercalation, processing temperature is 140-160 ℃, obtain polyvinyl chloride/montmorillonite nano-composite material, its performance sees Table 1.
Embodiment 6
With 100g polyvinyl chloride, 2-5g stablizer and the blend of 1g processing aid, stir with homogenizer, mix with 14.5g masterbatch 5 then, with twin-roll plastic mixing mill or forcing machine or Banbury mixer fusion intercalation, processing temperature is 140-160 ℃, obtain polyvinyl chloride/montmorillonite nano-composite material, its performance sees Table 1.
Embodiment 7
With 100g polyvinyl chloride, 2-5g stablizer and the blend of 1g processing aid, stir with homogenizer, mix with 15.5g masterbatch 6 then, with twin-roll plastic mixing mill or forcing machine or Banbury mixer fusion intercalation, processing temperature is 140-160 ℃, obtain polyvinyl chloride/montmorillonite nano-composite material, its performance sees Table 1.
Embodiment 8
With 100g polyvinyl chloride, 2-5g stablizer and the blend of 1g processing aid, stir with homogenizer, mix with 10.5g masterbatch 7 then, with twin-roll plastic mixing mill or forcing machine or Banbury mixer fusion intercalation, processing temperature is 140-160 ℃, obtain polyvinyl chloride/montmorillonite nano-composite material, its performance sees Table 1.
Embodiment 9
With 100g polyvinyl chloride, 2-5g stablizer and the blend of 1g processing aid, stir then with homogenizer and to mix with 11.5g masterbatch 8, with twin-roll plastic mixing mill or forcing machine or Banbury mixer fusion intercalation, processing temperature is 140-160 ℃, obtain polyvinyl chloride/montmorillonite nano-composite material, its performance sees Table 1.
Embodiment 10
With 100g polyvinyl chloride, 2-5g stablizer and the blend of 1g processing aid, stir with homogenizer, 12.5g masterbatch 9 mixes then, with twin-roll plastic mixing mill or forcing machine or Banbury mixer fusion intercalation, processing temperature is 140-160 ℃, obtain polyvinyl chloride/montmorillonite nano-composite material, its performance sees Table 1.
Embodiment 11
With 100g polyvinyl chloride, 2-5g stablizer and the blend of 1g processing aid, stir with homogenizer, mix with 13.5g masterbatch 10 then, with twin-roll plastic mixing mill or forcing machine or Banbury mixer fusion intercalation, processing temperature is 140-160 ℃, obtain polyvinyl chloride/montmorillonite nano-composite material, its performance sees Table 1.
Embodiment 12
With 100g polyvinyl chloride, 2-5g stablizer and the blend of 1g processing aid, stir with homogenizer, mix with 14.5g masterbatch 11 then, with twin-roll plastic mixing mill or forcing machine or Banbury mixer fusion intercalation, processing temperature is 140-160 ℃, obtain polyvinyl chloride/montmorillonite nano-composite material, its performance sees Table 1.
Embodiment 13
With 100g polyvinyl chloride, 2-5g stablizer and the blend of 1g processing aid, stir with homogenizer, mix with 15.5g masterbatch 12 then, with twin-roll plastic mixing mill or forcing machine or Banbury mixer fusion intercalation, processing temperature is 140-160 ℃, obtain polyvinyl chloride/montmorillonite nano-composite material, its performance sees Table 1.
The performance that table 1 fusion intercalation mother material prepares polyvinyl chloride/montmorillonite nano-composite material compares
Embodiment |
PVC (g) |
Intercalation resinous type and dosage (phr) |
Tensile strength (MPa) |
Notched Izod impact strength (KJ/m
2)
|
1 |
100 |
|
59.69 |
2.14 |
2 |
100 |
Intercalation masterbatch 1,10.5 |
48.90 |
17.41 |
3 |
100 |
Intercalation masterbatch 2,11.5 |
43.48 |
27.43 |
4 |
100 |
Intercalation masterbatch 3,12.5 |
41.57 |
22.45 |
5 |
100 |
Intercalation masterbatch 4,13.5 |
47.92 |
15.9 |
6 |
100 |
Intercalation masterbatch 5,14.5 |
40.80 |
12.86 |
7 |
100 |
Intercalation masterbatch 6,15.5 |
37.23 |
6.17 |
8 |
100 |
Intercalation masterbatch 7,10.5 |
55.04 |
3.96 |
9 |
100 |
Intercalation masterbatch 8,11.5 |
53.1 |
6.16 |
10 |
100 |
Intercalation masterbatch 9,12.5 |
52.28 |
5.47 |
11 |
100 |
Intercalation masterbatch 10,13.5 |
53.76 |
4.98 |
12 |
100 |
Intercalation masterbatch 11,14.5 |
50.52 |
3.59 |
13 |
100 |
Intercalation masterbatch 12,15.5 |
54.78 |
2.54 |