CN1326934C - 干混法聚氯乙烯搪塑粉料及其生产方法 - Google Patents
干混法聚氯乙烯搪塑粉料及其生产方法 Download PDFInfo
- Publication number
- CN1326934C CN1326934C CNB2005100169218A CN200510016921A CN1326934C CN 1326934 C CN1326934 C CN 1326934C CN B2005100169218 A CNB2005100169218 A CN B2005100169218A CN 200510016921 A CN200510016921 A CN 200510016921A CN 1326934 C CN1326934 C CN 1326934C
- Authority
- CN
- China
- Prior art keywords
- pvc
- powder material
- slushing
- slushing powder
- still
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明属于高分子改性材料,涉及一种PVC搪塑粉料及其制备方法。该粉料是以PVC为基料,添加一定比例的多种助剂,用干混法制得的中高档轿车仪表板蒙皮所需要的搪塑粉料。依据德国大众汽车公司TL52296标准进行检测,于120℃热存放500小时以后的性能:断裂强度变化率24.3%,(进口产品为77.0%,标准规定≤45%),断裂延伸率下降70.9%(进口产品为22.6,标准规定≤30%)。本发明制得的PVC搪塑粉料制品,供货状态下性能完全达到所述的TL52296标准。同时简化了生产过程,大大降低了能耗。
Description
技术领域
本发明属于高分子改性材料领域,涉及一种以聚氯乙烯为基料,添加多种助剂制成的聚氯乙烯搪塑粉料及该搪塑粉料的制备方法。
背景技术
近年来,我国汽车行业特别是中高挡轿车发展较快。为配合引进生产线国产化的需要,研究开发中高挡轿车仪表板蒙皮所需要的高分子搪塑粉料,已成为研发单位和生产企业的重要课题。目前,有关涉及以上具有实质的信息未见报导。据悉世界上最大的生产厂商法国阿托公司采用混料后,以单螺杆机进行混炼挤出,并于约-100℃液氮深冷下粉碎,然后经筛分、后处理等收集产品(见图1,但其具体配方仍不清楚)。该工艺工序较长,能耗较高等。所述的搪塑粉料一般采用聚氯乙烯(PVC)基料。
发明内容
本发明的目的为了配合国产化的需要,提供轿车仪表板蒙皮所需要的PVC搪塑粉料;本发明的另一个目的在于解决现有生产工艺中存在的不足,提供一种干混法生产PVC搪塑粉料的方法。
本发明的目的是通过如下的技术方案予以实现
一种干混法PVC搪塑粉料,其特征在于:它是由如下重量份配比的原料和助剂制成的,其组成为:
PVC树脂100 Palamall 654 70 钙锌复合稳定剂2~5
碳黑1 ACR201 3~5 硬脂酸辛酯3~5
外润滑剂 1~2 PVC糊树脂8~10
所述的PVC搪塑料的生产方法,将碳黑研磨为所需的粒度;按设计配比进行原料计量;按给定的配方进行混料,其特征在于:当釜温达到120℃启动冷混釜,高混釜温升至125~135℃时向冷混釜内放料,并降温至90℃时将物料放至料槽内,自然陈化24小时;然后,将上述经陈化后的半成品再经后处理、筛分,收集80~120目产品。
本发明与法国阿托公司生产工艺相比,生产流程短,操作简单,能耗明显降低。其产品依据德国大众汽车公司TL52296-94标准进行检测,在120℃下热存放500小时后,其断裂强度变化率为24.3%(进口产品77.0%,标准要求≤45%),断裂延伸率下降70.9%(进口产品22.6%,标准要求≤30%)。按照上述标准检测其详细结果见下表.
表皮试验〔(按TL52296-94)〕不合格性能(红色项)对照表
项次 | 标准 | 吉化 | 进口(现生产) |
耐干燥摩擦 | 表面色样光泽无变化≥4级 | 有可见摩擦痕迹、3级 | 有可见摩擦痕迹、2-3级 |
耐浸渍洗涤剂摩擦 | — | 红项 | 红项 |
102#汽油 | 表面色调光泽无变化、≥4级 | 合格 | 合格 |
石油醚 | 表面色调光泽无变化、≥4级 | 合格 | 合格 |
无水乙醇 | 表面色调光泽无变化、≥4级 | 合格 | 合格 |
气味C3 | C1≤2C2≤3C3≤3 | 3.03.04.5 | 3.03.04.0 |
500小时,120℃老化试验 | — | 红项 | 红项 |
抗拉伸强度变化 | ≤45% | 24.3% | 77% |
断裂延伸率变化 | ≤30% | 79.9% | 22.6% |
附图说明
图1法国阿托公司生产工艺流程示意框图
图2本发明的生产工艺流程示意框图
具体实施方式
现结合附图和具体实施方式对本发明描述如下。
实施例
见图2,本发明PVC搪塑粉料生产由下面过程组成:
①碳黑研磨:在三辊研磨机上已配好的碳黑研磨三次,使其细度≤30um;
②物料计量:将100份的PVC树脂、ACR201(甲基丙烯酸甲酯与丙烯烃酸酯的共聚物)3~5份投入高混釜内,启动搅拌1分钟后,搅拌下向釜内加入钙锌复合稳定剂2~5份,并于1分钟后再加入已研磨好的碳黑1份;
③混料:当釜温达35℃时继续向釜内加入增塑剂Palamall 654(已二酸多羟基醇衍生聚合型增塑剂)20份、内润滑剂硬脂酸辛酯1~3份;当温度升至60℃时再加入上述的增塑剂50份、内润滑剂2份;当温度升至80℃时再加入计量的外润滑剂1~2份。
④当釜温达120℃时启动泠混釜,高混釜温度升至125~135℃时向冷混釜内放料,并降温90℃时将物料放入料槽中,自然状态下陈化24小时;(从附图1与图2可见到本发明与法国阿托公司生产过程中最大的不同,就是本发明省去了单螺杆挤出和-100℃下的深冷粉碎两步过程)然后,
⑤将上述陈化的半成品,投入高混釜中,启动低混1分钟后停机,向釜内加入PVC糊树脂8~10份,继续搅拌,釜温达到40℃时放料进入振动筛分,收集80~120目产品。从自然陈化24小时来看,似乎延长生产所用的时间,但实际上,当进行第二批后处理时,为本批准备的陈化半成品料已准备好,且不需要有人跟踪操作,因此本发明同时又省工。
本发明所用的原料和助剂均从市场上购进。
Claims (2)
1、一种干混法聚氯乙烯搪塑粉料,其特征在于:它是由如下重量份配比的原料和助剂制成的,其组成为:
聚氯乙烯树脂 100 Palamall 65470 钙锌复合稳定剂 2~5
碳黑 1 ACR201 3~5 硬脂酸辛酯 3~5
外润滑剂 1~2 聚氯乙烯糊树脂8~10。
2、如权利要求1所述的聚氯乙烯搪塑料的生产方法,将碳黑研磨成所需粒度;按设计配比进行原料计量;按给定的配比进行混料,其特征在于:釜温达120℃启动冷混釜,高混釜温升至于125~135℃时向冷混釜内放料,并降温至90℃时将物料放至料槽内,自然陈化24小时,经陈化后的半成品再经后处理、筛分后收集80~120目产品。