CN1294959A - Manufacture of composite wood board with conducting function - Google Patents
Manufacture of composite wood board with conducting function Download PDFInfo
- Publication number
- CN1294959A CN1294959A CN 99122281 CN99122281A CN1294959A CN 1294959 A CN1294959 A CN 1294959A CN 99122281 CN99122281 CN 99122281 CN 99122281 A CN99122281 A CN 99122281A CN 1294959 A CN1294959 A CN 1294959A
- Authority
- CN
- China
- Prior art keywords
- wooden unit
- conduction
- wood board
- accounts
- composite wood
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
In order to obtain conducting composite wood board capable of shielding electromagnetic wave and resisting static electricity, the wood board has alternating laminated structure of mixture comprising conducing struffing and adhesive and wooden unit and thick layers connecting conducting stuffing on the sides of the laminated structure. The composite wood board has resistivity altered for different requirement and low free aldehyde releasing amount and thus no environmental pollution while maintaining the strength and natural grains of timber.
Description
The present invention relates to the manufacture method of a class composite wood board.
At present, traditional composite wood board is composited by wooden unit (veneer, wood shavings, fiber etc.) and binder resin (urea aldehyde, phenolic aldehyde etc.).Indoor design condition is down because the specific insulation of wood materials and binder resin is respectively 10
9～10
12With 10
12～10
13Ohmcm so the sheet material after compound still belongs to the insulator category, belongs to good electrical insulator during use.
Shielding electromagnetic wave or anlistatig conducting function wood materials have abroad appearred having, as: Japan Patent JP8148804A, JP51004596A and JP55015047B, make cement, timber, resin, paper surface conduction production method, owing to only relate to material surface, and do not relate to base material, static capacity is little, and is black; And for example: Japan Patent JP63303731A, JP62273805A and JP59094676A etc., utilize metal material (as: powder, fiber, salt, solution, paper tinsel) reaches the conducting function of wood materials, but, common Lauxite or phenolic resins can not make itself and lignocellulosic reach good bonding, and high performance epoxy resin or isocyanates, cost height not only, and irony equipment also produced serious bonding consequence, technologic adaptability is relatively poor, be difficult to by instructions for use controlling resistance rate, and service time one is long, shield effectiveness decline (annual decline 5 decibels); Also, utilize the wood materials high temperature carbonization to reach conductive effect just like Japan Patent JP7100986A and JP59147494A, complex process, cost is higher, do not have the compound comprehensive function of lamination, and shield effectiveness is poor; In addition, as U.S. Pat 4906484A, Japan Patent JP5185406A, JP5177610A, utilize mix that carbon particle, furnace black, pot are black, graphite, tar etc. realize still, whole base materials being carried out conductive processing by conducting function, antistatic cost is higher.
In view of this, the manufacture method that the purpose of this invention is to provide a kind of composite wood board with conducting function, it is the laminated construction that adds material, wooden unit and binder resin with conduction, can control the different resistivity that require quantitatively, the plate surface cleaning helps follow-up decoration processing simultaneously.
The object of the present invention is achieved like this: a kind of manufacture method of composite wood board with conducting function, and the step of its manufacturing is divided into: 1) timber subdivision, timber rotary-cut or slicing become the wooden unit of Monoplacophora; 2) heat drying; It is characterized in that: step 3) is executed conduction and is added material, this conduction is added material and is made up of the chopped carbon fiber of 0.5mm～4mm, 15 microns thick aquadag powder, 4 microns middle aquadag powder and 1 micron thin aquadag powder mixing, after mixing with Lauxite or aerodux then, be coated with again and impose on wooden cell surface; Order carries out 4 again) the assembly moulding, form alternate laminated construction, 5 with the wooden unit of multilayer) last, hot pressing forms sheet material.
A kind of manufacture method of composite wood board with conducting function, the step of its manufacturing is divided into: 1) timber subdivision is timber or its residue, non-wood plant fibre raw material subdivision wooden unit such as section, wood shavings and fibre bundle; 2) dried, classified; 3) applying glue mixes Lauxite or aerodux and waterproofing agent and wooden unit; It is characterized in that: step 4) is executed conduction and is added material, this conduction is added material and is mainly formed with surfactant and carbon series elements, wherein surfactant refers to antistatic additive, this antistatic additive is cationic, nonionic, the carbon series elements is the aquadag powder, this conduction is added material mix 5 with the wooden unit of a part of applying glue) moulding of mating formation, is the wooden unit formation of applying glue blank, and thereon, lower surface the conduction of executing that thickness 1mm～5mm is set adds the wooden elementary layer of material.6) last, hot pressing forms sheet material.
The chopped carbon fiber of described 0.5mm～4mm accounts for 2～10 grams of every square metre of wooden unit; 15 microns thick aquadag powder accounts for 5～15 grams of every square metre of wooden unit, and 4 microns middle aquadag powder accounts for 20～50 grams of every square metre of wooden unit, and 1 micron thin aquadag powder accounts for 5～15 grams of every square metre of wooden unit; Described cationic antistatic additive is the quaternary class, accounts for 2.0%～5.0% of wooden unit weight; Non-ionic antistatic agent is a glycerine, accounts for 2.0%～5.0% of wooden unit weight; The carbon series elements is the aquadag powder, accounts for 1.0%～4.0% of wooden unit weight.
Owing to adopt such scheme: can obtain the sheet material of different resistivity on request, and free aldehyde burst size is low, can produce and pollute, keep the intensity and the native texture of original sheet material simultaneously to environment.
The invention will be further described below in conjunction with drawings and Examples.
Fig. 1 is the first embodiment of the invention block diagram.
Fig. 2 is the second embodiment of the invention block diagram.
First embodiment as shown in Figure 1, is used to shield the manufacture method of electromagnetic composite wood board with conducting function, and its step is as follows:
1. timber subdivision:, be split into the wooden unit of Monoplacophora promptly timber rotary-cut or slicing.
2. heat drying:, serve as dry Jie with the highest 180 ℃ hot-air by the first moisture content of wooden unit
The wooden unit of verifying carries out drying; Or in the hot plate of 90～105 ℃ of temperature, pressure 0.4～0.5MPa, wooden unit is carried out drying.The moisture content of wooden unit, dry back reduces to 5%～8%.
3. execute conduction and add material:
Comprise chopped carbon fiber (0.5mm～4mm), 2～10g/m
2(optimum value 3g/m
2)
Thick aquadag powder (15 microns), 5～15g/m
2 (Optimum value 10g/m
2)
Middle aquadag powder (4 microns), 20～50g/m
2(optimum value 50g/m
2)
Thin aquadag powder (1 micron), 5～15g/m
2(optimum value 10g/m
2)
Above-mentioned conduction is added hot setting adhesive (applied amount 180～300g/m such as material and Lauxite, phenolic resins
2, Lauxite need add curing agent ammonium chloride a little) through an amount of aqueous diluent diluted mixture evenly after, be coated with and impose on wooden cell surface.
4. assembly moulding: conduction is added the mixture of material and binder resin, forms alternate laminated construction with the wooden unit of multilayer.
5. be hot pressed into plate: under 105～140 ℃ of temperature, pressure 0.8～1.4MPa, form the composite wood board with conducting function finished product.
The electromagnetic composite wood board with conducting function of the shielding of making as stated above, 12～35 decibels of its shield effectiveness (, Electromagnetic Interference or pollution intensity can be decayed 90%) to be example for 20 decibels to frequency 1.5GHz shielding electromagnetic waves usefulness.
Second embodiment as shown in Figure 2, is used for the manufacture method of anlistatig composite wood board with conducting function, and its step is as follows:
1. timber subdivision: promptly adopt timber or its residue, non-wood plant fibre raw material (shrub, agricultural crop straw, straw etc.) slicing or grinding method to form section, wood shavings and fiber wooden unit such as (bundles).
2. dried, classified: by the first moisture content of wooden unit, be drying medium, wooden unit is dried to moisture content 2%～6% with the highest 180～250 ℃ hot-air; Adopt the sieve method sorting, promptly by 3mm * 3mm screen cloth, stay the wooden unit on 0.4mm * 0.4mm screen cloth.
3. applying glue: hot setting adhesives such as Lauxite, phenolic resins (applied amount 6%～12%, Lauxite need add curing agent ammonium chloride a little), waterproofing agent (paraffin or paraffin wax emulsions applied amount 0.5%～1.0%) are sprayed in all wooden cell surfaces (promptly mixing with wooden unit).
4. execute conduction and add material: this conduction is added material and mainly is made up of surfactant (as: antistatic additive) and carbon series elements.From the wooden unit of above-mentioned applying glue, take out a part, this conduction is added material spray with it and mix.
Antistatic additive comprises cationic and nonionic, and its content is:
Cationic (the quaternary class is as dimethyl stearyl ethoxy quaternary ammonium nitrate, trihydroxyethyl methyl quaternary ammonium Methylsulfate etc.), 2.0%～5.0% (optimum value 3.9%);
Nonionic (polyalcohol is as glycerine etc.), 2.0%～5.0% (optimum value 3.6%);
The carbon series elements is the aquadag powder, 1 micron of granularity, and its content is 1.0%～4.0% (optimum value 1.9%).
Antistatic additive and carbon series elements account for 5%～14% of wooden unit weight, this conduction add material can by cationic antistatic additive, non-ionic antistatic agent, aquadag powder spray separately or mix after spray.
5. the moulding of mating formation: is the wooden unit formation of applying glue blank, and thereon, lower surface is provided with the wooden elementary layer that conduction is added material of executing of thickness 1mm～5mm.
6. be hot pressed into plate: under 140～180 ℃ of temperature, pressure 2.5～5.0MPa, form the composite wood board with conducting function finished product.
The anlistatig composite wood board with conducting function that makes as stated above, at moisture content 6%～8% o'clock its specific insulation from common sheet material 〉=10
10Ohmcm reduces to≤and 10
8Ohmcm.
In sum, the present invention can by apply conduction add material amount and with the shielding electromagnetic wave or the antistatic effect of the superimposed structure control composite board in wooden unit, thereby realize the large-scale quantified controlling of resistivity.
Claims (4)
1, a kind of manufacture method of composite wood board with conducting function, the step of its manufacturing is divided into: 1) timber subdivision, timber rotary-cut or slicing become the wooden unit of Monoplacophora; 2) heat drying; It is characterized in that: step 3) is executed conduction and is added material, this conduction is added material and is made up of the chopped carbon fiber of 0.5mm～4mm, 15 microns thick aquadag powder, 4 microns middle aquadag powder and 1 micron thin aquadag powder mixing, after mixing with Lauxite or aerodux then, be coated with again and impose on wooden cell surface; Order carries out 4 again) the assembly moulding, form alternate laminated construction, 5 with the wooden unit of multilayer) last, hot pressing forms sheet material.
2, a kind of manufacture method of composite wood board with conducting function, the step of its manufacturing is divided into: 1) timber subdivision is timber or its residue, non-wood plant fibre raw material subdivision wooden unit such as section, wood shavings and fibre bundle; 2) dried, classified; 3) applying glue mixes Lauxite or aerodux and waterproofing agent and wooden unit; It is characterized in that: step 4) is executed conduction and is added material, this conduction is added material and is mainly formed with surfactant and carbon series elements, wherein surfactant refers to antistatic additive, this antistatic additive is cationic, nonionic, the carbon series elements is the aquadag powder, this conduction is added material mix 5 with the wooden unit of a part of applying glue) moulding of mating formation, is the wooden unit formation of applying glue blank, and thereon, lower surface the conduction of executing that thickness 1mm～5mm is set adds the wooden elementary layer of material.6) last, hot pressing forms sheet material.
3, by the described manufacture method with the electromagnetic composite wood board with conducting function of shielding of claim 1, it is characterized in that: the chopped carbon fiber of described 0.5mm～4mm accounts for 2～10 grams of every square metre of wooden unit; 15 microns thick aquadag powder accounts for 5～15 grams of every square metre of wooden unit, and 4 microns middle aquadag powder accounts for 20～50 grams of every square metre of wooden unit, and 1 micron thin aquadag powder accounts for 5～15 grams of every square metre of wooden unit.
4, by the described manufacture method with anlistatig composite wood board with conducting function of claim 2, it is characterized in that: described cationic antistatic additive is the quaternary class, accounts for 2.0%～5.0% of wooden unit weight; Non-ionic antistatic agent is a glycerine, accounts for 2.0%～5.0% of wooden unit weight; The carbon series elements is the aquadag powder, accounts for 1.0%～4.0% of wooden unit weight.