CN1330587C - Magnetcisuspension polycoagulant, preparation method and application - Google Patents
Magnetcisuspension polycoagulant, preparation method and application Download PDFInfo
- Publication number
- CN1330587C CN1330587C CNB2004101025784A CN200410102578A CN1330587C CN 1330587 C CN1330587 C CN 1330587C CN B2004101025784 A CNB2004101025784 A CN B2004101025784A CN 200410102578 A CN200410102578 A CN 200410102578A CN 1330587 C CN1330587 C CN 1330587C
- Authority
- CN
- China
- Prior art keywords
- magnetcisuspension
- water
- oil
- polycoagulant
- flocculation agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention discloses magnetcisuspension polycoagulant, a preparation method and application thereof. Metered by weight, the magnetcisuspension polycoagulant contains 30 to 60 portions of 5% to 15% of polyacrylic acid liquid with molecular weight between 6000000 and 8000000, 20 to 40 portions of 20% to 40% of polysilicate aluminum, 2 to 10 portions of ferrous hydroxide, 2 to 10 portions of diatomite and 10 to 30 portions of water. The magnetcisuspension polycoagulant has a good flocculating and turbidity reducing function and a good oil removing function. The magnetcisuspension polycoagulant provided by the present invention causes that magnetic particles and non magnetic particles in water can be flocculated into large particles, oil in the water is adsorbed, and a rare earth magnetic disk is used for removing the large particles and the oil. The match of the rare earth magnetic disk and the magnetcisuspension polycoagulant has the advantages of short processing procedure, small occupation area, low use level, and high oil removing and turbidity reducing efficiency. The present invention matched with the rare earth magnetic disk can be widely used for treating various kinds of waste water containing suspended substances and the oil.
Description
Technical field
The present invention relates to a kind of flocculation agent, more particularly relate to a kind of magnetcisuspension flocculation agent that oily(waste)water reduces oil and suspension content that is used for, simultaneously, the invention still further relates to the preparation method of described magnetcisuspension flocculation agent and in Application of Sewage.
Background technology
Rare-earth magnetic disc equipment is to utilize magnetic diffusivity particulate matter in the magnetic suction drum planar water, to remove suspended substance in the water, is applied to sewage disposal.It is the magnetic material that rare-earth magnetic disc magnetic suction drum is configured to half area of rotary drum, second half is non magnetic material, half is immersed in rotary drum in the sewage, drum rotating is adsorbed in magnetic conduction suspended substance in the water on the rotary drum, go to position not under water with rotary drum, rubbing board is drawn together suspended substance and is removed, and arrives the purpose of clean water.Rare-earth magnetic disc equipment is mainly used in metallurgy industry and contains in the sewage disposal of magnetic conduction particulate matter, and its permeable material is mainly scum, ferric oxide etc.This equipment has the advantage that technical process is short, floor space is little.But often only do not contain the magnetic diffusivity suspended substance in the metallurgy industry sewage, especially steel-rolling sewage also contains a stand oil, and non-magnetic suspended substance and oil are that rare-earth magnetic disc can't be handled, and this has also just limited the application of rare-earth magnetic disc in sewage disposal.
Summary of the invention
Technical problem to be solved by this invention is to avoid above-mentioned deficiency of the prior art, and a kind of magnetcisuspension flocculation agent and its production and application is proposed, described magnetcisuspension flocculation agent cooperates rare-earth magnetic disc equipment to use, by throwing out with magnetic diffusivity suspended particulate in the sewage and the coacervation of non-magnetic suspended particulate, and oil in the planar water, rare-earth magnetic disc equipment is had simultaneously remove magnetic diffusivity suspended particulate in the sewage, non-magnetic suspended particulate and oily ability.
The invention provides a kind of magnetcisuspension flocculation agent, wherein by weight, comprise: 5%～15% molecular weight is 6,000,000～8,000,000 polyacrylic acid liquid 30-60 parts, 20%-40% aluminium silicate polymer solution 20-40 part, ferrous hydroxide 2-10 part, diatomite 2-10 part, water 10-30 part.
Preferably, described magnetcisuspension flocculation agent wherein by weight, comprises: 5%～15% molecular weight is 6,000,000～8,000,000 polyacrylic acid liquid 50-60 parts, 20%-40% aluminium silicate polymer 30-40 part, ferrous hydroxide 5-6 part, diatomite 2-3 part, water 10-20 part.
The invention provides the preparation method of described magnetcisuspension flocculation agent, this method may further comprise the steps: (1) adds entry and polyacrylic acid liquid in reactor, stir; (2) add ferrous hydroxide, be heated to 40-70 ℃, generate polyacrylic acid iron; (3) add diatomite, stir, mixing speed is 180-240 rev/min, and churning time is 20-30 minute, makes its thorough mixing; (4) add aluminium silicate polymer solution, stir, mixing speed is 180-240 rev/min, and churning time is 60-90 minute, and product is made.
The invention provides described magnetcisuspension flocculation agent in the Application of Sewage that contains suspended substance, oil.
The present invention has following advantage: magnetcisuspension flocculation agent of the present invention promptly has good flocculation and falls turbid effect, has good oil removing effect again.Throwing out: by the active group of this product polymer backbone, effect such as compression double electric layer, absorption, bridging becomes large stretch of flco with fine particulates coacervation in the sewage down, to quicken the sedimentation speed of suspended particulate.The oil removing effect: iron ion in the product in diatomite, the polyacrylic acid iron and the aluminum ion in the aluminium silicate polymer all have the effect of adsorbed oil, in water in particulate matter cohesion and the precipitation process, oil is adsorbed on the particulate matter in the water, together precipitates removal with suspended particulate.Utilize magnetcisuspension flocculation agent provided by the invention magnetic diffusivity particle and non-magnetic particle cohesion in the water can be macrobead, and oil in the planar water, utilize rare-earth magnetic disc to be removed again.It is short to adopt rare-earth magnetic disc to cooperate the magnetcisuspension flocculation agent to have treatment scheme, and floor space is little, and consumption is low, and the high advantage of turbid efficient falls in oil removing, cooperates rare-earth magnetic disc equipment can be widely used in various contain suspended substance (the part particle has magnetic diffusivity) and oily water processing.
Embodiment
Embodiment 1:
1130 kilograms in magnetcisuspension flocculation agent is prepared from for 200 kilograms at 550 kilograms of 6,000,000～8,000,000 polyacrylic acid liquid, 300 kilograms of 30% aluminium silicate polymer solution, 50 kilograms of ferrous hydroxides, 30 kilograms in diatomite, water by 10% molecular weight.The step for preparing this magnetcisuspension flocculation agent is: (1) adds 200 kg water and 550 kg polypropylene acid solution bodies in reactor, stir; (2) add 50 kg of hydrogen iron protoxides, be heated to 50 ℃, generate polyacrylic acid iron; (3) add 30 kilograms of diatomite, stir, mixing speed is 200 rev/mins, and churning time is 25 minutes, makes its thorough mixing; (4) add 300 kilograms of aluminium silicate polymer solution, stir, mixing speed is 200 rev/mins, and churning time is 80 minutes, makes this magnetcisuspension flocculation agent.
Be example with certain Steel Mill below, specify application and the effect thereof of this magnetcisuspension flocculation agent when cooperating the rare-earth magnetic disc device processes to contain suspended substance (the part particle has magnetic diffusivity) and oily water.
This Steel Mill's sewage quality is as follows:
| Project | Numerical value |
| The pH value | 5.5～8.5 |
| Hardness (mg/l) | 100～200 |
| Basicity (mg/l) | 50～150 |
| Specific conductivity (μ S/cm) | 200～500 |
| Suspended substance (mg/l) | 396 |
| Oil (mg/l) | 84 |
Wherein suspended substance weight ratio composition is:
| Composition | Weight ratio (%) |
| Fe | 10～20 |
| Fe 2O 3 | 30～50 |
| Ca | 2～6 |
| Si | 0.5～2 |
| Burning weight loss | 2～7 |
| Other | 15～35 |
Weight of oil than composition is:
| Composition | Weight ratio (%) |
| But oil slick | 50～70 |
| Oil in water emulsion | 30～50 |
Adopt rare-earth magnetic disc equipment to handle.When not adding this magnetcisuspension flocculation agent, the sewage quality after the processing is:
| Composition | Weight ratio (%) |
| Suspended substance (mg/l) | 120～150 |
| Oil (mg/l) | 65～75 |
Cooperate to add dosage when being this magnetcisuspension flocculation agent of 8mg/l, handle back water water quality and be:
| Composition | Weight ratio (%) |
| Suspended substance (mg/l) | 10～15 |
| Oil (mg/l) | 2.5～4.5 |
This shows and use the poly-agent of this magnetcisuspension can increase substantially the water treatment effect, show that fully the present invention has low dosage, technique effect efficiently.
Embodiment 2:
85 kilograms in magnetcisuspension flocculation agent is prepared from for 10 kilograms at 30 kilograms of 6,000,000～8,000,000 polyacrylic acid liquid, 40 kilograms of 21% aluminium silicate polymer solution, 3 kilograms of ferrous hydroxides, 2 kilograms in diatomite, water by 6% molecular weight.The step for preparing this magnetcisuspension flocculation agent is: (1) adds 10 kg water and 30 kg polypropylene acid solution bodies in reactor, stir; (2) add 3 kg of hydrogen iron protoxides, be heated to 45 ℃, generate polyacrylic acid iron; (3) add 2 kilograms of diatomite, stir, mixing speed is 180 rev/mins, and churning time is 20 minutes, makes its thorough mixing; (4) add 40 kilograms of aluminium silicate polymer solution, stir, mixing speed is 180 rev/mins, and churning time is 60 minutes, makes this magnetcisuspension flocculation agent.Use this magnetcisuspension flocculation agent cooperation rare-earth magnetic disc equipment can handle the sewage that contains suspended substance, oil, as the sewage disposal of Steel Plant, the sewage disposal of mechanical industry etc., the poly-agent of this magnetcisuspension adds by sewage load, and dosage is 3-20mg/L.
Embodiment 3: 129 kilograms in magnetcisuspension flocculation agent, make for 30 kilograms at 60 kilograms of 6,000,000～8,000,000 polyacrylic acid liquid, 20 kilograms of 40% aluminium silicate polymer solution, 9 kilograms of ferrous hydroxides, 10 kilograms in diatomite, water by 13% molecular weight.The step for preparing this magnetcisuspension flocculation agent is: (1) adds 30 kg water and 60 kg polypropylene acid solution bodies in reactor, stir; (2) add 9 kg of hydrogen iron protoxides, be heated to 69 ℃, generate polyacrylic acid iron; (3) add 10 kilograms of diatomite, stir, mixing speed is 235 rev/mins, and churning time is 30 minutes, makes its thorough mixing; (4) add 20 kilograms of aluminium silicate polymer solution, stir, mixing speed is 235 rev/mins, and churning time is 85 minutes, makes this magnetcisuspension flocculation agent.Use this magnetcisuspension flocculation agent cooperation rare-earth magnetic disc equipment can handle the sewage that contains suspended substance, oil, as the sewage disposal of Steel Plant, the sewage disposal of mechanical industry etc., the poly-agent of this magnetcisuspension adds by sewage load, and dosage is 3-20mg/L.
Claims (4)
1, a kind of magnetcisuspension flocculation agent wherein by weight, comprises:
5%～15% molecular weight is 6,000,000～8,000,000 polyacrylic acid liquid 30-60 parts, 20%-40% aluminium silicate polymer solution 20-40 part, ferrous hydroxide 2-10 part, diatomite 2-10 part, water 10-30 part.
2, magnetcisuspension flocculation agent as claimed in claim 1 wherein by weight, comprises:
5%～15% molecular weight is 6,000,000～8,000,000 polyacrylic acid liquid 50-60 parts, 20%-40% aluminium silicate polymer 30-40 part, ferrous hydroxide 5-6 part, diatomite 2-3 part, water 10-20 part.
3, the preparation method of magnetcisuspension flocculation agent as claimed in claim 1 or 2 is characterized in that this method may further comprise the steps:
(1) in reactor, adds entry and polyacrylic acid liquid, stir;
(2) add ferrous hydroxide, be heated to 40-70 ℃, generate polyacrylic acid iron;
(3) add diatomite, stir, mixing speed is 180-240 rev/min, and churning time is 20-30 minute, makes its thorough mixing;
(4) add aluminium silicate polymer solution, stir, mixing speed is 180-240 rev/min, and churning time is 60-90 minute, and product is made.
4, magnetcisuspension flocculation agent as claimed in claim 1 or 2 is in the Application of Sewage that contains suspended substance, oil.