CN1238315A - Process for producing powdered coal ash products as building material with boiler fume - Google Patents
Process for producing powdered coal ash products as building material with boiler fume Download PDFInfo
- Publication number
- CN1238315A CN1238315A CN99114911A CN99114911A CN1238315A CN 1238315 A CN1238315 A CN 1238315A CN 99114911 A CN99114911 A CN 99114911A CN 99114911 A CN99114911 A CN 99114911A CN 1238315 A CN1238315 A CN 1238315A
- Authority
- CN
- China
- Prior art keywords
- flue gas
- building material
- gas
- utilize
- kiln
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A process for making fly ash products as building material with boiler fume features that a by-pass piepline is arranged between boiler draught fan and chimney, the boiler fume is led out by draught fan for conditioning, and the conditioned fume is passed into curing kiln in which the building material products made up of slags, fly ash and lime (or calcium carbide dregs) are cured. The acidic gas in fume is adsorbed by said building material to neutralize its strong alkaline matter contained in it, and the afterheat and CO2 gas in fume are used to cure the building material for higher strength. Its advantages reasonable technology and low investment in equipment.
Description
The present invention relates to flue gas processing and flyash and comprehensive utilization of slag technology.
Will discharge a large amount of approximately flue gases during the coal firing boiler burning, discharge flyash and slag simultaneously, contain a large amount of sulfide in institute's discharged flue gas, obnoxious flavour and flue dust such as nitride work the mischief to surrounding environment; The accumulation serious environment pollution of a large amount of slags and flyash.Therefore all study it both at home and abroad and handle and the method for utilizing, so that turn harm into good, the protection environment.To the processing of flue gas desulfurization, prior art is because investment is big, the operative technique complexity, and maintenance cost height, and because gaseous constituent complexity in the flue gas, quantity discharged is big, economic benefit is not remarkable, the employing high chimney emission so general factory is how not treated.To the utilization of coal ash aspect, existing be used to produce pulverized fuel ash cement, steam-cured fly ash brick, fired fly ash brick also utilizes flyash to make the adulterant or the aggregate of some material of construction, also is used to build the road or the technology of agricultural improvement soil or the like.The applicant had once applied in nineteen ninety that " utilizing boiler smoke to produce the method for carbonized silicate building materials products " was also authorized, the patent No.: 90109430.7, this application has proposed to utilize boiler smoke to produce the method for carbonized silicate building materials products, solve some problems that prior art exists, obtained reasonable effect in actual applications; But some complexity of its technology, equipment is many, investment is big, uses maintenance inconvenient.
In order to overcome the deficiency of above-mentioned flue gas utilization and utilization of fly ash aspect, an object of the present invention is the treatment of wastes with processes of wastes against one another, turn harm into good, promptly with slag, flyash and lime (carbide slag) are main production raw material, make the building materials base substrate, place flue gas to handle curing kilns, utilize boiler smoke that the building material made base substrate is carried out maintenance, thereby make powdered coal ash products as building material, to reach the purpose of slag, flyash, smoke comprehensive utilization; Another object of the present invention is: the production method that provides will be simpler more than original technology, the structure of its production line more rationally, reduced investment, easy to use and maintenance.
The present invention constitutes like this: between boiler induced-draft fan (1) and chimney (2) bypass duct is set, utilize induced draft fan (3) that flue gas is drawn, to setter (4), send into the kiln tail that flue gas is handled curing kilns (5) again through the flue gas of regulating after handling, to in the kiln by slag, flyash, lime (or carbide slag) carries out maintenance for the building material made base substrate of main raw material, in maintenance processes, utilize highly basic material (the efficient oxidation calcium) in the base substrate to the CO2 in the flue gas, sour gas such as SO2 adsorb neutralizing treatment, simultaneously utilize CO2 gas and waste heat in the flue gas that base substrate is carried out maintenance again, to make building material made with certain intensity, tail gas is expelled to tail gas funnel (6) emptying from kiln hood, also utilize induced draft fan (3) that flue gas is drawn, to setter (4), send into the end that flue gas is handled curing kilns (5) again through the flue gas of regulating after handling, tail gas is expelled to tail gas funnel (6) emptying from the other end of kiln (5).
Accompanying drawing 1 is a process flow diagram of the present invention.
Compared with prior art, the present invention can be used for sulfur dioxide concentration less than 2% large and medium-sized Industrial Boiler The flue gas processing and utilizing and the comprehensive utilization of flyash, slag, can be used as two-stage dust removal and the desulfurization of boiler smoke Device, the present invention combines flue gas two-stage dust removal, desulfurization and flyash and the utilization of protecting slag together, reduced investment, Social benefit and remarkable in economical benefits; Be that No. 90109430.7 patents are compared with the patent No. particularly, its technology more Add rationally, equipment investment is few, use and maintenance is convenient, economic benefit is more obvious, has reached of the present invention Goal of the invention.
Embodiments of the invention:
Produce flyash standard brick: mainly adopt flyash, slag, lime (or carbide slag) is prepared burden for main raw material, proportioning is: flyash and slag: lime (or carbide slag)=70-85%: 30-15%, stir in adding water after this ratio batching, went into to digest warehousing 3-4 days, add the water stirring again and send into the brick pressing machine moulding, make the standard adobe, send into flue gas with dolly and handle curing kilns, flue gas is drawn from power plant with induced draft fan, to setter, utilize setter to regulate the humidity and the temperature of flue gas, send into flue gas processing curing kilns again, adobe was carried out maintenance 3-7 days through the flue gas of regulating after handling, promptly make finished product, sharp exhausted tail gas is from the tail gas funnel emptying.
Claims (2)
1, utilize boiler smoke to produce the method for powdered coal ash products as building material, it is characterized in that: between boiler induced-draft fan (1) and chimney (2), a bypass duct is set, utilize induced draft fan (3) that flue gas is drawn, to setter (4), send into the kiln tail that flue gas is handled curing kilns (5) again through the flue gas of regulating after handling, to in the kiln by slag, flyash, lime (or carbide slag) carries out maintenance for the building material made base substrate of main raw material, in maintenance processes, utilize highly basic material (the efficient oxidation calcium) in the base substrate to the CO2 in the flue gas, sour gas such as SO2 adsorb neutralizing treatment, simultaneously utilize CO2 gas and waste heat in the flue gas that base substrate is carried out maintenance again, to make the building material made with certain intensity, tail gas is expelled to tail gas funnel (6) emptying from kiln hood.
2, according to the described this method of utilizing boiler smoke to produce powdered coal ash products as building material of claim 1, it is characterized in that: utilize induced draft fan (3) with flue gas draw, to setter (4), send into the end that flue gas is handled curing kilns (5) again through the flue gas of regulating after handling, tail gas is expelled to tail gas funnel (6) emptying from the other end of kiln (5).