CN1272491C - Method for producing conductive cloth and its product - Google Patents
Method for producing conductive cloth and its product Download PDFInfo
- Publication number
- CN1272491C CN1272491C CN 02124462 CN02124462A CN1272491C CN 1272491 C CN1272491 C CN 1272491C CN 02124462 CN02124462 CN 02124462 CN 02124462 A CN02124462 A CN 02124462A CN 1272491 C CN1272491 C CN 1272491C
- Authority
- CN
- China
- Prior art keywords
- conductive cloth
- yarn
- conductive fabric
- metal yarns
- finished product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a method for producing conductive cloth and a product thereof. In the method, metallic yarn and natural fiber are used as raw materials; simultaneously, a thread, such as a rubber thread, a stainless steel wire, a woollen thread, etc., of which the durability is fully improved is added in the process of knitting fiber after the yarn coating process that a spun yarn wire is wound and coated by the metallic yarn, such as natural wool and rabbit hairs or wool and rabbit hairs treated by infrared rays, etc. The shape of large-area conductive cloth is formed; then, the conductive cloth can be further made into conductive cloth in different shapes so as to be used conveniently according to the requirements of users. Various pigments can be directly dipped and dyed on the yarn before the conductive cloth is formed; the formed conductive cloth has abundant color change; besides, a current controller can be externally connected with the formed article of the conductive cloth to connect proper current so as to achieve electrotherapy effect when a formed article of the conductive cloth is applied to medical use. Because the conductive cloth is formed by the knitting of natural spun yarn, the surface still has a comfortable advantage; the conductive cloth can be directly cleaned and repeatedly used; in addition, the conductive cloth can keeps a long service life.
Description
Technical field
The present invention relates to a kind of making forming technique of conductive fabric, refer to a kind of manufacture method that can produce the conductive fabric that is different from conventional conductive cloth and products thereof especially.
Background technology
According to present commercially available low frequency current for treatment device about medical application, basically take as the leading factor with practicality with electrotherapy, promptly utilize smaller power and reduced-current to continue the nerve of human body privileged site is stimulated, reach the therapeutic efficiency that promotes local blood circulation etc.; Its primary structure a controller that provides the conductive fabric and that contacts with human body skin to see through the function selection of wire coupling is provided constitutes, wherein this plated conductive cloth is the composite bed structure that is made of base material, nickel, copper sulfide etc., and the end in plated conductive cloth is provided with conducting resinl again, another side then is provided with the conduction button, this conducting resinl can adhere to and be positioned on the human body skin, the conduction button then is to utilize lead and controller to link conducting, reaches required result of treatment whereby.
This kind belongs to low-frequency therapeutic equipment present, though can be because of reaching electrotherapeutic effect to a certain degree, and have usability medically, still, also have shortcoming as described below:
1, conducting resinl is made for environmental-protecting material not, if abandoned environmental issue; And this conducting resinl is airtight, causes allergic phenomenon easily for the patient of skin sensitivity, and has very uncomfortable sensation.
2, the area of this plated conductive cloth is too little, causes treatment face too narrow, poor effect; Secondly, under limited plated conductive glue quantity, must constantly reach, thereby hide hygienic issues, and must go again and purchase conducting resinl and cause the increase cost in the repeated use mode.
3 moreover, can reach conducting function because of this plated conductive cloth must have conducting resinl, therefore if must washing, then can make conducting resinl ineffective for fear of health.
Therefore, comprehensive above content as can be known, existing low frequency current for treatment device has the space and the necessity of further improvement really.Moreover, along with quick transition of epoch, the importance that general family possesses the medical appurtenance that simple and easy use is arranged also highlights gradually, in many cases if can obtain at any time, greatest help will be arranged the user of needs, all accepted by masses based on the product and the serviceability of electrotherapy especially at present.
Summary of the invention
Main purpose of the present invention be produced plated conductive cloth of the existing method for making of improvement and structure thereof existingly can't wash, not only unhygienic but also do not meet environmental requirement even shortcoming such as poor effect in the use, and provide a kind of and utilize that different material, method are woven experiment, the preparation method of the conductive fabric improved and use the various finished product that this conductive fabric constitutes.
Another object of the present invention is can be with natural fiber dyed processing earlier, make the large tracts of land conductive fabric of weaving forming like the different tone of formation according to the user, make this conductive fabric except that having unique originally comfortable sense of touch, have more manufacture method of the conductive fabric that has the abundant colors variation and products thereof.
The manufacture method of conductive fabric of the present invention may further comprise the steps:
The selection of A, raw material: employed raw material includes good Metal Yarns of electric conductivity and natural staple fibre, or through the far infrared silk thread of far infrared processed, or the elastic gum silk thread;
B, bag yarn: above-mentioned raw materials is wrapped the yarn operation, be covered with the Metal Yarns kenel with natural fiber silk foreign volume is wrapped, and make it reach optimum coiling density degree;
C, braiding: above-mentioned coiling Metal Yarns is woven through Yarn feeder, and add the silk that is enough to promote its durability as rubber thread, stainless steel wire, wool silk etc. during the course, obtain weaving smooth, the even good large-area conductive fabric material of durability again whereby.
The diameter of Metal Yarns is in 0.035～0.08mm scope described in the manufacture method of conductive fabric of the present invention.
In the wrapped kenel that is covered with Metal Yarns of natural fiber silk foreign volume, its optimum coiling density degree is for being wound with 3～25 Metal Yarns of rolling up on the natural fiber silk of about 1cm length described in the manufacture method of conductive fabric of the present invention.
Natural fiber silk raw material described in the conductive cloth making method of the present invention is the processing of can directly being dyeed earlier, continues to carry out set bag yarn and handle, be woven into processes such as finished product again, so will can be made into the conductive fabric with various change color.
The conductive fabric finished product that conductive cloth making method of the present invention makes can be any kenel, and the right position is provided with the conduction button on finished product, and combines with a controller by the connection conducting of lead.
When the conductive fabric material that adopts manufacture method of the present invention to make was made all kinds of finished product again, this finished product promptly had following advantage:
1, contact area is big.
2, any position of applicable human body.
3, ventilative, soft, comfortable and easy to use.
4, antibiotic, deodorization, hygiene effect is good.
But 5 repeated washings, compliance with environmental protection requirements.
6, with low cost.
For example: use the ceramic powders blending after on the textiles, have and be difficult for dropping, and can keep the advantage of normal permanent time mutually, make the consumer after buying this kind textiles, can accept the far infrared that radiates out by ceramic powders for a long time, reach the medical functions that stimulates circulation.
Purpose, characteristic, advantage and whole making flow process thereof below in conjunction with further manufacture method of understanding conductive fabric of the present invention of drawings and Examples and products thereof.
Description of drawings
Accompanying drawing 1 is a flow chart of the present invention.
Accompanying drawing 2 is the finished product kenel of a preferred embodiment of the present invention.
Accompanying drawing 3 is the exploded view of a preferred embodiment of the present invention.
Accompanying drawing 4 is another flow chart of the present invention.
Wherein, the label in the described accompanying drawing is expressed as respectively:
10, be auxiliary implement; 11, be public conduction button;
12, be female conduction button; 13, be lead;
14, be controller.
Specific embodiment
Provided by the present invention is a kind of manufacture method and products thereof of conductive fabric, can be divided into Related product two parts of the made conductive fabric of the manufacture method of conductive fabric and Using such method.Please cooperate and consult shown in the accompanying drawing 1, wherein:
(1), about the part of manufacture method:
At first be the selection of raw material: employed raw material includes the good Metal Yarns of electric conductivity, and preferably diameter is in 0.035～0.08mm scope; Nature (weak point) fiber, as wool, the rabbit hair etc., or through the far infrared silk thread of far infrared processed, or be that the elastic gum silk thread also can.Because far infrared belongs to a kind of physics light, it is characterized in that having stronger warm-heat effect, human body had multiple efficacies such as the metabolism of the human body of promotion, blood circulation, ferment growth and tissue resurrection, and effect is very powerful, so far-infrared radiation often is used in the medical application, therefore also for promoting the medical effect of the made conductive fabric of this method, be the best so employing far infrared filament is the practice of raw material.
Secondly be suitable processing machine: according to raw materials such as above-mentioned Metal Yarns and natural fiber silks, utilize a Yarn feeder to carry out its bag yarn operation, with the wrapped Metal Yarns kenel that is covered with of this natural fiber silk foreign volume, and make it reach optimum coiling density degree, and must be preceding topic not break, and form about 1cm length the natural fiber silk and on to be wound with 3～25 Metal Yarns of rolling up be optimum.So, can make the flatness of the Metal Yarns that all coilings finish obtain uniformity, the treatment stability when being applied to low frequency so as to lifting.
Then be the braiding of conductive fabric: the Metal Yarns of above-mentioned coiling is carried out weaving operation through Yarn feeder, in the braiding process, add again simultaneously as the silk that is enough to promote its durability for the basis such as rubber thread, stainless steel wire, far infrared filament, wool silk, so as to when being woven into large-area conductive fabric material, decapacitation has evenly, durability is good and compliance with environmental protection requirements outside, again with effects such as antibiotic, deodorizations.
(2), about manufacturing the part of Related product:
According to above-mentioned in type conductive fabric material, make all kinds of finished product kenels according to actual demand, in order to the medical application aspect that is applied to as low frequency current for treatment etc.Please further consult shown in accompanying drawing 2, the accompanying drawing 3, promptly disclosed a kind of with conductive fabric tubular and the gripping formula electrotherapy of not having a seam kenel with auxiliary implement 10: on appropriate location on the body of this auxiliary implement 10, be provided with public conduction button 11, conduct electricity the connection conducting of button 12 lead 13 and be provided with the mother who matches, and combine with a controller 14 by an end; So, utilize the flow through size of current of conductive fabric of controlling of this controller 14 on the implementation, to make the people when carrying out electrotherapy, can discharge suitable electric current via conductive fabric user's affected part is continued to stimulate its peripheral nerve, the far infrared filament that while contains because of conductive fabric, so, further promote the blood circulation effect and the metabolic function of this affected part after the follow current effect, producing activation phenomenon because of heating.
During use, weave the Metal Yarns that are wound with 3～25 volumes on the natural fiber silk of optimum data with 1cm length of reeling between the metallic yarn of this conductive fabric and natural fiber and be the use of suitable method for making of the present invention, and can be woven into density, the equal favorable conductive cloth of flatness in view of the above, and best low-frequency stable treatment degree can be provided.
Please cooperate another implementing procedure figure that consults shown in the accompanying drawing 4 again, in above-mentioned conductive fabric forming process, the natural fiber silk is the processing of can directly dyeing earlier, continues to carry out set bag yarn and handle, be woven into processes such as finished product again, so will can be made into the conductive fabric with various change color.When it was made into all kinds of different finished product, this finished product of military order has abundant colors to be changed, and the tool aesthetic, and unlikely too dull.
In addition, the present invention more can be widely used in multiple different field when bag yarn finished product, such as: static elimination, anti-electromagnetic wave, anti-cutting, conductive yam raw material and low frequency current for treatment such as use at the aspect.
Claims (5)
1, a kind of conductive cloth making method is characterized in that may further comprise the steps:
The selection of A, raw material: employed raw material includes good Metal Yarns of electric conductivity and natural staple fibre, or through the far infrared silk thread of far infrared processed, or the elastic gum silk thread;
B, bag yarn: above-mentioned raw materials is wrapped the yarn operation, with the wrapped Metal Yarns that is covered with of natural fiber silk foreign volume;
C, braiding: above-mentioned coiling Metal Yarns is woven through Yarn feeder, and add rubber thread, stainless steel wire, the wool silk that can promote its durability during the course.
2, the manufacture method of conductive fabric according to claim 1, the diameter that it is characterized in that described Metal Yarns is in 0.035～0.08mm scope.
3, the manufacture method of conductive fabric according to claim 1 is characterized in that being wound with on the natural fiber silk that described coiling density degree in the wrapped process that is covered with Metal Yarns of natural fiber silk foreign volume is a 1cm length Metal Yarns of 3～25 volumes.
4, the manufacture method of conductive fabric as claimed in claim 1 is characterized in that earlier described natural fiber silk raw material being dyeed processing, continues and wraps the yarn processing, is woven into the finished product process.
5, conductive fabric finished product, it is characterized in that adopting manufacture method as one of claim 1-4 to make, be any kenel wherein, and on the appropriate location on the finished product, be provided with the conduction button, and combine with a controller by the connection conducting of lead with the finished product that conductive fabric was constituted.