CN1231614C - 电解铝用氧化亚铜基的金属陶瓷惰性阳极材料 - Google Patents

电解铝用氧化亚铜基的金属陶瓷惰性阳极材料 Download PDF

Info

Publication number
CN1231614C
CN1231614C CN 03132536 CN03132536A CN1231614C CN 1231614 C CN1231614 C CN 1231614C CN 03132536 CN03132536 CN 03132536 CN 03132536 A CN03132536 A CN 03132536A CN 1231614 C CN1231614 C CN 1231614C
Authority
CN
China
Prior art keywords
aluminium
anode material
present
inert anode
oxide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 03132536
Other languages
English (en)
Other versions
CN1482281A (zh
Inventor
邵文柱
甄良
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Harbin Institute of Technology
Original Assignee
Harbin Institute of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Harbin Institute of Technology filed Critical Harbin Institute of Technology
Priority to CN 03132536 priority Critical patent/CN1231614C/zh
Publication of CN1482281A publication Critical patent/CN1482281A/zh
Application granted granted Critical
Publication of CN1231614C publication Critical patent/CN1231614C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

电解铝用氧化亚铜基的金属陶瓷惰性阳极材料，它涉及电化学电解技术，具体涉及生产原生铝的惰性阳极材料的组合物。本发明由金属铜、三氧化二铝、氧化亚铜组成；各组份按重量百分比如下：铜15～30%、三氧化二铝≤30%、余量是氧化亚铜；本发明降低了阳极材料的腐蚀速率，并使阴极产物—铝中的杂质含量降至最低。具有在电解铝过程中能耗低、无环境污染、电极寿命长、材料导电性高、抗腐蚀性强、成本低、原生铝的纯度高的优点。

Description

电解铝用氧化亚铜基的金属陶瓷惰性阳极材料
技术领域：本发明涉及电化学电解技术，具体涉及生产原生铝的惰性阳极材料的组合物。
背景技术：目前国际上电解铝采用的碳——石墨阳极存在燃烧产物严重污染环境问题。霍尔——埃鲁电解法所用的是碳阳极，铝在阴极上析出，并在电解槽底部形成熔融物，阳极上析出的氧与阳极材料化合，挥发出CO2和CO(占50％)。废气中还含有致癌的多环碳氢化合物(如萘基苯并芘)，以及碳的氟化物。此外，阳极材料本身的生产过程也都产生大量有毒废物。无论是在电解过程中，还是在阳极材料预生产过程中，在产生大量有毒废物的同时，还会造成阳极材料的大量损耗，实际生产中，每生产一吨原生铝要消耗阳极材料550kg(占原生铝成本的10％以上)，这将造成极大的生态危害。
发明内容：本发明的目的是提供一种电解铝用氧化亚铜基的金属陶瓷惰性阳极材料，它具有在电解铝过程中能耗低、无环境污染、电极寿命长的特点。本发明由金属铜、三氧化二铝、氧化亚铜组成；各组份按重量百分比如下：铜15～30％、三氧化二铝≤30％、余量是氧化亚铜；各组份按重量百分比如下：铜15～20％、三氧化二铝5～25％、余量是氧化亚铜；各组份按重量百分比如下：铜15％、三氧化二铝15％、余量是氧化亚铜。本发明降低了阳极材料的腐蚀速率，并使阴极产物——铝中的杂质含量降至最低。它具有在电解铝过程中能耗低、无环境污染、电极寿命长、材料导电性高、抗腐蚀性强、成本低、原生铝的纯度高的优点。
具体实施方式：本实施方式由铜、三氧化二铝、氧化亚铜组成；各组份按重量百分比是：铜15％、三氧化二铝30％、氧化亚铜55％。本实施方式的制备方法是：利用粉末冶金法，将上述组分的粉末按百分比混合，然后将混合好的粉末压制成坯料再进行烧结，之后的复压主要是为提高它的密度，最终采用退火以消除应力和优化组织。

Claims (3)

1、电解铝用氧化亚铜基的金属陶瓷惰性阳极材料，其特征在于它由金属铜、三氧化二铝、氧化亚铜组成；各组份按重量百分比如下：铜15～30％、三氧化二铝≤30％、余量是氧化亚铜。
2、根据权利要求1所述的电解铝用氧化亚铜基的金属陶瓷惰性阳极材料，其特征在于阳极材料各组份按重量百分比如下：铜15～20％、三氧化二铝5～25％、余量是氧化亚铜。
3、根据权利要求1所述的电解铝用氧化亚铜基的金属陶瓷惰性阳极材料，其特征在于阳极材料各组份按重量百分比如下：铜15％、三氧化二铝15％、余量是氧化亚铜。
CN 03132536 2003-07-29 2003-07-29 电解铝用氧化亚铜基的金属陶瓷惰性阳极材料 Expired - Fee Related CN1231614C (zh)