CN1259593A - Prodn. method of potassium titanate whisker and fiber - Google Patents
Prodn. method of potassium titanate whisker and fiber Download PDFInfo
- Publication number
- CN1259593A CN1259593A CN 99114005 CN99114005A CN1259593A CN 1259593 A CN1259593 A CN 1259593A CN 99114005 CN99114005 CN 99114005 CN 99114005 A CN99114005 A CN 99114005A CN 1259593 A CN1259593 A CN 1259593A
- Authority
- CN
- China
- Prior art keywords
- raw material
- potassium titanate
- fiber
- water
- hours
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Method of mfg. potassium titanate whisker and fibe uses titanium compound and potassium containing compound as raw material, it is characterized in that: reaction precusor must contain amorphous titanium compound and water; before synthesis, evenly mixed raw material is piled into 0.1-3 cm layer, the raw material TiO2/K2O=1.5-4 (mol ratio) is mixed with water 20-80 wt.%, sinter under 800-1100 deg.C for 30 min. to 4 hr. hydrolyze to remove potassium, filter, crystallize. The whisker obtained by present invention is uniform in diameter, diameter d=0.2-1.5 micro meter, length l=20-100 micro meter.
Description
The present invention relates to the manufacture method of potassium titanate crystal whisker and fiber.
Potassium titanate crystal whisker and fiber are the very excellent matrix material fortifying fibres of a kind of performance, use K usually
2OnTiO
2Represent its composition, n=1,2,4,6,8, wherein with n=4,6, i.e. the practical value maximum of potassium tetratitanate and crystal whisker of hexa potassium titanate, potassium tetratitanate has good chemically reactive; Six potassium titanates have good mechanics and physicals, stable chemical property, excellent erosion resistance, heat-resisting thermal insulation, wear resistance, high electric insulating quality, also has the infrared reflectance height, thermal conductivity is extremely low under the high temperature, the characteristics that hardness is low, high molecular polymer, metal, ceramic and other composite material after it strengthens all are improved largely at aspects such as high temperature resistant, wear resistance, weathering resistance, mechanical properties.Particularly six potassium titanates are as the fortifying fibre of friction materials, and replacing strong carcinogens asbestos has avoided environmental pollution on the one hand; Improve frictional coefficient, the thermostability of friction materials on the other hand, improved security, had remarkable social benefit.Therefore the manufacturing of potassium titanate crystal whisker and fiber and application are subjected to extensive concern day by day.
The manufacture method of potassium titanate crystal whisker and fiber has a lot
(1,2), as sintering process
(3,4), flux method
(5), scorification, hydrothermal method etc.These methods respectively have relative merits.The crystal mass of hydrothermal method is good, but hypertonia is dangerous big, is not suitable for suitability for industrialized production; The yield height of flux method, good crystalline, but fusing assistant price height, circulation separation costs height, so production cost height; The temperature of reaction height of scorification, yield is low; Minimum, the whisker yield height of the cost of sintering process in all methods, so the most suitable industrialization of sintering process, but the disadvantage of this method is that the synthetic whisker is shorter, and only several microns, crystallinity is bad.Although the cost of sintering process is minimum in all methods in addition, also have a segment distance from the accessible price of large-scale application, its high cost has limited its further application.Therefore press for exploitation a kind of low cost, high quality and have the manufacturing process of the potassium titanate crystal whisker and the fiber of good composite performance.
The objective of the invention is to avoid above-mentioned the deficiencies in the prior art part and provide a kind of, not only relaxed reaction conditions by changing the reaction precursor body and adopting novel sintering processing; And, make fiber separate fibre, yield raising, the potassium titanate crystal whisker that the quality of what is more important whisker and flux method are suitable and the manufacture method of fiber easily because sinter is loose.
Purpose of the present invention can reach by following measure:
The manufacture method of a kind of potassium titanate crystal whisker and fiber is with titanium compound such as anatase titanium dioxide, rutile titanium dioxide etc. and potassium-containing compound such as KCl, KNO
3, K
2CO
3, KOH etc. is as raw material, it is characterized in that: the reaction precursor body must contain the amorphous compound (as hydrolyzed titanium dioxide, metatitanic acid, ilmenite, ilmenite concentrate etc.) and the water of titanium; Before synthetic the raw material that mixes is piled into the thin layer of thick 0.1～3cm; Technological process is:
---raw material is amounted to into TiO
2With K
2O presses TiO
2/ K
2O=1.5～4 (mol ratio) preparation back and the abundant mixing of water are pulp-like until no cluster of grains coalescence, and viscosity is 500～20000 centipoises, total water content 20～80% (wt%);
---raw material 800～1100 ℃ of temperature, was synthesized 30 minutes～4 hours;
---sintered product is immersed in 4～40 times the water 30 minutes～8 hours, 20～90 ℃ of water temperatures are the H of 0.1～6mol/L with concentration
2SO
4, HCl, HNO
3Add Deng mineral acid, impel K
+Leach, up to pH=7.5～12.5, and half an hour, interior pH changed less than 0.1～0.3, and immersion process is stirred, 50～800 rev/mins of mixing speed;
---filter;
---crystallization is handled, and dry thing is dry under 200 ℃-300 ℃, obtains containing the potassium titanate crystal whisker and the fiber of crystal water, and the residence time is 2 hours～5 hours; Perhaps with dry thing at 600 ℃ of-1000 ℃ of following sintering, obtain not having the potassium titanate crystal whisker and the fiber of crystal water, the residence time is 30 minutes～2 hours.
The product that the present invention makes both can be six potassium titanate K
2O6TiO
2, also can be six potassium titanate hydrate K
2O6TiO
2MH
2O (m=0～6).
Embodiment 1:
1. preparation of raw material: hydrolysis TiO
2, technical grade K
2CO
3(purity 99.5%wt%), KCl provide K to account for 3% (wt%), H
2O.Above-mentioned raw materials uniform mixing, wherein TiO
2/ K
2O=1.5 (mol than), moisture 70%, the viscosity of the material that mixes is 5000 centipoises; 2. the reaction mass that mixes evenly is applied to the aluminum oxide backing plate, thickness is 0.5cm, and temperature of reaction is 850 ℃, and the reaction times is 1 hour; 3. sintered product is put in 10 times 50 ℃ the water and soaks after 2 hours, with the H of 5mol/L
2SO
4Be titrated to pH=9.5, and pH changes less than 0.3 in 20 minutes.Cooperate in the above process and stir, stir speed (S.S.) is 400 rev/mins; 4. filter; 5. dry 150 ℃ * 2.5 hours; 6. crystallisation procedure does: 1000 ℃ * 2 hours.
Said process obtains crystal whisker of hexa potassium titanate, and diameter is 0.2～0.5 μ m, and length is 20～100 μ m.
Embodiment 2:
1. preparation of raw material: anatase titanium dioxide TiO
2, metatitanic acid (H
2TiO
3), technical grade K
2CO
3(99.5%wt%), KOH provides K to account for 5% (wt%), H
2O.Above-mentioned raw materials uniform mixing, wherein TiO
2/ K
2O=2.5 (mol than), moisture 45%, the viscosity of the material that mixes is 8500 centipoises; 2. the reaction mass that mixes evenly is applied to the aluminum oxide backing plate, thickness is 0.7cm, and temperature of reaction is 920 ℃, and the reaction times is 4 hours; 3. sintered product is put in 4 times 80 ℃ the water and soaks after 1 hour, with the H of 4mol/L
2SO
4Be titrated to pH=9.5, and change less than 0.3 in 20 minutes.Cooperate in the above process and stir, stir speed (S.S.) is 500 rev/mins; 4. filter; 5. crystallisation procedure does: 300 ℃ * 5 hours.
Said process obtains the hydrate of six potassium titanates, and diameter is 0.2～0.5 μ m, and length is 20～80 μ m.
Embodiment 3:
1. preparation of raw material: anatase titanium dioxide TiO
2, hydrolysis TiO
2, technical grade K
2CO
3(99.5%wt%).Above-mentioned raw materials uniform mixing, wherein TiO
2/ K
2O=3 (mol than), moisture 60%, the viscosity of the material that mixes is 7000 centipoises; 2. the reaction mass that mixes evenly is applied to the aluminum oxide backing plate, thickness is 0.9cm, and temperature of reaction is 1050 ℃, and the reaction times is 2 hours; 3. sintered product is put in 20 times 25 ℃ the water and soaks after 6 hours, with the H of 5mol/L
2SO
4Be titrated to pH=9.5, and pH changes less than 0.3 in 20 minutes.Cooperate in the above process and stir, stir speed (S.S.) is 500 rev/mins; 4. filter; 5. dry 170 ℃ * 2.5 hours; 6. crystallisation procedure does: 1000 ℃ * 2 hours.
Said process obtains crystal whisker of hexa potassium titanate, and diameter is 0.2～0.5 μ m, and length is 30～100 μ m.
Comparative example:
1. preparation of raw material: anatase titanium dioxide TiO
2, technical grade K
2CO
3(99.5%wt%), above-mentioned raw materials uniform mixing, wherein TiO
2/ K
2O=3 (mol ratio); 2. the high temperature sintering temperature is 1100 ℃, and the reaction times is 3 hours; 3. sintered product is put in 20 times 25 ℃ the water and soaks after 6 hours, with the H of 5mol/L
2SO
4Be titrated to pH=9.5, and change less than 0.3 in 20 minutes.Cooperate in the above process and stir, stir speed (S.S.) is 500 rev/mins; 4. filter; 5. dry 170 ℃ * 2.5 hours; 6. crystallisation procedure does: 1000 ℃ * 2 hours.
Said process obtains crystal whisker of hexa potassium titanate, and diameter is 0.5～1 μ m, and length is 10～30 μ m.
By embodiment and comparative example more as can be seen: the present invention is by changing the reaction precursor body and adopting novel sintering processing, and not only sintering temperature reduces, and reacts completely, yield improves; And make fiber separate fibre easily because sinter is loose; The quality of what is more important whisker is significantly improved, with flux method quite.The diameter of whiskers homogeneous that the present invention makes, fiber is elongated, diameter d=0.2～1.5 μ m, length l=20～100 μ m.Because the change of raw material, the manufacturing cost of potassium titanate crystal whisker of the present invention is lower, is suitable for large-scale industrialization production.
Reference
1, clear water discipline husband チ Application acid カ リ ゥ system fiber, chemical industry (day), 1980, (5), 87～92, (7), 104～108
2, red legendization, Ke Jiajun, novel inorganic whisker---potassium titanate crystal whisker, chemistry circular, 1994, (4): 5～10
3、JP63-260821
4、JP02-21460
5, Huai gift, Zhao Kuanfang, the preparation method of potassium titanate crystal whisker, CN1093760A
Claims (2)
1, the manufacture method of a kind of potassium titanate crystal whisker and fiber is with titanium compound such as anatase titanium dioxide, rutile titanium dioxide etc. and potassium-containing compound such as KCl, KNO
3, K
2CO
3, KOH etc. is as raw material, it is characterized in that: the reaction precursor body must contain the amorphous compound and the water of titanium; Before synthetic the raw material that mixes is piled into the thin layer of thick 0.1～3cm; Technological process is:
---raw material is pressed TiO
2/ K
2O=1.5～4 (mol ratio) preparation, compound moisture 20～80% mixes;
---raw material 800～1100 ℃ of temperature, was synthesized 30 minutes～4 hours;
---sintered product is immersed in 4～40 times the water 30 minutes～8 hours, 20～90 ℃ of water temperatures add mineral acid up to pH=7.5～12.5;
---filter;
---crystallization is handled.
2, the manufacture method of potassium titanate crystal whisker according to claim 1 and fiber, the amorphous compound that it is characterized in that titanium is hydrolyzed titanium dioxide, metatitanic acid, ilmenite, ilmenite concentrate.