CN1274406C - Method for preparing deaminating adsorbent - Google Patents
Method for preparing deaminating adsorbent Download PDFInfo
- Publication number
- CN1274406C CN1274406C CN 200310104989 CN200310104989A CN1274406C CN 1274406 C CN1274406 C CN 1274406C CN 200310104989 CN200310104989 CN 200310104989 CN 200310104989 A CN200310104989 A CN 200310104989A CN 1274406 C CN1274406 C CN 1274406C
- Authority
- CN
- China
- Prior art keywords
- acid
- accordance
- nay molecular
- water
- molecular sieve
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
The present invention relates to a method for preparing an absorbing agent which can simultaneously removing ammonia nitrogen, calcium ions and magnesium ions in waste water. NaY molecular sieves are used as principal raw material to be uniformly mixed with aluminium hydroxide dry gel powders, sesbania powders, organic acid and inorganic acid, and then, the mixture is shaped and calcined to obtain the adsorbing agent. Compared with common NaY molecular sieves, the ammonium ion absorbing capability of the adsorbing agent prepared by adopting the method of the present invention is improved greatly, and simultaneously, the adsorbing agent can also remove calcium ions and magnesium ions in water. Effluent water can be used as compensation water for circulating cooling water.
Description
Technical field
The present invention relates to a kind of preparation of adsorbent method, especially a kind of preparation of adsorbent method of adsorbing ammonia nitrogen and calcium ion, magnesium ion simultaneously.
Background technology
Nitride is one of major pollutants in the waste water, and the form that exists of nitrogen mainly contains: NH
3, NH
4 +, NO
2, NO
3, organic nitrogen, NH in petrochemical wastewater
4 +The nitrogen of form is main, modal pollutant.Nitrogen in the water makes body eutrophication, thus breed bacteria and algae.
In waste water advanced treatment technology, absorption is effective method, and adsorbent of the prior art has: active carbon, activated coal, carclazyte, diatomite, bentonite, montmorillonite, clay, zeolite, resin, slag, wood chip, coal ash, humic acid etc.The character of various adsorbents is not quite similar, and active carbon is the adsorbent that generally adopts in the present wastewater treatment.Active carbon mainly is the amino molecule (NH in the adsorbed water
3) nitrogen of form, adsorption capacity is limited.NACF is mainly used in and is adsorbed with organic pollutants, and to NH
4 +Adsorbance limited, generally be used for the oil plant comprehensive wastewater and handle.
Zeolite is to NH
4 +Selectivity better, but the adsorption capacity of non-modified zeolite is lower, several various main natural zeolites absorption NH
4 +The effect situation of-N sees Table 1.
Several zeolite NH of table 1
4 +The adsorption capacity of-N
Zeolite type | The Si/Al atomic ratio | Crystallographic system | mgNH 4 +-N/g zeolite |
Chabasie | 2 | Tripartite | 5 |
Modenite | 5 | Quadrature | 2.6 |
Erionite | 3 | Six sides | 3.8 |
Clinoptilolite | 4.5 | Monocline | 2.6 |
A type zeolite | 1 | Cube | 7.0 |
X type zeolite | 1.25 | Cube | 6.4 |
Y-type zeolite | 2.0 | Cube | 5.0 |
T type zeolite | 3.5 | Cube | 3.4 |
The ZC-1 type zeolite treatment containing wastewater from catalyst that Qiu's electricity cloud etc. are handled with modification " processing of ammonia nitrogen in the containing wastewater from catalyst " (" mining metallurgical engineering " rolled up the 47th~55 page of the 1st phase in 1994 14), as desorbed solution, its zeolite is 6~9mgNH to the ammonia nitrogen absorption amount with sodium chloride
4 +-N/g.Han Huiru in " the right zeolite of Anhui Nan Tian to water in the research of ammonia nitrogen absorption performance " (18 the 4th phases of volume of " Jilin Institute of Chemical Technology journal " calendar year 2001), adopts using natural clinoptilolite etc. to adsorb NH in the waste water at " utilizing natural zeolite to handle the technical study of ammoniated wastewater " (" Treatment of Industrial Water " 1997 17 the 5th phases of volume) and Liu Yulin etc.
4 +-N, its zeolite is to NH
4 +-N adsorbance is 11~12mgNH
4 +-N/g zeolite, and the latter points out that this zeolite is not suitable for the wastewater treatment of calcic and magnesium ion.Xiao Tiancun etc. are in " being used for removing the research of the NaA-1 type ion-exchanger of water ammonia nitrogen " (" chemical industry environmental protection " 1997 17 the 6th phases of volume), to be used for discarded A molecular sieve chloroform, NaOH and the sodium chloride modification of ethene drying, be used for chemical fertilizer factory's nitrogen-containing wastewater, adsorbance reaches 32mgNH
4 +-N/g, but also point out to be applicable to the wastewater treatment that contains potassium ion and calcium ion.NaOH and sodium chloride solution are all adopted in the regeneration of above-mentioned zeolite adsorbents, and cost is higher.CN86106921A is a primary raw material with using natural clinoptilolite or modenite, adding a certain amount of aluminium hydroxide, potassium chloride, NaOH and water mixes, carry out complexity then and become steps such as glue, crystallization for a long time, synthetic a kind of adsorbent, the potassium ion or the ammonium ion that can be used for adsorbed water, its preparation process are comparatively complicated.US4,522,727 disclose a kind of L type synthetic zeolite and T type zeolite treatment pisciculture wastewater treatment method used, and have reduced the concentration of non-ionic ammonia in the fishpond, to NH
4 +The adsorption effect of-N is not obvious.US4,717,483 based on activated alumina, cooperates y-type zeolite to make a kind of adsorbent, and molecules of ammonia, sulfide and organic matter in the absorption leather-making waste water are not considered NH
4 +The influence of-N adsorption effect.In the prior art, a lot of for the method for modifying of Y zeolite, as acid treatment, hydrothermal treatment consists etc., but be primarily aimed at the modification of the Y zeolite that is used for catalyst, not at carrying out modification as adsorbent.
Summary of the invention
At the deficiencies in the prior art, the purpose of this invention is to provide a kind of wastewater treatment preparation of adsorbent method up to standard of removing ammonia nitrogen, calcium ion, magnesium ion and iron ion simultaneously, the water after the processing can be used for the supplementing water of recirculated cooling water.
Preparation of adsorbent method of the present invention may further comprise the steps:
(1) is primary raw material with the NaY molecular sieve, mixes that the weight ratio of mixing is 60~80%: 1~20%: 1~10%: 1~10%: 1~10% with aluminium hydrate powder, extrusion aid, organic acid and inorganic acid.
(2) moulding.Make diameter 0.5~2mm by banded extruder, length is the fine strip shape of 1~5cm.
(3) roasting.Under 300 ℃~500 ℃ temperature, roasting 4~10 hours.
Wherein the NaY molecular sieve is natural NaY molecular sieve, and the Si/Al atomic ratio is generally 2~5.Aluminium hydrate powder is the aluminium hydrate powder of preparation such as Alchlor process, aluminum sulfate method, carbon dioxide process, and in the SB powder one or more.Extrusion aid is generally the blue or green powder in field etc., and organic acid is one or more in formic acid, acetate, propionic acid, maleic acid, citric acid, tartaric acid, glutaric acid, the adipic acid etc., and inorganic acid is one or more in hydrochloric acid, sulfuric acid, nitric acid, the phosphoric acid etc.
The adsorbent employing concentration of the inventive method preparation is 1~20% sodium carbonate liquor regeneration, and adsorption capacity can be recovered more than 90%.
The NH of the natural NaY molecular sieve of handling without the inventive method
4 +-N adsorption capacity is less, is generally about 5.0mg/g, after process the method for the invention is prepared into new adsorbent, and the NH of adsorbent
4 +-N adsorption capacity improves greatly, can reach more than the 30mg/g, and ammonia-N removal rate reached 90w% when above, simultaneously to the clearance of calcium ion and magnesium ion greater than 95w%.Regenerated liquid can effectively be regenerated to adsorbent, recovers the adsorption capacity of adsorbent to ammonia nitrogen, calcium ion and magnesium ion.
The specific embodiment
Below in conjunction with embodiment the solution of the present invention and effect are described.
Embodiment 1
Preparation of adsorbent:
(1) is that 2 natural NaY molecular sieve is a primary raw material with the Si/Al atomic ratio, mixes by following part by weight with SB powder, the blue or green powder in field, citric acid and nitric acid: 70: 12: 5: 8: 5.
(2) moulding.Make diameter 1mm by banded extruder, average length is the fine strip shape of 1.5cm.
(3) roasting.Under 350 ℃, roasting 8 hours.
Adsorption effect:
The adsorbent of said process preparation is packed in the ion exchange column, 18 liters of post dischargeable capacitys, ion exchange column is equipped with adsorbent 12kg, handles water yield 50L/h, and the regeneration period is 16h, air speed 2.7h
-1Adopting concentration is the regeneration of 15% sodium carbonate liquor.Influent ammonium concentration 2905mg/L, dynamically ammonia nitrogen exchange capacity 34.17mgNH
4 +-N/g.Water inlet calcium ion concentration 38mg/L, water outlet mean concentration 0.6mg/L, average removal rate 99%.Water inlet magnesium ion concentration 15mg/L, water outlet magnesium ion 0.15mg/L, average removal rate 99%.
Embodiment 2
Preparation of adsorbent:
(1) be that 3 natural NaY molecular sieve is a primary raw material with the Si/Al atomic ratio, the blue or green powder in aluminum hydroxide solid elastomer powder, field, tartaric acid and the hydrochloric acid produced with Alchlor process mix by following part by weight: 75: 10: 3: 4: 8.
(2) moulding.Make diameter 1mm by banded extruder, average length is the fine strip shape of 1.5cm.
(3) roasting.Under 400 ℃, roasting 6 hours.
Adsorption effect:
Other condition is identical with embodiment 1, and the rising influent ammonium concentration is to 3874mg/L, and calcium ion concentration is to 70mg/L, and magnesium ion concentration is to 30mg/L, and adopting concentration is the regeneration of 20% sodium carbonate liquor.Handling the water yield and air speed remains unchanged.Regeneration period is 16h.Dynamic ammonia nitrogen exchange capacity 33.66mgNH
4+-N/g.Water outlet calcium ion mean concentration 2.5mg/L, average removal rate 96%, water outlet magnesium ion mean concentration 1.0mg/L, average removal rate 97%.
Embodiment 3
Preparation of adsorbent:
(1) be that 3 natural NaY molecular sieve is a primary raw material with the Si/Al atomic ratio, 1: 1 mixture of the blue or green powder of producing with carbon dioxide process in aluminum hydroxide solid elastomer powder, field, acetate and citric acid and nitric acid mix by following part by weight: 65: 15: 4: 8: 8.
(2) moulding.Make diameter 1mm by banded extruder, average length is the fine strip shape of 1.5cm.
(3) roasting.Under 450 ℃, roasting 4 hours.
Adsorption effect:
At influent ammonium concentration is 4855mg/L, calcium 40mg/L, and magnesium 25mg/L, treating capacity 20L/h, corresponding air speed is 1.1h
-1, the regeneration period is when being 24h.Adopting concentration is the regeneration of 18% sodium carbonate liquor.Regeneration period is 16h.Dynamic ammonia nitrogen exchange capacity 38.16mgNH
4 +-N/g.Water outlet calcium ion mean concentration 2.5mg/L, average removal rate 96%, water outlet magnesium ion mean concentration 1.0mg/L, average removal rate 97%.
Claims (7)
1, a kind of ammonium preparation of adsorbent method of taking off may further comprise the steps:
(1) is primary raw material with the NaY molecular sieve, mixes that the weight ratio of mixing is 60~80%: 1~20%: 1~10%: 1~10%: 1~10% with aluminium hydrate powder, extrusion aid, organic acid and inorganic acid;
(2) moulding;
(3) roasting was 300 ℃~500 ℃ following roastings 4~10 hours.
2, in accordance with the method for claim 1, it is characterized in that described forming process of (2) step is: make diameter 0.5~2mm on banded extruder, length is the fine strip shape of 1~5cm.
3, in accordance with the method for claim 1, it is characterized in that described NaY molecular sieve is natural NaY molecular sieve.
4, in accordance with the method for claim 1, the Si/Al atomic ratio that it is characterized in that described natural NaY molecular sieve is 2~5.
5, in accordance with the method for claim 1, it is characterized in that described aluminium hydrate powder is the aluminium hydrate powder of Alchlor process, aluminum sulfate method, carbon dioxide process preparation, and in the SB powder one or more.
6, in accordance with the method for claim 1, it is characterized in that described organic acid is one or more in formic acid, acetate, propionic acid, maleic acid, citric acid, tartaric acid, glutaric acid, the adipic acid.
7, in accordance with the method for claim 1, it is characterized in that described inorganic acid is one or more in hydrochloric acid, sulfuric acid, nitric acid, the phosphoric acid.