CN1312242C - Laminated adhesive aluminium foil band and it mfg. process - Google Patents
Laminated adhesive aluminium foil band and it mfg. process Download PDFInfo
- Publication number
- CN1312242C CN1312242C CNB2005100745392A CN200510074539A CN1312242C CN 1312242 C CN1312242 C CN 1312242C CN B2005100745392 A CNB2005100745392 A CN B2005100745392A CN 200510074539 A CN200510074539 A CN 200510074539A CN 1312242 C CN1312242 C CN 1312242C
- Authority
- CN
- China
- Prior art keywords
- layer
- aluminium foil
- line
- glue
- plastic film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention provides an aluminium foil adhesive band with double films and a manufacturing method thereof, which relates to an aluminium foil adhesive band, particularly to an aluminium foil adhesive band which adopts a double film and a manufacturing method thereof. The present invention provides an improved aluminium foil adhesive band and a manufacturing method thereof and is provided with a plastic film layer and an aluminium foil layer; an intermediate adhesive layer is arranged between the plastic film layer and the aluminium foil layer, and a bottom adhesive layer is arranged on the bottom surface of the aluminium foil layer. The present invention has the steps that: adhesive is coated on the upper surface of the plastic film layer to form the intermediate adhesive layer; the aluminium foil layer is covered on the intermediate adhesive layer; adhesive is coated on the lower surface of the aluminium foil layer to form the bottom adhesive layer; thus, the aluminium foil adhesive band with double films is manufactured. The present invention has the characteristics of good anti-corrosive performance, tension resistance, easy tearing, good initial viscosity, good holding viscosity, convenient and wide operation, low cost, high utilizing rate and reduction of resource waste.
Description
Technical field
The present invention relates to a kind of aluminum foil and adhesive tape, especially relate to a kind of aluminum foil and adhesive tape and manufacture method thereof that adopts multiple film.
Background technology
Existing aluminum foil and adhesive tape, for example the aluminum foil and adhesive tape of Xiamen vast of heaven plasticizing company limited product is a three-decker, and is superimposed by aluminium foil layer and separator paper layer, is coated with one deck glue between aluminium foil layer and separator paper layer.Its main drawback is the separator paper layer that needs with thicker, the waste resource, and the cost height, the physical length of 1 rolls of aluminum foil adhesive tape is shorter, and utilization ratio is low, and the easy moisture absorption of interleaving paper is gone mouldy.Its product can not get fine solution for a long time.The ZL01265953.3 patent provides a kind of conductive aluminum foil adhesive tape, comprise insulation layer, its surface-coated has tackiness agent, and its special character is: described tackiness agent is the electro-conductive adhesive that is mixed with uniform conducting particles in it, is coated with primer between this electro-conductive adhesive and insulation layer.
Summary of the invention
The objective of the invention is to provides a kind of improved aluminum foil and adhesive tape and manufacture method thereof at deficiencies such as existing aluminum foil and adhesive tape waste resource, cost height, utilization ratio are low.The present invention mainly adopts the technical scheme that replaces interleaving paper with multiple film for this reason.
The said laminated adhesive aluminium foil band of the present invention is provided with plastic film layers and aluminium foil layer, it between plastic film layers and aluminium foil layer intermediate gelatine layer, establish the bottom glue-line in the bottom surface of aluminium foil layer, said plastic film layers is selected from polyester (PET) thin film layer, polyvinyl chloride (PVC) thin film layer, phthalic acid (PTA) thin film layer, ethylene glycol (EG) thin film layer, polyethylene (PE) thin film layer etc., polypropylene bidirection drawing (BOPP) thin film layer or polypropylene (PP) thin film layer etc., said intermediate gelatine layer is selected from the water-based glue-line, the oiliness glue-line, pressure-sensitive adhesive layer, multiple film glue-line of oiliness or aqueous laminating glue-line etc., intermediate gelatine layer preferably is selected from oiliness glue-line or aqueous laminating glue-line.Said bottom glue-line is selected from water-based glue-line, oiliness glue-line, pressure-sensitive adhesive layer, the multiple film glue-line of oiliness or aqueous laminating glue-line etc., and the bottom glue-line preferably is selected from water-based glue-line, oiliness glue-line or pressure-sensitive adhesive layer etc.The thickness of aluminium foil layer is 4～40 μ m, preferred 10～25 μ m; The thickness of plastic film layers is 4～40 μ m, preferred 10～25 μ m; The thickness of intermediate gelatine layer is 4～40 μ m, preferred 4～10 μ m; The thickness of bottom glue-line is 4～40 μ m, preferred 15～30 μ m.
The manufacture method of the said laminated adhesive aluminium foil band of the present invention the steps include:
1), forms intermediate gelatine layer at plastic film layers upper surface gluing;
2) answering aluminium foil layer on the intermediate gelatine layer;
3) at the lower surface gluing of aluminium foil layer, form the bottom glue-line, promptly make laminated adhesive aluminium foil band.
When plastic film layers upper surface gluing, can adopt gluing roller gluing, after 5～10m drying tunnel, drying tunnel temperature is 80～100 ℃, arrives pressure roll again behind pony press, and the temperature of pressure roll is 80～100 ℃, and speed is 10～30m/min, forms intermediate gelatine layer.
Laminated adhesive aluminium foil band can be processed into the laminated adhesive aluminium foil band volume.
Compare with existing aluminum foil and adhesive tape, the present invention has good anticorrosion, tension, easily tear fracture, tack and hold the good characteristic of viscosity, uses not only convenient but also extensively, and cost is low, and the utilization ratio height has reduced the wasting of resources.
Description of drawings
Fig. 1 is the structural representation of the embodiment of the invention.
Embodiment
Embodiment 1
As shown in Figure 1, the said laminated adhesive aluminium foil band of the present invention is provided with plastic film layers 1 and aluminium foil layer 2, be coated with oily gum at plastic film layers 1 upper surface, adopt gluing roller gluing, after the 5m drying tunnel, drying tunnel temperature is 80 ℃, behind pony press, arrive pressure roll again, the temperature of pressure roll is 80 ℃, and speed is 10m/min, forms intermediate gelatine layer 3.Answering aluminium foil layer 2 on the intermediate gelatine layer 3, at the coated on bottom side water-base cement of aluminium foil layer 2, form bottom glue-line 4, promptly make laminated adhesive aluminium foil band.Laminated adhesive aluminium foil band is processed into the laminated adhesive aluminium foil band volume.
The thickness of aluminium foil layer 2 is 4 μ m; The thickness of plastic film layers 1 is 10 μ m; The thickness of intermediate gelatine layer 3 is 10 μ m, and the thickness of bottom glue-line 4 is 4 μ m.
Embodiment 2
Similar to Example 1, its difference is that the step of processing laminated adhesive aluminium foil band is: be coated with aqueous laminating adhesive at plastic film layers 1 upper surface, adopt gluing roller gluing, after 8m drying tunnel, drying tunnel temperature is 90 ℃, arrives pressure roll again behind pony press, and the temperature of pressure roll is 90 ℃, speed is 30m/min, forms intermediate gelatine layer 3.Answering aluminium foil layer 2 on the intermediate gelatine layer 3, at the coated on bottom side oily gum of aluminium foil layer 2, form bottom glue-line 4, promptly make laminated adhesive aluminium foil band.Laminated adhesive aluminium foil band is processed into the laminated adhesive aluminium foil band volume.
The thickness of aluminium foil layer is 10 μ m; The thickness of plastic film layers is 25 μ m; The thickness of intermediate gelatine layer is 15 μ m, and the thickness of bottom glue-line is 10 μ m.
Embodiment 3
Similar to Example 1, its difference is that the step of processing laminated adhesive aluminium foil band is: be coated with water-base cement at plastic film layers 1 upper surface, adopt gluing roller gluing, after 10m drying tunnel, drying tunnel temperature is 100 ℃, arrives pressure roll again behind pony press, and the temperature of pressure roll is 100 ℃, speed is 25m/min, forms intermediate gelatine layer 3.Answering aluminium foil layer 2 on the intermediate gelatine layer 3, at the coated on bottom side pressure sensitive adhesive of aluminium foil layer 2, form bottom glue-line 4, promptly make laminated adhesive aluminium foil band.Laminated adhesive aluminium foil band is processed into the laminated adhesive aluminium foil band volume.
The thickness of aluminium foil layer is 15 μ m; The thickness of plastic film layers is 4 μ m; The thickness of intermediate gelatine layer is 4 μ m, and the thickness of bottom glue-line is 20 μ m.
Embodiment 4
Similar to Example 1, its difference is that the step of processing laminated adhesive aluminium foil band is: be coated with pressure sensitive adhesive at plastic film layers 1 upper surface, adopt gluing roller gluing, after 10m drying tunnel, drying tunnel temperature is 85 ℃, arrives pressure roll again behind pony press, and the temperature of pressure roll is 95 ℃, speed is 20m/min, forms intermediate gelatine layer 3.Answering aluminium foil layer 2 on the intermediate gelatine layer 3,, forming bottom glue-line 4, promptly making laminated adhesive aluminium foil band at the multiple film glue of the coated on bottom side oiliness of aluminium foil layer 2.Laminated adhesive aluminium foil band is processed into the laminated adhesive aluminium foil band volume.
The thickness of aluminium foil layer is 20 μ m; The thickness of plastic film layers is 35 μ m; The thickness of intermediate gelatine layer is 25 μ m, and the thickness of bottom glue-line is 25 μ m.
Embodiment 5
Similar to Example 1, its difference is that the step of processing laminated adhesive aluminium foil band is: be coated with the multiple film glue of oiliness at plastic film layers 1 upper surface, adopt gluing roller gluing, after 6m drying tunnel, drying tunnel temperature is 100 ℃, arrives pressure roll again behind pony press, and the temperature of pressure roll is 85 ℃, speed is 25m/min, forms intermediate gelatine layer 3.Answering aluminium foil layer 2 on the intermediate gelatine layer 3, at the coated on bottom side water-base cement of aluminium foil layer 2, form bottom glue-line 4, promptly make laminated adhesive aluminium foil band.Laminated adhesive aluminium foil band is processed into the laminated adhesive aluminium foil band volume.
The thickness of aluminium foil layer is 25 μ m; The thickness of plastic film layers is 40 μ m; The thickness of intermediate gelatine layer is 35 μ m, and the thickness of bottom glue-line is 30 μ m.
Embodiment 6
Similar to Example 1, its difference is that the step of processing laminated adhesive aluminium foil band is: be coated with aqueous laminating adhesive at plastic film layers 1 upper surface, adopt gluing roller gluing, after 7m drying tunnel, drying tunnel temperature is 100 ℃, arrives pressure roll again behind pony press, and the temperature of pressure roll is 100 ℃, speed is 20m/min, forms intermediate gelatine layer 3.Answering aluminium foil layer 2 on the intermediate gelatine layer 3, at the coated on bottom side water-base cement of aluminium foil layer 2, form bottom glue-line 4, promptly make laminated adhesive aluminium foil band.Laminated adhesive aluminium foil band is processed into the laminated adhesive aluminium foil band volume.
The thickness of aluminium foil layer is 30 μ m; The thickness of plastic film layers is 10 μ m; The thickness of intermediate gelatine layer is 20 μ m, and the thickness of bottom glue-line is 15 μ m.
Embodiment 7
Similar to Example 1, its difference is that the step of processing laminated adhesive aluminium foil band is: be coated with oily gum at plastic film layers 1 upper surface, adopt gluing roller gluing, after 8m drying tunnel, drying tunnel temperature is 95 ℃, arrives pressure roll again behind pony press, and the temperature of pressure roll is 85 ℃, speed is 15m/min, forms intermediate gelatine layer 3.Answering aluminium foil layer 2 on the intermediate gelatine layer 3, at the coated on bottom side oily gum of aluminium foil layer 2, form bottom glue-line 4, promptly make laminated adhesive aluminium foil band.Laminated adhesive aluminium foil band is processed into the laminated adhesive aluminium foil band volume.
The thickness of aluminium foil layer is 35 μ m; The thickness of plastic film layers is 30 μ m; The thickness of intermediate gelatine layer is 40 μ m, and the thickness of bottom glue-line is 35 μ m.
Embodiment 8
Similar to Example 1, its difference is that the step of processing laminated adhesive aluminium foil band is: be coated with aqueous laminating adhesive at plastic film layers 1 upper surface, adopt gluing roller gluing, after 10m drying tunnel, drying tunnel temperature is 80 ℃, arrives pressure roll again behind pony press, and the temperature of pressure roll is 90 ℃, speed is 15m/min, forms intermediate gelatine layer 3.Answering aluminium foil layer 2 on the intermediate gelatine layer 3, at the coated on bottom side pressure sensitive adhesive of aluminium foil layer 2, form bottom glue-line 4, promptly make laminated adhesive aluminium foil band.Laminated adhesive aluminium foil band is processed into the laminated adhesive aluminium foil band volume.
The thickness of aluminium foil layer is 40 μ m; The thickness of plastic film layers is 20 μ m; The thickness of intermediate gelatine layer is 10 μ m, and the thickness of bottom glue-line is 40 μ m.
Claims (4)
1, laminated adhesive aluminium foil band is characterized in that being provided with plastic film layers and aluminium foil layer, is intermediate gelatine layer between plastic film layers and aluminium foil layer, establishes the bottom glue-line in the bottom surface of aluminium foil layer;
Described plastic film layers is selected from laminated polyester film, polyvinyl chloride film layer, phthalic acid thin film layer, ethylene glycol thin film layer, film layer or layer of polypropylene foil;
Described intermediate gelatine layer is selected from oiliness glue-line or aqueous laminating glue-line;
Described bottom glue-line is selected from water-based glue-line or oiliness glue-line;
The thickness of described aluminium foil layer is 10～25 μ m; The thickness of plastic film layers is 10～25 μ m; The thickness of intermediate gelatine layer is 4～10 μ m; The thickness of bottom glue-line is 15～30 μ m.
2, laminated adhesive aluminium foil band as claimed in claim 1 is characterized in that described layer of polypropylene foil is the polypropylene bidirection drawing thin film layer.
3, laminated adhesive aluminium foil band as claimed in claim 1 is characterized in that described water-based glue-line and oiliness glue-line are pressure-sensitive adhesive layer.
4, as the manufacture method of described laminated adhesive aluminium foil band one of in the claim 1 to 3, it is characterized in that the steps include:
1) at plastic film layers upper surface gluing, adopt gluing roller gluing, after 5～10m drying tunnel, drying tunnel temperature is 80～100 ℃, arrives pressure roll again behind pony press, and the temperature of pressure roll is 80～100 ℃, and speed is 10～30m/min, forms intermediate gelatine layer;
2) answering aluminium foil layer on the intermediate gelatine layer;
3) at the lower surface gluing of aluminium foil layer, form the bottom glue-line, promptly make laminated adhesive aluminium foil band.