CN1271697A - 一种高性能混凝土矿物超细粉 - Google Patents
一种高性能混凝土矿物超细粉 Download PDFInfo
- Publication number
- CN1271697A CN1271697A CN00109125A CN00109125A CN1271697A CN 1271697 A CN1271697 A CN 1271697A CN 00109125 A CN00109125 A CN 00109125A CN 00109125 A CN00109125 A CN 00109125A CN 1271697 A CN1271697 A CN 1271697A
- Authority
- CN
- China
- Prior art keywords
- ultra
- performance concrete
- concrete
- mineral powder
- fine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种高性能混凝土矿物超细粉,它由矿渣、沸石岩、粉煤灰、长青石、生石灰组成,经称重、超细磨、混合、均化而成。它价格便宜,使用方便,物美价廉,稳定性强,原材料来源广,选择当地能取代水泥的矿物即可进行合理的优选搭配,使其在性能上既能取长补短,又能互相激发,发挥出高水平、高效益的作用。
Description
本发明涉及一种高性能混凝土矿物超细粉,具体的说是涉及一种由多种矿物配制而成的,增强幅度大的一种高性能混凝土矿物超细粉。属于配制高性能混凝土的新材料。
目前,随着建筑技术的进步及建筑物向高层化、大荷载、大跨度、薄壁化及要求延长建筑物使用寿命的需要,国内外混凝土技术正处于从传统的混凝土向高性能混凝土转换。矿物超细粉是配制高性能混凝土不可缺少的一种新材料。目前在国内用于配制高性能混凝土的材料一般都是采用单一的矿物超细粉,即采用超细矿渣粉或超细粉煤灰或沸石粉等,利用其中任意一种矿物超细粉配制高性能混凝土。现有的用单一的矿物超细粉配制出的高性能混凝土有其不理想的方面,如:有的对混凝土28天的增强幅度不大,即小于20%;有的取代水泥的数量少,即小于30%;有的含碱量偏高,不利于抑制碱骨料反应;有的配制出的高性能混凝土达不到高耐久性的要求等。故现有的用于配制高性能混凝土的矿物超细粉有待于进一步改进,以提高高性能混凝土的产质量。
本发明的目的在于提供一种由多种矿物配制而成,对混凝土增强幅度大的,耐久性好的一种高性能混凝土矿物超细粉。
本发明的目的是这样实现的:它由矿渣、沸石岩、粉煤灰、长青石、生石灰组成,经称重、超细磨、混合、均化而成,其特征在于它是由下述重量百分比的原料制备的一种高性能混凝土矿物超细粉:
矿 渣 30-35% 沸石岩 20-25%
粉煤灰 35-40% 长青石 5-10%
生石灰 0-7%。
将选出的原材料,采用超细磨,即可磨制出高质量的一种高性能混凝土矿物超细粉,又名为DBF高性能混凝土矿物超细粉。
本发明的一种高性能混凝土矿物超细粉,其特征还在于:
①比表面积:400m-800m/Kg
②需水量比:<95%
③28天胶砂抗压强度比:>110%。
本发明与现有技术相比,它价格便宜,使用方便,物美价廉,稳定性强,原材料来源广,选择当地所产的上述原料即可进行合理的优选搭配,使其在性能上既能取长补短,又能互相激发,发挥出高水平、高效益的作用。
以下结合实施例进一步说明本发明
本发明的原料可以由上述5种或4种或3种原料组成,本发明实施例1由5种原料组成,本发明实施例2由4种原料组成,它们均能发挥出高水平、高效益的作用,这里不再赘述。
实施例1
①对当地用作矿物超细粉的原材料进行调查、取样,并称重下述原料:
矿渣32.5Kg,沸石岩22.5Kg,粉煤灰35Kg,长青石5Kg,生石灰5Kg,
②用超细磨进行粉磨,使其比表面积达到600/Kg,
③将上述细粉混合,均化,
④装入袋中,即得100Kg本发明一种高性能混凝土矿物超细粉,又名为DBF高性能混凝土矿物超细粉。
实施例2
①对当地用作矿物超细粉的原材料进行调查、取样,并称重下述原料:
矿渣35Kg,沸石岩20Kg,粉煤灰35Kg,长青石10Kg,
②用超细磨进行粉磨,使其比表面积达到600/Kg,
③将上述细粉混合,均化,
④装入袋中,即得100Kg本发明一种高性能混凝土矿物超细粉,又名为DBF高性能混凝土矿物超细粉。
将DBF高性能混凝土矿物超细粉和混凝土高效减水剂掺入用525号水泥拌制的混凝土中(同时等量取代出30-45%的水泥)即能配制出高质量的C60-C80的高性能混凝土。
采DBF用高性能混凝土矿物超细粉配制出的高性能混凝土的技术性能如下:
与不掺超细粉的比较:
①在不增加用水量的情况下,能使基准混凝土坍落度增大至180-250mm,坍落度在2小时内损失小于10%,
②混凝土扩展度大于500mm,流下时间小于30秒(倒坍落度筒法)。
③混凝土28天强度为不掺的120%以上,增强效果显著。
④混凝土掺DBF后水化热低,3天、7天水化热比不掺者分别降低30%和20%。
⑤比相同强度的高强度混凝土含碱量降低40-50%,能抑制碱骨料反应。
⑥抗渗标号达到P30时,试件内部渗水小于10mm。
⑦抗冻融(-20℃)D300时,重量和强度无损失。
⑧碳化实验(CO浓度20%),28天碳化深度为零。
与其它现有的矿物超细粉配出的高性能混凝土相比,在技术性能上有如下优越性:
①用DBF高性能混凝土矿物超细粉等量取代水泥最高可达50%,比一般矿物超细粉能多取代水泥15-20%,
②用DBF矿物超细粉配制出的高性能混凝土28天强度提高25%,比用一般矿物超细粉配出的高性能混凝土强度提高10%左右。
③掺DBF矿物超细粉的混凝土比掺其它矿物超细粉的混凝土水化热降低10%左右。
④掺DBF矿物超细粉的混凝土比掺其它矿物超细粉的混凝土含碱量降低10-15%
⑤掺DBF矿物超细粉的混凝土比掺其它矿物超细粉的混凝土的抗渗标号和抗冻标号分别提高15-25%和20-30%
⑥掺DBF矿物超细粉的混凝土比掺其它的矿物超细粉的混凝土的碳化深度低20%左右。
Claims (2)
1、一种高性能混凝土矿物超细粉,它由矿渣、沸石岩、粉煤灰、长青石、生石灰组成,经称重、超细磨、混合、均化而成,其特征在于它是由下述重量百分比的原料制备的一种高性能混凝土矿物超细粉:
矿 渣 30-35% 沸石岩 20-25%
粉煤灰 35-40% 长青石 5-10%
生石灰 0-7%。
2、根据权利要求1所述的一种高性能混凝土矿物超细粉,其特征还在于:
①比表面积:400m-800m/Kg
②需水量比:<95%
③28天胶砂抗压强度比:>110%。