CN1233775C - 一种用于融化雪和冰的组合物 - Google Patents
一种用于融化雪和冰的组合物 Download PDFInfo
- Publication number
- CN1233775C CN1233775C CN 03153230 CN03153230A CN1233775C CN 1233775 C CN1233775 C CN 1233775C CN 03153230 CN03153230 CN 03153230 CN 03153230 A CN03153230 A CN 03153230A CN 1233775 C CN1233775 C CN 1233775C
- Authority
- CN
- China
- Prior art keywords
- ice
- snow
- melt
- weight part
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种用于融化雪和冰的组合物,包括40-70重量份乙二醇,5-20重量份醋酸钠和0.5-3重量份硝酸盐。将上述组分与适量水混合即可制备融雪和融冰产品。由本发明的组合物获得的融雪或融冰产品具有融雪、融冰迅速,无腐蚀等优点,克服了传统融雪融冰剂对路面的腐蚀作用,以及不能有效消除目前机动车辆由于路面光滑而造成的交通事故和道路封闭等缺点。
Description
发明领域
本发明涉及一种用于融化雪和冰的组合物,由该组合物获得的融雪或融冰产品及制备方法,尤其是用于融化机动车行车道路、街道、人行道等之上的雪和冰的组合物,由该组合物获得的融雪或融冰产品及制备方法。
背景技术
北方地区冬季气温低于零度的持续时间较长,下雪后机动车辆行驶的道路或街道路面非常光滑,车辆行驶制动转向易于失控,特别是弯道坡道处及长年不见太阳的背阴路段,交通事故在所难免,人民生命财产受到极大危害,严重时造成道路封闭,中断交通,直接影响国民经济建设。
因此,对冬季公路和街道下雪后的车辆安全行驶所需的融雪或融冰产品存在着迫切的需求。
发明内容
本发明的目的是提供一种用于融化雪和冰的组合物。由本发明的组合物获得的融雪或融冰产品具有融雪、融冰迅速,无腐蚀等优点,克服了传统融雪融冰剂对路面的腐蚀作用,以及不能有效消除目前机动车辆由于路面光滑而造成的交通事故和道路封闭等缺点。
本发明的组合物包括以下组分:
乙二醇 40-70重量份
醋酸钠 5-20重量份
硝酸盐 0.5-3重量份。
本发明的组合物优选包括:
乙二醇 50-60重量份
醋酸钠 8-15重量份
硝酸盐 1-2重量份。
其中所述硝酸盐优选是硝酸铵或硝酸钠,其中硝酸铵是更为优选的。
醋酸钠和硝酸盐可以用其水合物代替,水合物的用量应使得它的盐的重量(不包括水分子的重量)是在上述范围内。
本发明还提供了制备融雪或融冰产品的方法,包括将5-20重量份醋酸钠和0.5-3重量份硝酸盐溶入20-40重量份,优选约23-35重量份的水中,再加入40-70重量份乙二醇,均匀混合。
本发明的融雪或融冰产品还可以简单地通过将40-70重量份乙二醇,5-20重量份醋酸钠和0.5-3重量份硝酸盐与20-40重量份,优选约23-35重量份的水中均匀混合来制备。
混合容器可以是任意容器,例如塑料桶或铁制桶,搅拌棒可以是任意材质的。例如用铁制桶混合,木棒为搅拌棒搅拌混合。如用带搅拌的反应釜作为制备容器则更为方便。
本发明另外提供了由上述组合物获得融雪或融冰产品。本发明的产品为液态水溶液。
乙二醇还可以使用其各种浓度的水溶液,但应使得最终产品中的水含量是在上述配比范围内,即在水含量低于20重量份的情况下,加入适量水,在水含量高于40重量份的情况下,去除一部分水。
使用由乙二醇为主要原料的水溶液产品,洒于路面雪或冰表面,立即开始融化,融化后的液体流入路边边沟,或辅助以人工扫入路边边沟或下水道内。
选无毒无味的乙二醇,是利用其能大幅度地降低水的冰点的作用(约-45℃),来达到融雪、融冰的目的。
为避免乙二醇微酸性腐蚀路面,加入适量醋酸钠,因其水解显弱碱性可达中和的目的。
加入适量盐,尤其硝酸铵,可起到与乙二醇协同降低水的冰点的作用。
同时,含硝酸铵的水溶液流入道路两旁,渗入绿化带,如春后可增加植物所需肥力,变“废”为宝,故为环保型产品。
上述原料均可从市场购得。
本发明还提供了上述融雪或融冰产品在路边或街道融雪或融冰领域中的应用。
使用时,将上述产品直接均匀地喷洒在雪或冰的表面,喷洒量视雪或冰的堆积厚度和密实程度而定,堆积厚度厚密实性大时,可加大喷洒量,反之亦然。该用量可以通过工作人员的实践或经验来确定。
融雪或融冰剂喷洒后,立即看到雪或冰融为水或水雪,水冰混合物的可流动体。若此流动体较厚不易自然流入边沟下水道时,可借助人力用硬扫帚扫入路边。坡道路面不存在此现象。
本发明具有以下优点和效果:
(1)原料廉价易得;
(2)融雪和融冰效果优良;
(3)使用及加工方法简单;
(4)无毒无味、无腐蚀性,不污染环境,不腐蚀水泥、沥青道路或街道表面,也不腐蚀车辆轮胎;
(5)不影响土壤结构;
(6)与传统的同类型融雪融冰产品相比,最大的不同特点是:充分考虑控制产品自身的酸碱性;利用醋酸钠水解显碱性的特点,有效地中和主要原料乙二醇水溶液的弱酸性,使得产品水溶液十分接近中性,故属优良的环保型产品。
本发明的产品在陕西北部和内蒙古南部的部分路面,特别是弯道坡道路面、街道冬季融雪融冰使用,效果优良,深受交通部分欢迎。
实施例
以下通过实施例来进一步阐述本发明,应该理解的是,这些实施例仅用于例证的目的,决不对本发明的范围构成任何限制。
实施例1
将8kg的醋酸钠和1kg的硝酸铵溶于塑料大桶中的31.85kg的水中,用木棒搅拌溶解后,加入59.15kg的乙二醇,再用木棒搅拌混合均匀,制得本发明的融雪和融冰产品。
实施例2
将5kg的醋酸钠和0.5kg的硝酸铵溶于铁皮制大罐中的22.75kg的水中,用木棒搅拌溶解后,加入42.25kg的乙二醇,再用木棒搅拌混合均匀,制得本发明的融雪和融冰产品。
实施例3
将20kg的醋酸钠和3kg的硝酸铵溶于铁皮制大罐中的35kg的水中,用木棒搅拌溶解后,加入65kg的乙二醇,再用铁棒搅拌混合均匀,制得本发明的融雪和融冰产品。
实施例4
将13kg的醋酸钠和1.7kg的硝酸铵溶于带搅拌器的反应釜中的29.75kg的水中,搅拌溶解后,加入55.25kg的乙二醇,再用铁棒搅拌混合均匀,制得本发明的融雪和融冰产品。
实施例5
将8kg的醋酸钠和1kg的硝酸钠溶于塑料大桶中的31.85kg的水中,用木棒搅拌溶解后,加入59.15kg的乙二醇,再用木棒搅拌混合均匀,制得本发明的融雪和融冰产品。
实施例6
将5kg的醋酸钠和0.5kg的硝酸钠溶于铁皮制大罐中的22.75kg的水中,用木棒搅拌溶解后,加入42.25kg的乙二醇,再用木棒搅拌混合均匀,制得本发明的融雪和融冰产品。
实施例7
将20kg的醋酸钠和3kg的硝酸钠溶于铁皮制大罐中的35kg的水中,用木棒搅拌溶解后,加入65kg的乙二醇,再用铁棒搅拌混合均匀,制得本发明的融雪和融冰产品。
实施例8
将13kg的醋酸钠和1.7kg的硝酸钠溶于带搅拌器的反应釜中的29.75kg的水中,搅拌溶解后,加入55.25kg的乙二醇,再用铁棒搅拌混合均匀,制得本发明的融雪和融冰产品。
Claims (5)
1.一种用于融化雪和/或冰的组合物,其特征在于由以下组分组成:
乙二醇 40-70重量份
醋酸钠 5-20重量份
硝酸盐 0.5-3重量份
水 20-40重量份。
2.根据权利要求1所述的组合物,其特征在于:乙二醇为50-60重量份,醋酸钠为8-15重量份,硝酸盐为1-2重量份。
3.根据权利要求1或2所述的组合物,其中所述的硝酸盐选自硝酸铵或硝酸钠。
4.如权利要求1所述的组合物的制备方法,其特征在于将5-20重量份的醋酸钠和0.5-3重量份的硝酸盐溶于20-40重量份的水中,再加入40-70重量份的乙二醇,均匀混合。
5.如权利要求1-3任一项权利要求所述组合物在路面或街道融雪或融冰领域的应用。