CN1285383A - 含松香和紫胶的热熔胶粉及其制法 - Google Patents

含松香和紫胶的热熔胶粉及其制法 Download PDF

Info

Publication number
CN1285383A
CN1285383A CN 00117420 CN00117420A CN1285383A CN 1285383 A CN1285383 A CN 1285383A CN 00117420 CN00117420 CN 00117420 CN 00117420 A CN00117420 A CN 00117420A CN 1285383 A CN1285383 A CN 1285383A
Authority
CN
China
Prior art keywords
silicone oil
melt adhesive
rosin
hot
adhesive powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 00117420
Other languages
English (en)
Other versions
CN1092222C (zh
Inventor
哈成勇
王炽瑜
袁金伦
彭树海
刘跃平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangzhou Institute of Chemistry of CAS
Original Assignee
Guangzhou Institute of Chemistry of CAS
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangzhou Institute of Chemistry of CAS filed Critical Guangzhou Institute of Chemistry of CAS
Priority to CN00117420A priority Critical patent/CN1092222C/zh
Publication of CN1285383A publication Critical patent/CN1285383A/zh
Application granted granted Critical
Publication of CN1092222C publication Critical patent/CN1092222C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明涉及含松香和紫胶的精密磁石切割用热熔胶粉及其制法。该热熔胶粉按重量份数计,组成包括松香30～50份、紫胶30～50份、聚合松香3～8份、经硅油表面处理的轻质碳酸钙2～5份;制法是先将轻质碳酸钙用硅油有机溶液进行表面处理,然后取已分别粉碎的松香、紫胶、聚合松香置于混合器中,搅拌下加入经硅油表面处理的轻质碳酸钙,继续搅拌一小时后,出料即得所述热熔胶粉。该热熔胶粉能够常温贮存,性能保持不变,使用方便。

Description

含松香和紫胶的热熔胶粉及其制法
本发明涉及含松香和紫胶的热熔胶粉及其制法，尤其是作为精密磁石切割用的含松香和紫胶的热熔胶粉及其制法。
紫胶为一类性质优良的天然树脂，常用于木制家具的底漆；也用作为高档、特殊用途的胶粘剂(王孟钟，黄应昌主编，《胶粘剂应用手册》，化学工业出版社，北京，1987年，第一版，第86页)，1976年，印度有人提出用紫胶或改性紫胶作为各类粘接剂，但产品均不是粉末态，也不用于金属切割[李生贵译，王定选校，《林化科技》，No.5：60(1976)]。松香也是一类天然树脂，它性质脆、硬，虽然有一定的粘接力，也有用于粘接剂的报道(王孟钟，黄应昌主编，《胶粘剂应用手册》，化学工业出版社，北京，1987年，第一版，第85～86页)，但无法单独作为粘接料出现，尤其没有在强烈机械切割、振动下作为粘接剂的报道。
精密磁石切割用胶粘剂是以粉末状经过筛网直接均匀洒落在磁石表面，多层叠合后，置入烘箱，待热熔胶熔化后，取出、冷却，待切割。在精密微型电机和喇叭中大量使用异型磁石，切割此类磁石对加工精度要求很高，普通胶粘剂很难达到其苛刻的要求。松香与紫胶可以组成能够满足精密异型磁石切割加工要求的胶粘剂，但这两种原材料组成的产品不能以粉末态存在，必须在磁石切割现场粉碎或融化它们才能使用。进口产品虽然可以以粉末态存在，但只能低温(10℃以下)贮存半年，否则会损失性能，影响使用。
本发明的目的是提供一种含松香和紫胶的精密磁石切割用热熔胶粉，它不仅可以制成粉末态，而且能够常温贮存，对性能及使用无不良影响，可以进一步简化、方便操作，节省能源，提高效率。
本发明的另一个目的是提供这种热熔胶粉的制法。
本发明提供的含松香和紫胶的精密磁石切割用热熔胶粉，按重量份数计，其组成包括：
松香                         30～50份、
紫胶                         30～50份、
聚合松香                      3～8份、
经硅油表面处理的轻质碳酸钙    2～5份，
其中硅油占轻质碳酸钙重量的2～8％，以5～8％为佳。
上述松香中枞酸重量含量以25～60％为佳；
所用硅油以粘度介于1～50 Pa·S之间为宜，尤其可以是二甲基硅油(也称聚二甲基硅氧烷，Dimethicone)。硅油粘度太高则分散较困难。
本发明所提供的含松香和紫胶的热熔胶粉的制法如下：首先将轻质碳酸钙用硅油有机溶液进行表面处理，然后取已分别粉碎的松香、紫胶、聚合松香置于混合器中，搅拌下加入经硅油表面处理的轻质碳酸钙，继续搅拌一小时后，出料，可得粉末态含松香和紫胶的精密磁石切割用热熔胶粉。
硅油有机溶液一般可采用丙酮作溶剂，硅油重量浓度为2～8％为宜，以5～6％为佳。
本发明提供的作为精密磁石切割用的含松香和紫胶的胶粘剂，由于其中的经硅油表面处理的轻质碳酸钙起到固体分散剂的作用，因此可以预先制备成为粉末态，而且能够常温贮存，贮存期长达1～2年，性能保持不变；同时，本热熔胶的粘接强度均大于110N/cm2，比常规产品的80～90N/cm2高。该热熔胶简化、方便了使用，节省了能源，提高了效率。
以下实施例的份数、含量均按重量计。
实施例1
取轻质碳酸钙100份于无死角锥状混合器中，在搅拌状态下，将5份二甲基硅油配成浓度为5％的丙酮溶液喷入；室温下，继续搅拌一小时，以确保混合均匀。然后，密封釜盖，减压，将丙酮蒸发除去；直至经处理的碳酸钙挥发份小于0.1％；解除真空，出料。产物为经硅油表面处理的轻质碳酸钙。
实施例2
取甲级松香50份，紫胶30份，聚合松香4份，分别粉碎至通过φ0.1mm的筛子，在无死角锥状混合器中，边搅拌边加入经硅油处理的轻质碳酸钙5份，继续搅拌一小时后，过φ0.1mm筛出料。该热熔胶的粘接强度112N/cm2。将该热熔胶粉常温储存一年，性能指标没有劣化。
实施例3
取甲级松香40份，紫胶50份，聚合松香8份，分别粉碎至通过φ0.1mm的筛子，在无死角锥状混合器中，边搅拌边加入经硅油处理过的轻质碳酸钙2份，继续搅拌一小时后，过φ0.1mm筛出料。该热熔胶的粘接强度125N/cm2。将该热熔胶粉常温储存一年，性能指标没有劣化。
实施例4
取甲级松香30份，紫胶40份，聚合松香6份，分别粉碎至通过φ0.1mm的筛子，在无死角锥状混合器中，边搅拌边加入经硅油处理过的轻质碳酸钙4份，继续搅拌一小时后，过φ0.1mm筛出料。该热熔胶的粘接强度116N/cm2。将该热熔胶粉常温储存一年，性能指标没有劣化。

Claims (7)

1、一种含松香和紫胶的精密磁石切割用热熔胶粉，其特征在于按重量份数计，组成包括：
松香                        30～50份、
紫胶                        30～50份、
聚合松香                     3～8份、
经硅油表面处理的轻质碳酸钙   2～5份，
其中硅油占轻质碳酸钙重量的2～8％。
2、根据权利要求1中所述的热熔胶粉，其特征在于所述的松香中枞酸重量含量为25～60％。
3、根据权利要求1中所述的热熔胶粉，其特征在于所述硅油粘度介于1～50Pa·S之间。
4、根据权利要求1或3中所述的热熔胶粉，其特征在于所述硅油为二甲基硅油。
5、一种权利要求1中所述热熔胶粉的制法，其特征在于首先将轻质碳酸钙用硅油有机溶液进行表面处理，然后取已分别粉碎的松香、紫胶、聚合松香置于混合器中，搅拌下加入经硅油表面处理的轻质碳酸钙，继续搅拌一小时后，出料即得所述热熔胶粉。
6、根据权利要求5中所述的制法，其特征在于所述硅油有机溶液采用丙酮作溶剂，硅油重量浓度为2～8％。
7、根据权利要求6中所述的制法，其特征在于所述硅油重量浓度为5～6％。
CN00117420A 2000-09-18 2000-09-18 含松香和紫胶的热熔胶粉及其制法 Expired - Fee Related CN1092222C (zh)