Summary of the invention: the object of the present invention is to provide a kind ofly can make the fertilizer product quality on average and the organic and inorganic of easier granulation series composite fertilizer granulation agent, it is made up of the raw material of following parts by weight: 2.5~3 parts of W-Gums, 2.5~3 parts of tapioca (flour)s, 2.5~3.5 parts of industrial trisodium phosphates, 2.5~3.5 parts in hydrogen peroxide, 5~7 parts of weathered coals, 1~1.5 part in potassium hydroxide, 5~7 parts of wilkinites, 1~1.5 part of sodium bicarbonate, 0.5~1 part in bicarbonate of ammonia, 1.5~3.3 parts of polyvinyl alcohol.The invention has the advantages that: it has solved in the organic-inorganic complex fertilizer production because density variation causes the uneven problem of quality product; It has improved the bulk specific gravity of organic-inorganic complex fertilizer, and fertilizer product is more suitable in mechanized application; When the organic content in the fertilizer surpasses 30%, adds product of the present invention, then solved the difficulty of granulating, granule strength is low, the problem of easy-weathering; This product need not add materials such as a large amount of clays, wilkinite, talcum powder in process of production, relatively can improve the content of effective ingredient in the fertilizer with traditional product, makes fertilizer execute easy disintegrating in the soil again; After in fertilizer, adding product of the present invention, the shelf-time of having improved fertilizer.The performance that product of the present invention can reach: after in organic materials, adding product of the present invention, can make product except that having good strength property, also have water-retentivity, to the oxidation-resistance of ammonia nitrogen, to the physiological activity of plant.After adding product of the present invention plant is had no side effect.The index of product of the present invention: 1, grey pulverulent solids; 2, PH: scope 6.0~8.0; 3, arsenic≤30 (mg/Kg); 4, lead≤60 (mg/Kg); 5, mercury≤5 (mg/Kg); 6, chromium≤70 (mg/Kg); 7, cadmium≤3 (mg/Kg).
Embodiment one: present embodiment is made up of the raw material of following parts by weight: 2.5~3 parts of W-Gums, 2.5~3 parts of tapioca (flour)s, 2.5~3.5 parts of industry trisodium phosphates, 2.5~3.5 parts in hydrogen peroxide, 5~7 parts of weathered coals, 1~1.5 part in potassium hydroxide, 5~7 parts of wilkinites, 1~1.5 part of sodium bicarbonate, 0.5~1 part in bicarbonate of ammonia, 1.5~3.3 parts of polyvinyl alcohol.
Embodiment two: the shared parts by weight of each raw material are in the present embodiment: 2.55~2.65 parts of W-Gums, 2.55~2.65 parts of tapioca (flour)s, 2.6~2.8 parts of industry trisodium phosphates, 2.6~2.8 parts in hydrogen peroxide, 5.2~5.6 parts of weathered coals, 1.1~1.2 parts in potassium hydroxide, 5.2~5.6 parts of wilkinites, 1.1~1.2 parts of sodium bicarbonates, 0.55~0.65 part in bicarbonate of ammonia, 1.6~2.0 parts of polyvinyl alcohol.
Embodiment three: the shared parts by weight of each raw material are in the present embodiment: 2.7~2.8 parts of W-Gums, 2.7~2.8 parts of tapioca (flour)s, 2.9~3.1 parts of industry trisodium phosphates, 2.9~3.1 parts in hydrogen peroxide, 5.7~6.3 parts of weathered coals, 1.25~1.4 parts in potassium hydroxide, 5.7~6.3 parts of wilkinites, 1.25~1.35 parts of sodium bicarbonates, 0.7~0.8 part in bicarbonate of ammonia, 2.2~2.7 parts of polyvinyl alcohol.
Embodiment four: present embodiment is that the shared parts by weight of each raw material are: 2.85~2.95 parts of W-Gums, 2.85~2.95 parts of tapioca (flour)s, 3.2~3.4 parts of industry trisodium phosphates, 3.2~3.4 parts in hydrogen peroxide, 6.4~6.8 parts of weathered coals, 1.42~1.48 parts in potassium hydroxide, 6.4~6.8 parts of wilkinites, 1.4~1.45 parts of sodium bicarbonates, 0.85~0.95 part in bicarbonate of ammonia, 2.8~3.2 parts of polyvinyl alcohol.
Embodiment five: 2.5~3 parts of W-Gums, 2.5~3 portions of tapioca (flour)s, 2.5~3.5 parts of industrial trisodium phosphates and 2.5~3.5 parts of hydrogen peroxide added react after 1.5~2 parts water mixes, wash after the reaction, dry, the A material; 5~7 parts of weathered coals, 1~1.5 part of potassium hydroxide are carried out hybrid reaction after adding 3~3.5 parts of water, get the B material; 5~7 parts of wilkinites, 1~15 part of sodium bicarbonate, 0.5~1 part of bicarbonate of ammonia are reacted after adding 3.5~4 parts of water, wash after the reaction, dewater, get the C material; 1.5~3.3 parts of polyvinyl alcohol are the D material; With above-mentioned A material 0.5kg, B material 1.0kg, C material 1.0kg, D material 0.3kg, grass meal 100kg, humic acids ore deposit 20kg, water 10~20ml.To puddle in the above-mentioned material adding mixer, the residence time of material in mixer is 5-10 minute; To puddle uniform material then enters and carries out the extruding type granulation in the tablets press and get final product; The material of granulating and forming dried by drying production line just make fertilizer.
Embodiment six: present embodiment and embodiment five differences are; to puddle in above-mentioned A material 0.5kg, B material 1.0kg, C material 1.0kg, D material 0.5kg, chicken manure 100kg, the humic acids ore deposit 20kg adding mixer; the residence time of material in mixer is 5-10 minute; to puddle uniform material then enters in disc type or the rotary drum granulator; spray an amount of water and granulate, the particle of granulating and forming is dried by drying production line just make fertilizer again.