CN1304650C - 一种相变复合纺丝原液及其制备和应用 - Google Patents

一种相变复合纺丝原液及其制备和应用 Download PDF

Info

Publication number
CN1304650C
CN1304650C CN 03129652 CN03129652A CN1304650C CN 1304650 C CN1304650 C CN 1304650C CN 03129652 CN03129652 CN 03129652 CN 03129652 A CN03129652 A CN 03129652A CN 1304650 C CN1304650 C CN 1304650C
Authority
CN
China
Prior art keywords
fiber
phase change
solvent
solution
spinning
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 03129652
Other languages
English (en)
Other versions
CN1493720A (zh
Inventor
陈彦模
朱美芳
张瑜
许文菊
左伟伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Donghua University
Original Assignee
Donghua University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Donghua University filed Critical Donghua University
Priority to CN 03129652 priority Critical patent/CN1304650C/zh
Publication of CN1493720A publication Critical patent/CN1493720A/zh
Application granted granted Critical
Publication of CN1304650C publication Critical patent/CN1304650C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明涉及一种相变复合纺丝原液及其制备和应用，属纺丝原液制备和应用技术领域。该原液含溶质和溶剂，溶质是相变物质和成纤高聚物材料，相变物质是聚烯烃类，成纤高聚物材料是纤维素及其衍生物、甲壳素及其衍生物、聚丙烯腈或聚乙烯醇，溶剂是DMSO、酮、有机酸、蒸馏水或DMF和丙酮的混合物。利用该原液，在静电纺设备上通过静电纺丝法：加料、静电纺丝和纤维收集三步制备超细相变纤维和超细相变纤维毡。该原液应用于静电纺丝，具有良好的可纺性。利用超细相变纤维可以做成兼有呼吸性、防护性和温度舒适性的多功能防护服。

Description

一种相变复合纺丝原液及其制备和应用
                     技术领域
本发明涉及一种相变复合纺丝原液及其制备和应用，属纺丝原液制备和应用技术领域。
                     背景技术
利用某些物质在相转变过程中的吸热和放热现象，可以进行热能贮存和温度调节控制。利用这些低温热能储存相变物质来制备温适纤维和纺织品的研究从80年代就开始了。Vigo等人自80年代中期开始研究将中空纤维浸渍在聚乙二醇(PEG)或塑晶(plastic crystalline)材料的溶液或熔体中，使聚乙二醇或塑晶进入纤维内部，得到在-40～60℃温度具有相变特性的纤维。这种纤维的内径较大，相变物质残留于纤维表面。目前已经商品化的是微胶囊包覆相变材料或粉末，主要用于常规服用纤维。
静电纺丝法即聚合物喷射静电拉伸纺丝法，是一种制备超细纤维的重要方法。用该法制得的纤维比传统的纺丝方法细得多，纤维直径一般在数十到上千纳米。该法一般用于纺制PEO、PAN、PBI等的超细纤维和超细纤维毡，但应用该法纺制具有相变储热功能的超细纤维和超细纤维毡的研究至今尚未见报道。
                   发明内容
本发明要解决的第一个技术问题是提出一种相变复合纺丝原液，该原液含溶质和溶剂，溶质溶于溶剂中，其特征在于，溶质是相变物质和成纤高聚物材料，相变物质是聚烯烃类，成纤高聚物材料是纤维素及其衍生物、甲壳素及其衍生物、聚丙烯腈或聚乙烯醇，相变物质和成纤高聚物材料分别溶解于同一种溶剂中后混合均匀，溶剂是DMSO、酮、有机酸、蒸馏水或DMF和丙酮的混合物。利用该原液通过静电纺丝法可制备超细相变纤维和超细相变纤维毡。
本发明要解决的第二个技术问题是提供一种相变复合纺丝原液的制备。本发明通过以下技术方案使上述技术问题得到解决：通过配制相变物质溶液A、配制成纤高聚物材料溶液B、混合溶液A和溶液B至均匀三步制得相变复合纺丝原液，溶液A和溶液B的溶剂相同。
现详细说明本发明所述的相变复合纺丝原液的制备。所述的相变复合纺丝原液的制备，其特征在于，操作步骤：
第一步配制溶液A
将相变物质溶解在溶剂中，搅拌均匀，配制成溶液A，浓度为2～30wt％，相变物质是聚烯烃类、PMA或PA，溶剂是DMSO、酮、有机酸、蒸馏水或DMF和丙酮的混合物；
第二步配制溶液B
将成纤高聚物材料溶解在溶剂中，搅拌均匀，配制成溶液B，浓度在2～3Owt％，成纤高聚物材料是纤维素及其衍生物、甲壳素及其衍生物、聚丙烯腈或聚乙烯醇，溶剂是DMSO、酮、有机酸、蒸馏水或DMF和丙酮的混合物，溶液A和溶液B中的溶剂相同；
第三步混合溶液A和溶液B
将溶液A加入溶液B混合均匀，相变物质和成纤高聚物的重量比为20～70∶80～30，纺丝原液浓度为8～15wt％。
本发明的进一步特征在于，成纤高聚物材料是微晶纤维素、木浆粕、二醋酸纤维素或三醋酸纤维素；溶剂是丙酮、甲基乙基酮或醋酸。
本发明要解决的第三个技术问题是提供一种相变复合纺丝原液的应用。本发明采用以下技术方案解决上述技术问题：利用本发明所述的相变复合纺丝原液，在静电纺丝设备上通过静电纺丝法：加料、静电纺丝和纤维收集三步制备超细相变纤维和超细相变纤维毡。
现结合附图详细说明本发明所述的相变复合纺丝原液的应用。
所述的相变复合纺丝原液的应用，需在静电纺丝设备上实施，其特征在于，操作步骤：
第一步加料
将所述的相变复合纺丝原液经脱泡、过滤后注入计量泵1中，计量泵1的泵体保温温度为20～90℃；
第二步静电纺丝
原液在高压静电作用下通过喷丝模口2在泰勒点3处被加速形成喷射细流5，喷丝模口2的毛细管孔径为0.2～0.8mm，纺程上采用20～100℃的空气为介质，气流速度为0～1m/min，静电场电压为10～60kv；
第三步纤维收集
喷射细流5在喷射过程中溶剂挥发固化后落在纤维接受装置4上，制得超细相变纤维和超细相变纤维毡，纤维的平均直径为20～600nm，纤维和纤维毡升温时相变温度为26～70℃，降温时相变温度为38～14℃，相变焓为20～250J/g。
本发明的优点：
一、本发明所述的相变复合纺丝原液应用于静电纺丝，具有良好的可纺性。
二、本发明的应用所制得的超细相变纤维和超细相变纤维毡具有很高的比表面积和表面积体积比、很强的吸附力以及良好的过滤性、阻隔性和优良的温度调节性能。适用于生产聚合物超细纤维非织造布，该产品可用作特殊温度要求下使用的过滤材料、高功能材料、屏蔽材料、生物和医疗用品、精密微型元器件的防护用品等，在起到一般超细纤维作用的同时可以将所包覆物体的温度保持在一定的范围，从而避免了物体在温度过高或过低时受到损伤。利用超细相变纤维的低密度、高孔隙度、大比表面积和相变性能可以做成兼有可呼吸性、防护性和温度舒适性的多功能防护服。
               附图说明
图1是静电纺丝过程示意图。其中，1是计量泵，2是喷丝模口，3是泰勒点，4是纤维接受装置，5是喷射细流。静电场电压为10～60kv，施加在+、-端之间。
                   具体实施方式
所有实施例完全按照上述的一种相变复合纺丝原液的制备和应用的操作步骤操作。
实施例1
相变复合纺丝原液的制备：
相变物质为PMA或PA，溶剂为DMF和丙酮的混合物，DMF和丙酮的共混重量比例为50∶50～98∶2；成纤高聚物材料为聚丙烯腈，溶剂为DMF和丙酮的混合物，DMF和丙酮的共混重量比例为50∶50～98∶2；相变物质与成纤高聚物的重量比为50～70∶50～30，纺丝原液浓度为8～15wt％。
相变复合纺丝原液的应用：
计量泵1的泵体保温温度为50～90℃；喷丝模口2的毛细管孔径为0.3～0.8mm，纺程上采用50～100℃的空气为介质，气流速度为0～1m/min，静电场电压为10～60kv；制得的纤维的平均直径为100～600nm，纤维和纤维毡升温时相变温度为50～70℃，降温时相变温度为45～38℃，相变焓为100～250J/g。

Claims (4)

1.一种相变复合纺丝原液，含溶质和溶剂，溶质溶于溶剂中，其特征在于，溶质是相变物质和成纤高聚物材料，相变物质是聚烯烃类，成纤高聚物材料是纤维素及其衍生物、甲壳素及其衍生物、聚丙烯腈或聚乙烯醇，溶剂是DMSO、酮、有机酸、蒸馏水或DMF和丙酮的混合物。
2.权利要求1所述的相变复合纺丝原液的制备，其特征在于，操作步骤：
第一步 配制溶液A
将相变物质溶解在溶剂中，搅拌均匀，配制成溶液A，浓度为2～30wt％，相变物质是聚烯烃类、PMA或PA，溶剂是DMSO、酮、有机酸、蒸馏水或DMF和丙酮的混合物；
第二步 配制溶液B
将成纤高聚物材料溶解在溶剂中，搅拌均匀，配制成溶液B，浓度在2～30wt％，成纤高聚物材料是纤维素及其衍生物、甲壳素及其衍生物、聚丙烯腈或聚乙烯醇，溶剂是DMSO、酮、有机酸、蒸馏水或DMF和丙酮的混合物，溶液A和溶液B中的溶剂相同；
第三步 混合溶液A和溶液B
将溶液A加入溶液B混合均匀，相变物质和成纤高聚物的重量比为20～70∶80～30，纺丝原液浓度为8～15wt％。
3.根据权利要求2所述的相变复合纺丝原液的制备，其特征在于，成纤高聚物材料是微晶纤维素、木浆粕、二醋酸纤维素或三醋酸纤维素；溶剂是丙酮、甲基乙基酮或醋酸。
4.权利要求1所述的相变复合纺丝原液的应用，需在静电纺丝设备上实施，其特征在于，操作步骤：
第一步 加料
将所述的相变复合纺丝原液经脱泡、过滤后注入计量泵(1)中，计量泵(1)的泵体保温温度为20～90℃；
计量泵(1)的泵体保温温度为20～90℃；
第二步 静电纺丝
原液在高压静电作用下通过喷丝模口(2)在泰勒点(3)处被加速形成喷射细流(5)，喷丝模口(2)的毛细管孔径为0.2～0.8mm，纺程上采用20～100℃的空气为介质，气流速度为0～1m/min，静电场电压为10～60kv；
第三步 纤维收集
喷射细流(5)在喷射过程中溶剂挥发固化后落在纤维接受装置(4)上，制得超细相变纤维和超细相变纤维毡，纤维的平均直径为20～600nm，纤维和纤维毡升温时相变温度为26～70℃，降温时相变温度为38～14℃，相变焓为20～250J/g。
CN 03129652 2003-07-02 2003-07-02 一种相变复合纺丝原液及其制备和应用 Expired - Fee Related CN1304650C (zh)